Avaliação espectrofotométrica do manchamento de resinas odontológicas contendo nanopartículas

Composite resins have been subjected to structural modifications aiming at improved optical and mechanical properties. The present study consisted in an in vitro evaluation of the staining behavior of two nanohybrid resins (NH1 and NH2), a nanoparticulated resin (NP) and a microhybrid resin (MH). Samples of these materials were prepared and immersed in commonly ingested drinks, i.e., coffee, red wine and acai berry for periods of time varying from 1 to 60 days. Cylindrical samples of each resin were shaped using a metallic die and polymerized during 30 s both on the bottom and top of its disk. All samples were polished and immersed in the staining solutions. After 24 hours, three samples of each resin immersed in each solution were removed and placed in a spectrofotome ter for analysis. To that end, the samples were previously diluted in HCl at 50%. Tukey tests were carried out in the statistical analysis of the results. The results revealed that there was a clear difference in the staining behavior of each material. The nanoparticulated resin did not show better color stability compared to the microhybrid resin. Moreover, all resins stained with time. The degree of staining decreased in the sequence nanoparticulated, microhybrid, nanohybrid MH2 and MH1. Wine was the most aggressive drink followed by coffee and acai berry. SEM and image analysis revealed significant porosity on the surface of MH resin and relatively large pores on a NP sample. The NH2 resin was characterized by homogeneous dispersion of particles and limited porosity. Finally, the NH1 resin depicted the lowest porosity level. The results revealed that staining is likely related to the concentration of inorganic pa rticles and surface porosity

Análise da influência dos diferentes tempos de polimerização por luz incandescente sobre a resistência ao desgaste abrasivo de resinas compostas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microdureza de resinas em função da cor e luz halógena

O objetivo desse trabalho foi avaliar a influência da intensidade da luz e cor de uma resina composta no grau de dureza Knoop. Corpos-de-prova foram confeccionados utilizando-se matrizes de poliéster envoltas por um anel de cobre, contendo uma cavidade padronizada de 6 mm de diâmetro por 2 mm de espessura. Estas cavidades foram preenchidas com resina composta selecionada, Fill Magic - Vigodent, com as cores A3, B3, C3, D3 e I, fotopolimerizadas através de um fotopolimerizador Elipar, calibrado para produzir 3 intensidades de luz diferentes: 450 mW/cm², 800 mW/cm² e uma intensidade de luz crescente de 100 a 800 mW/cm². Foram confeccionados 90 corpos-de-prova em que o tempo de exposição da resina à luz halógena foi de 40 s. As amostras foram armazenadas em tubos de ensaio com água destilada a 37 ± 1ºC. Após este período, foram realizados os testes de dureza Knoop na região de superfície e fundo. Os resultados mostraram que houve diferença estatística em relação a intensidade de luz, entretanto em relação a cor, não houve diferença estatística. Os autores concluíram que a cor do compósito não influencia a dureza Knoop e que a intensidade progressiva promoveu os melhores resultados de dureza Knoop.

Adhesives with different pHs: Effect on the MTBS of chemically activated and light-activated composites to human dentin

Purpose: To evaluate the bond strength between human dentin and composites, using two light-activated single-bottle total-etch adhesive systems with different pHs combined with chemically activated and light-activated-composites. The tested hypothesis was that the dentin bond strength is not influenced by an adhesive system of low pH, combined with chemically activated or light-activated composites. Material and Method: Flat dentin surfaces of twenty-eight human third molars were allocated in 4 groups (n=7), depending on the adhesive system: (One Step Plus-OS and Prime & Bond NT-PB) and composite (light-activated Filtek Z-100 [Z100] and chemically activated Bisfil 2B [B2B]). Each adhesive system was applied on acid-etched dentin and then one of the composites was added to form a 5 mm-high resin block. The specimens were stored in tap water (37 degrees C/24 h) and sectioned into two axes, x and y. This was done with a diamond disk under coolant irrigation to obtain beams with a cross-section area of approximately 0.8 mm(2). Each specimen was then attached to a custom-made device and submitted to the microtensile test (1 mm.min(-1)). Data were analyzed using two-way ANOVA and Tukey's tests (p<0.05). Results: the anticipated hypothesis was not confirmed (p<0.0001). The bond strengths (MPa) were not statistically different between the two adhesive systems when light-activated composite was used (OS+Z100 = 24.7 +/- 7.1(a); PB+Z100 = 23.8 +/- 5.7(a)). However, with use of the chemically activated composite (B2B), PB (7.8 +/- 3.6(b) MPa) showed significantly lower dentin bond strengths than OS (32.2 +/- 7.6(a)). Conclusion: the low pH of the adhesive system can affect the bond of chemically activated composite to dentin. on the other hand, under the present conditions, the low pH did not seem to affect the bond of light-activated composites to dentin significantly.

