Efeito da moagem de alta energia na microestrutura e nas propriedades magnéticas do compósito wc-10%p.Co

This work a studied the high energy milling effect in microstructure and magnetic properties of the WC-10wt.%Co composite. The composite powders were prepared by mechanical mixed and milled at 2 hours, 100 hours, 200 hours and 300 hours in planetary milling. After this process the composite were compacted in stainless steel die with cylindrical county of 10 mm of diameter, at pressure 200 Mpa and sintered in a resistive furnace in argon atmosphere at 1400 oC for 5 min. The sintered composite were cutted, inlaid, sandpapered, and polished. The microestrutural parameters of the composite was analyzed by X-ray diffraction, scanning electronic microscopy, optical microscopy, hardness, magnetic propriety and Rietveld method analyze. The results shows, with milling time increase the particle size decrease, it possibility minor temperature of sintering. The increase of milling time caused allotropic transformation in cobalt phase and cold welding between particles. The cold welding caused the formation of the particle composite. The X-ray diffraction pattern of composite powders shows the WC peaks intensity decrease with the milling time increase. The X-ray diffraction pattern of the composite sintered samples shows the other phases. The magnetic measurements detected a significant increase in the coercitive field and a decrease in the saturation magnetization with milling time increase. The increase coercitive field it was also verified with decrease grain size with milling time increase. For the composite powders the increase coercitive field it was verified with particle size reduction and saturation magnetization variation is relate with the variation of free cobalt. The Rietveld method analyze shows at milling time increase the mean crystalline size of WC, and Co-cfc phases in composite sintered sample are higher than in composite powders. The mean crystallite size of Co-hc phase in composite powders is higher than in composite sintered sample. The mean lattice strains of WC, Co-hc and Co-cfc phases in composite powders are higher than in composite sintered samples. The cells parameters of the composite powder decrease at milling time increase this effect came from the particle size reduction at milling time increase. In sintered composite the cells parameters is constant with milling time increase

Degradação do PMMA através da reação despolimerização uitlizando catalisadores de óxidos mistos

In this work, mixed oxides were synthesized by two methods: polymeric precursor and gel-combustion. The oxides, Niquelate of Lanthanum, Cobaltate of Lanthanum and Cuprate of Lanthanum were synthesized by the polymeric precursor method, and treated at 300 º C for 2 hours, calcined at 800 º C for 6h in air atmosphere. In gel-combustion method were produced and oxides using urea and citric acid as fuel, forming for each fuel the following oxides Ferrate of Lanthanum, Cobaltato of Lanthanum and Ferrato of Cobalt and Lanthanum, which were submitted to the combustion process assisted by microwave power maximum of 10min. The samples were characterized by: thermogravimetric analysis, X-ray diffraction; fisisorção of N2 (BET method) and scanning electron microscopy. The reactions catalytic of depolymerization of poly (methyl methacrylate), were performed in a reactor of silica, with catalytic and heating system equipped with a data acquisition system and the gas chromatograph. For the catalysts synthesized using the polymeric precursor method, the cuprate of lanthanum was best for the depolymerization of the recycled polymer, obtaining 100% conversion in less time 554 (min), and the pure polymer, was the Niquelate of Lanthanum, with 100% conversion in less time 314 (min). By gel-combustion method using urea as fuel which was the best result obtained Ferrate of Lanthanum for the pure polymer with 100% conversion in less time 657 (min), and the recycled polymer was Cobaltate of Lanthanum with 100 % conversion in less time 779 (min). And using citric acid to obtain the best result for the pure polymer, was Ferrate of Lanthanum with 100% conversion in less time 821 (min and) for the recycled polymer, was Ferrate of Lanthanum with 98.28% conversion in less time 635 (min)

Síntese de pigmentos cerâmicos inorgânicos nanométricos e encapsulados com estrutura core-shell pela rota dos precursores poliméricos

