Surface Insulation Resistance Degradation and Electrochemical Migration on Printed Circuit Boards

Widespread adoption of lead-free materials and processing for printed circuit board (PCB) assembly has raised reliability concerns regarding surface insulation resistance (SIR) degradation and electrochemical migration (ECM). As PCB conductor spacings decrease, electronic products become more susceptible to these failures mechanisms, especially in the presence of surface contamination and flux residues which might remain after no-clean processing. Moreover, the probability of failure due to SIR degradation and ECM is affected by the interaction between physical factors (such as temperature, relative humidity, electric field) and chemical factors (such as solder alloy, substrate material, no-clean processing). Current industry standards for assessing SIR reliability are designed to serve as short-term qualification tests, typically lasting 72 to 168 hours, and do not provide a prediction of reliability in long-term applications. The risk of electrochemical migration with lead-free assemblies has not been adequately investigated. Furthermore, the mechanism of electrochemical migration is not completely understood. For example, the role of path formation has not been discussed in previous studies. Another issue is that there are very few studies on development of rapid assessment methodologies for characterizing materials such as solder flux with respect to their potential for promoting ECM. In this dissertation, the following research accomplishments are described: 1). Long-term temp-humidity-bias (THB) testing over 8,000 hours assessing the reliability of printed circuit boards processed with a variety of lead-free solder pastes, solder pad finishes, and substrates. 2). Identification of silver migration from Sn3.5Ag and Sn3.0Ag0.5Cu lead-free solder, which is a completely new finding compared with previous research. 3). Established the role of path formation as a step in the ECM process, and provided clarification of the sequence of individual steps in the mechanism of ECM: path formation, electrodeposition, ion transport, electrodeposition, and filament formation. 4). Developed appropriate accelerated testing conditions for assessing the no-clean processed PCBs' susceptibility to ECM: a). Conductor spacings in test structures should be reduced in order to reflect the trend of higher density electronics and the effect of path formation, independent of electric field, on the time-to-failure. b). THB testing temperatures should be modified according to the material present on the PCB, since testing at 85oC can cause the evaporation of weak organic acids (WOAs) in the flux residues, leading one to underestimate the risk of ECM. 5). Correlated temp-humidity-bias testing with ion chromatography analysis and potentiostat measurement to develop an efficient and effective assessment methodology to characterize the effect of no-clean processing on ECM.

Development and testing of an intermediate temperature glass sealant for use in mixed ionic and electronic conducting membrane reactors

High temperature ceramic membranes have interesting possibilities for application in areas of new and developing technologies such as hydrocarbon combustion with carbon dioxide capture and electrochemical promotion of catalysis (EPOC). However, membrane module sealing remains a significant technical challenge. In this work a borosilicate glass sealant (50SiO₂·25B₂O₃·25Na₂O, mol%) was developed to fit the requirements of sealing an air separation membrane system at intermediate temperatures (300-600 °C). The seal was assessed by testing the leak rates under a range of conditions. The parameters tested included the effect of flowrate on the leak rate, the heating and cooling rates of the reactor and the range of temperatures under which the system could operate. Tests for durability and reliability were also performed. It was found that the most favourable reactor configuration employed a reactor with the ceramic pellet placed underneath the inner chamber alumina tube (inverted configuration), using a quartz wool support to keep the membrane in place prior to sealing. Using this configuration the new glass-based seal was found to be a more suitable sealant than traditional alternatives; it produced lower leak rates at all desirable flowrates, with the potential for rapid heating and cooling and multiple cycling, allowing for prolonged usage. © 2010 Elsevier B.V. All rights reserved.