Microleakage evaluation of pit and fissure sealants done with different procedures, materials, and laser after invasive technique

This study evaluated the microleakage of pit and fissure sealants after different surface preparation (invasive technique and laser irradiation) and the use of different materials (fluoride resin-filled sealant, resin-modified glass ionomer cement and adhesive system). Eighty-four pre molars were used in this study, which were divided into seven groups. After the accomplishment of the different treatments, these were submitted to thermocycling process and assess for microleakage by examination under an epifluorescent microscope and scored zero to seven. Two specimens of each group were observed under scanning electron microscope (SEM). The results showed that laser irradiation did not lessen microleakage in pit and fissures when using a filled-resin sealant with fluoride or a resin-modified glass ionomer cement. The use of laser irradiation and adhesive system, followed by a resin-filled sealant with fluoride, showed the lowest microleakage scores in pit and fissures. Comparing this group to the resin-modified glass ionomer cement group, there was statistical significance. The use of a adhesive system decreased microleakage when using a fluoride resin-filled sealant with or without previous laser irradiation; although it was not statistically significant.

Use of one-bottle adhesive as an intermediate bonding layer to reduce sealant microleakage on saliva-contaminated enamel

Purpose: To evaluate the influence of three different adhesives, each used as an intermediary layer, on microleakage of sealants applied under condition of salivary contamination. Materials and Methods: Six different experimental conditions were compared, 3 with adhesives and 3 without. After prophylaxis and acid etching of enamel, salivary contamination was placed for 10 s. In Group SC the sealant was applied after saliva without bonding agent and then light-cured. In Group SCA, after saliva, the surface was air dried, and then the sealant was applied and cured. In Groups ScB, SB and PB, a bonding agent (Scotchbond Dual Cure/3M, Single Bond/3M and Prime & Bond 2.1/Dentsply, respectively) was applied after the saliva and prior to the sealant application and curing. After storage in distilled water at 37°C for 24 hrs, the teeth were submitted to 500 thermal cycles (5°C and 55°C), and silver nitrate was used as a leakage tracer. Leakage data were collected on cross sections as percentage of total enamel-sealant interface length. Representative samples were evaluated under SEM. Results: Sealants placed on contaminated enamel with no bonding agent showed extensive microleakage (94.27% in SC; 42.65% in SCA). The SEM revealed gaps as wide as 20 μm in areas where silver nitrate leakage could be visualized. In contrast, all bonding agent groups showed leakage less than 6.9%. Placement of sealant with a dentin-bonding agent on contaminated enamel significantly reduced microleakage (P< 0.0001). The use of a bonding agent as an intermediary layer between enamel and sealant significantly reduced saliva's effect on sealant microleakage.

Effect of different dye solutions on the evaluation of the sealing ability of Mineral Trioxide Aggregate.

Alkaline materials have shown incompatibility with methylene blue dye in leakage experiments. The goal of the present study was to analyze the effect of different dyes on the evaluation of the apical sealing ability of Mineral Trioxide Aggregate root-end fillings. Fifty-six extracted human canines were submitted to root canal instrumentation and obturation. After apical resection, retrograde cavities were prepared and teeth were randomly divided into four experimental (n = 13) and two control groups (n = 2). The following root-end filling materials were used: groups 1 and 2--Pro Root MTA (Dentsply), groups 3 and 4--zinc oxide-eugenol cement (ZOE). Teeth in groups 1 and 3 were immersed in 2% methylene blue solution, while teeth in groups 2 and 4 were immersed in 0.2% rhodamine B in a reduced pressure environment for 48 hours. Teeth were then longitudinally sectioned and leakage was evaluated. Results were submitted to statistical analysis (ANOVA and Tukey's test). Group 1 presented the least leakage (p < 0.05). It was concluded that the evaluation of the sealing ability of MTA is influenced by the dye used, since this material presented better sealing ability when evaluated with Methylene Blue, but was similar to ZOE when evaluated with rhodamine B.

