Non-Destructive Evaluation of Ion-Implanted Semiconductor Thin Films Using Photothermal Deflections Spectroscopy

Materials and equipment which fail to achieve the design requirements or projected life due to undetected defects may require expensive repair or early replacement. Such defects may also be the cause of unsafe conditions or catastrophic unexpected failure, and will lead to loss of revenue due to plant shutdown. Non-Destructive Evaluation (NDE) / Non Destructive Testing (NDT) is used for the examination of materials and components without changing or destroying their usefulness. NDT can be applied to each stage of a system’s construction, to monitor the integrity of the system or structure throughout its life.

Effect of Substrate Temperature on the Structural and Luminescent Characteristics of RF-Magnetron-Sputtered ZnGa2O4:Dy3+ Thin Films

ZnGa2O4:Dy3+ phosphor thin films were deposited on quartz substrates by radio frequency rf magnetron sputtering and the effect of substrate temperature on its structural and luminescent properties was investigated. Polycrystalline film could be deposited even at room temperature. The crystalline behavior, Zn/Ga ratio, and surface morphology of the films were found to be highly sensitive to substrate temperature. Under UV illumination, the as-deposited films at and above 300°C gave white luminescence even without any postdeposition treatments. The photoluminescent PL emission can be attributed to the combined effect of multicolor emissions from the single luminescence center Dy3+ via host-sensitization. Maximum PL emission intensity was observed for the film deposited at 600°C, and the CIE chromaticity coordinates of the emission were determined to be x,y = 0.34, 0.31 .

Optical and electrical properties of co-sputtered amorphous transparent conducting zinc indium tin oxide thin films

Highly conductive and transparent thin films of amorphous zinc indium tin oxide are prepared at room temperature by co-sputtering of zinc 10 oxide and indium tin oxide. Cationic contents in the films are varied by adjusting the power to the sputtering targets. Optical transmission study of 11 films showed an average transmission greater than 85% across the visible region. Maximum conductivity of 6×102 S cm−1 is obtained for Zn/In/ 12 Sn atomic ratio 0.4/0.4/0.2 in the film. Hall mobility strongly depends on carrier concentration and maximum mobility obtained is 18 cm2 V−1 s−1 13 at a carrier concentration of 2.1×1020 cm−3. Optical band gap of films varied from 3.44 eV to 3 eV with the increase of zinc content in the film 14 while the refractive index of the films at 600 nm is about 2.0.