Influence of water flow rate on shear bond strength of resin composite to Er : YAG cavity preparation

Purpose: To evaluate in vitro the influence of water flow rate on shear bond strength of a resin composite to enamel and dentin after Er:YAG cavity preparation. Methods: Ten bovine incisors were selected and roots removed. Crowns were sectioned in four pieces, resulting in 40 samples that were individually embedded in polyester resin (n=10), and ground to plane the enamel and expose the dentin. The bonding site was delimited and samples were randomly assigned according to cavity preparation: (1) Er:YAG/1.0 mL/minute; (2) Er:YAG/1.5 mL/minute; (3) Er:YAG/2.0 mL/minute and (4) High speed handpiece/bur (control group). Samples were fixed to a metallic device, where composite resin cylinders were prepared. Subsequently, they were stored for 24 hours and subjected to a shear bond strength test (500N at 0.5 mm/minute). Results: Means (MPa) were: enamel: 1: 12.8; 2: 16.8; 3: 17.5; 4: 36.0 and Dentin: 1: 13.6; 2: 18.7; 3: 12.1; 4: 21.3. Data were submitted to ANOVA and Tukey`s test. Adhesion to enamel was more efficient than for dentin. The cavities prepared with conventional bur (control) presented higher statistically significant bond strength values (P<0.05) than for Er:YAG laser for both enamel and dentin. No significant differences were observed between water flow rates employed during enamel ablation. For dentin, the shear bond strength of 2.0 mL/minute water flow rate was lower than for 1.5 mL/minute and 1.0 mL/minute rates. The Er:YAG laser adversely affected shear bond strength of resin composite to both enamel and dentin, regardless of the water flow rate used.

Influence of dentin cavity surface finishing on micro-tensile bond strength of adhesives

The current trend toward minimal-invasive dentistry has introduced innovative techniques for cavity preparation. Chemical vapor deposition (CVD) and laser-irradiation technology have been employed as an alternative to the common use of regular burs in high-speed turbines. Objectives. The purpose of this study was to assess the influence of alternative techniques for cavity preparation on the bonding effectiveness of different adhesives to dentin, and to evaluate the morphological characteristics of dentin prepared with those techniques. Methods. One etch&rinse adhesive (OptiBond FL, Kerr) and three self-etch systems (Adper Prompt L-Pop, 3M ESPE; Clearfil SE Bond, Kuraray; Clearfil S3 Bond, Kuraray) were applied on dentin prepared with a regular bur in a turbine, with a CVD bur in a turbine, with a CVD tip in ultrasound and with an ErCr:YSGG laser. The micro-tensile bond strength (mu TBS) was determined after storage in water for 24 h at 37 degrees C, and morphological evaluation was performed by means of field -emission -gun scanning electron microscopy (Feg-SEM). Results. Feg-SEM evaluation revealed different morphological features on the dentin surface after the usage of both the conventional and alternative techniques for cavity preparation, more specifically regarding smear-layer thickness and surface roughness. CVD bur-cut, CVD ultra-sonoabraded and laser-irradiated dentin resulted in lower mu TBSs than conventionally bur-cut dentin, irrespective of the adhesive employed. Significance. The techniques, such as CVD diamond-bur cutting, CVD diamond ultra-sonoabrasion and laser-irradiation, used for cavity preparation may affect the bonding effectiveness of adhesives to dentin, irrespective of their acidity or approach. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influência da laserterapia na proliferação de células-tronco do ligamento periodontal humano

Low level laser irradiation (LLLI) has been used in Dentistry to promote wound healing and tissue regeneration. The literature shows a positive effect of LLLI on cell proliferation, but little is known about their effectiveness in promoting stem cells proliferation. The aim of this study was to evaluate the effect of LLLI on the proliferative rate of human periodontal ligament stem cells. Extracts of periodontal ligament were isolated from two third molars removed by surgical and/or orthodontic indication. After enzymatic digestion, the cells were grown in α-MEM culture medium supplemented with antibiotics and 15% fetal bovine serum. On the third subculture, the cells were irradiated with a InGaAlP-diode laser, using two different energy densities (0,5J/cm 2 - 16 seconds and 1,0J/cm² - 33 seconds), with wavelength of 660nm and output power of 30mW. A new irradiation, using the same parameters, was performed 48h after the first. A control group (non irradiated) was kept under the same experimental culture conditions. The Trypan blue exclusion test and the mitochondrial activity of the cells measured by MTT [3-(4,5-Dimethylthiazol-2-yl)-2,5-Diphenyltetrazolium Bromide] essay were performed to assess the cell proliferation in the intervals of 0, 24, 48 e 72 h after irradiation. The data of cell counts were submitted to nonparametrical statistical tests (Kruskal-Wallis and Mann-Whitney), considering a confidence interval of 95%. DAPI (4 -6-Diamidino-2-phenylindole) staining of the cells was performed at 72h interval to evaluate possible nuclear morphological changes induced by LLLI. The results of this study show that the energy density of 1,0 J/cm² promoted greater cell proliferation compared to the other groups (control and 0,5 J/cm²) at intervals of 48 and 72h. The mitochondrial activity measured by MTT essay showed similar results to the Trypan blue cell counting test. The group irradiated with 1,0J/cm² exhibited a significantly higher MTT activity in the intervals of 48 and 72h, when compared to the group irradiated with 0,5J/cm². No nuclear morphological change was observed in the cells from the three groups studied. It is concluded that LLLI has stimulatory effects on the proliferation of human periodontal ligament stem cells. Therefore, the use of laser irradiation in this cell type may be important to promote future advances in periodontal regeneration

