Formation Of Dendritic Nanostructures In Pyrex Glass Anodically Bonded To Silicon Coated With An Aluminum Thin Film

Anodic bonding with thin films of metal or alloy as an intermediate layer, finds increasing applications in micro/nanoelectromechanical systems. At the bonding temperature of 350 degrees C, voltage of 400 V, and 30 min duration, the anodic bonding is completed between Pyrex glass and crystalline silicon coated with an aluminum thin film with a thickness comprised between 50 and 230 nm. Sodium-depleted layers and dendritic nanostructures were observed in Pyrex 7740 glass adjacent to the bonding interface. The sodium depletion width does not increase remarkably with the thickness of aluminum film. The dendritic nanostructures result from aluminum diffusion into the Pyrex glass. This experimental research is expected to enhance the understanding of how the depletion layer and dendritic nanostructures affect the quality of anodic bonding. (C) 2007 Elsevier B.V. All rights reserved.

Fractal Pattern Formation In Anodic Bonding Of Pyrex Glass/Al/Si

Anodic bonding of Pyrex glass/Al/Si is an important bonding technique in micro/nanoelectromechanical systems (MEMS/NEMS) industry. The anodic bonding of Pyrex 7740 glass/Aluminum film/Silicon is completed at the temperature from 300 degrees C to 375 degrees C with a bonding voltage between 150 V and 450 V. The fractal patterns are formed in the intermediate Al thin film. This pattern has the fractal dimension of the typical two-dimensional diffusion-limited aggregation (2D DLA) process, and the fractal dimension is around 1.7. The fractal patterns consist of Al and Si crystalline grains, and their occurrences are due to the limited diffusion, aggregation, and crystallization of Si and Al atoms in the intermediate Al layers. The formation of the fractal pattern is helpful to enhance the bonding strength between the Pyrex 7740 glass and the aluminum thin film coated on the crystal silicon substrates.

Tensile Tests Of Micro Anchors Anodically Bonded Between Pyrex Glass And Aluminum Thin Film Coated On Silicon Wafer

Micro anchor is a kind of typical structures in micro/nano electromechanical systems (MEMS/NEMS), and it can be made by anodic bonding process, with thin films of metal or alloy as an intermediate layer. At the relative low temperature and voltage, specimens with actually sized micro anchor structures were anodically bonded using Pyrex 7740 glass and patterned crystalline silicon chips coated with aluminum thin film with a thickness comprised between 50 nm and 230 nm. To evaluate the bonding quality, tensile pulling tests have been finished with newly designed flexible fixtures for these specimens. The experimental results exhibit that the bonding tensile strength increases with the bonding temperature and voltage, but it decreases with the increase of the thickness of Al intermediate layer. This kind of thickness effect of the intermediate layer was not mentioned in the literature on anodic bonding. (C) 2008 Elsevier Ltd. All rights reserved.

Formation of dendritic nanostructures in Pyrex glass anodically bonded to silicon coated with an aluminum thin film

Anodic bonding with thin films of metal or alloy as an intermediate layer, finds increasing applications in micro/nanoelectromechanical systems. At the bonding temperature of 350 degrees C, voltage of 400 V, and 30 min duration, the anodic bonding is completed between Pyrex glass and crystalline silicon coated with an aluminum thin film with a thickness comprised between 50 and 230 nm. Sodium-depleted layers and dendritic nanostructures were observed in Pyrex 7740 glass adjacent to the bonding interface. The sodium depletion width does not increase remarkably with the thickness of aluminum film. The dendritic nanostructures result from aluminum diffusion into the Pyrex glass. This experimental research is expected to enhance the understanding of how the depletion layer and dendritic nanostructures affect the quality of anodic bonding. (C) 2007 Elsevier B.V. All rights reserved.

Silicon nanopore array structure using porous anodic alumina

A free-standing, bidirectionally permeable and ultra-thin (500-1000 nm) porous anodic alumina membrane was fabricated using a two-step aluminium anodization process, which was then placed on top of a silicon film as an etching mask. The pattern was transferred to silicon using dry-etching technology, and the silicon nanopore array structure was formed. The factors which afflct the pattern transfer process are discussed. Observation of the nanopatterned sample under a scanning electron microscope shows that the structure obtained by this method is made up of uniform and highly ordered holes, which attains to 125 nm depth. The photoluminescence spectrum from the nanopatterned sample,the surface of which has been thermal-oxidized, shows that the the luminesce is evidently enhanced, the mechanism of which is based on the normally weak TO phonon assisted bandgap light-emission process, and the physical reasons that underlic the enhancement have been analyzed. The PL results do show an attractive optical characteristic, which provides a promising pathway to achieve efficient light emission from silicon.

