Effect of eugenol-based endodontic sealer on the adhesion of intraradicular posts cemented after different periods

OBJECTIVE: This study evaluated in vitro the influence of an eugenol-based sealer (EndoFill) on the retention of stainless steel prefabricated posts cemented with zinc phosphate and resin-based (Panavia F) cements after different periods of root canal obturation, using the pull-out test. MATERIAL AND METHODS: Sixty upper canines were decoronated and the roots were embedded in resin blocks. The specimens were distributed into 3 groups, according to the period elapsed between canal obturation and post cementation: Group I - immediately; Group II - 72 h and Group III - 4 months. The groups were subdivided according to the type of cement used for post cementation: A - zinc phosphate and B - Panavia F. Following the experimental periods, specimens were subjected to pullout test in an Instron machine with application of tensile force at a crosshead speed of 0.5 mm/min until post dislodgement. The maximum forces required for post removal were recorded (kN) and means were subjected to statistical analysis by 2-way ANOVA and Tukey-Kramer test (α=0.001) RESULTS: There were statistically significant differences (p<0.01) between the posts cemented with zinc phosphate cement (0.2112 kN) and Panavia F (0.0501 kN). However, no statistically significant differences (p>0.05) were found between the three post cementation periods, regardless of the cement. CONCLUSIONS: It was concluded that the eugenol-based sealer influenced the tensile strength of the posts cemented with the resin cement, but had no influence on the time waited between root canal obturation and post space preparation/post cementation.

In vitro analysis of thermocompaction time and gutta-percha type on quality of main canal and lateral canals filling

The aim of this study was to evaluate the quality of filling in main and lateral root canals performed with the McSpadden technique, regarding the time spent on the procedure and the type of gutta-percha employed. Fifty simulated root canals, made with six lateral canals placed two apiece in the cervical, middle and apical thirds of the root, were divided into 5 groups. Group A: McSpadden technique with conventional gutta-percha, performed with sufficient time for canal filling; Group B: McSpadden technique with conventional gutta-percha, performed in twice the mean time used in Group A; Group C: McSpadden technique with TP gutta-percha, performed with sufficient time for canal filling; Group D: McSpadden technique with TP gutta-percha, performed in twice the mean time used in Group C; Group E: lateral condensation technique. Images of the filled root canals were taken using a stereomicroscope and analyzed using the Leica QWIN Pro software for filling material flow, gutta-percha filling extension and sealer flow. Data were analyzed by analysis of variance (ANOVA) and Tukey test (p < 0.05). The best values of penetration in lateral canals in the middle third occurred in the groups where TP gutta-percha was used. However, in the apical third, group B showed the best values. Although a longer time of compactor use allows greater penetration of the filling material into the lateral canals, the presence of voids resulted in bad quality radiographic images, suggesting porosity. The best quality of filling material was observed in Group A (McSpadden technique with conventional Gutta-Percha, performed with sufficient time for root canal filling).

Apical Leakage of Three Resin-Based Endodontic Sealers after 810-nm-Diode Laser Irradiation

Objective: To evaluate the influence of 810-nm-diode laser irradiation, applied before root canal filling, on apical sealing ability of three different resin-based sealers (AH Plus, EndoRez, and RealSeal). Background: Lasers have been widely used in endodontics. The dentin wall changes caused by laser irradiation could improve the sealing ability of endodontic cements. Methods: Sixty single-rooted human teeth were divided into six groups, according to the endodontic sealer used and previous 810-nm-diode laser irradiation. The protocol for laser irradiation was 2.5W in a continuous wave, in scanning mode, with four irradiations per tooth. After sample preparation, they were analyzed according to apical leakage with silver nitrate impregnation. Results: The RealSeal sealer achieved minimum leakage rates (1.24 mm), with significant differences at the 1% level (Tukey's test, p < 0.01) from AH Plus (1.84 mm) in nonirradiated groups. When the laser was used, there were also significant differences at the 5% level (p < 0.05) between irradiated groups (1.31 and 1.78 mm, respectively). Conclusion: The 810-nm-diode laser irradiation did not promote significant differences in apical leakage.