In vitro evaluation of apical microleakage using different root-end filling materials

The objective of this study was to evaluate the apical leakage of retrograde cavities filled with Portland Cement (Concrebrás S/A-MG-Brazil), ProRoot MTA™ (Dentsply International, Johnson City, TN, USA) and Sealapex (Kerr Corporation, Orange, California, USA) with addition of zinc oxide (Odahcam Herpo Produtos Dentários Ltda, Rio de Janeiro, RJ, Brazil). Forty-two extracted single-rooted human teeth were decoronated and used for this study. The root canals were instrumented at 1.0mm short of the apical foramen using the step-back technique to an apical ISO size 60. The roots were obturated with gutta-percha points and sealer Sealapex (Kerr Corporation-USA) and then 3mm of each root apex was sectioned at a 90° angle. Ultrasonic retrograde preparation was performed with a diamond tip to 3mm depth and the roots were randomly divided into 3 groups according to the filling material: G1-Portland, G2-ProRoot MTA, G3- Sealapex zinc oxide-added cement. The root surfaces were covered with nail varnish up to 2mm from the apical foramen, immersed in simulated tissue fluid for 30 days, and then immersed in 0.2% Rhodamine B solution for 24 hours for evaluation of marginal leakage. The results showed mean leakage of 0.75, 0.35 and 0.35 for groups 1, 2 and 3, respectively; however, Kruskal-Wallis test revealed that there was no statistically significant difference among the results (p>0.05).

Effect of microwave disinfection procedures on torsional bond strengths of two hard chairside denture reline materials

Purpose: This study evaluated the potential effects of denture base resin water storage time and an effective denture disinfection method (microwave irradiation at 650 W for 6 minutes) on the torsional bond strength between two hard chairside reline resins (GC Reline and New Truliner) and one heat-polymerizing denture base acrylic resin (Lucitone 199). Materials and Methods: Cylindrical (30 x 3.9 mm) denture base specimens (n = 160) were stored in water at 37°C (2 or 30 days) before bonding. A section (3.0 mm) was removed from the center of the specimens, surfaces prepared, and the reline materials packed into the space. After polymerization, specimens were divided into four groups (n = 10): Group 1 (G1) - tests performed after bonding; Group 2 (G2) - specimens immersed in water (200 ml) and irradiated twice (650 W for 6 minutes); Group 3 (G3) - specimens irradiated daily until seven cycles of disinfection; Group 4 (G4) - specimens immersed in water (37°C) for 7 days. Specimens were submitted to a torsional test (0.1 Nm/min), and the torsional strengths (MPa) and the mode of failure were recorded. Data from each reline material were analyzed by a two-way analysis of variance, followed by Neuman-Keuls test (p = 0.05). Results: For both Lucitone 199 water storage periods, before bonding to GC Reline resin, the mean torsional strengths of G2 (2 days - 138 MPa; 30 days - 132 MPa), G3 (2 days - 126 MPa; 30 days - 130 MPa), and G4 (2 days - 130 MPa; 30 days - 137 MPa) were significantly higher (p < 0.05) than G1 (2 days - 108 MPa; 30 days - 115 MPa). Similar results were found for Lucitone 199 specimens bonded to New Truliner resin, with G1 specimens (2 days - 73 MPa; 30 days - 71 MPa) exhibiting significantly lower mean torsional bond strength (p < 0.05) than G2 (2 day - 86 MPa; 30 days - 90 MPa), G3 (2 days - 82 MPa; 30 days - 82 MPa), and G4 specimens (2 days - 78 MPa; 30 days - 79 MPa). The adhesion of both materials was not affected by water storage time of Lucitone 199 (p > 0.05). GC reline showed a mixed mode of failure (adhesive/cohesive) and New Truliner failed adhesively. Conclusions: Up to seven microwave disinfection cycles did not decrease the torsional bond strengths between the hard reline resins, GC Reline and New Truliner to the denture base resin Lucitone 199. The effect of additional disinfection cycles on reline material may be clinically significant and requires further study. Copyright © 2006 by The American College of Prosthodontists.

