The effects of ZnGa2O4 formation on structural and optical properties of ZnO : Ga powders

Gallium-doped zinc oxide (ZnO:Ga 1, 2 3, 4 and 5 at%) samples were prepared in powder form by modifying the Pechini method. The formation of zinc gallate (ZnGa2O4) With the spinel crystal structure was observed even in ZnO:Ga 1 at% by X-ray diffraction. The presence of ZnGa2O4 in ZnO:Ga samples was also evidenced by luminescence spectroscopy through its blue emission at 430 nm, assigned to charge transfer between Ga3+ at regular octahedral symmetry and its surrounding O2- ions. The amount of ZnGa2O4 increases as the dopant concentration increases, as observed by the quantitative phase analysis by the Rietveld method. (C) 2006 Elsevier B.V. All rights reserved.

Biodisponibilidade de fontes orgânicas e inorgânicas de zinco em ovinos

This research was done to compare the effects of different zinc sources and doses in the Santa Ines sheep diet. Forty lambs at weaning, with 18,4kg BW were randomly allotted and fed 10 treatments: 1- base diet without zinc supplementation; 2- base diet + 200mg Zn/kg of DM as zinc oxide; 3- base diet + 400mg Zn/kg of DM as zinc oxide; 4- base diet + 600mg Zn/kg of DM as zinc oxide; 5- base diet + 200mg Zn/kg of DM as amino acid zinc; 6- base diet + 400mg Zn/kg of DM as amino acid zinc; 7- base diet + 600mg Zn/kg of DM as amino acid zinc; 8- base diet + 200mg Zn/kg of DM as proteinato zinc; 9- base diet + 400mg Zn/kg of DM as proteinato zinc; 10- base diet + 600mg Zn/kg of DM as proteinato zinc. The animals were weighed and sampled for blood zinc analysis, phosphatase alkaline analysis and immunoglobulins G and M analysis. At the end of the experiment liver samples were collected to study the zinc hepatic levels. There was no difference in phosphatase alkaline levels, hepatic zinc levels and weight gain (P>0,05) but differences (P<0,05) in plasmatic zinc levels and in IgG and IgM levels were observed. Based on liver tissue uptake, estimates of the zinc bioavailability, through the regression equations showed that the organic and inorganic sources of zinc did not differ.

Microwave Hydrothermal Synthesis and Photocatalytic Performance of ZnO and M:ZnO Nanostructures (M = V, Fe, Co)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Changes on iron electrode surface during hydrogen permeation in borate buffer solution

Hydrogen interaction with oxide films grown on iron electrodes at open circuit potential (E-oc) and in the passive region (+0.30 V-ECS) was studied by chronopotentiometry, chronoamperometry and electrochemical impedance spectroscopy techniques. The results were obtained in deaerated 0.3 mol L-1 H3BO3 + 0.075 mol L-1 Na2B4O7 (BB, pH 8.4) solution before, during and after hydrogen permeation. The iron oxide film modification was also investigated by means of in situ X-ray absorption near-edge spectroscopy (XANES) and scanning electrochemical microscopy (SECM) before and during hydrogen permeation. The main conclusion was that the passive film is reduced during the hydrogen diffusion. The hydrogen permeation stabilizes the iron surface at a potential close to the thermodynamic water stability line where hydrogen evolution can occur. The stationary condition required for the determination of the permeation parameters cannot be easily attained on iron surface during hydrogen permeation. Moreover, additional attention must be paid when obtaining the transport parameters using the classical permeation cell. (c) 2007 Elsevier Ltd. All rights reserved.

CATHODIC BEHAVIOUR of ANODIZED TITANIUM IN SIMULATED PHYSIOLOGICAL CONDITIONS

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

A new interpretation for the degradation phenomenon of ZnO varistors

The electrical degradation phenomena of zinc oxide-based varistors were studied using a high-energy current pulse and a.c. polarization at different temperatures. Activation energy measurements during the degradation process showed that these phenomena are associated with diffusion and that the diffusion-controlling species are slower than Zn., For degradation promoted by current pulses of 8×20 μs, the Schottky potential barrier deformation was measured. A decrease in height and width of the potential barrier due to the reduction of surface states density, N s, without a significant change in donor density, N d, was observed. To explain these results, a modification of the unstable components model is proposed for the potential barrier in which the degradation is due to oxi-reduction reactions between atomic defects. These reactions promote the elimination of zinc vacancies and/or adsorbed oxygen on the grain boundaries. © 1992 Chapman & Hall.