The present work has as objective the development of ceramic pigments based in iron oxides and cobalt through the polymeric precursor method, as well as study their characteristics and properties using methods of physical, chemical, morphological and optical characterizations.In this work was used iron nitrate, and cobalt citrate as precursor and nanometer silica as a matrix. The synthesis was based on dissolving the citric acid as complexing agent, addition of metal oxides, such as chromophores ions and polymerization with ethylene glycol. The powder obtained has undergone pre-ignition, breakdown and thermal treatments at different calcination temperatures (700 °C, 800 °C, 900 °C, 1000 °C and 1100 °C). Thermogravimetric analyzes were performed (BT) and Differential Thermal Analysis (DTA), in order to evaluate the term decomposition of samples, beyond characterization by techniques such as BET, which classified as microporous materials samples calcined at 700 ° C, 800 º C and 900 º C and non-porous when annealed at 1000 ° C and 1100 º C, X-ray diffraction (XRD), which identified the formation of two crystalline phases, the Cobalt Ferrite (CoFe2O4) and Cristobalite (SiO2), Scanning Electron Microscopy (SEM) revealed the formation of agglomerates of particles slightly rounded;and Analysis of Colorimetry, temperature of 700 °C, 800 °C and 900 °C showed a brown color and 1000 °C and 1100 °C violet

Comportamento magnético de compósitos de matriz polimérica com adição de ferritas

Polymer matrix composites offer advantages for many applications due their combination of properties, which includes low density, high specific strength and modulus of elasticity and corrosion resistance. However, the application of non-destructive techniques using magnetic sensors for the evaluation these materials is not possible since the materials are non-magnetizable. Ferrites are materials with excellent magnetic properties, chemical stability and corrosion resistance. Due to these properties, these materials are promising for the development of polymer composites with magnetic properties. In this work, glass fiber / epoxy circular plates were produced with 10 wt% of cobalt or barium ferrite particles. The cobalt ferrite was synthesized by the Pechini method. The commercial barium ferrite was subjected to a milling process to study the effect of particle size on the magnetic properties of the material. The characterization of the ferrites was carried out by x-ray diffraction (XRD), field emission gun scanning electron microscopy (FEG-SEM) and vibrating sample magnetometry (VSM). Circular notches of 1, 5 and 10 mm diameter were introduced in the composite plates using a drill bit for the non-destructive evaluation by the technique of magnetic flux leakage (MFL). The results indicated that the magnetic signals measured in plates with barium ferrite without milling and cobalt ferrite showed good correlation with the presence of notches. The milling process for 12 h and 20 h did not contribute to improve the identification of smaller size notches (1 mm). However, the smaller particle size produced smoother magnetic curves, with fewer discontinuities and improved signal-to-noise ratio. In summary, the results suggest that the proposed approach has great potential for the detection of damage in polymer composites structures

Multifuncionalização de nanopartículas de CoFe2O4 pela incorporação da prata na sua superfície : síntese e caracterização

Tese (doutorado)—Universidade de Brasília, Instituto de Física, 2015.

Studio e ottimizzazione del processo di fabbricazione additiva (SLM) per applicazioni in ambito biomedicale: produzione di protesi e strutture reticolari

Il progetto di dottorato che verrà presentato in questa tesi è focalizzato sullo sviluppo di un metodo sperimentale per la produzione di protesi personalizzate utilizzando il processo di fabbricazione additiva di Selective Laser Melting (SLM). L’obiettivo è quello di definire una condizione di processo ottimizzata per applicazioni in ambito chirurgico che possa essere generalizzabile, ovvero che ne garantisca la riproducibilità al variare dell’anatomia del paziente e che rappresenti la base per estendere il metodo ad altre componenti protesiche. Il lavoro si è sviluppato lungo due linee principali, la cui convergenza ha permesso di realizzare prototipi di protesi complete utilizzando un solo processo: da una parte la produzione di componenti a massima densità per il raggiungimento di elevate resistenze meccaniche, buona resistenza ad usura e corrosione e controllo di tensioni residue e deformazione delle parti stampate. Dall’altra si sono studiate strutture reticolari a geometria e porosità controllata per favorire l’osteointegrazione della componente protesica post impianto. In questo studio sono stati messe a confronto le possibili combinazioni tra parametri di processo e sono state individuate le correlazioni con le proprietà finali dei componenti stampati. Partendo da queste relazioni si sono sviluppate le strategie tecnologiche per la progettazione e la produzione dei componenti. I test sperimentali svolti e i risultati ottenuti hanno dimostrato la fattibilità dell’utilizzo del processo SLM per la produzione di protesi personalizzate e sono stati fabbricati i primi prototipi funzionali. La fabbricazione di protesi personalizzate richiede, però, anche la progettazione e la produzione di strumentario chirurgico ad hoc. Per questo motivo, parallelamente allo studio della lega di Cromo Cobalto, sono stati eseguiti i test anche su campioni in INOX 316L. Anche in questo caso è stato possibile individuare una finestra operativa di processo che garantisse proprietà meccaniche comparabili, e in alcuni casi superiori, a quelle ottenute con processi convenzionali.