Anodic Stripping Voltammetry at Bismuth-Coated and Uncoated Carbon Microdisk Electrodes:Application to Trace Metals Analysis in Flood Samples

This article reports on the performance of a bismuth-coated carbon microdisk electrode (BiFμE) for the determination of trace heavy metals by anodic stripping voltammetry (ASV). The BiFμE was prepared by electrodeposition of a metallic bismuth film onto the microdisk, by applying an in-situ electroplating procedure. To test the performance of the BiFμE, ASV measurements were performed on synthetic solutions containing Cd2+, Pb2+, and Cu2+ as target ions. The results indicated that cadmium and lead gave well-defined ASV peaks with no interference, and their quantitative determination could be carried out straightforwardly. In particular, linear calibration curves over the range 5.0 x 10-8-1.0 x 10-6M for both ions, and detection limits of 7.8 and 2.9 nM, for cadmium and lead, respectively, after applying a 60 sec preconcentration step, were obtained. The reproducibility was also satisfactory, the relative standard deviation (RSD) being within 2.5% for both ions. Copper, instead, gave an ASV response that. in most experimental conditions, overlapped with that of bismuth. This circumstance made the determination of copper at the BiFμE difficult. Since the latter element could be detected reliably at the uncoated carbon microdisk electrode (CμE), both BiFμE and CμE were employed, respectively, for the determination of lead and copper ions in drinking water, wine, and tomato sauce.

Properties of poly(sodium 4-styrenesulfonate)-ionic liquid composite film and its application in the determination of trace metals combined with bismuth film electrode

A new kind of bismuth film modified electrode to sensitively detect trace metal ions based on incorporating highly conductive ionic liquids 1-butyl-3-methyl-imidazolium hexafluorophosphate (BMIMPF6) in solid matrices at glassy carbon (GC) was investigated. Poly(sodium 4-styrenesulfonate) (PSS), silica, and Nafion were selected as the solid matrices. The electrochemical properties of the mixed films modified GC were evaluated. The electron transfer rate of Fe(CN)(6)(4-)/Fe(CN)(6)(3-) can be effectively improved at the PSS-BMIMPF6 modified GC.

Nafion-graphene nanocomposite film as enhanced sensing platform for ultrasensitive determination of cadmium

In this work, an ultrasensitive platform for the detection of cadmium (Cd2+) combining the nafion-graphene nanocomposite film with differential pulse anodic stripping voltammetry (DPASV) analysis was presented. It is found that this sensing platform exhibits enhanced response to the determination of the Cd2+ and has been used to determine the Cd2+ in real sample with good recovery.

High-sensitivity determination of lead and cadmium based on the Nafion-graphene composite film

Graphene nanosheets, dispersed in Nafion (Nafion-G) solution, were used in combination with in situ plated bismuth film electrode for fabricating the enhanced electrochemical sensing platform to determine the lead (Pb2+) and cadmium (Cd2+) by differential pulse anodic stripping voltammetry (DPASV). The electrochemical properties of the composite film modified glassy carbon electrode were investigated. It is found that the prepared Nafion-G composite film not only exhibited improved sensitivity for the metal ion detections, but also alleviated the interferences due to the synergistic effect of graphene nanosheets and Nafion. The linear calibration curves ranged from 0.5 mu g L-1 to 50 mu g L-1 for Pb2+ and 1.5 mu g L-1 to 30 mu g L-1 for Cd2+. respectively. The detection limits (S/N = 3) were estimated to be around 0.02 mu g L-1 for Pb2+ and Cd2+. The practical application of the proposed method was verified in the water sample determination.

The electrocatalytic oxidation of ascorbic acid on polyaniline film synthesized in the presence of camphorsulfonic acid

Polyaniline-camphorsulfonic acid (PAN-CSA) composite film on platinum electrode surface has been synthesized via the electrochemical polymerization of aniline in the presence of camphorsulfonic acid (CSA). It was found that the doping of polyaniline (PAN) with CSA extends the electroactivity of PAN in neutral and even in alkaline media. The PAN-CSA composite film coated platinum electrodes are shown to be good electrocatalytic surfaces for the oxidation of ascorbic acid (AA) in phosphate buffer solution (PBS) of pH 7.0. The anodic peak potential of AA shifts from 0.63 V at the bare platinum electrode to 0.34 V at the PAN-CSA composite modified platinum electrode with a greatly enhanced current response. A linear calibration graph is obtained over the AA concentration range of 5-50 mM using cyclic voltammetry. The kinetics of the catalytic reaction are investigated using rotating disk electrode voltammetry and chronoamperometry. The results are explained using the theory of electrocatalytic reactions at chemically modified electrodes. The PAN-CSA composite on the electrode surface shows good reproducibility and stability.

Electrocatalytic oxidation of ascorbic acid by ferrocene in lipid film cast on a glassy carbon electrode

A ferrocene-dimyristoyl phosphatidylcholine (DMPC) film electrode was prepared by casting the solution of ferrocene and DMPC in chloroform onto a glassy carbon electrode surface. Ferrocene retained in the biological membrane gave a couple of irreversible peaks of cyclic voltammogram. The electrode exhibited good electrocatalytic activity for the oxidation of ascorbic acid (H(2)A) in phosphate buffer (pH 6.64) with an anodic peak potential of +340 mV (vs. Ag/AgCl). The anodic current was directly proportional to the square root of the scan rate below 150 mV s(-1). The influence of the pH value was investigated and it was observed that pH 6.64 was the suitable value to the anodic peak potential and current. The thickness of the film and the interference of uric acid were also studied. The electrode can be used to determine H(2)A in the presence of equimolar uric acid. The catalytic peak current increased linearly with the concentration of H(2)A in the range of 1 X 10(-4)-5 X 10(-3) mol L-1.