Measurement of sealant surface area by clinical/computerized analysis: 11-year results.

OBJECTIVE: To analyze the clinical behavior of 2 pit and fissure sealants through clinical/computerized evaluation. METHOD AND MATERIALS: Occlusal sealants were placed on maxillary and mandibular first and second premolars according to a split-mouth design. All premolars were sealed with either Concise (3M Espe) or Prisma Shield (Caulk/Dentsply) sealant agents. A hematoxylin-based staining solution was applied on the occlusal surface 7 days, 18 months, 36 months, and 11 years after occlusal sealing to allow checking of the sealant material on the surface. At each analysis time all occlusal surfaces were photographed, and the photographs corresponding to each time period were analyzed with SigmaScan 4.0 Software. The alterations of the sealed area of each sealant were analyzed with the software and recorded. Next, the measurements of the areas were tabulated and analyzed according to each period. Analysis of variance (ANOVA), with parts subdivided into time, and the t test, with a significance level of 5%, were used. RESULTS: The greatest sealed area was maintained by the sealant Concise. However, over the course of 11 years, all sealants began to show the same level of alteration in sealed area. CONCLUSION: The sealing materials showed alteration in sealed area over time, but they were efficient in controlling caries lesion formation on premolar pits and fissures.

Periapical tissue healing after post space preparation with or without use of a protection plug and root canal exposure to the oral environment. Study in dogs

The purpose of this study was to evaluate the influence of coronal leakage on the healing of dogs' periapical tissues after root canal filling, post space preparation and protection or not with a temporary sealer plug. Forty root canals of dogs' teeth were instrumented and filled by the lateral condensation technique with gutta-percha points and Endomethasone or CRCS sealers. After post space preparation, the remaining filling material was protected or not with a plug of temporary Coltosol sealer and exposed to the oral environment for 90 days. Thereafter, the animals were sacrificed and the specimens were removed and prepared for histomorphological and histobacteriological analysis. The findings revealed 35% of microbial leakage in the groups without plugs and 15% of leakage in the groups with plugs. Statistical analysis showed that the use of a Coltosol plug improved significantly the histomorphological results regardless of the type of root canal sealer (p=0.05) and that CRCS and Endomethasone sealers showed similar results (p>0.05).

Influence of microwave polymerization method and thickness on porosity of acrylic resin

Purpose: This study evaluated the influence of polymerization cycle and thickness of maxillary complete denture bases on the porosity of acrylic resin. Materials and Methods: Two heat-activated denture base resins - one conventional (Clássico) and one designed for microwave polymerization (Onda-Cryl) - were used. Four groups were established, according to polymerization cycles: A (Onda-Cryl, short microwave cycle), B (Onda-Cryl, long microwave cycle), C (Onda-Cryl, manufacturing microwave cycle), and T (Clássico, water bath). Porosity was evaluated for different thicknesses (2.0, 3.5, and 5.0 mm; thicknesses I, II, and III, respectively) by measurement of the specimen volume before and after its immersion in water. The percent porosity data were submitted to Kruskal-Wallis for comparison among the groups. Results: The Kruskal-Wallis test detected that the combinations of the different cycles and thicknesses showed significant differences, and the mean ranks of percent porosity showed differences only in the thinnest (2.0 mm) microwave-polymerized specimens (A = 53.55, B = 40.80, and C = 90.70). Thickness did not affect the results for cycle T (I = 96.15, II = 70.20, and III = 82.70), because porosity values were similar in the three thicknesses. Conclusions: Microwave polymerization cycles and the specimen thickness of acrylic resin influenced porosity. Porosity differences were not observed in the polymerized resin bases in the water bath cycle for any thickness. © 2007 by The American College of Prosthodontists.