Radiographic and microbiologic evaluation of posttreatment apical and periapical repair of root canals of dogs' teeth with experimentally induced chronic lesion

The objective of the present study was to evaluate radiographically and bacteriologically apical and periapical repair in dogs' teeth with induced chronic periapical lesions with the use of two different operative techniques (techniques 1 and 2). The study was conducted on 40 root canals of upper and lower premolars from two dogs aged approximately 12 months. Periapical lesions were induced by leaving the root canals exposed to the oral environment for 5 days and then sealing them with zinc oxide-eugenol for 45 days. After this period, radiographic examination revealed the occurrence of a radiolucent lesion and endodontic treatment was started. The two techniques did not differ in terms of chemomechanical preparation, final filling, or type of cement, but differed in terms of irrigating solution and the presence of an antibacterial dressing. Thus 4% to 6% hypochlorite and hydrogen peroxide (10 volumes) were used in technique 1 during chemomechanical preparation and an antibacterial dressing based on calcium hydroxide was applied between sessions, whereas Dakin's fluid (0.5% sodium hypochlorite solution) and a final filling with no antibacterial dressing were used in technique 2. After chemomechanical preparation, the root canals were filled with gutta-percha cones and Sealapex (Sealapex-Sybron, Kerr, Sao Paulo, Brazil), and the animals were killed 270 days after the final filling. Blocks were cut into 6-μm sections and stained by the Brown and Brenn method. Radiographic, histomicrobiologic and statistical analysis permitted us to conclude the following: radiographically there was a marked reduction or even the disappearance of the radiolucent area present before treatment with greater success in the group treated with technique 1 (group I) than in the group treated with technique 2 (group II); the extent of bacterial invasion of dentinal tubules was greater and more intense in group II than in group I; and the amount of microorganisms detected in the ramifications of the apical delta and in the lumen of the root canal was intense in group II and mild or absent in group I. © 1994.

Effect of dentine surface treatment on leakage of root fillings with a glass ionomer sealer.

The purpose of this study was to observe the quality of seal of the glass ionomer cement, Ketac-Endo, after treatment of the root canal wall. The root canals of 140 extracted human teeth were prepared biomechanically. The root canals were treated with either EDTA or received an intracanal dressing of calcium hydroxide or camphorated paramonochlorphenol. The root canals were filled by the lateral condensation technique with gutta-percha points and the sealer Ketac-Endo, or zinc oxide-eugenol cement or Sealapex. The teeth were placed into a 2% methylene blue dye solution inside a flask, which was attached to a vacuum pump. Leakage was measured linearly. Sealapex exhibited significantly less leakage than Ketac-Endo or zinc oxide-eugenol cement (P<0.01). The use of EDTA and intermediary dressings reduced significantly (P<0.01) the leakage observed with the zinc oxide-eugenol sealer and Ketac-Endo.

Apical leakage following root canal dressing with calcium hydroxide.

The purpose of this study was to analyse the apical leakage in teeth filled by the lateral condensation technique following medication with calcium hydroxide. One hundred and twenty extracted human teeth were biomechanically prepared by using exclusively reaming motion with files up to #40. Half of the teeth received a calcium hydroxide dressing for 3 days. The medication was removed by irrigation and reaming motion with files #40 up to #70. The teeth were divided in 6 experimental groups, according to the dimension of the utilized instrument. The root canals were filled and posteriorly the teeth were placed into a 2% methylene blue dye solution inside a flask, which was attached to a vacuum pump. Leakage was measured linearly, and the results showed significantly (p<0.01) less leakage in the experimental groups that received calcium hydroxide dressings than in the control groups. The results persisted even after the removal of 300 micrometers of dentin from the root canal dentinal walls.

pH changes at the surface of root dentin when using root canal sealers containing calcium hydroxide