Electrocatalytic oxidation of ascorbic acid by norepinephrine embedded in lipid cast film at glassy carbon electrode

A stable lipid cast film was made by casting a lipid in chloroform onto a glassy carbon electrode. We imbedded a new mediator norepinephrine into this lipid cast film, which was considered as a biological membrane model. Through electro catalytic oxidation of ascorbic acid by this system, the anodic overpotential was reduced by about 250 mV compared with that obtained at a bare glassy carbon electrode. The electrochemical behavior of norepinephrine in the cast film was controlled by diffusion. The obtained diffusion coefficient of ascorbic acid was 1.87 x 10(-5) cm 2 s(-1). The catalytic current increased linearly with the concentration of ascorbic acid in the range from 0.5 to 10 mM. Using cyclic voltammetry, we obtained two peaks for ascorbic acid and uric acid in the same solution. The separation between the two peaks is about 147 mV. (C) 2001 Elsevier Science Ltd. All rights reserved.

Oxidation of NADH by dopamine incorporated in lipid film cast onto a glassy carbon electrode

Stable lipid film was made by casting lipid in chloroform onto a glassy carbon electrode. This model of a biological membrane was used to investigate the oxidation of dihydronicotinamide adenine dinucleotide (NADH) by dopamine. After this electrode had been immersed in dopamine solution for 10 h, it was found that some dopamine had been incorporated in the film. The cyclic voltammogram was obtained for the oxidation of 2.0 X 10(-3) mol 1(-1) NADH with dopamine incorporated in the films. All electrochemical experiments were performed in 0.005 mol 1(-1) phosphate buffer (pH 7.0) containing 0.1 mol 1(-1) NaCl without oxygen. The oxidation current increased gradually with successive sweeps and reached steady state. It was a different phenomenon from previous results. The anodic overpotential was reduced by about 130 mV compared with that obtained at a bare glassy carbon electrode. The diffusion coefficient for 2.0 X 10(-3) mol 1(-1) NADH was 6.7 X 10(-6) cm(2) s(-1). (C) 1999 Elsevier Science S.A. All rights reserved.

Unidirectional current flow of reversible redox couples on a MoO3 film-modified microelectrode

In this paper, we have investigated the reactivity of the molybdenum oxide film toward some standard redox systems (e.g., ferrocene (Fc) and its derivatives) and observed a few interesting phenomena. The results demonstrate that the electrochemical behaviour of Fc and its derivatives at the oxide-modified carbon fiber (CF) microelectrode differs from that at a bare CF microelectrode, The conductivity of the molybdenum oxide film is seriously affected by the range and the direction of the potential scan, which influences the electrochemical behaviour of these redox systems at the film electrode. If the cycling potential is more positive than the reduction potential of the molybdenum oxide film, the reduction and oxidation peak currents of Fc and its derivatives could not be observed. The result indicates that the molybdenum oxide film on a microelectrode surface cannot transfer electrons between the surface of the electrode and Fc or its derivatives due to the existence of a high resistance between the interface in these potential ranges. On the other hand, if the lower limit of the scan potential was extended to a potential more negative than the reduction peak potential of the film, the oxidation peak of Fc or its derivatives appeared at about the potential relative to E-0 of Fc or its derivatives on the bare electrode, and the peak current is proportional to the concentration of these couples in the electrolyte. To our surprise, the peak height on the modified electrode is much larger than that on the bare CF microelectrode under the same conditions in the range of low concentration of these couples, and the oxidation peak potential of these couples is more negative than that on the bare CF microelectrode. On the basis of the experimental observation, we propose that these redox couples may undergo an interaction with the reduction state of the molybdenum oxide film. The new phenomena that we observed have been explained by using this interaction. (C) 1997 Elsevier Science S.A.

Electrocatalytic oxidation of methanol on polypyrrole film modified with platinum microparticles

The electrocatalytic oxidation of methanol on polypyrrole (PPy) film modified with platinum microparticles has been studied by means of electrochemical and in situ Fourier transform infrared techniques. The Pt microparticles, which were incorporated in the PPy film by the technique of cyclic voltammetry, were uniformly dispersed. The modified electrode exhibits significant electrocatalytic activity for the oxidation of methanol. The catalytic activities were found to be dependent on Pt loading and the thickness of the PPy film. The linearly adsorbed CO species is the only intermediate of electrochemical oxidation of methanol and can be readily oxidized at the modified electrodes. The enhanced electrocatalytic activities may be due to the uniform dispersion of Pt microparticles in the PPy film and the synergistic effects of the highly dispersed Pt microparticles and the PPy film. Finally, a reaction mechanism is suggested.