Ultra-Structural Changes at the Apical Stop Irradiated with CO(2) Laser

Objective: This study evaluated ultra-structural dentine changes at the apical stop after CO(2) laser irradiation used during biomechanical preparation. Background: Most studies evaluating the sealing efficiency of CO(2) lasers have been carried out after apical root canal resections and retro-filling procedures. Methods: Sixty human canines were prepared with #1 to #6 Largo burs. The apical stops were established at 1 mm (n = 30) and 2 mm (n = 30) from the apex. Final irrigation was performed with 1% NaOCl and 15% EDTA followed by 20 ml of distilled and deionized water. Specimens were subdivided into three subgroups (n = 10 for each stop distance): GI-no radiation (n = 20); GII-3W potency (n = 20), GIII-5W potency (n = 20). After preparation, specimens were evaluated by scanning electron microscopy, with ultra-structural changes classified according to a scoring system based on six qualitatively different outcomes. Results: Statistical analysis using the Mann-Whitney test confirmed more intense results for the specimens irradiated at 5 W potency than at 3 W (p<0.0001). The Kruskal-Wallis test indicated that when using the same potencies (3 or 5 W) at 1 and 2 mm from the apex, there were no statistically significant differences in ultra-structural changes. Conclusions: Our results showed that ultra-structural changes ranged from smear layer removal to dentine fusion. As laser potency was increased from 3 to 5 W, ultra-structural changes included extensive fused lava-like areas sealing the apical foramen.

Ultrastructural analysis of root canal dentine irradiated with 980-nm diode laser energy at different parameters

Objective: The purpose of this in vitro study was to investigate using the scanning electron microscope (SEM) the ultrastructural morphological changes of the radicular dentine surface after irradiation with 980-nm diode laser energy at different parameters and angles of incidence. Background Data: There have been limited reports on the effects of diode laser irradiation at 980 nm on radicular dentin morphology. Materials and Methods: Seventy-two maxillary canines were sectioned and roots were biomechanically prepared using K3 rotary instruments. The teeth were irrigated with 2 mL of distilled water between files and final irrigation was performed with 10 mL of distilled water. The teeth were then randomly divided into five groups (n = 8 each) according to their diode laser parameters: Group 1: no irradiation (control); group 2: 1.5 W/continuous wave (CW) emission (the manufacturer's parameters); group 3: 1.5 W/100 Hz; group 4: 3 W/CW; and group 5: 3 W/100 Hz. Laser energy was applied with helicoid movements (parallel to the canal walls) for 20 sec. Eight additional teeth for each group were endodontically prepared and split longitudinally and irradiation was applied perpendicularly to the root surface. Results: Statistical analysis showed no difference between the root canal thirds irradiated with the 980-nm diode laser, and similar results between the parameters 1.5 W/CW and 3 W/100 Hz (p > 0.05). Conclusion: When considering different output powers and delivery modes our results showed that changes varied from smear layer removal to dentine fusion.

Analysis of four gutta-percha techniques used to fill mesial root canals of mandibular molars

P>Aim To compare the percentage of gutta-percha, sealer and voids and the influence of isthmuses in mesial root canals of mandibular molars filled with different techniques. Methodology Canals in 60 mesial roots of mandibular first molars were prepared with ProTaper instruments to size F2 (size 25, 0.08 taper) and filled using a single-cone, lateral compaction, System B or Thermafil techniques. An epoxy resin sealer was labelled with Rhodamine-B dye to allow analysis under a confocal microscope. The percentage of gutta-percha, sealer and area of voids was calculated at 2, 4 and 6 mm from the apex, using Image Tool 3.0 software. Statistical analysis was performed using nonparametric Kruskal-Wallis and Dunn tests (P < 0.05). The influence of isthmuses on the presence or absence of voids was evaluated using the Fisher test. Results At the 2 mm level, the percentage of gutta-percha, sealer and voids was similar amongst the System B, lateral compaction and single-cone techniques. The single-cone technique revealed significantly less gutta-percha, more sealer and voids in comparison with the Thermafil technique at the 2 and 4 mm level (P < 0.05). The analysis of all sections (2, 4 and 6 mm) revealed that more gutta-percha and less sealer and voids were found in root canals filled with Thermafil and System B techniques (P < 0.05). The Fisher test revealed that the presence of isthmuses increased the occurence of voids in the lateral compaction group only (P < 0.05). Conclusion Gutta-percha, sealer filled area and voids were dependent on the canal-filling technique. The presence of isthmuses may influence the quality of root filling.