Caratterizzazione ottica e fotoelettrochimica di fotoanodi di triossido di tungsteno e bismuto vanadato (WO3/BiVO4) con catalizzatore (CoFe-PB)

Il presente lavoro di tesi si propone di illustrare il meccanismo di funzionamento delle celle fotoelettrochimiche (PEC cell) per la produzione di idrogeno, grazie allo studio di diversi semiconduttori, attraverso il cosiddetto fenomeno del water splitting. Nella cella `e stata testata un’eterogiunzione di Triossido di Tungsteno (WO3), una di Triossido di Tungsteno e Bismuto Vanadato (BiVO4) e una terza analoga alla precedente con l’aggiunta di un catalizzatore (CoFe–PB, cobalto-ferro blu di Prussia) per diminuire l’effetto della ricombinazione delle coppie elettrone - lacuna. All’interno della cella il campione era immerso in una soluzione di Acetato (CH3 COO – ) 0.2 M a pH 5. Le principali grandezze misurate sono la fotocorrente prodotta all’interno della cella e il tasso di riduzione e ossidazione dell’acqua.

Studio dell'anisotropia magnetica di bistrati ibridi ferromagnete-organico

L’anisotropia magnetica di film sottili ferromagnetici è un parametro fondamentale nel campo della spintronica. Recenti lavori hanno dimostrato che la formazione di un’interfaccia tra film sottili ferromagnetici e materiali organici è in grado di modificare, l’anisotropia magnetica del costituente inorganico. Questa specifica interfaccia è stata definita spinterface ed è di grande interesse in un’ottica di ingegnerizzazione delle proprietà magnetiche di dispositivi spintronici. Pertanto, in questo lavoro di tesi ho analizzato l’anisotropia magnetica di un film policristallino di Cobalto ricoperto da una molecola organica largamente utilizzata in dispositivi spintronici e optoelettronici, la Gallio-chinolina (Gaq3), con l’obiettivo di verificare il ruolo della molecola nella definizione delle proprietà magnetiche dello strato di Cobalto. Per valutare l’impatto della formazione di spinterface, ho confrontato i risultati sperimentali con quelli ottenuti per un bistrato di riferimento Cobalto/Alluminio (Co/Al). Per comprendere i risultati sperimentali introdurrò nel primo capitolo i concetti fondamentali del magnetismo di film sottili, in particolare i vari contributi di anisotropia magnetica, il concetto di dominio magnetico e il modello di Stoner Wohlfarth. Il secondo capitolo verrà dedicato alla descrizione del concetto di spinterface e come questa interfaccia possa modificare le proprietà magnetiche dei film sottili. Nel terzo capitolo verranno descritte le tecniche di deposizione in Ultra Alto Vuoto con cui sono stati realizzati i bistrati Co/Gaq3 e Co/Al mentre nel quarto capitolo descriver`o il funzionamento del magnetometro MOKE, lo strumento con cui ho studiato l’anisotropia magnetica dei campioni prodotti. I dati sperimentali e la loro discussione saranno presentati nel quinto capitolo dove ho verificato la presenza di effetti di spinterface attraverso l’osservazione di un aumento della coercitività del campione Co/Gaq3.