Effects of substrate temperature on the microstructure of YBa2Cu3O7-δ films grown on (001) Y-ZrO2 substrates

High-quality YBa2Cu3O7-δ films grown on (001) single-crystal Y-ZrO2 substrates by pulsed laser deposition have been studied as a function of substrate temperature using transmission electron microscopy. A transition from epitaxial films to c-axis oriented polycrystalline films was observed at 740°C. An intermediate, polycrystalline, BaZrO3 layer was formed from a reaction between the film and the substrate. A dominant orientation relationship of [001] YBCO//[001]int. layer//[001]YSZ and [110] YBCO//[110]int. layer//[100]YSZ was observed. The formation of grain boundaries in the films resulted in an increased microwave surface resistance and a decreased critical-current density. The superconducting transition temperature remained fairly constant at about 90 K.

Early stages of growth of YBa2Cu3O7-δ high Tc superconducting films on (001) Y-ZrO2 substrates

The early stages of growth of high quality YBa2Cu 3O7-δ (YBCO) films grown on (001) Y-ZrO2 (YSZ) substrates by pulsed laser deposition have been studied using a combination of atomic force microscopy and transmission electron microscopy. A one unit cell thick YBCO layer and relatively large CuO particles formed in the initial stages. Additional YBCO grew on top of the first layer in the form of one or a few unit cell high c-axis oriented islands about 30 nm in diameter. The rounded islands subsequently coalesced into faceted domains. Elongated Y 2BaCuO5 particles nucleated after the first layer of YBCO. A highly textured BaZrO3 layer formed between the YSZ and the YBCO with a cube-on-cube dominant orientation relationship with respect to the YBCO film.

Microstructure of an artificial grain boundary weak link in an YBa2Cu3O(7-δ) thin film grown on a (100)(110), [001]-tilt Y-ZrO2 bicrystal

The microstructure of an artificial grain boundary in an YBa2Cu3O7-δ (YBCO) thin film grown on a (100)(110), [001]-tilt yttria-stabilized-zirconia (YSZ) bicrystal substrate has been studied using transmission electron microscopy (TEM). The orientation relationship between the YBCO film and the YSZ substrate was [001]YBCO∥[001]YSZ and [110]YBCO∥[100]YSZ for each half of the bicrystal film. However, the exact boundary geometry of the bicrystal substrate was not transferred to the film. The substrate boundary was straight while the film boundary was wavy. In several cases there was bending of the lattice confined within a distance of a few basal-plane lattice spacings from the boundary plane and microfaceting. No intergranular secondary phase was observed but about 25% of the boundary was covered by c-axis-tilted YBCO grains and a-axis-oriented grains, both of which were typically adjacent to CuO grains or surrounded by a thin Cu-rich amorphous layer.

Comments on the phase diagrams and crystallisation paths of Y-Ba-Cu-O materials

Our micro structural characterisation of Y-Ba-Cu-O quenched partial melts shows that the BaCuO2 (BC1) phase is crystalline at temperatures as high as 1100°C, and that the partial melt self-establishes a micro structural gradient from the surface towards the interior of the samples, which can be associated with a gradient in an equivalent partial pressure of O2 (pO2). The extension of the Y2BaCuO5-YBa2Cu3O7-x (Y211-Y123) tie-line intersects the primary crystallisation field of BC1 first. The actual peritectic reaction that takes place is Y2BaCuO5(s) + BaCuO2(s) + 2BaCu2O2(L) + 1/2O2 → 2YBa2Cu3O6(s). Two schematic representations which allow an analysis of the pO2 dependence are given. The gradient in micro structure self-established by the sample acts as a driving force for texturing. With this new perspective gained about the actual peritectic reaction and mechanisms of melt-texturing of Y123, it is possible to explain most of the aspects about partial melt-texturing. In addition, it seems possible to devise heat treatments that may allow for the production of well-oriented single domains with very large diameters. © 1999 Elsevier Science B.V.

Observation of exsolution textures within Ba-Cu-O-rich solidified melts of Y-Ba-Cu-O materials and their relationship to Y123 nucleation and texturing

Layers (about 60-100 μm thick) of almost pure BaCuO2 (BC1), as determined using X-ray diffractometry (XRD) and scanning electron microscopy (SEM), coat the surfaces of YBa2Cu3O7-x (Y123) samples partial melt processed using a single-zone vertical furnace. The actual Cu/Ba ratio of the BC1 phase is 1.2-1.3 as determined using energy dispersive X-ray spectrometry (EDS). The nominally BC1 phase displays an exsolution of BC1.5 or BC2 in the form of thin plates (about 50-100 nm thick) along {100}-type cleavage planes or facets. The exsolved phase also fills cracks within the BC1 layer that require it to be in a molten state at some stage of processing. The samples were influenced by Pt contamination from the supporting wire, which may have stabilised the BC1.5 phase. Many of the Y123 grains have the same morphology as the exsolution domains, and run nearly parallel to the thin plates of the exsolved phases, strongly indicating that Y123 nucleation took place at the interface between the BC1 and the BC1.5 or BC2 exsolved phases. The network of nearly parallel exsolved 'channels' provides a matrix and a mechanism through which a high degree of local texture can be initiated in the material.