Effectiveness of six different disinfectants on removing five microbial species and effects on the topographic characteristics of acrylic resin

Purpose: The aim of this study was to evaluate the effectiveness of disinfectant solutions (1% sodium hypochlorite, 2% chlorhexidine digluconate, 2% glutaraldehyde, 100% vinegar, tabs of sodium perborate-based denture cleanser, and 3.8% sodium perborate) in the disinfection of acrylic resin specimens (n = 10/group) contaminated in vitro by Candida albicans, Streptococcus mutans, S. aureus, Escherichia coli, or Bacillus subtilis as measured by residual colony-forming unit (CFU). In a separate experiment, acrylic resin was treated with disinfectants to monitor potential effects on surface roughness, Ra (μm), which might facilitate microbial adherence. Materials and Methods: Three hundred fifty acrylic resin specimens contaminated in vitro with 1×10 6 cells/ml suspensions of standard strains of the cited microorganisms were immersed in the disinfectants for 10 minutes; the control group was not submitted to any disinfection process. Final counts of microorganisms per ml were performed by plating method for the evaluation of microbial level reduction. Results were compared statistically by ANOVA and Tukey's test (p ≤ 0.05). In a parallel study aiming to evaluate the effect of the tested disinfectant on resin surface, 60 specimens were analyzed in a digital rugosimeter before and after ten cycles of 10-minute immersion in the disinfectants. Measurements of superficial roughness, Ra (μm), were compared statistically by paired t-test (p ≤ 0.05). Results: The results showed that 1% sodium hypochlorite, 2% glutaraldehyde, and 2% chlorhexidine digluconate were most effective against the analyzed microorganisms, followed by 100% vinegar, 3.8% sodium perborate, and tabs of sodium perborate-based denture cleanser. Superficial roughness of the specimens was higher after disinfection cycles with 3.8% sodium perborate (p = 0.03) and lower after the cycles with 2% chlorhexidine digluconate (p = 0.04). Conclusion: Within the limits of this experiment, it could be concluded that 1% sodium hypochlorite, 2% glutaraldehyde, 2% chlorexidine, 100% vinegar, and 3.8% sodium perborate are valid alternatives for the disinfection of acrylic resin. © 2008 by The American College of Prosthodontists.

Influence of storage period and effect of different brands of acrylic resin on the dimensional accuracy of the maxillary denture base

The aim of this study was to evaluate the dimensional changes of denture bases made from different resins after different storage periods. For this purpose, 25 sets of plaster models/resin bases were prepared using 4 acrylic resins submitted to two types of polymerization: 1- QC-20 submitted to polymerization by microwave energy; 2- QC-20 submitted to polymerization by water hot bath; 3- Vipi Cril submitted to polymerization by water hot bath; 4- Vipi Wave submitted to polymerization by microwave energy; and 5- Onda Cryl submitted to polymerization by microwave energy. After polymerization, the specimens were sectioned for accuracy readings using a comparison microscope. Readings were taken at 3 points: the crests of the right (A) and left (B) ridges, and the median region of the palate, in 4 different periods. The data obtained were submitted to two-way ANOVA and Tukey's test at 5% significance level. The greatest distortions were found in the posterior palatal region of the base (M), with statistically significant difference (p<0.05) for the studied resins. All acrylic resins presented dimensional changes and the storage period influenced these alterations.

Influência dos agentes clareadores na microdureza de resina composta nanoparticulada

Objective: To assess the effect of bleaching agents on the microhardness of nanoparticle resin composite. Methods: Twenty-eight cylindrical test specimens (8× 1mm) of Filtek™ Supreme XT resin (3M/ESPE) were prepared and divided into 5 groups. The initial Vickers microhardness was measured (load of 50 grams force for 30 seconds) on the top surface of the test specimens. The groups were treated and divided as follows: G1 - artificial saliva (21 days - control); G2 - 7% hydrogen peroxide gel applied for 4h/day, for 14 days; G3 - 10% carbamide peroxide for 4h/day, for 14 days: G4 - 35% hydrogen peroxide gel applied in three sessions of 30 minutes each, with an interval of one week (21 days) between the sessions; G5 - 35% carbamide peroxide, three sessions of 30 minutes each, with an interval of one week (21 days) between the sessions. The top surfaces of the test specimens received treatment and were submitted to the Vickers microhardness test. Results: The results obtained were submitted to the Analysis of Variance at a fixed criterion, at a level of significance of p=0.05. No significant differences were observed among the treatments tested (p=0.42) when compared with G1. Significant differences (Tukey test) were found when the initial microhardness values were compared with the values after experimental treatments (p<0.01). Conclusion: The application of bleaching agents did not alter the microhardness of resin composites. Therefore, there is no need to change restorations after bleaching.