Electrochemical performance of LiFe1-xMnxPO4/C materials prepared by ball milling

LiFe1-xMnxPO4/C composite materials as cathode materials in Li-ion batteries have been synthesised and their electrochemical properties have been investigated. The samples were synthesised by using high energy ball milling of commercially available precursors (Li2C2O4, FeC2O4.2H2O, MnC2O4.2H2O, NH4H2PO4) and then heated at 600°C. The morphology and structure of the heated samples were analysed by means of SEM and X-ray diffraction. The olivine structure of the LiFe1-xMnxPO4/C composite was obtained. A slight shift of the peaks to smaller 2θ angles with the increasing Mn/Fe ratios is observed due to the increase in lattice parameters. The influence of different Mn/Fe ratios on electrical and electrochemical performances were studied by charge-discharge and cyclic voltammetry (CV) testing. The CV curves of the pure LiFePO4 and LiMnPO4 show the expected Fe2+/Fe3+ peak around 3·5 V and Mn2+/Mn3+ peak around 4·1 V, respectively. The addition of manganese increases the discharge voltage from 3·5 to 4·1 V.