The magnetic exchange interactions in chromium chalcogenide spinels

The chromium chalcogenide spinels, MCr2X4 (M = Zn, Cd, Hg; X = O, S, Se), have been the subject of considerable interest in recent years. In each case the crystal structure is that of a normal spinel with the chromium ions exclusively occupying the octahedral (B) sites, so that when diamagnetic ions are located at the tetrahedral (A) sites the only magnetic interactions present are those between B-site ions. Despite such apparently simple circumstances a rich variety of magnetic behaviour is exhibited. For the oxides the ground state spin configurations are antiferromagnetic whilst for the selenides ferromagnetic interactions dominate and several authors have drawn attention to the fact that the nature of the dominant interaction is a function of the nearest neighbour chromium - chromium separation. However, at least two of the compounds exhibit spiral structures and it has been proved difficult to account for the various spin configurations within a unified theory of the magnetic interactions involved. More recently, the possibility of formulating a simplified interpretation of the magnetic interactions has been provided by the discovery that the crystal struture of spinels does not always conform to the centrosymmetrical symmetry Fd3m that has been conventionally assumed. The deviation from this symmetry is associated with small < 111> displacements of the octahedrally coordinated metal ions and the structures so obtained are more correctly referred to the non-centrosymmetrical space group F43m. In the present study, therefore, extensive X-ray diffraction data have been collected from four chromium chalcogenide specimens and used to refine the corresponding structural parameters assuming F43m symmetry and also with conventional symmetry. The diffracted intensities from three of the compounds concerned cannot be satisfactorily accounted for on the basis of conventional symmetry and new locations have been found for the chromium ions in these cases. It is shown, however, that these displacements in chromium positions only partially resolve the difficulties in interpreting the magnetic behaviour. A re-examination of the magnetic data from different authors indicates much greater uncertainty in their measurements than they had claimed. By taking this into consideration it is shown that a unified theory of magnetic behaviour for the chromium chalcogenide spinels is a real possibility.

Glasslike ordering and spatial inhomogeneity of magnetic structure in Ba3FeRu2O9: Role of Fe/Ru site disorder

Several doped 6H hexagonal ruthenates, having the general formula Ba3MRu2O9, have been studied over a significant period of time to understand the unusual magnetism of ruthenium metal. However, among them, the M = Fe compound appears different since it is observed that unlike others, the 3d Fe ions and 4d Ru ions can easily exchange their crystallographic positions, and as a result many possible magnetic interactions become realizable. The present study involving several experimental methods on this compound establishes that the magnetic structure of Ba3FeRu2O9 is indeed very different from all other 6H ruthenates. Local structural study reveals that the possible Fe/Ru site disorder further extends to create local chemical inhomogeneity, affecting the high-temperature magnetism of this material. There is a gradual decrease of Fe-57 Mossbauer spectral intensity with decreasing temperature (below 100 K), which reveals that there is a large spread in the magnetic ordering temperatures, corresponding to many spatially inhomogeneous regions. However, finally at about 25 K, the whole compound is found to take up a global glasslike magnetic ordering.

A Rare Phenoxido/Acetato/Azido Bridged Trinuclear and an Unprecedented Phenoxido/Azido Bridged One-Dimensional Polynuclear Nickel(II) Complexes: Synthesis, Crystal Structure, and Magnetic Properties with Theoretical Investigations on the Exchange Mechanism

The reaction of a tridentate Schiff base ligand HL (2-(3-dimethylaminopropylimino)-methyl]-phenol) with Ni(II) acetate or perchlorate salts in the presence of azide as coligand has led to two new Ni(II) complexes of formulas Ni3L2(OAc)(2)(mu(1,1)-N-3)(2)(H2O)(2)]center dot 2H(2)O (1) and Ni2L2(mu(1,1)-N-3) (mu(1,3)-N-3)](n)(2). Single crystal X-ray structures show that complex 1 is a linear trinuclear Ni(II) compound containing a mu(2)-phenwddo, an end-on (EO) azido and a syn-syn acetato bridge between the terminal and the central Ni(II) ions. Complex 2 can be viewed as a one-dimensional (1D) chain in which the triply bridged (di-mu(2)-phenoxido and EO azido) dimeric Ni-2 units are linked to each other in a zigzag pattern by a single end-to-end (EE) azido bridge. Variable-temperature magnetic susceptibility studies indicate the presence of moderate ferromagnetic exchange coupling in complex 1 with J value of 16.51(6) cm(-1). The magnetic behavior of 2 can be fitted in an alternating ferro- and antiferromagnetic model J(FM) = +34.2(2.8) cm(-1) and J(AF) = -21.6(1.1) cm(-1)] corresponding to the triple bridged dinuclear core and EE azido bridge respectively. Density functional theory (DFT) calculations were performed to corroborate the magnetic results of 1 and 2. The contributions of the different bridges toward magnetic interactions in both compounds have also been calculated.