Treatment of Experimental Periodontal Disease by Photodynamic Therapy in Rats With Diabetes

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Treatment of experimental periodontal disease by photodynamic therapy in immunosuppressed rats

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Radiographic assessment of photodynamic therapy as an adjunctive treatment on induced periodontitis in immunosuppressed rats

Objective: The aim of this study was to assess radiographically the effect of photodynamic therapy (PDT) as an adjunctive treatment to scaling and root planing (SRP) on induced periodontitis in dexamethasone-induced immunosuppressed rats. Material and Methods: The animals were divided into 2 groups: ND group (n=60): saline treatment; D group (n=60): dexamethasone treatment. In both ND and D groups, periodontal disease was induced by the placement of a ligature in the left first mandibular molar. After 7 days, ligature was removed and all animals received SRP, being divided according to the following treatments: SRP: saline and PDT: phenothiazinium dye (TBO) plus laser irradiation. Ten animals per treatment were killed at 7, 15 and 30 days. The distance between the cementoenamel junction and the height of the alveolar bone crest in the mesial surface of the mandibular left first molars was determined in millimeters in each radiograph. The radiographic values were analyzed statistically by ANOVA and Tukey's test at a p value <0.05. Results: Intragroup radiographic assessment (ND and D groups) showed that there was statistically significant less bone loss in the animals treated with PDT in all experimental periods compared to those submitted to SRP. Intergroup radiographic analysis (ND and D groups) demonstrated that there was greater bone loss in the ND group treated with SRP compared to the D group treated with PDT at 7 and 30 days. Conclusion: PDT was an effective adjunctive treatment to SRP on induced periodontitis in dexamethasone-induced immunosuppressed rats.

Clinical and microbiological effects of photodynamic therapy associated with nonsurgical periodontal treatment. A 6-month follow-up

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Treatment of experimental periodontal disease with antimicrobial photodynamic therapy in nicotine-modified rats

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Susceptibility of Candida albicans, Staphylococcus aureus, and Streptococcus mutans biofilms to photodynamic inactivation: an in vitro study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effects of Nd : YAG and Er : YAG lasers on the sealing of root canal fillings

Objective: the ability of the laser irradiation to promote the cleaning and disinfection of the radicular canal system has become this type of treatment in a viable and real alternative in endodontics. The purpose of this study was to evaluate the apical marginal sealing of root canal fillings after the irradiation with the laser of Nd:YAG or of Er:YAG. Materials and Methods: Forty-two human, extracted single-rooted teeth had their crowns sectioned and the root canals prepared with a no. 70 K-file. Then, they were dried and divided into three groups according to canal wall treatment: group 1: the canals were filled with EDTA for 3 min, followed by irrigation with 1% sodium hypochlorite solution; group 2: the canal walls were irradiated with Nd:YAG laser; and group 3: the canal walls were irradiated with Er:YAG laser. Afterwards, the root canals were obturated by the lateral condensation technique. The roots were externally waterproof, except in the apical foramen and immerged in 2% methylene blue aqueous solution during 48 hours. Results: the results showed that the largest infiltrations happened in the group 3-Er:YAG (7.3 mm), proceeded by the group 1-EDTA (1.6 mm) and by the group 2-Nd:YAG (0.6 mm). The group Er:YAG differed statistically of the others (p < 0.05). Conclusion: It was concluded that the Er:YAG laser intracanal irradiation previously to the root canal filling must be used with caution until future research is define the best parameters for it's use.

