Preparation of 9.5/65/35 PLZT powders by organic precursor method

In this study the preparation of 9.5/65/35 PLZT ceramic powders were investigated. The powders with the formula Pb0.905La0.095(Zr0.65 Ti0.35)0.976O3 + 3.5 w% PbO were prepared using Pechini process and partial oxalate method. The powder phase formation, powder morphology, and green density of PLZT were shown.

Study of crystallite size and strain as a function of morphological evolution in zinc oxide powder obtained from hydroxycarbonate precursor

In this work, zinc oxide samples were obtained from hydroxycarbonate by thermal decomposition at 300°C. Zinc hydroxycarbonate samples were produced by homogeneous precipitation over different periods of time. The method used to obtain zinc oxide produces different morphologies as a function of the precursor precipitation time. Among the obtained particle shapes were porous spherical aggregates, spherulitic needle aggregates, and single acicular particles. This work investigated spherulitic needle-aggregate formation and the correlation among morphology, domain size, and microstrain. Transmission electron microscopy data revealed that the acicular particles that form the spherulitic needle aggregates consist of nanometer crystallites. Apparent crystallite size and microstrain in the directions perpendicular to (h00), (h0l), (hk0), and (00l) planes were invariable as a function of precursor precipitation time. From the results, it was possible to conclude that the precursor precipitation period directly influenced the morphology of the zinc oxide but did not influence average crystallite size and microstrain for ZnO samples. Therefore, using this route, it was possible to prepare zinc oxide with different morphologies without microstructural alterations. © 2001 International Centre for Diffraction Data.

Influence of barium and strontium addition on the ratio c/a of PZT obtained by the polymeric precursor method

Lead zirconate titanate powder, with Zr/Ti ratio of 50/50 was prepared by Pechini method after adding up to 10,0 mol% of Ba +2 and Sr +2 ions. Tetragonal phase is favored by the increase of barium and strontium concentration in the LiNbO 3 crystal lattice. The ratio c/a for tetragonal phase increases with the content of Ba +2 and Sr +2.

Structure and properties of donor doped barium titanate prepared by citrate process

Niobium doped barium titanate was prepared using two procedures. First, doped barium titanate was prepared starting from citrate solutions of all components and second, pure barium titanate powder was obtained from the citrate solutions and after that doped. Besides niobium, a small amount of manganese, as acceptor dopant was added. Phase composition, crystal structure, microstructure and dielectric properties were reported. The influence of powder processing on the properties of niobium doped barium titanate was analysed. The grain growth and the concentration of dopants on the dielectric properties were considered. © 2002 Taylor & Francis.

Structural, dielectric and ferroelectric properties of Nb-doped PZT thin films produced by oxide precursor method

Recently, was proposed a chemical method for preparation of ferroelectric thin films based on oxide precursors. In this work, PZT thin films were prepared to attest the viability of this method for cation-substitution. In this study, a small concentration of Nb (5 mol%) was selected as substitute of B-site in ABO 3 structure of PZT. Dielectric and ferroelectric properties of PZT films were studied as a function of cation-substitution. Results for Nb-PZT were compared with PZT films undoped. The values of dielectric constant, at typical 100 kHz frequency, were 358 and 137, for PZT and Nb-PZT films respectively. Remanent polarizations of these films were respectively 7.33 μ C/cm 2 and 13.3 μ C/cm 2 , while the measured coercive fields were 101 kV/cm and 93 kV/cm. As a result, changes on observed dielectric and ferroelectric values confirm the Nb substitution in PZT thin film produced by oxide precursor method. © 2002 Taylor & Francis.

Crystallographic, dielectric and optical properties of SrBi 2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (Pt/Ti/SiO 2 /Si), n -type (100)-oriented and p -type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P r values of 6.24 μC/cm 2 and 31.5 kV/cm for the film annealed at 800 C. The film deposited onto fused silica and treated at 700 C presented around 80% of transmittance. © 2002 Taylor & Francis.

