Recrystallization of HDPE in HDPE/iPP quenched films

Epitaxial crystallization behavior of HDPE/iPP double layers under quenching and annealing conditions has been studied by means of transmission electron microscopy (TEM). The results obtained from bright field TEM observations indicate that in the as-quenched state the HDPE that is in direct contact with the surface of the oriented iPP substrate recrystallizes in the form of oriented crystallites dispersed on the iPP substrate. The electron diffraction results show that besides the two normally observed epitaxial orientations between HDPE and iPP, there is also a special orientation with [001](HDPE)parallel to[001](iPP). The HDPE which is in contact with the clean surface of a glass slide crystallizes in small lamellae with random orientation. In the boundary region, the epitaxially crystallized HDPE small lamellae stop right on the boundary of the oriented iPP film. If the quenched samples are annealed at 128 degrees C (below T-m of HDPE) for 2 h, the small HDPE crystals grow to thick lamellae in both areas. But only the epitaxial orientation of HDPE with [001](HDPE)parallel to[101](iPP) has been observed.