Osteoconductivity of modified fluorcanasite glass-ceramics for bone tissue augmentation and repair

Modified fluorcanasite glasses were fabricated by either altering the molar ratios of Na(2)O and CaO or by adding P(2)O(5) to the parent stoichiometric glass compositions. Glasses were converted to glass-ceramics by a controlled two-stage heat treatment process. Rods (2 mm x 4 mm) were produced using the conventional lost-wax casting technique. Osteoconductive 45S5 bioglass was used as a reference material. Biocompatibility and osteoconductivity were investigated by implantation into healing defects (2 mm) in the midshaft of rabbit femora. Tissue response was investigated using conventional histology and scanning electron microscopy. Histological and histomorphometric evaluation of specimens after 12 weeks implantation showed significantly more bone contact with the surface of 45S5 bioglass implants when compared with other test materials. When the bone contact for each material was compared between experimental time points, the Glass-Ceramic 2 (CaO rich) group showed significant difference (p = 0.027) at 4 weeks, but no direct contact at 12 weeks. Histology and backscattered electron photomicrographs showed that modified fluorcanasite glass-ceramic implants had greater osteoconductivity than the parent stoichiometric composition. Of the new materials, fluorcanasite glass-ceramic implants modified by the addition of P(2)O(5) showed the greatest stimulation of new mineralized bone tissue formation adjacent to the implants after 4 and 12 weeks implantation. (C) 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 94A: 760-768, 2010

COLOR STABILITY OF DENTAL CERAMICS SUBMITTED TO ARTIFICIAL ACCELERATED AGING AFTER REPEATED FIRINGS

Statement of problem. Color stability is an important factor to ensure the long-term clinical success of ceramic restorations. There is a lack of information on how color is affected by fabrication procedures, such as the number of firings. Purpose. The purpose of this study was to evaluate the effects that the number of firings and type of substrate have on the color stability of dental ceramic submitted to artificial accelerated aging. Material and methods. Sixty specimens were fabricated: 30 metal ceramic (Verabond II + IPS d.SIGN) and 30 all-ceramic (IPS d.SIGN). Specimens were divided into 3 groups (n=10), and submitted to 2, 3, or 4 firings (+/- 900 degrees C), respectively, according to the manufacturer`s instructions. Color readings were obtained with a spectro photometer before and after artificial accelerated aging, and L*, a*, and b* coordinates and total color variation (Delta E) were analyzed (2-way ANOVA, Bonferroni, (alpha=05). Results. For metal ceramic specimens, differences for the L* coordinates were significant (P<.05) only for the group submitted to 3 firings. With respect to the all-ceramic specimens, smaller L* coordinates were obtained for greater a* and b* coordinates, indicating that the greater the number of firings, the darker and more reddish/yellowish the specimen. All Delta E values, for all groups, were below 1.0. All-ceramic specimens submitted to 3 and 4 firings presented Delta E means differing statistically (P<.05) from those of the metal ceramic group. Conclusions. The type of substrate and number of firings affected the color stability of the ceramic material tested. Artificial accelerated aging did not produce perceptible color stability changes (Delta E<1.0). (J Prosthet Dent 2009-101:13-18)

Thermoluminescence dating of Brazilian indigenous ceramics

Two indigenous ceramics fragments, one from Lagoa Queimada (LQ) and another from Barra dos Negros (BN), both sites located on Bahia state (Brazil), were dated by termoluminescence (TL) method. Each fragment was physically prepared and divided into two fractions, one was used for TL measurement and the other for annual dose determination. The TL fraction was chemically treated, divided in sub samples and irradiated with several doses. The plot extrapolation from TL intensities as function of radiation dose enabled the determination of the accumulated dose (D(ac)), 3.99 Gy and 1.88 Gy for LQ and BN, respectively. The annual dose was obtained through the uranium, thorium and potassium determination by ICP-MS. The annual doses (D(an)) obtained were 2.86 and 2.26 mGy/year. The estimated ages were similar to 1375 and 709 y for BN and LQ ceramics, respectively. The ages agreed with the archaeologists` estimation for the Aratu and Tupi tradition periods, respectively.