Growth and properties of a multilayer system based on Y1Ba 2Cu3Ox and amorphous Y-ZrO2

The growth of c-axis oriented Y1Ba2Cu 3Ox thin films on an amorphous buffer layer of Y-ZrO 2, deposited on sapphire substrates, was investigated. Both films were grown by a pulsed laser deposition technique. A strong correlation was observed between the properties of Y1Ba2Cu 3Ox and the thickness of the buffer layer. A Tc of 89 K was obtained for an optimal buffer layer thickness of 9 nm. A model that adequately describes the film growth process was developed. A multilayer system of Y1Ba2Cu3Ox and amorphous Y-ZrO2 was grown and a Tc of 87 K for the upper c-axis oriented layer was measured.

Properties of artificial grain boundary weak links grown on Y-ZrO 2 bicrystals

Weak links were fabricated by pulsed laser deposition of YBa 2Cu3Ox thin films on Y-ZrO2 bicrystal substrates. They were formed by transferring the bicrystal boundary into the epitaxial film during the film growth. Their properties were determined by the misorientation angle ( theta ) between the two halves of the bicrystal. The transport properties of the weak links were studied as a function of theta and an exponential dependence of the weak link critical current density was observed for angles up to 45 degrees . Clear Josephson effects with good microwave and magnetic field response were observed.

Phase composition of the rapidly quenched melt of YBa2Cu3O7-y+20 mol% Y2BaCuO5

Samples of YBa2Cu3O7-y+20 mol% Y2BaCuO5, with thicknesses ranging between 50-250 μm, have been melt processed and rapidly quenched from temperatures between 985 and 1100°C by immersing them in liquid nitrogen. The phase composition and microstructures of these samples have been characterised using a combination of X-ray diffractometry, optical microscopy and scanning electron microscopy with energy dispersive X-ray spectroscopy. The quenched melt of samples quenched from temperatures greater than 985°C appears relatively homogeneous but consists of Ba2Cu3Ox (BC1.5) and BaCu2O2 (BC2) regions. At about 985°C, BaCuO2 (BC1) crystallises from the melt and most of the BC1.5 decomposes into BC1 and CuO or into BC1 and BC2. The crystallisation of BC1 induces segregation of elements in the melt and this is very significant for the melt texturing of YBCO.

Effects of PtO2 and CeO2 additives on the microstructures of the quenched melts of Y-Ba-Cu-O materials

The microstructures of the quenched melts of samples of Y123 and Y123+15-20 mol% Y211 with PtO2 and CeO2 additives have been examined with optical microscopy, Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectrometry (EDS) and X-ray Diffractometry (XRD). Significantly higher temperatures are required for the formation of dendritic or lamellar eutectic patterns throughout the samples with PtO2 and CeO2 additives as compared to samples without additives. The BaCuO2 (BCl) phase appears first in solid form and, instead of rapidly melting, is slowly dissolving or decomposing in the oxygen depleted melt. PtO2 and CeO2 additives slow down or shift to higher temperatures the dissolution or decomposition process of BCl. A larger fraction of BCl in solid form explains why samples with additives have higher viscosities and hence lower diffusivities than samples without additives. There is also a reduction in the Y solubility to about half the value in samples without additives. The mechanism that limits the Ostwald ripening of the Y211 particles is correlated to the morphology of the quenched partial melt. It is diffusion controlled for a finely mixed morphology and interface-controlled when the melt quenches into dendritic or lamellar eutectic patterns. The change in the morphology of the Y211 particles from blocky to acicular is related to an equivalent undercooling of the Y-Ba-Cu-O partial melt, particularly through the crystallization of BCl.

Phase evolution of the quenched melt of YBa2Cu3O7-y with 20 mol% Y2BaCuO5 additions

Samples of YBa2Cu3O7-y + 20 mol% Y2BaCuO5 have been melt processed and quenched from temperatures ranging from 975 to 1100°C. The microstructure of the samples have been characterized via a combination of x-ray diffractometry, optical microscopy, scanning electron microscopy, energy dispersive x-ray spectrometry and wavelength dispersive x-ray spectrometry. BaCuO2 (BC1) and BaCu2O2 (BC2) crystallize from the melt of samples quenched from temperatures between 985 and 1100°C in air. The average yttrium content differs for BC1 and BC2, and it is 4.3 and 5.1 at.%, respectively. Holding times of 20 hours at temperatures above or equal to 1040°C give rise to a dendritic pattern of BC1 surrounded by BC2. The complex changes of the nature of the melt as a function of temperature and time are likely to play a significant role in the mechanism of melt texturing.