Morphological Evolution in Air-Stable Metallic Iron Nanostructures and Their Magnetic Study

Iron nanostructures with morphology ranging from discrete nanoparticles to nearly monodisperse hierarchical nanostructures have been successfully synthesized using solvated metal atom dispersion (SMAD) method. Such a morphological evolution was realized by tuning the molar ratio of ligand to metal. Surface energy minimization in confluence with strong magnetic interactions and ligand-based stabilization results in the formation of nanospheres of iron. The as-prepared amorphous iron nanostructures exhibit remarkably high coercivity in comparison to the discrete nanoparticles and bulk counterpart. Annealing the as-prepared amorphous Fe nanostructures under anaerobic conditions affords air-stable carbon-encapsulated Fe(0) and Fe3C nanostructures with retention of the morphology. The resulting nanostructures were thoroughly analyzed by powder X-ray diffraction (PXRD), thermogravimetric analysis (TGA), transmission electron microscopy (TEM), and Raman spectroscopy. TGA brought out that Fe3C nanostructures are more robust toward oxidation than those of a-Fe. Finally, detailed magnetic studies were carried out by superconducting quantum interference device (SQUID) magnetometer and it was found that the magnetic properties remain conserved even upon exposure of the annealed samples to ambient conditions for months.

Stabilization of Cu-7 clusters in azide networks: syntheses, structures and magnetic behaviour

Two new azide bridged copper(II) coordination polymer compounds, Cu-7(N-3)(14)(C3H10N2)(C4H13N3)]n (I) and Cu-7(N-3)(14)(C3H10N2)(C5H15N3)(2)](n) (II) where C3H10N2 = 1,2-diaminopropane (1,2-DAP); C4H13N3 = di-ethylenetriamine (DETA); C5H15N3 = N-2-aminoethyl-1,3-propanediamine (AEDAP)] were prepared by employing a room temperature diffusion technique involving three layers. Single crystal studies reveal that both compounds I and II, have similar connectivity forming Cu7 clusters through end-on (EO) bonding of the azide. The Cu-7 clusters are connected through end-to-end (EE) connectivity of the azides forming three-dimensional structures. Magnetic studies confirmed the ferromagnetic interactions within the Cu-7 units and revealed the occurrence of concomitant ferro- and antiferro-magnetic interactions between these clusters. As a result I behaves as a weak-ferromagnet with T-C = 10 K.

Magnetocaloric effect and magnetic properties of Tb0.9 Sn0.1 MnO3

The magnetocaloric effect in magnetic materials is of great interest nowadays. In this article we present an investigation about the magnetic properties near the magnetic transition in a polycrystalline sample of a manganite Tb0.9 Sn0.1 MnO3. Particularly, we are interested in describing the nature of the magnetic interactions and the magnetocaloric effect in this compound. The temperature dependence of the magnetization was measured to determine the characteristics of the magnetic transition and the magnetic entropy change was calculated from magnetization curves at different temperatures. The magnetic solid is paramagnetic at high temperatures. We observe a dominant antiferromagnetic interaction below Tn =38 K for low applied magnetic fields; the presence of Sn doping in this compound decreases the Ńel temperature of the pure TbMnO3 system. A drastic increase in the magnetization as a function of temperature near the magnetic transition suggests a strong magnetocaloric effect. We found a large magnetic entropy change Δ SM (T) of about -4 J/kg K at H=3 T. We believe that the magnetic entropy change is associated with the magnetic transition and we interpret it as due to the coupling between the magnetic field and the spin ordering. This relatively large value and broad temperature interval (about 35 K) of the magnetocaloric effect make the present compound a promising candidate for magnetic refrigerators at low temperatures. © 2007 American Institute of Physics.

LiMn2-xTixO4 spinel-type compounds (x ≤ 1): Structural, electrical and magnetic properties

LiMn2-xTixO4 compounds with 0 ≤ x ≤ 1 were prepared by solid state reaction and Pechini technique. Powder X-ray diffraction showed that all samples crystallize with the spinel crystal structure (S.G. Fd3-m). The cubic unit-cell parameter increases with the Ti content. The influence of the Ti content and cationic distribution on the magnetic properties of the compounds was studied by measuring the temperature and magnetic field dependences of the magnetization: substitution by non-magnetic d0 Ti4+ ions appeared to weaken the magnetic interactions between the manganese ions. The electrical properties of LiMnTiO4 were studied by AC impedance spectroscopy and DC polarisation measurements, which revealed the electronic character of the conduction process. © 2006 Elsevier B.V. All rights reserved.