Bacterial leakage in obturated root canals-part 2: a comparative histologic and microbiologic analyses

Objective. In this study, presence of dentin infection in root canals, obturated with 4 techniques submitted to the bacterial leakage test, was evaluated using histologic methods. Study design. The canals of palatal roots of 160 molars were instrumented and divided into different groups, according to the obturation technique used (lateral condensation, MicroSeal system, Touch `n Heat + Ultrafil, and Tagger`s hybrid technique) and extent of the remaining obturation material (5 mm and 10 mm). Ten additional roots were used as control samples. The roots were sterilized in ethylene oxide and mounted on a device for evaluation of bacterial leakage using the bacteria Enterococcus faecalis for 120 days. After the leakage test, roots were microscopically analyzed for the presence of dentin infection in the root canals and dentinal tubules. Results. A total of 154 specimens were analyzed using both methodologies in the experimental groups; 50 root canals (32.4%) showed bacterial leakage at the end of the experimental period, and 118 (76.6%) showed the presence of bacteria in the root canals using the histologic criteria. The lateral condensation technique allowed lower penetration of bacteria in the root canals and dentinal tubules, followed by Touch `n Heat + Ultrafil, MicroSeal, and Tagger`s hybrid technique, which allowed significantly greater penetration of bacteria. Root canals with 10 mm of remaining obturation material presented similar bacterial penetration as root canals with 5 mm. Conclusions. Even when an adequate seal of the apical foramen was shown by the absence of turbidity in the bacterial leakage test, E. faecalis dentin infection was present in a high percentage of the root canals after 120 days of root filling exposure to the bacteria. Tagger`s hybrid technique presented greater quantity of bacteria in histologic sections than root canals obturated with the other techniques. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2010; 109: 788-794)

Analysis of the gutta-percha filled area in C-shaped mandibular molars obturated with a modified MicroSeal technique

To analyse the gutta-percha filled area of C-shaped molar teeth root filled with the modified MicroSeal technique with reference to the radiographic features and the C-shaped canal configuration. Twenty-three mandibular second molar teeth with C-shaped roots were classified according to their radiographic features as: type I - merging, type II - symmetrical and type III - asymmetrical. The canals were root filled using a modified technique of the MicroSeal system. Horizontal sections at intervals of 600 mu m were made 1 mm from the apex to the subpulpal floor level. The percentage of gutta-percha area from the apical, middle and coronal levels of the radiographic types was analysed using the Kruskal-Wallis test. Complementary analysis of the C-shaped canal configurations (C1, C2 and C3) determined from cross-sections from the apical third was performed in a similar way. No significant differences were found between the radiographic types in terms of the percentage of gutta-percha area at any level (P > 0.05): apical third, type I: 77.04%, II: 70.48% and III: 77.13%, middle third, type I: 95.72%, II: 93.17%, III: 91.13% and coronal level, type I: 98.30%, II: 98.25%, III: 97.14%. Overall, the percentage of the filling material was lower in the apical third (P < 0.05). No significant differences were found between the C-shaped canal configurations apically; C1: 72.64%, C2: 79.62%, C3: 73.51% (P > 0.05). The percentage of area filled with gutta-percha was similar in the three radiographic types and canal configuration categories of C-shaped molars. These results show the difficulty of achieving predictable filling of the root canal system when this anatomical variation exists. In general, the apical third was less completely filled.

Bacterial leakage in root canals obturated by different techniques. Part 1: microbiologic evaluation

Objective. This study compared the coronal bacterial leakage of root canals obturated by different techniques and with different lengths of obturation. Study design. The canals of palatal roots of 160 maxillary molars were instrumented and divided into different groups according to the obturation technique used (lateral condensation, Microseal system, Touch `n Heat + Ultrafil system, or Tagger`s hybrid technique) and the length of obturation (5 mm or 10 mm). The roots were impermeabilized, sterilized in ethylene oxide, and mounted on a device for evaluation of the bacterial leakage. Results. Tagger`s hybrid technique produced a statistically greater number of specimens with coronal leakage than the other techniques. There was no statistically significant difference between the lateral condensation, Touch `n Heat + Ultrafil, and Microseal groups. Root canals with 10 mm of obturation produced a statistically significantly smaller number of specimens with leakage than root canals with 5 mm of obturation. Conclusion. Tagger`s hybrid technique produced a greater number of specimens with coronal leakage than the other techniques, and a greater number of root canals with 5 mm of obturation leaked than root canals with 10 mm of obturation.