The purpose of this study was to investigate long-term pH changes in cavities prepared in root surface dentin of extracted teeth after obturation of the root canal with gutta-percha and a variety of sealers containing calcium hydroxide. After cleaning and shaping, root canals in 50 recently extracted, human single-rooted teeth were divided into five groups. Each of four groups was obturated with gutta-percha and either Sealapex, Sealer 26, Apexit, or CRCS, all of which contain calcium hydroxide. The remaining group served as the control and was not obturated with gutta-percha or sealer. Cavities were prepared in the facial surface of the roots in the cervical and middle regions. The pH was measured in these dentinal cavities at the initiation of the experiment, and 3, 7, 14, 21, 28, 45, 60, 90, and 120 days after obturation. Results indicate that the pH at the surface of the root does not become alkaline when calcium hydroxide cements are used as root canal sealers. Regardless of the sealer used, the observed pattern of pH change was not different from that seen in the control group of roots that were not treated with sealer. It is concluded that calcium hydroxide-containing cements, although suitable for use as root canal sealants, do not produce an alkaline pH at the root surface. If such a pH change is related to treatment of root resorption, these sealants do not contribute to this treatment. Copyright © 1996 by The American Association of Endodontists.

Apical leakage after root canal filling with an experimental calcium hydroxide gutta-percha point

This study was an in vitro analysis of the apical seal of root canals filled with an experimental calcium hydroxide gutta-percha point. One hundred and ten recently extracted human permanent teeth with a single root were used. The root canals were biomechanically prepared, and some received a dressing of calcium hydroxide for 7 days. Root canals not dressed were filled by the lateral condensation technique with either regular gutta-percha or calcium hydroxide gutta-percha points. The dressed root canals were filled with the same sealers and regular gutta-percha points. The specimens were placed into a 2% methylene blue dye solution under vacuum, and the apical leakage was linearly evaluated. The experimental groups with calcium hydroxide dressing and the one with calcium hydroxide gutta-percha points exhibited significantly (p < 0.05) less leakage than the groups filled with regular gutta-percha points. The results obtained indicated that calcium hydroxide guttapercha points produced an improvement in the apical sealing quality of the root canal filling. Copyright © 1996 by The American Association of Endodontists.

Calcium hydroxide root canal sealers: Evaluation of pH, calcium ion concentration and conductivity

The calcium hydroxide ionization of four root canal sealers (Sealapex, CRCS, Sealer 26, and Apexit) was studied by measuring conductivity and pH and by conducting atomic absorption spectrophotometry. Samples 6 mm in diameter and 15 mm long were prepared from these sealers. After setting and 48 h storage in a desiccator, five samples of each material were placed in 50 mL distilled water and analysed after 0,1,2,4, 6 and 24 h and 5, 15 and 30 days. The results showed that Sealapex was the root canal sealer showing the highest pH, ionic calcium and total calcium values (P<0.05) throughout the experimental period, followed by CRCS, Apexit and Sealer 26.

Effect of different root canal sealers on periapical repair of teeth with chronic periradicular periodontitis

Teeth with induced chronic periradicular periodontitis in dogs were root canal treated. After the biomechanical preparation, using K files and 5.25% sodium hypochlorite as the irrigant solution, all root canals were dressed with an antibacterial dressing based on calcium hydroxide, which was left in place for 7 days. After this time, the root canals were obturated with lateral condensation of cold gutta-percha with either a calcium hydroxide root canal filling material (Sealapex) or a zinc oxide-eugenol sealer (Fill Canal). After 270 days, histopathological analysis showed better apical and periapical repair in the teeth obturated with Sealapex (P < 0.05).

Calcium hydroxide and a corticosteroid-antibiotic association as dressings in cases of biopulpectomy. A comparative study in dogs' teeth.

The subject of this paper was to study the behavior of the periapical tissues of dogs' teeth after biopulpectomy and dressing with calcium hydroxide or a corticosteroid-antibiotic association, before root canal filling with zinc oxide eugenol (ZOE) or Sealapex sealers. The teeth were overinstrumented and dressed for 7 days before the root canal filling. The animals were sacrificed 180 days after treatment and the specimens were prepared for morphological analysis. Specimens treated with Sealapex presented a higher number of cases with biological closure than ZOE. When the root canals were filled with ZOE, better results were observed with the use of the Ca(OH)2 dressing.