Development of Electrochemical Sensors for the Determination of Certain Pharmaceuticals

The quality of a drug is determined after establishing its authenticity by testing its purity and quality of the pure substance in the drug and its formulations.Ion selective sensors have become one of the most effective and powerful means for analytical scientists in the determination of drug substances and are playing an increasing role in pharmaceutical analysis.ISEs are cost effective,easy to prepare and can be rapidly manipulated . Potentiometric ion selective sensors have been developed for six drugs namely trimethoprim, ketoconazole, lamivudine, domperidon, nimesulide and Lomefloxacin. The sensors fabricated include both PVC membrane sensor as well as carbon paste sensor. A total of sixteen different sensors have been developed. The response parameters of all the sensors have been studied and the sensors were applied to the determination of the drugs in pharmaceutical formulations and also in real samples like urine.

New crevice corrosion testing method and its use in the investigation of oil stain

A new electrochemical method was developed to investigate crevice corrosion and its inhibitors. A wire beam electrode was used to allow electrochemical parameters to be measured directly from the crevice area. As an example, oil stain was investigated using this method.

Electrochemical methods applied in innovative corrosion inhibitor experiments : case studies

Electrochemical methods can be used more effectively if innovative experiments are designed and employed. This is especially true if a corrosion system to be tested involves inhibitors that could change the mechanism and pattern of corrosion in complex ways. This paper discusses corrosion inhibitor test design using several practical cases as examples. Particular attention is on difficult issues such as the simulation of localized corrosion phenomena and the influence of corrosion mechanism on inhibitor test results. ©2012 by NACE International.

Review of critical issues in carbon dioxide corrosion testing and monitoring techniques

This paper presents a brief review of major techniques applied in carbon dioxide corrosion testing and monitoring. The focus is on the advantages and disadvantages of variously designed testing apparatus and monitoring devices for localized corrosion detection and assessment. Critical factors affecting the reliability and accuracy of major corrosion testing techniques are briefly discussed. It is concluded that major reasons that lead to reporting of inaccurate corrosion rates and patterns include: (i) limitations in conventional electrochemical and nonelectrochemical methods for localized corrosion measurements, and difficulties in data interpretation; (ii) challenges in simulating localized corrosion mechanisms and their changes with the extension of corrosion testing. Underdeposit corrosion testing is presented as a case to illustrate challenges in simulating localized corrosion processes and mechanisms. Experiment data have been presented to show potential difficulties of the artificial pit electrode method in evaluating underdeposit corrosion and its inhibitors. The wire beam electrode method has been used to study underdeposit corrosion with and without inhibitor present. Several interesting corrosion mechanisms have been revealed at different stages of underdeposit corrosion processes.

Effect of the degree of crystallinity on the electrochemical behavior of Mg65Cu25Y10 and Mg70Zn25Ca5 bulk metallic glasses

The effect of varying the percent crystallinity on the electrochemical behavior of Mg65Cu25Y10 and Mg70Zn25Ca5 bulk metallic glasses was studied. The alloys were heat-treated to achieve desired microstructures ranging from fully amorphous to fully crystalline, providing a systematic basis for subsequent testing. Potentiodynamic experiments in 0.01 M sodium chloride (NaCl) were used, whereby both the amorphous and partially crystallized samples were observed to have more noble corrosion potentials and lower anodic kinetics. However, this was accompanied by more rapid cathodic kinetics relative to their fully crystalline counterparts, meaning that corrosion rates were not significantly lower in the amorphous state. To describe the electrochemical response as a function of the degree of crystallinity, differential scanning calorimetry (DSC), scanning electron microscopy, x-ray diffraction (XRD), and electrical conductivity measurements were undertaken, where it was found that crystallinity alone is not necessarily the controlling factor and microchemistry that evolves upon devitrification, plays a key role in the electrochemical response of these materials.