Evaluation of physicochemical properties of four root canal sealers

P>Aim To assess the physicochemical properties and the surface morphology of AH Plus, GuttaFlow, RoekoSeal and Activ GP root canal sealers. Methodology Five samples of each material were evaluated for setting time, dimensional alteration, solubility and radiopacity tests, according to ANSI/ADA Specification 57. A total of 50 mL of deionized distilled water from the solubility tests were used to measure the metal solubility by atomic absorption spectrometry. The morphologies of the external surface and the cross-section of the samples were analysed by means of a scanning electron microscope (SEM). Statistical analysis was performed by using one-way anova and post hoc Tukey-Kramer tests with the null hypothesis set as 5%. Results AH Plus had the longest setting time (580.6 +/- 3.05 min) (P < 0.05). Activ GP did not have a mean value on the radiopacity and solubility tests (1.31 +/- 0.35 mm and 11.8 +/- 0.43%, respectively) in accordance with ANSI/ADA, being significantly different from the other materials (P < 0.05), which had mean values for these tests in accordance with the ADA`s requirements. GuttaFlow was the only sealer that conformed to the Specification 57 concerning the dimensional alteration test (0.44 +/- 0.16%) (P < 0.05). The spectrometry test revealed significant Ca2+, K+, Zn2+ ion release from Activ GP sealer (32.57 +/- 5.0, 1.57 +/- 0.22 and 8.20 +/- 1.74 mu g mL-1, respectively). In SEM analysis, the loss of matrix was evident and the filler particles were more distinguishable in all groups. Conclusions The setting time of all sealers was in accordance with ANSI/ADA`s requirements. Activ GP did not fulfill ANSI/ADA`s protocols regarding radiopacity, dimensional alteration and solubility. GuttaFlow was the only sealer that conformed to the Specification 57 in all tests. SEM analysis revealed that the surfaces of all sealers had micromorphological changes after the solubility test.

Apical limit of root canal filling and its relationship with success on endodontic treatment of a mandibular molar: 11-year follow-up

Objective. This article discusses the relationship between apical limit of root canal filling and success on endodontic treatment of a mandibular molar. Study design. A mandibular right first molar with vital pulp was endodontically treated, and 3 years later periapical lesions on mesial and distal roots were detected. The canals were retreated and obturated to the same levels as in the previous treatment. Results. An 8-year radiographic follow-up showed repair of the periapical lesions on both roots. Conclusions. Results suggest that the apical limit of obturation seems to have no influence in the repair of periapical tissues in mandibular molars. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2011; 112: e48-e50)

A comparative study of physicochemical properties of AH Plus, Epiphany, and Epiphany SE root canal sealers

P>Aim To assess the physicochemical properties and the surface morphology of AH Plus, Epiphany, and Epiphany SE root canal sealers. Methodology Five samples of each material were employed for each test according to ANSI/ADA specification 57. The samples were assigned to four groups: (i) AH Plus; (ii) Epiphany; (iii) Epiphany + Thinning Resin; (iv) Epiphany SE. The distilled water used during the solubility test was submitted to spectrometry to verify the release of calcium ions. The morphologies of the external surface and the cross-section of the samples were analysed by means of a scanning electron microscope (SEM). Statistical analysis was performed by using One-Way anova and post hoc Tukey-Kramer tests with the null hypothesis set as 5%. Results Setting time, flow and radiopacity results were in accordance with ANSI/ADA requirements whereas the dimensional change of all sealers and solubility of Epiphany did not fulfil ANSI/ADA protocols. AH Plus and Epiphany SE were similar in terms of flow, radiopacity, solubility and dimensional change. The spectrometry test revealed significant calcium ion release from Epiphany with and without the thinning resin. SEM analysis revealed essentially a homogeneous surface with compact layer and some rough areas. Conclusions Setting time, flow, and radiopacity tests conformed to ANSI/ADA standardization. The dimensional change in all groups and the solubility of Epiphany were greater than values considered acceptable, with higher amounts of calcium ion release. Epiphany SE revealed more organized, compacted, and homogeneous polymers in a reduced resin matrix when compared with the other groups.