Dating archeological ceramics from the Valley of Vitor, Arequipa by the TL method

The age of some ancient pottery from the Valley of Vitor in the region of Arequipa, Peru, is determined by the thermoluminescence (TL) method. For dating, a 325 degrees C TL peak was used and irradiation with -dose from 5 to 50Gy was carried out for the additive method, and from 0.4 to 5Gy for the regeneration method. For these dose values, the TL intensity is observed to grow linearly, obtaining an accumulated dose of 1.62 +/- 0.09Gy and 1.36 +/- 0.03Gy for the additive and regeneration methods, respectively. The age (A) of the sample was calculated by the two methods, being A=867 +/- 195 years after Christ (AC) for the additive method and A=1050 +/- 157 years AC for the regeneration method. Both results are within 800-1200 years AC, which is the period of the Wari culture.

Optical and dielectric relaxor behaviour of Ba(Zr(0.25)Ti(0.75))O(3) ceramic explained by means of distorted clusters

In this work, Ba(Zr(0.25)Ti(0.75))O(3) ceramic was prepared by solid-state reaction. This material was characterized by x-ray diffraction and Fourier transform Raman spectroscopy. The temperature dependent dielectric properties were investigated in the frequency range from 1 kHz to 1 MHz. The dielectric measurements indicated a diffuse phase transition. The broadening of the dielectric permittivity in the frequency range as well as its shifting at higher temperatures indicated a relaxor-like behaviour for this material. The diffusivity and the relaxation strength were estimated using the modified Curie-Weiss law. The optical properties were analysed by ultraviolet-visible (UV-vis) absorption spectroscopy and photoluminescence (PL) measurements at room temperature. The UV-vis spectrum indicated that the Ba(Zr(0.25)Ti(0.75))O(3) ceramic has an optical band gap of 2.98 eV. A blue PL emission was observed for this compound when excited with 350 nm wavelength. The polarity as well as the PL property of this material was attributed to the presence of polar [TiO(6)] distorted clusters into a globally cubic matrix.

Structural Phase Transition Studies on PMN-0.35PT using Infrared Spectroscopy

The purpose of the present work is to report studies on structural phase transition for PMN-xPT ferroelectric, with melt PbTiO3 composition around the MPB (x = 0.35 mol %), using infrared spectroscopy technique. The study was centered on monitoring the behavior of the 1-(NbO), 1-(TiO) and 1-(MgO) stretching modes as a function of temperature. The increasing as a function of temperature for 1-(TiO) and 1-(MgO) modes, observed between 230 and 300 K, can be related to the monoclinic (MC) + tetragonal (T) phase coexistence in the PMN-PT.

Correlations between chemical composition and provenance of Justino site ceramics by INAA

Instrumental neutron activation analysis (INAA), have been used for the definition of compositional groups of potteries from Justino site, Brazil, according to the chemical similarities of ceramic paste. The outliers were identified by means of robust Mahalanobis distance. The temper effect in the ceramic paste was studied by means of modified Mahalanobis filter. The results were interpreted by means of cluster, principal components, and discriminant analyses. This work provides contributions for the reconstruction of the prehistory of baixo Sao Francisco region, and for the reconstitution of the Brazilian Northeast ceramist population of general frame.

Persistent luminescence of Eu(2+) and Dy(3+) doped barium aluminate (BaAl(2)O(4):Eu(2+),Dy(3+)) materials

Polycrystalline Eu(2+) and Dy(3+) doped barium aluminate materials, BaAl(2)O(4):Eu(2+),Dy(3+), were prepared with solid state reactions at temperatures between 700 and 1500 degrees C. The influence of the thermal treatments on the stability, homogeneity and structure as well as to the UV-excited and persistent luminescence of the materials was investigated by X-ray powder diffraction, SEM imaging and infrared spectroscopies as well as by steady state luminescence spectroscopy and persistent luminescence decay curves, respectively. The IR spectra of the materials prepared at 250, 700, and 1500 degrees C follow the formation of BaAl(2)O(4) composition whereas the X-ray powder diffraction of compounds revealed how the hexagonal structure was obtained. The morphology of the materials at high temperatures indicated important aggregation due to sintering. The luminescence decay of the quite narrow Eu(2+) band at ca. 500 nm shows the presence of persistent luminescence after UV irradiation. The dopant (Eu(2+)) and co-clopant (Dy(3+)) concentrations affect the crystallinity and luminescence properties of the materials. (C) 2009 Elsevier B.V. All rights reserved.

