Effect of lamellar thickness on the epitaxial crystallization of PE on oriented iPP films

The effects of lamellar thickness on the epitaxial crystallization of polyethylene on the oriented isotatic polypropylene have been studied by means of transmission electron microscopy. The results obtained from the bright field electron microscopy and electron diffraction show that the epitaxial orientation of the PE crystals on the iPP substrate depends not only on the thickness of the oriented iPP lamellae, but also on the lamellar thickness of PE crystals. No epitaxial orientation relationship between PE crystal and iPP substrate can be found, when the PE crystals are thicker than the lamellar thickness of iPP along the matching direction. This suggests, that the epitaxial nucleation of PE in the PE/iPP epitaxial system is controlled not only by the chain-row matching, but also by a secondary nucleation process.

Recrystallization of HDPE in HDPE/iPP quenched films

Epitaxial crystallization behavior of HDPE/iPP double layers under quenching and annealing conditions has been studied by means of transmission electron microscopy (TEM). The results obtained from bright field TEM observations indicate that in the as-quenched state the HDPE that is in direct contact with the surface of the oriented iPP substrate recrystallizes in the form of oriented crystallites dispersed on the iPP substrate. The electron diffraction results show that besides the two normally observed epitaxial orientations between HDPE and iPP, there is also a special orientation with [001](HDPE)parallel to[001](iPP). The HDPE which is in contact with the clean surface of a glass slide crystallizes in small lamellae with random orientation. In the boundary region, the epitaxially crystallized HDPE small lamellae stop right on the boundary of the oriented iPP film. If the quenched samples are annealed at 128 degrees C (below T-m of HDPE) for 2 h, the small HDPE crystals grow to thick lamellae in both areas. But only the epitaxial orientation of HDPE with [001](HDPE)parallel to[101](iPP) has been observed.

Epitaxial crystallization in the sPP/nylon-12 semicrystalline polymer system

The epitaxial crystallization behaviour of syndiotactic polypropylene (sPP) on highly oriented nylon-12 substrates has been investigated by means of transmission electron microscopy. The results obtained from bright field electron microscopy and electron diffraction indicate that sPP crystals grow epitaxially on the oriented nylon-12 substrate with their c-axes +/- 37 degrees apart from the chain axis of the nylon-12 substrate. The contact planes of the sPP crystals are the (100) lattice planes. Moreover, the epitaxial crystallization of nylon-12 on highly oriented sPP substrates from a dilute solution in cyclohexanone has also been studied using optical microscopy. The results show that the nylon-12 crystals grow epitaxially on the oriented sPP substrate with the oriented nylon-12 lamellae forming large, anisotropic domains. Copyright (C) 1996 Elsevier Science Ltd.

STEREOCHEMICAL CONTROL IN PROPYLENE POLYMERIZATION WITH A ASYMMETRICALLY SUBSTITUTED TITANOCENE/METHYLALUMINOXANE CATALYST

A new mono-substituted titanocene, (eta(5)-cyclopentadienyl) [eta(5)-(1-(4-methoxyphenyl) cyclohexyl) cyclopentadienyl] dichlorotitanium (I), has been prepared via a novel modified synthesis, and its X-ray crystal structure has been determined. It crystallizes in the orthorhombic space group P2(1)2(1)2(1) with cell constants a=0.968 0(5) nm, b=1.284 6(5) nm, c=1.694 4(6) nm, Z=4, R=0.066. The I/methylaluminoxane (MAO) catalyst system produces at different polymerization temperatures either an isotactic or a syndiotactic polypropylene, both of which have the combined influence of enantiomorphic-site control and chain-end control, or an atactic polypropylene controlled by Bernoullian propagation mechanism.

Blends of Polypropylene and Syndiotactic 1,2-Polybutadiene: Morphology, Crystallization Behaviors and Mechanical Properties

Morphologies, crystallization behavior and mechanical properties of polypropylene(PP)/syndiotactic 1,2-polybutadiene(s-1,2 PB) blends were investigated. Morphology observation shows the well dispersed domains of s-1,2 PB in PP matrix with the rather small domain sizes from 0.1 to 0.5 mu m when the s-1,2 PB content increases from 5% to 20% (mass fraction) in the blends, and the phase structure tends to become co-continuous as s-1,2 PB content further increases.

Morphology, tensile strength and thermal behavior of isotactic polypropylene/syndiotactic polystyrene blends compatibilized by SEBS copolymers

The effects of three triblock copolymers of poly [styrene-b-(ethylene-co-butylene)-b-styrene] (SEBS) of different molecular weight (MW) on the morphology, tensile strength and thermal behavior of isotactic polypropylene/syndiotactic polystyrene (iPP/sPS, 80/20) blend are investigated. Morphology observation shows that both the medium MW and the lower MW SEBS are more effective than the higher MW SEBS in compatibilizing the blends. Tensile tests revels both the medium and low MW compatibilizer lead to a significant improvement in tensile strength, while the higher MW compatibilizer is efficient in increasing the elongation at break of the blends. The localization of compatibilizers in the blends is observed by mean of SEM and the correlation between the distribution of the compatibilizers and mechanical properties of the blends is evaluated. The mechanical properties of the iPP/sPS blends depend on not only the interfacial activity of the compatibilizers but also the distribution of the compatibilizer in the blend. Addition of the compatibilizers to the blend causes a remarkable decrease in the magnitude of the crystallization peak of sPS at its usual T-c. Vicat softening points demonstrate that the heat resistance of iPP/sPS blend is much higher than that of the pure iPP.