Bond Strength of Fiber Posts to Weakened Roots After Resin Restoration With Different Light-Curing Times

Introduction: This study evaluated the bond strength of translucent fiber posts to experimentally weakened radicular dentin restored with composite resin and polymerized with different light-exposure time. Methods: Roots of 60 maxillary incisors were used. Twenty-four hours after obturation, the filling materials of root canals were removed to a depth of 12 mm, and 4 groups were randomly formed. In 3 groups, root dentin was flared to produce a space between fiber post and canal walls. In the control group, the roots were not experimentally weakened. The flared roots were bulk restored with composite resin, which was light-activated through the translucent post for 40, 80, or 120 seconds. Posts were cemented, and after 24 hours, all roots were sectioned transversely in the coronal, middle, and apical regions, producing 1-mm-thick slices. Push-out test was performed, and failure modes were observed. Results The quantitative analysis showed significant statistical difference only among groups (P <.001). Comparing the weakened/restored groups, composite light-exposure time did not influence the results. Overall, adhesive failures occurred more frequently than other types of failures. Cohesive failures occurred only in the weakened/restored roots. Conclusions Intracanal root restoration with composite resin and translucent fiber posts provided similar or higher bond strength to dentin than the control group, regardless of the light-exposure time used for polymerization. (J Endod 2009;35:1034-1039)

The anatomy of two-rooted mandibular canines determined using micro-computed tomography

P>Aim To investigate the internal and external anatomy of extracted human mandibular canines with two roots and two distinct canals using micro-computed tomography (mu CT). Methodology Fourteen two-rooted human mandibular canines were scanned using a high-resolution mu CT system (SkyScan 1174v2; SkyScan N.V., Kontich, Belgium). The images were processed to evaluate the size of the roots, the furcation regions, the presence of accessory canals, the mean distances between several anatomical landmarks, the position of the apical foramina, the direction of root curvatures, the cross-sectional appearances (SMI index), the volume and surface areas of the root canals. Results Root bifurcation was located in both apical (44%, n = 6) and middle (58%, n = 8) thirds of the root. The size of the buccal and lingual roots was similar in 29% of the sample. From a buccal view, no curvature towards the lingual or buccal direction occurred in either roots. From a proximal view, no straight lingual root occurred. In both views, S-shaped roots were found in 21% of the specimens. Location of the apical foramen varied considerably, tending to the mesio-buccal aspect of both roots. Lateral and furcation canals were observed mostly in the cervical third in 29% and 65% of the sample, respectively. The structure model index (SMI) index ranged from 1.87 to 3.86, with a mean value of 2.93 +/- 0.46. Mean volume and area of the root canals were 11.52 +/- 3.44 mm3 and 71.16 +/- 11.83 mm2, respectively. Conclusions The evaluation of two-rooted mandibular canines revealed that bifurcations occurred in the apical and middle third. S-shaped roots were found in 21% of the specimens. Mean volume, surface area and SMI index of the root canals were 11.52 mm3, 71.16 mm2 and 2.93, respectively.

Bond strength of AH Plus and Epiphany sealers on root dentine irradiated with 980 nm diode laser

Aim To evaluate the bond strength of AH Plus and Epiphany sealers to human root canal dentine irradiated with a 980 nm diode laser at different power and frequency parameters, using the push-out test. Methodology Sixty canine roots were sectioned below the cementoenamel junction to provide 4-mm-thick dentine discs that had their root canals prepared with a tapered bur and irrigated with sodium hypochlorite, ethylenediaminetetraacetic acid and distilled water. The specimens were assigned to five groups (n = 12): one control (no laser) and four experimental groups that were submitted to 980 nm diode laser irradiation at different power (1.5 and 3.0 W) and frequency (continuous wave and 100 Hz) parameters. Half of specimens in each group had their canals filled with AH Plus sealer and half with Epiphany. The push-out test was performed and data (MPa) were analysed statistically by ANOVA and Tukey`s test (P < 0.05). The specimens were split longitudinally and examined under SEM to assess the failure modes after sealer displacement. Results The specimens irradiated with the diode laser and filled with AH Plus had significantly higher bond strength values (8.69 +/- 2.44) than those irradiated and filled with Epiphany (3.28 +/- 1.58) and the nonirradiated controls (3.86 +/- 0.60). The specimens filled with Epiphany did not differ significantly to each other or to the control (1.75 +/- 0.69). There was a predominance of adhesive failures at Epiphany-dentine interface (77%) and mixed failures at AH Plus-dentine interface (67%). Conclusions The 980 nm diode laser irradiation of root canal dentine increased the bond strength of AH Plus sealer, but did not affect the adhesion of Epiphany sealer.