Magnetic Properties of FePt Nanoparticles Prepared by a Micellar Method

FePt nanoparticles with average size of 9 nm were synthesized using a diblock polymer micellar method combined with plasma treatment. To prevent from oxidation under ambient conditions, immediately after plasma treatment, the FePt nanoparticle arrays were in situ transferred into the film-growth chamber where they were covered by an SiO2 overlayer. A nearly complete transformation of L1(0) FePt was achieved for samples annealed at temperatures above 700 A degrees C. The well control on the FePt stoichiometry and avoidance from surface oxidation largely enhanced the coercivity, and a value as high as 10 kOe was obtained in this study. An evaluation of magnetic interactions was made using the so-called isothermal remanence (IRM) and dc-demagnetization (DCD) remanence curves and Kelly-Henkel plots (Delta M measurement). The Delta M measurement reveals that the resultant FePt nanoparticles exhibit a rather weak interparticle dipolar coupling, and the absence of interparticle exchange interaction suggests no significant particle agglomeration occurred during the post-annealing. Additionally, a slight parallel magnetic anisotropy was also observed. The results indicate the micellar method has a high potential in preparing FePt nanoparticle arrays used for ultrahigh density recording media.

MAGNETIC-PROPERTIES OF LANTHANUM MANGANITE AND VALENCE EQUILIBRIA OF MANGANESE

The paramagnetic susceptibility of lanthanum manganite has been measured over a wide temperature range (100-1073 K). On the basis of the thermodynamic equilibria between the various manganese ions with different valence and spin states and the magnetic interactions between the various manganese ions, a semiempirical formula has been proposed to calculate the paramagnetic susceptibilities of lanthanum manganite at different temperatures. The results indicate that most of the discrepancies between the calculated and experimental reciprocal susceptibilities of lanthanum manganite are less than 10% and that the relative contents of the various manganese ions in lanthanum manganite vary with temperature. The relative content of the trivalent manganese ion with a high spin state is dominant over the whole temperature range, while be relative content of the tetravalent manganese ion with a high spin state decreases monotonously with increasing temperature. At 300 K the calculated relative content of the tetravalent manganese ion in lanthanum manganite is about 34%, which is in good agreement with the experimental result (30%). There are some divalent manganese ions present in lanthanum manganite from low temperature to high temperature. The ratio of the relative contents of the tetravalent and divalent manganese ions in the compound varies with temperature. Above 750 K the relative content of the tetravalent manganese ion is less than that of the divalent manganese ion. The variation in the electrical resistivity of lanthanum manganite with temperature has also been interpreted reasonably.

Magnetic short-range order in the new ternary phase Mn8Pd15Si7

A new compound, Mn8Pd15Si7, is reported to crystallize in a face centered cubic unit cell of dimension a = 12.0141(2) angstrom, space groupFm (3) over barm, and can thus be classified as a G-phase. The crystal structure was studied by single crystal X-ray diffraction, X-ray and neutron powder diffraction and electron diffraction. A filled Mg6Cu16Si7 type structure was found, corresponding to the Sc11Ir4 type structure. The magnetic properties were investigated by magnetization measurements and Reverse Monte Carlo modeling of low temperature magnetic short-range order (SRO). Dominating near neighbor antiferromagnetic correlations were found between the Mn atoms and geometric frustration in combination with random magnetic interactions via metal sites with partial Mn occupancy were suggested to hinder formation of long-range magnetic order. 

Growth and magnetic properties of multiferroic LaxBi1-xMnO3 thin films

A comparative study of LaxBi1-xMnO3 thin films grown on SrTiO3 substrates is reported. It is shown that these films grow epitaxially in a narrow pressure-temperature range. A detailed structural and compositional characterization of the films is performed within the growth window. The structure and the magnetization of this system are investigated. We find a clear correlation between the magnetization and the unit-cell volume that we ascribe to Bi deficiency and the resultant introduction of a mixed valence on the Mn ions. On these grounds, we show that the reduced magnetization of LaxBi1-xMnO3 thin films compared to the bulk can be explained quantitatively by a simple model, taking into account the deviation from nominal composition and the Goodenough-Kanamori-Anderson rules of magnetic interactions.

Absence of collective effects in Heisenberg systems with localized magnetic moments

Existence of collective effects in magnetic coupling in ionic solids is studied by mapping spin eigenstates of the Heisenberg and exact nonrelativistic Hamiltonians on cluster models representing KNiF3, K2NiF4, NiO, and La2CuO4. Ab initio techniques are used to estimate the Heisenberg constant J. For clusters with two magnetic centers, the values obtained are about the same for models having more magnetic centers. The absence of collective effects in J strongly suggests that magnetic interactions in this kind of ionic solids are genuinely local and entangle only the two magnetic centers involved.

Local character of magnetic coupling in ionic solids

Magnetic interactions in ionic solids are studied using parameter-free methods designed to provide accurate energy differences associated with quantum states defining the Heisenberg constant J. For a series of ionic solids including KNiF3, K2NiF4, KCuF3, K2CuF4, and high- Tc parent compound La2CuO4, the J experimental value is quantitatively reproduced. This result has fundamental implications because J values have been calculated from a finite cluster model whereas experiments refer to infinite solids. The present study permits us to firmly establish that in these wide-gap insulators, J is determined from strongly local electronic interactions involving two magnetic centers only thus providing an ab initio support to commonly used model Hamiltonians.