Crystallization and phase behavior of crystalline syndiotactic 1,2-polybutadiene/isotactic polypropylene blends in solution-cast thin films

Crystallization and phase behavior in solution-cast thin films of crystalline syndiotactic 1,2-polybutadiene (s-1,2-PB) and isotactic polypropylene (i-PP) blends have been investigated by transmission electron microscopy (TEM), atomic force microscopy (AFM) and field-emission scanning electron microscopy (FESEM) techniques. Thin films of pure s-1,2-PB consist of parallel lamellae with the c-axis perpendicular to the film plane and the lateral scale in micrometer size, while those of i-PP are composed of cross-hatched and single-crystal-like lamellae. For the blends, TEM and AFM observations show that with addition of i-PP, the s-1,2-PB long lamellae become bended and i-PP itself tends to form dispersed convex regions oil a continuous s-1,2-PB phase even when i-PP is the predominant component, which indicates a strong phase separation between the two polymers during film formation. FESEM micrographs of both lower and upper surfaces of the films reveal that the s-1,2-PB lamellae pass through i-PPconvex regions from the bottom, i.e. the dispersed i-PP regions lie on the continuous s-1,2-PB phase. The structural development is attributed to an interplay of crystallization and phase separation of the blends in the film forming process.

Time-resolved synchrotron SAXS observations on sheared syndiotactic poly(propylene) crystallization process

The in situ crystallization kinetics of syndiotactic poly(propylene) (sPP) has been investigated by synchrotron small-angle X-ray scattering (SAXS). The structure evolutions during the isothermal crystallization of sPP with different shear rates have been observed. The results show that shear accelerates the process of crystallization kinetics. Even under low shear rate, the lamellae can be distinctly oriented. In contrast, the lamellar parameters such as the long period, lamellar thickness, and the scattering invariant 0 can change obviously only under high shear rate.

TEM studies on single crystal structure of syndiotactic poly(propene-co-butene-1)s

Themorphologies and structures of single crystals of syndiotactic poly(propene-co-1-butene) (PPBU) with 1-butene contents of 2.6, 4.2, 9.9, 16.2, and 47.9 mol % are studied by transmission electron microscopy and electron diffraction. The electron diffraction results show that the 1-butene units are included in the crystalline phase of the sPP homopolymer. A small amount of 1-butene (<4.2 mol %) has no significant influence on the antichiral chain packing of sPP. With increasing content of 1-butene units, an increasing packing disorder is observed in the PPBU copolymers. The antichiral packing model is, however, always the predominant chain packing structure of the copolymers with the analyzed composition. Bright-field electron microscopy observation shows that the PPBU single crystals exhibit always regular rectangular or lathlike shapes with preferred growth direction along their crystallographic b-axes owing to their packing features. The incorporated 1-butene units influence the crystallization behavior of sPP distinctly. With the increase of the 1-butene units, the aspect ratio of the single crystals increases. Furthermore, the typical transverse microcracks and ripples of the highly stereoregular sPP are no more so prominent for the copolymers. The microcracks are occasionally observed in the single crystals of copolymers with low 1-butene content (less than or equal to4.2 mol %), while transverse ripples are only seen in the crystals of the copolymer having a 1-butene content of 9.9 mol %. With a further increase in the content of 1-butene units, the copolymers behave like the low stereoregular sPP, where neither cracks nor ripples are observed any more.

A novel profluorescent dinitroxide for imaging polypropylene degradation

Free-radical processes underpin the thermo-oxidative degradation of polyolefins. Thus, to extend the lifetime of these polymers, stabilizers are generally added during processing to scavenge the free radicals formed as the polymer degrades. Nitroxide radical precursors, such as hindered amine stabilizers (HAS),1,2 are common polypropylene additives as the nitroxide moiety is a potent scavenger of polymer alkyl radicals (R¥). Oxidation of HAS by radicals formed during polypropylene degradation yields nitroxide radicals (RRNO¥), which rapidly trap the polymer degradation species to produce alkoxyamines, thus retarding oxidative polymer degradation. This increase in polymer stability is demonstrated by a lengthening of the “induction period” of the polymer (the time prior to a sharp rise in the oxidation of the polymer). Instrumental techniques such as chemiluminescence or infrared spectroscopy are somewhat limited in detecting changes in the polymer during the initial stages of degradation. Therefore, other methods for observing polymer degradation have been sought as the useful life of a polymer does not extend far beyond its “induction period”