Therapeutic response of benzodiazepine, orphenadrine citrate and occlusal splint association in TMD pain

Loss of function, muscle inflammation, and pain are some of the signs and symptoms of temporomandibular dysfunction (TMD). Pharmacological strategies to minimize the clinical manifestation of these disorders often focus on blocking or inhibiting the pain-causing symptom. Resources such as muscle-relaxants, anxiety-relief drugs, and splint therapy are often used to reduce muscular hyperactivity related to TMD muscle pain. This study compares the effect of a randomly ordered association of occlusal splint therapy (S), nonsteroid anti-inflammatory with a muscle-relaxant drug (orphenadrine citrate) (O), and an anxiety-relief drug (benzodiazepine) (B), to ease painful TMD muscle symptoms. Clinical and anamnestic analyses were recorded in accordance with the Helkimo TMD index and applied before and after treatments. Twenty-one group two Helkimo TMD adult female patients were treated, all of whom were subjected to the three random therapeutic associations proposed: SBO, BOS, and OSB. The same operator applied the three specific associations over a period of 21 days in the proposed sequence, seven days for each therapy. The results show that all the groups presented the best results in terms of relief from pain after the therapeutic association (28.5% showed a decrease and 47.6% showed an absence of symptoms). No significant difference was observed among association therapeutic protocols. Copyright © 2003 by CHROMA, Inc.

Structure study of donor doped barium titanate prepared from citrate solutions

Barium titanates doped with Nb5+, and Y3+, were prepared. The starting powders were synthesized from citrate solutions by the Pechini process and partial Pechini process in two steps. Sintering was performed in the range from 1310° up to 1380°C for 2 hours in air atmosphere. The structural study concerning the incorporation of Nb and Y ions in the barium titanate crystal lattice was performed by XRD, XANES and EXAFS techniques. The dielectric properties were analyzed and the relationship between properties and structure of doped barium titanate was established.

Synthesis and characterization of 0.9PMN-0.1PT powders by the use of a modified columbite precursor

The complex perovskite compound 0.9PbMg 1/3Nb 2/3O 3-0.1PbTiO 3 is one of the most promising relaxor ceramic because the addition of lead titanate increases T m, by about 5°C/mol% from intrinsic T m value for pure PMN (near -7 to -15°C). A Ti-modified columbite precursor was used to prepare PMN-PT powders containing single perovskite phase. This variation on columbite route includes Ti insertion in MgNb 2O 6 orthorhombic structure so that individual PT synthesis becomes unnecessary. Furthermore, effects of Li additive on columbite and PMN-PT structures were studied by XRD to verify the phase formation at each processing step. XRD data were also used for the structural refinement by Rietveld method. The additive acts increasing columbite powders crystallinity, and the amount of perovskite phase was insignificantly decreased by lithium addition. By SEM micrographs it was observed that Li presence in PMN-PT powders leads to the formation of rounded primary particles and for lmol% of additive, the grain size is not changed, different from when this concentration is enhanced to 2mol%.

Physical characterization of K-doped 0.9PMN-0.1PT synthesized by an association of the columbite route and the polymeric precursor method

The solid solution 0.9PbMg 1/3Nb 2/3O 3-0.1PbTiO 3 is one of the most widely investigated relaxor ceramic, because of its high dielectric constant and low sintering temperatures. PMN-PT powders containing single perovskite phase were prepared by using a Timodified columbite precursor obtained by the polymeric precursor method. Such precursor reacts directly with stoichiometric amount of PbO to obtain pyrochlore-free PMN-PT powders. The structural effects of K additive included in the columbite precursor and 0.9PMN-0.1PT powders were also studied. The phase formation at each processing step was verified by XRD analysis, being these results used for the structural refinement by the Rietveld method. It was verified the addition of K in the columbite precursor promotes a slight increasing in the powder crystallinity. There was not a decrease in the amount of perovskite phase PMN-PT for 1mol% of K, and the particle and grain size were reduced, making this additive a powerful tool for grain size control.

Microstructural and electrical properties of the sofc anode precursor YSZ/NiO composite prepared by A liquid mixture technique

A detailed study of the microstructural and electrical properties of the yttria-stabilized zirconia/nickel oxide (YSZ/NiO) composite was performed. This material is the precursor to the solid oxide fuel cell anode cermet YSZ/Ni. A liquid mixture technique was developed to produce the YSZ/NiO composite to fabricate high-performance SOFC anodes. This technique resulted in fine and homogeneous powders and specimens with high electrical conductivity. The combined results showed that this technique is suitable for the production of the anode cermet.