Raman investigation of structural photoinduced irreversible changes of Ga10Ge25S65 chalcogenide glasses

The influence of time exposure, when exposed to above band gap light (3,52 eV) and annealing, on Ga10Ge25S65 glasses has been studied through their effects on the structure and optical properties. To evaluate the photostructural change infrared and Raman spectra for bulk Ga10Ge25S65 glasses have been measured before and after exposure. The Raman spectra are interpreted in terms of models in which the Ge atoms are fourfold coordinated and the S atoms are two fold coordinated. The observed changes in the spectral region of (S-S) stretching vibration (470-490 cm (-1)) is a direct evidence for the occurrence of important structural changes in local bonding configuration caused by optical irradiation. It is shown that the dominant photostrucural changes are chain formation tendency of the chalcogenide atoms under the laser irradiation rather than rings.

Holographic recording in [Sb(Po-3)(3)](n)-Sb2O3 glassy films by photoinduced volume and refraction index changes

Glassy films of 0.2[Sb(PO3)(3)]-0,8Sb(2)O(3) with 0.8 mum-thickness were deposited on quartz substrates by electron beam evaporation. A contraction in the film thickness (photoinduced decrease in volume) and photobleaching effect associated with a decrease of up to 25% in the index of refraction has been observed in the films after irradiation near the bandgap (3.89 eV), using the 350.7 nm (3.54 eV) Kr+ ion laser line with 2.5 W/cm(2) for 30 min. A loss of 30% in the phosphorus concentration was measured by wavelength dispersive X-ray microanalysis in the film after laser irradiation with 5.0 W/cm(2) for 1.0 h. These photoinduced changes in the samples are dependent on the power density and intensity profile of the laser beam. Using a Lloyd's mirror setup for continuous wave holography it was possible to record holographic gratings with period from 500 nm up to 20 mum and depth profile of similar to50 nm in the films after laser irradiation with 5.0 W/cm(2) for 1 h. Real-time diffraction efficiency measurements have shown that ultraviolet irradiation induces first a refractive index grating formation, and after this, the photocon traction effect takes place generating an irreversible relief grating. Diffraction efficiency up to 10% was achieved for the recorded gratings. 3D-refraction index measurements and atomic force microscopy images are presented. (C) 2004 Elsevier B.V. All rights reserved.

Indocyanine green nanoparticles useful for photomedicine

Objective: the aim of this study was to evaluate the potential application of biodegradable nanoparticles (NPs) containing indocyanine green (ICG) in photodynamic therapy (PDT). Methods: Important parameters, such as particle size and external morphology, were established by dynamic light scattering (DLS) and scanning electron microscopy (SEM). Also, drug encapsulation efficiency and in vitro release behavior were evaluated by spectroscopic methods. Results: the particles are spherical in shape, they exhibit an 817-nm diameter, and they have a low tendency to aggregate. The loading efficiency was 65%. ICG photophysical parameters showed a bathocromic shift in ICG-loaded nanoparticles (ICG-NP). Analysis of the cell P388-D1 in the presence of the ICG-NP by SEM showed that the majority of the nanoparticles were uptaken by phagocytic cells after 2 h of incubation. After laser irradiation photodamage was observed in P388-D1 cells where ICG-NPs had been uptaken by phagocytic cells. Conclusion: Polymeric NPs work as an efficient drug delivery system for PDT drugs, and this approach can be used in the administration of amphiphilic photosensitizers in the treatment of neoplasic cells.

Glasses in the SbPO4-WO3 system

Glasses in the binary system (100 - x)SbPO4-xWO3 (20 <= x <= 60, x in mol%) have been prepared and characterized. Differential thermal analysis (DTA) shows that the glass transition temperature, T-g increases from 412 degrees C, for samples containing 20 mol% of WO3 to 481 degrees C observed for glass containing 60 mol%. Sample containing 40 mol% in WO3 were observed to be the most stable against devitrification. The structural organization of the glasses has been studied by using Fourier transform infra-red (FTIR), Raman, P-31 Magic angle spinning (MAS) and spin echo nuclear magnetic resonance (NMR) spectroscopies. Results suggest two distinct networks comprising the glass structure, one with high SbPO4 content and the other characteristic of the highest WO3 content samples. The glasses present photochromic properties. Colour changes are observed for samples after exposure to ultraviolet or visible laser light. XANES, at L-1 absorption edge of tungsten, suggests partial reduction from W6+ to W5+ species during the laser irradiation. The photochromic effects and the colour changes, promoted by laser excitation, are reversible and easily removed by heat for during 1 h at 150 degrees C. Subsequent 'write/erase' cycles can be done without degradation of the glasses. (C) 2007 Elsevier B.V. All rights reserved.

Photoexpansion and photobleaching effects in oxysulfide thin films of the GeS2+Ga2O3 system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)