Structure, ferroelectric/magnetoelectric properties and leakage current density of (Bi0.85Nd0.15)FeO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Investigation on the structural properties in Er-doped PbTiO3 compounds: A correlation between experimental and theoretical results

The aim of this work is to investigate the structural properties of the (Pb1-xErx)TiO3 (PET) powders, with x varying from 0.01 to 0.08, prepared by the polymeric precursor method. Combined X-ray diffraction, Raman spectroscopy and ab initio calculation reveal a diffuse phase-transition of a tetragonal to a cubic phase. The crystalline models built allowed to calculate electronic properties and to analyze the behavior of the doping element in the structure of the material, which are consistent with the experimental results that indicate the beginning of phase-transition from tetragonal to cubic. (C) 2007 Elsevier B.V. All rights reserved.

Dielectric properties of pure and lanthanum modified bismuth titanate thin films

We investigated the dielectric properties of pure and lanthanum modified bismuth titanate thin films obtained by the polymeric precursor method. X-ray diffraction of the film annealed at 300 degrees C for 2h indicates a disordered structure. Lanthanum addition increases gradually the dielectric permittivity of films, keeping unchanged their loss tangent. From C-V curve we can see no hysteresis behavior indicating the absence of domain structure. The decrease in the conductivity for the heavily doped Bi4Ti3O12 (BIT) must be associated to the unidentified crystal defects. For comparison, dielectric properties of crystalline BIT film were also investigated. (C) 2007 Published by Elsevier B.V.

Structural conditions that leads to photoluminescence emission in SrTiO3: An experimental and theoretical approach

Complex cluster [TiO5 center dot V-O(z)] and [SrO11 center dot V-O(z)] (where V-O(z)=V-O(X), V-O(center dot), V-O(center dot center dot)) vacancies were identified in disordered SrTiO3 powders prepared by the polymeric precursor method, based on experimental measurements by x-ray absorption near edge structure spectroscopy. The paramagnetic complex states of [TiO5 center dot V-O(center dot)] and [SrO11 center dot V-O(center dot)] with unpaired electrons were confirmed by electron paramagnetic resonance spectroscopy. The disordered powders showed strong photoluminescence at room temperature. Structural defects of disordered powders, in terms of band diagram, density of states, and electronic charges, were interpreted using high-level quantum mechanical calculations in the density functional framework. The four periodic models used here were consistent with the experimental data and explained the presence of photoluminescence. (C) 2008 American Institute of Physics.

Reply to Comment on 'Pb1-xCaxTiO3 solid solution (x=0.0, 0.25, 0.50, and 0.75): A theoretical and experimental approach'

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The role of oxygen vacancy in the photoluminescence property at room temperature of the CaTiO3

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Direct amorphous-to-cubic perovskite phase transformation for lead titanate

The phase evolution of lead titanate processed by the polymeric precursor method was investigated by thermal analysis, X-ray diffraction, and high-resolution transmission electron microscopy. The results showed that the cubic perovskite PbTiO3 (PT) phase is formed from an inorganic amorphous precursor at a temperature of 444 °C. A gradual transition from cubic to tetragonal perovskite PT was observed with the increase of calcination time at this temperature. HRTEM results showed that the cubic PT particles have a size of around 5 nm. The identification of cubic PT as an intermediate phase supports the hypothesis that the chemical homogeneity was kept at the molecular level during the synthesis process, with no cation segregation.

Photoluminescence of disordered ABO3 perovskites

Intense photoluminescence in highly disordered (amorphous) BaTiO3, PbTiO3, and SrTiO3 prepared by the polymeric precursor method was observed at room temperature. The emission band maxima from the three materials are in the visible region and depend on the exciting wavelength. The origin of the photoluminescence was not exactly identified. However, the line shape indicates that confinement effects are not probable. The experimental results indicate that it could be related to the disordered perovskite structure. © 2000 American Institute of Physics.

Influencia del tratamiento térmico en la cristalización y rugosidad de películas delgadas de LiNbO3 depositadas por el método Spin Coating

Lithium niobate (LiNbO3) thin films with 1/1 stoichiometry were prepared by a spin-coating from polymeric precursor method. The films deposited on silicon (100) substrates, were thermally treated from 400° to 600°C for 3 hours in order to study the influence of thermal treatment on the crystallinity, microstructure, grain size and roughness. X-ray diffraction (XRD) results showed that LiNbO3 phase crystallizes at low temperature (400°C). It was observed by scanning electron microscopy (SEM) that it is possible to obtain dense thin films at temperatures around 500°C. The atomic force microscopy (AFM) results showed that the grain size and roughness are strongly influenced by the annealing temperature.