Preparation of lanthanum doped Bi4Ti3O12 ceramics by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4 - xLaxTi3O12 (BLT) ceramics, with x ranging from 0 to 0.75 were prepared by the polymeric precursor method. Orthorhombicity of the system is decreased with the increase of lanthanum content in the bismuth titanate (BIT) crystal lattice. No secondary phases were evident after lanthanum addition. Increasing lanthanum content causes a structural distortion in the bismuth titanate lattice. The shape of the grains is strongly influenced by the lanthanum added to the system. © 2005 Elsevier B.V. All rights reserved.

Structural and optical properties of Eu3+ and Mg2+ doped LiTaO3 obtained via the polymeric precursor method

This work reports on the pure lithium tantalate (LiTaO3), europium (III)-doped LiTaO3 and magnesium (II)-europium (III)-doped LiTaO3 preparared by the polymeric precursor method, using four different powered samples of Eu3+ ion concentrations 0.1 to 1at %. Structural and optical properties of powders have been studied. The different possible sites occupied by the rare earth were examined. The phase contents and lattice parameters were studied by the Rietveld method and the structural disorder in the LiTaO3 host caused by Eu3+ ions was analyzed. Results indicated LiTaO3 free of secondary phases at 650°C and the photoluminescence (PL) emission spectra showed the characteristic sharp emission bands given by Eu3+ ions when they are excited at a wavelength of 399 nm. An increase of dopants contents caused a non-homogeneous broadening and showed a slightly larger one when Mg was added. A displacement of the transition 5D0-7F0 to shorter wavelengths as function of Eu3+ concentration was also noticed.

Influence of concentration, time and method of application of citric acid and sodium citrate in root conditioning.

The aim of this study was to establish the parameters of concentration, time and mode of application of citric acid and sodium citrate in relation to root conditioning. A total of 495 samples were obtained and equally distributed among 11 groups (5 for testing different concentrations of citric acid, 5 for testing different concentrations of sodium citrate and 1 control group). After laboratorial processing, the samples were analyzed under scanning electron microscopy. A previously calibrated and blind examiner evaluated micrographs of the samples. Non-parametric statistical analysis was performed to analyze the data obtained. Brushing 25% citric acid for 3 min, promoted greater exposure of collagen fibers in comparison with the brushing of 1% citric acid for 1 minute and its topical application at 1% for 3 min. Sodium citrate exposed collagen fibers in a few number of samples. Despite the lack of statistical significance, better results for collagen exposure were obtained with brushing application of 25% citric acid for 3 min than with other application parameter. Sodium citrate produced a few number of samples with collagen exposure, so it is not indicated for root conditioning.

Evaluation of the effects of nicorandil and its molecular precursor (without radical NO) on proliferation and apoptosis of 786-cell

Nicorandil is a nitric oxide (NO) donor used in the treatment of angina symptoms. It has also been reported to protect cells and affect the proliferation and death of cells in some tissues. The molecules that interfere with these processes can cause dysfunction in healthy tissues but can also assist in the therapy of some disorders. In this study we examined the effect of nicorandil and of the molecular precursor that does not have the NO radical (N-(beta-hydroxyethyl) nicotinamide) on the cell proliferation and death of human renal carcinoma cells (786-O) under normal oxygenation conditions. The molecular precursor was used in order to analyze the effects independents of NO. In the cytotoxicity test, nicorandil was shown to be cytotoxic at very high concentrations and it was more cytotoxic than its precursor (cytotoxic at concentrations of 2,000 and 3,000 μg/mL, respectively). We propose that the lower cytotoxicity of the precursor is due to the absence of the NO radical. In this study, the cells exposed to nicorandil showed neither statistically significant changes in cell proliferation nor increases in apoptosis or genotoxicity. The precursor generated similar results to those of nicorandil. We conclude that nicorandil causes no changes in the proliferation or apoptosis of the cell 786-O in normal oxygenation conditions. Moreover, the lack of NO radical in the precursor molecule did not show a different result, except in the cell cytotoxicity. © 2013 Springer Science+Business Media Dordrecht.