Studying the cathodic disbondment of coatings using electrochemical impedance spectroscopy

The disbondment of protective organic coatings is a widely reported pipeline coating failure mode in the oil and gas industry. Traditional methods of evaluating cathodic disbondment of pipeline coatings are based on visual inspection of pipeline conditions, and laboratory testing of cathodic disbondment resistance (CDR) using standard methods such as ASTM G8. Although some other laboratory-based techniques, such as scanning kelvin probe and scanning acoustic microscopy have been used to study the cathodic disbondment (CD) of coatings, these are often difficult to apply in practical testing. Over the past decade, electrochemical impedance spectroscopy (EIS) has been employed as a potential method for measuring CD. This paper reports preliminary results from an EIS study designed to characterise CD behaviour of epoxy coatings under excessive cathodic protection. EIS data correlated well with the area of disbonded coating. Analysis of EIS data can provide valuable information on the initiation and rates of CD.

Electrochemical performance of LiFe1-xMnxPO4/C materials prepared by ball milling

LiFe1-xMnxPO4/C composite materials as cathode materials in Li-ion batteries have been synthesised and their electrochemical properties have been investigated. The samples were synthesised by using high energy ball milling of commercially available precursors (Li2C2O4, FeC2O4.2H2O, MnC2O4.2H2O, NH4H2PO4) and then heated at 600°C. The morphology and structure of the heated samples were analysed by means of SEM and X-ray diffraction. The olivine structure of the LiFe1-xMnxPO4/C composite was obtained. A slight shift of the peaks to smaller 2θ angles with the increasing Mn/Fe ratios is observed due to the increase in lattice parameters. The influence of different Mn/Fe ratios on electrical and electrochemical performances were studied by charge-discharge and cyclic voltammetry (CV) testing. The CV curves of the pure LiFePO4 and LiMnPO4 show the expected Fe2+/Fe3+ peak around 3·5 V and Mn2+/Mn3+ peak around 4·1 V, respectively. The addition of manganese increases the discharge voltage from 3·5 to 4·1 V.

Electrochemical impedance spectroscopy as a tool to measure cathodic disbondment on coated steel surfaces: capabilities and limitations

The disbondment of protective organic coatings under excessive cathodic protection potentials is a widely reported coating failure mechanism. Traditional methods of evaluating cathodic disbondment are based on ex situ visual inspection of coated metal surfaces after being exposed to standard cathodic disbondment testing conditions for a long period of time. Although electrochemical impedance spectroscopy (EIS) has been employed as an effective means of evaluating various anti-corrosion properties of organic coatings; its application for assessing the cathodic disbondment resistance of coatings has not been sufficiently exploited. This paper reports an experimental study aimed at developing EIS into a tool for in situ measurement and monitoring of cathodic disbondment of coatings. A clear correlation between EIS parameters and the disbonded coating areas has been confirmed upon short term exposure of epoxy-coated steel electrodes to cathodic disbondment conditions; however the degree of this correlation was found to decrease with the extension of exposure duration. This observation suggests that EIS loses its sensitivity with the propagation of coating disbondment, and that in order to achieve quantitative determination of the coating cathodic disbondment localized EIS measurements are required to measure the parameters related to local disbonded areas.

Development and testing of anode-supported solid oxide fuel cells with slurry-coated electrolyte and cathode

A laboratory setup was designed and put into operation for the development of solid oxide fuel cells (SOFCs). The whole project consisted of the preparation of the component materials: anode, cathode and electrolyte, and the buildup of a hydrogen leaking-free sample chamber with platinum leads and current collectors for measuring the electrochemical properties of single SOFCs. Several anode-supported single SOFCs of the type (ZrO(2):Y(2)O(3)+NiO) thick anode/(ZrO(2):Y(2)O(3)) thin electrolyte/(La(0.65)Sr(0.35)MnO(3)+ZrO(2):Y(2)O(3)) thin cathode have been prepared and tested at 700 and 800 degrees C after in situ H(2) anode reduction. The main results show that the slurry-coating method resulted in single-cells with good reproducibility and reasonable performance, suggesting that this method can be considered for fabrication of SOFCs. (c) 2005 Elsevier B.V. All rights reserved.

