Fabrication of Silicon-Based Template-Assisted Nanoelectrode Arrays and Ohmic Contact Properties Investigation

A convenient fabrication technology for large-area, highly-ordered nanoelectrode arrays on silicon substrate has been described here, using porous anodic alumina (PAA) as a template. The ultrathin PAA membranes were anodic oxidized utilizing a two-step anodization method, from Al film evaporated on substrate. The purposes for the use of two-step anodization were, first, improving the regularity of the porous structures, and second reducing the thickness of the membranes to 100 similar to 200 nm we desired. Then the nanoelectrode arrays were obtained by electroless depositing Ni-W alloy into the through pores of PAA membranes, making the alloy isolated by the insulating pore walls and contacting with the silicon substrates at the bottoms of pores. The Ni-W alloy was also electroless deposited at the back surface of silicon to form back electrode. Then ohmic contact properties between silicon and Ni-W alloy were investigated after rapid thermal annealing. Scanning electron microscopy (SEM) observations showed the structure characteristics, and the influence factors of fabrication effect were discussed. The current voltage (I-V) curves revealed the contact properties. After annealing in N-2 at 700 degrees C, good linear property was shown with contact resistance of 33 Omega, which confirmed ohmic contacts between silicon and electrodes. These results presented significant application potential of this technology in nanosize current-injection devices in optoelectronics, microelectronics and bio-medical fields.

A plasma sputtering decoration route to producing thickness-tunable ZnO/TiO2 core/shell nanorod arrays

We report a radio frequency magnetron sputtering method for producing TiO2 shell coatings directly on the surface of ZnO nanorod arrays. ZnO nanorod arrays were firstly fabricated on transparent conducting oxide substrates by a hydrothermal route, and subsequently decorated with TiO2 by a plasma sputtering deposition process. The core/shell nanorods have single-crystal ZnO cores and anatase TiO2 shells. The shells are homogeneously coated onto the whole ZnO nanorods without thickness change. This approach enables us to tailor the thickness of the TiO2 shell for desired photovoltaic applications on a one-nanometer scale. The function of the TiO2 shell as a blocking layer for increasing charge separation and suppression of the surface recombination was tested in dye-sensitized solar cells. The enhanced photocurrent and open-circuit voltage gave rise to increased photovoltaic efficiency and decreased dark current, indicating successful functioning of the TiO2 shell.

Enhanced durability of Li-O2 batteries employing vertically standing Ti nanowire array supported cathodes

Ti nanowire arrays vertically standing on Ti foam prepared by a facile corrosion method were used as self-supported Li-O₂ battery cathodes. The batteries exhibited enhanced durability at high rate current densities (e.g. cycling 640 times at 5 A g^-1).

ZnO nanostructures grown on epitaxial GaN

Presented is the growth of zinc oxide nanorod/nanowire arrays on gallium nitride epitaxial layers. A hierarchical zinc oxide morphology comprising of different scale zinc oxide nanostructures was observed. The first tier of the surface comprised of typical zinc oxide nanorods, with most bridging to adjacent nanorods. While the second tier comprised of smaller zinc oxide nanowires approximately 30 nm in width often growing atop the aforementioned bridges. Samples were analysed via scanning electron microscopy, as well as, cross-sectional and high resolution transmission electron microscopy to elucidate the detailed growth and structural elements of the heterostructure. © 2009 Elsevier B.V. All rights reserved.

From Hexagonally Arrayed Nanorods To Ordered Porous Film Through Controlling The Morphology Of Zno Crystals

The macrostructure can be changed by changing the morphology of its units. In this article, we use a colloidal template route, combined with hydrothermal growth method, to get the hexagonally arrayed ZnO nanorods on the polycrystalline ZnO substrate. More significantly, through controlling the morphology of ZnO crystals by adding structure-directing agent in the precursor solution, the highly ordered porous ZnO films were obtained instead of ZnO nanorods. This templated solvent-thermal method has great potential in micro/nano-fabrication. (C) 2008 Elsevier B.V. All rights reserved.

Flexible array sensors based on zinc oxide nanowires for touch displays

Recent efforts towards the fabrication of touch sensing systems are presented, in which zinc oxide nanowire arrays are embedded in a polymer matrix to produce an engineered composite material. In the future, these sensor systems will be fully flexible and multi-touch as intended for Nokia's 'Morph' concept device.

Electronic structure of ZnO wurtzite quantum wires

The electronic structure and optical properties of ZnO wurtzite quantum wires with radius R >= 3 nm are studied in the framework of six-band effective-mass envelope function theory. The hole effective-mass parameters of ZnO wurtzite material are calculated by the empirical pseudopotential method. It is found that the electron states are either two-fold or four-fold degenerate. There is a dark exciton effect when the radius R of the ZnO quantum wires is in the range of [3,19.1] nm (dark range in our model). The dark ranges of other wurtzite semiconductor quantum wires are calculated for comparison. The dark range becomes smaller when the |Delta(so)| is larger, which also happens in the quantum-dot systems. The linear polarization factor of ZnO quantum wires is larger when the temperature is higher.