Photoluminescence in amorphous (PbLa)TiO3 thin films deposited on different substrates

Pb1-xLaxTiO3 thin films, (X=0.0; 13 and 0.27mol%) were prepared by the polymeric precursor method. Thin films were deposited on Pt/Ti/SiO2/Si(111), Si(100) and glass substrates by spin coating, and annealed in the 200-300°C range in an O2 atmosphere. X-ray diffraction, scanning electron microscopy and atomic force microscopy were used for the microstructural characterization of the thin films. Photoluminescence (PL) at room temperature has been observed in thin films of (PbLa)TiO3. The films deposited on Pt/Ti/SiO2/Si substrates present PL intensity greater than those deposited on glass and silicon substrates. The intensity of PL in these thin films was found to be dependent on the thermal treatment and lanthanum molar concentration. © 2002 Elsevier Science B.V. All rights reserved.

Effect of Nb on barium titanate prepared from citrate solutions

The influence of the addition of dopants on the microstructure development and electrical properties of BaTiO3 doped with 0.2, 0.4, 0.6, 0.8 mol% of Nb and 0.01 mol% of Mn based compounds was studied. Doped barium titanate was prepared using the polymeric precursor method from citrate solutions. The powders calcined at 700°C for 4 hours were analysed by infrared (IR) spectroscopy to verify the presence of carbonates, and by X-ray diffraction (XRD) for phase formation. The phase composition, microstructure and dielectric properties show a strong dependence on the amount of added niobium.

Structural phase evolution of strontium-doped lead titanate thin films prepared by the soft chemical technique

Strontium-modified lead titanate thin films with composition Pb1-xSrxTiO3 were grown on Pt/Ti/SiO2/Si substrates using the polymeric precursor method. The structural phase evolution as a function of the Sr contents was studied using micro-Raman scattering, specular reflectance infrared Fourier transform spectroscopy, and x-ray diffraction. The results showed a gradual change from tetragonal to cubic structure, the transition occurring at about x = 0.58. The infrared reflectance spectra showed that the frequency of several peaks decreases as the strontium concentration increases. These features are correlated with a decrease in the tetragonal distortion of the TiO6 octahedra as the strontium concentration increases.

Temperature and stoichiometry effect on microstructural and ferroelectric properties of Pb(Zr1-xTix)O3 thin films prepared by chemical soulution deposition

Lead zirconate titanate (PZT) solutions were prepared using a polymeric precursor method, Zr n-propoxide and Ti i-propoxide were used as starting materials with ethylene glycol and water as solvents. The PZT solution was spin-coated on Pt/Ti/SiO2/Si substrates, baked on a hot plate, and finally heat-treated in a tube furnace between 400 and 800°C. The surface morphology and grain size of the films were characterized by atomic force microscopy (AFM), using a tapping mode with amplitude modulation. The films, thermal annealed at temperatures higher than 500°C, exhibited a dense microstructure, without noticeable cracks or voids. Electrical properties were investigated as a function of composition and annealing temperature.

Influence of oxygen atmosphere on LiNbO3 thin films prepared by Pechini process

Thin films of lithium niobate were deposited on the Pt/Ti/SiO2 (111) substrates by the polymeric precursor method (Pechini process). Annealing in static air and oxygen atmosphere was performed at 500°C for 3 hours. The films obtained were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The dielectric constant, dissipation factor and resistance were measured in frequency region from 10 Hz to 10 MHz. Electrical characterizations of the films pointed to ferroelectricity via hysteresis loop. The influence of oxygen atmosphere on crystallization and properties of LiNbO3 thin films is discussed.

Métodos químicos para obtener varistores basados en SnO2

Synthesis of SnO2 ceramic powders was made by coprecipitation method and polymeric precursor method (Pechini) to obtain Sn-Co-Nb-Ti-Al varistor systems. The particles of the obtained ceramic powder presented nanometric size and SnO2 was the principal crystalline phase in them according to X-ray diffraction results. To determine the behavior of the synthesized samples in front of the thermal treatments, thermal analysis (DTA/TG) were made. Dilatometric studies on previously pressed samples were carried out. The optimal conditions of sintering of this raw material were determined. Microstructures and electric properties of sintered samples were studied using scanning electron microscopy (SEM) and I-V characteristics curves. The samples presented varistor behavior independent of the synthesis method used, with high nonlinearity values as 32. The presence of Al3+ favored the concentration of oxygen vacancies, and the grain growth.