On the development of the electrochemical potentiokinetic method

The development of electrochemical potentiokinetic methods as applied to the testing of metals and alloys is followed from its early phases up to its latest advances relating to intergranular corrosion, SCC and pitting corrosion tests of stainless steels and special alloys and to the examination of their structure and properties. In assessing the susceptibility to intergranular and pitting corrosion by potentiokinetic polarization tests, the polarization curves which apply to the bulk of the alloy grains (the matrix) must be distinguished from those pertaining to grain boundaries. Cyclic polarization measurements such as the electrochemical potentiokinetic reactivation (EPR) test make it possible to derive the alloy's susceptibility to intergranular, pitting and crevice corrosion from characteristic potentials and other quantities determined in the 'double loop' test. EPR is rapid and responds to the combined effects of a number of factors that influence the properties of materials. The electrochemical p otentiokinetic tests are sensitive enough to detect structural changes in heat treated materials ranging far beyond the stainless steels alone, and can be used for non-destructive testing aimed at elucidating the properties and behavior of materials. © 2001 Elsevier Science Ltd. All rights reserved.

Forensic electrochemistry: indirect electrochemical sensing of the components of the new psychoactive substance Synthacaine

Synthacaine is a New Psychoactive Substance which is, due to its inherent psychoactive properties, reported to imitate the effects of cocaine and is therefore consequently branded as legal cocaine. The only analytical approach reported to date for the sensing of Synthacaine is mass spectrometry. In this paper, we explore and evaluate a range of potential analytical techniques for its quantification and potential use in the field screening Synthacaine using Raman spectroscopy, presumptive (colour) testing, High Performance Liquid Chromatography (HPLC) and electrochemistry. HPLC analysis of street samples reveals that Synthacaine comprises a mixture of methiopropamine (MPA) and 2-aminoindane (2-AI). Raman spectroscopy and presumptive (colour) tests, the Marquis, Mandelin, Simon's and Robadope test, are evaluated towards a potential in-the-field screening approach but are found to not be able to discriminate between the two when they are both present in the same sample, as is the case in the real street samples. We report for the first time a novel indirect electrochemical protocol for the sensing of MPA and 2-AI which is independently validated in street samples with HPLC. This novel electrochemical approach based upon one-shot disposable cost effective screen-printed graphite macroelectrodes holds potential for in-the-field screening for Synthacaine.

Development and testing of an asymmetric capacitor with a nickel-carbon foam positive electrode

Electrochemical capacitors (ECs), also known as supercapacitors or ultracapacitors, are energy storage devices with properties between batteries and conventional capacitors. EC have evolved through several generations. The trend in EC is to combine a double-layer electrode with a battery-type electrode in an asymmetric capacitor configuration. The double-layer electrode is usually an activated carbon (AC) since it has high surface area, good conductivity, and relatively low cost. The battery-type electrode usually consists of PbO2 or Ni(OH)2. In this research, a graphitic carbon foam was impregnated with Co-substituted Ni(OH)2 using electrochemical deposition to serve as the positive electrode in the asymmetric capacitor. The purpose was to reduce the cost and weight of the ECs while maintaining or increasing capacitance and gravimetric energy storage density. The XRD result indicated that the nickel-carbon foam electrode was a typical α-Ni(OH)2. The specific capacitance of the nickel-carbon foam electrode was 2641 F/g at 5 mA/cm2, higher than the previously reported value of 2080 F/g for a 7.5% Al-substituted α-Ni(OH)2 electrode. Three different ACs (RP-20, YP-50F, and Ketjenblack EC-600JD) were evaluated through their morphology and electrochemical performance to determine their suitability for use in ECs. The study indicated that YP-50F demonstrated the better overall performance because of the combination of micropore and mesopore structures. Therefore, YP-50F was chosen to combine with the nickel-carbon foam electrode for further evaluation. Six cells with different mass ratios of negative to positive active mass were fabricated to study the electrochemical performance. Among the different mass ratios, the asymmetric capacitor with the mass ratio of 3.71 gave the highest specific energy and specific power, 24.5 W.h/kg and 498 W/kg, respectively.