重离子蚀刻径迹中金属纳米线阵列的研制

本论文主要进行了核孔膜的蚀刻和紫外光辐照效应研究，以及在核孔膜模板内进行Cu、CO金属纳米线阵列的制备研究。在UNILAC（GSI，Darmstadt）加速器上真空和室温条件下对30μm厚的聚碳酸酯（PC）薄膜进行快重离子辐照，照射离子为11． 4 MeV／u的Au离子，辐照剂量在lion／cm，-3X109i0ns／cm，之间。重离子辐照导致在PC中产生潜径迹，通过化学蚀刻的方法将潜径迹放大而形成孔道。蚀刻速率与蚀刻温度、蚀刻液浓度、紫外光辐照敏化等参数密切相关。结果表明随着温度的升高蚀刻液浓度的增加、紫外光辐照时间的增长径迹蚀刻速率剧烈增加。此外，通过紫外可见光谱和力学性能测试发现，紫外光辐照会使Pc膜的光学性能和力学性能发生显著的变化。在能量密度为16mw／cm2的紫外光下，当膜两侧分别经过17．5小时的光照以后，392 nm处的吸收峰消失，而且其断裂伸长率大大减小。作为紫外光辐照效应的一个应用，我们利用“紫外光辐照＋液氮冷冻”的方法成功制备出了核孔膜断面的扫描电子显微镜样品，此方法能使样品的断面含有较少的残余应力从而使膜在断裂过程中没有发生明显的变形，使断面很好显现了膜和孔道的原始信息，如孔密度、形状、尺寸等。利用PC核孔膜作为模板用电化学沉积方法制备出了金属纳米线阵列。用磁控溅射的方法在PC膜模板的一面沉积一层Pt金属薄膜在电沉积过程中用作阴极。在自制的电沉积系统中用直流沉积的方法在PC核孔膜模板中成功制备出了Cu和Co金属纳米线，并运用SEM、xRD、VSM等手段对纳米线进行分析。结果表明，制备出的Cu纳米线长度约为30μm，直径从nm到协m量级，具有面心立方（fcc）结构，且纯度很高没有发现杂质。对Co纳米线阵列的xRD结果进行分析可以看出，制备出的c。纳米线阵列具有两种晶体结构：单相hcp结构和hcp、fcc共存结构。从vsM测量结果可以看出，Co纳米线阵列存在磁各向异性，即平行于纳米线轴向和垂直于纳米线轴向的剩余磁化强度和矫顽力存在明显差异，这主要是由于纳米线的形状各向异性和纳米线之间的磁相互作用引起的。

Nanoporous In2O3 nanocrystal clusters: One-step synthesis, thermal stability and optical property

Nanoporous In2O3 nanocrystal clusters with high surface areas have been synthesized by a one-step solvent-thermal method at a relatively low temperature. On the basis of our experimental data and nanomaterial growth mechanism, a template-assistant dehydration accompanied by aggregation mechanism was proposed to explain their formation. Besides, the influence of the high-temperature treatment on their porous structure and optical properties were studied and compared by various technologies.

Template-free, surfactantless route to fabricate In(OH)(3) monocrystalline nanoarchitectures and their conversion to In2O3

In this work, a one-dimensional microrod-based three-dimensional flowerlike indium hydroxide (In(OH)(3)) structure was fabricated, without any templates or surfactants, using a well-known hydrothermal approach at a non-high temperature. In2O3 with similar morphology was formed by annealing In(OH)3 precursors and was characterized by Raman spectrum and photoluminescence (PL) spectrum in detail.

Self-assembled 3D microflowery In(OH)(3) architecture and its conversion to In2O3

Using sodium dodecyl sulfate (SDS), a 3D microflowery indium hydroxide [In(OH)(3)] structure assembled from 2D nanoflakes was fabricated in a large quantity via a hydrothermal approach at relative low temperature. The obtained In(OH)(3) flowers exhibited a narrow size range between 4 and 6 mu m. The properties of these composites were characterized by XRD, EDX, FE-SEM, TEM, SAED, and TGA. In this work, both the use of urea and SDS and the amounts of these components played important roles in the formation of In(OH)3 with different nanostructures.

Biofilm-Engineered Nanostructures

The use of biofilms as nanostructure-engineering materials is discussed and exemplified using ZnO nanorods. Three examples are presented for illustration, the immobilization of ZnO-nanorod arrays on the inner wall of a polystyrene centrifuge tube using S. thermophilus, the morphological organization of ZnO "filters" using S. thermophilus. And the design and implementation of a ZnO-decorated Ag framework using E. coli.

CuIn(WO4)(2) nanospindles and nanorods: controlled synthesis and host for lanthanide near-infrared luminescence properties

CuIn(WO4)(2) porous nanospindles and nanorods were synthesized through a low-cost hydrothermal method without introducing any template or surfactants. An interesting formation mechanism, namely "oriented attachment", was observed for the growth of nanorods based on the experimental process and the anisotropic intrinsic crystalline structure of CuIn(WO4)(2), which is uncommon in such a system. The near-infrared luminescence of lanthanide ions (Er, Nd, Yb and Ho) doped CuIn(WO4)(2) nanostructures, especially in the 1300-1600 nm region, was discussed and of particular interest for telecommunications applications. X-Ray diffraction, scanning electron microscopy, transmission electron microscopy, electron diffraction and photoluminescence spectra were used to characterize these materials.