Microstructure of epitaxial YBa2Cu3O7-δ thin films on (001)-tilt Y-ZrO2 bicrystals

The microstructures of the grain boundaries in epitaxial YBa2Cu3O7-δ thin films grown on [001]-tilt yttria-stabilized ZrO2 bicrystal substrates were characterized by TEM and at. force microscopy. The exact boundary plane geometries of the bicrystal substrates were not transferred to the films which instead had wiggling grain boundaries. [on SciFinder(R)]

The role of Y-box binding protein 1 in prostate cancer

This thesis examined the possible role of Y-box binding protein 1 (YBX1) in prostate cancer aggression and spread. Novel roles were uncovered for YBX1 in the regulation of several genes previously implicated in prostate cancer, as well as showing an effect for YBX1 in increasing tumour cell invasion and movement and reciprocal regulation of androgen-regulated gene networks. In addition, it was found that Y-box 1 regulated several other well-known cancer genes implicated in breast and other cancers. The work performed in this thesis has strengthened the foundations for pursuing YBX1 as a possible central target molecule in prostate cancer therapeutics.

Sexualities and sensitivities: Queer(y)ing the ethics of youth research in the field

In contemporary Western societies, the years between childhood and young adulthood are commonly understood to be (trans)formative in the reflexive project of sexual self-making (Russell et al. 2012). As sexual subjects in the making, youthful bodies, desires and sexual activities are often perceived as both volatile and vulnerable, thus subjected to instruction and discipline, protection and surveillance. Accordingly, young people’s sexual proximities are closely monitored by social institutions and ‘(hetero)normalising regimes’ (Warner 1999) for any signs that may compromise the end goal of development—a ‘normal’ reproductive heterosexual monogamous adult...

Proposing and developing a definition and conceptual framework for health care resilience to cope with disasters [Resiliencia: Propuesta y desarrollo de la definicion y del marco conceptual en relacion a los desastres en el ambito sanitario]

La creación del término resiliencia en salud es un paso importante hacia la construcción de comunidades más resilientes para afrontar mejor los desastres futuros. Hasta la fecha, sin embargo, parece que hay poca literatura sobre cómo el concepto de resiliencia en salud debe ser definido. Este artículo tiene como objetivo construir un enfoque de gestión de desastres de salud integral guiado por el concepto de resiliencia. Se realizaron busquedas en bases de datos electrónicas de salud para recuperar publicaciones críticas que pueden haber contribuido a los fines y objetivos de la investigación. Un total de 61 publicaciones se incluyeron en el análisis final de este documento, que se centraron en aquéllas que proporcionan una descripción completa de las teorías y definiciones de resiliencia ante los desastres y las que proponen una definición y un marco conceptual para la capacidad de resiliencia en salud. La resiliencia es una capacidad inherente de adaptación para hacer frente a la incertidumbre del futuro. Esto implica el uso de múltiples estrategias, un enfoque de riesgos máximos y tratar de lograr un resultado positivo a través de la vinculación y cooperación entre los distintos elementos de la comunidad. Resiliencia en salud puede definirse como la capacidad de las organizaciones de salud para resistir, absorber, y responder al impacto de los desastres, mientras mantiene las funciones esenciales y se recupera a su estado original o se adapta a un nuevo estado. Puede evaluarse por criterios como la robustez, la redundancia, el ingenio y la rapidez e incluye las dimensiones clave de la vulnerabilidad y la seguridad, los recursos y la preparación para casos de desastre, la continuidad de los servicios esenciales de salud, la recuperación y la adaptación. Este nuevo concepto define las capacidades en gestión de desastres de las organizaciones sanitarias, las tareas de gestión, actividades y resultados de desastres juntos en una visión de conjunto integral, y utiliza un enfoque integrado y con un objetivo alcanzable. Se necesita urgentemente investigación futura de su medición

Peer assisted learning and generation Y : a case study

In recent years Australian Law Schools have implemented various forms of peer assisted learning or mentoring, including career mentoring by former students of final year students and orientation mentoring or tutoring by later year students of incoming first year students. The focus of these programs therefore is on the transition into or out of law school. There is not always as great an emphasis however, as part of this transition, on the use of law students belonging to the same unit cohort as a learning resource for each other within their degree. This is despite the claimed preference of Generation Y students for collaborative learning environments, authentic learning experiences and the development of marketable workplace skills. In the workplace, be it professional legal practice or otherwise, colleagues rely heavily on each other for information, support and guidance. In the undergraduate law degree at the Queensland University of Technology (‘QUT’) the Torts Student Peer Mentor Program aims to supplement a student’s understanding of the substantive law of torts with the development of life-long skills. As such it has the primary objective, albeit through discussion facilitated by more senior students, of encouraging first year students to develop for themselves the skills they need to be successful both as law students and as legal practitioners. Examples of such skills include those relevant to: preparation for assessment tasks; group work; problem solving, cognition and critical thinking; independent learning; and communication. Significantly, in this way, not only do the mentees benefit from involvement in the program, but the peer mentors, or program facilitators, themselves also benefit from their participation in the real world learning environment the program provides. This paper outlines the development and implementation of the above program, the pedagogy which influenced it, and its impact on student learning experiences