Quenching of Photoactivity in Phthalocyanine Copper(II)-Titanate Nanotube Hybrid Systems

Titanate nanotubes (TiNTs) were obtained by hydrothermal treatment of anatase powder in aqueous NaOH solution and then modified with 2,9,16,23-tertracarboxyl phthalocyanine copper(H) (CuPc). This hybrid organic inorganic nanoscopic system was characterized by X-ray diffraction, microscopy, and spectroscopy. Transmission electron microscopy (TEM) images of pure and modified TiNTs revealed multiwall structures with an average outer diameter of 9 nm and a length of several hundred nanometers. The tubular morphology of the TiNTs was covered with CuPc-film. The amount of CuPc adsorbed onto the TiNTs was quantified by electron paramagnetic resonance (EPR). Using the same technique and spin-trapping methodology, the photogeneration of reactive oxygen species (ROS) from the TiNTs was systematically investigated. A drastic quenching of photoactivity was observed in the CuPc/TiNT hybrid system. Electron transfer from excited CuPc states to the TiNT conduction band followed by electron recombination may be the cause of this quenching.

Barium uptake by maize plants as affected by sewage sludge in a long-term field study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

EFFECT of DIFFERENT SOLID AMOUNTS IN THE PHYSICAL and MICROSCOPICAL PROPERTIES of SiC POROUS CERAMICS

The presence of pores in ceramics is directly related to the chosen forming process. So, in the starch consolidation method, the ceramics show, after burning, pores with morphology similar to that presented by this organic material. on the other hand, the increase in solid load leads up to alterations in dispersion viscosity, increasing the thermal stresses during drying and sintering processes. In order to verify the solid percentage influence in ceramic final properties, samples were prepared with silicon carbide in different compositions using or not starch as binder agent and pore forming element. The characterization of the ceramic pieces was performed by superficial roughness measurements, porosity besides by optical and scanning electron microscopy. The results showed ceramics with SiC and starch presented physical and microscopic properties slightly higher in relation to those with only ceramic powder in their composition. The presence of organic material, agglomerated and foam during the forming were essential for the final properties of the studied samples.

Análise de antenas utilizando substrato cerâmico, zpt, produzido por síntese auto propagante para aplicações em sistemas de micro-ondas

Ceramic substrates have been investigated by researchers around the world and has achieved a high interest in the scientific community, because they had high dielectric constants and excellent performance in the structures employed. Such ceramics result in miniaturized structures with dimensions well reduced and high radiation efficiency. In this work, we have used a new ceramic material called lead zinc titanate in the form of Zn0,8Pb0,2TiO3, capable of being used as a dielectric substrate in the construction of various structures of antennas. The method used in constructing the ceramic combustion synthesis was Self- Sustained High Temperature (SHS - "Self-Propagating High-Temperature Synthesis") which is defined as a process that uses highly exothermic reactions to produce various materials. Once initiated the reaction area in the reaction mixture, the heat generated is sufficient to become self-sustaining combustion in the form of a wave that propagates converting the reaction mixture into the product of interest. Were analyzed aspects of the formation of the composite Zn0,8Pb0,2TiO3 by SHS powders and characterized. The analysis consisted of determining the parameters of the reaction for the formation of the composite, as the ignition temperature and reaction mechanisms. The production of composite Zn0,8Pb0,2TiO3 by SHS performed in the laboratory, was the result of a total control of combustion temperature and after obtaining the powder began the development of ceramics. The product was obtained in the form of regular, alternating layers of porous ceramics and was obtained by uniaxial pressing. 10 The product was characterized by analysis of dilatometry, X-ray diffraction analysis and scanning electron microscopy. One of the contributions typically defined in this work is the development of a new dielectric material, nevertheless presented previously in the literature. Therefore, the structures of the antennas presented in this work consisted of new dielectric ceramics based Zn0,8Pb0,2TiO3 usually used as dielectric substrate. The materials produced were characterized in the microwave range. These are dielectrics with high relative permittivity and low loss tangent. The Ansoft HFSS, commercial program employee, using the finite element method, and was used for analysis of antennas studied in this work

Síntese de pigmentos cerâmicos inorgânicos nanométricos pela rota dos precursores poliméricos

Considering the constant evolution of technology in growth and the need for production techniques in the ceramics area to move forward together, we sought in this study, the research and development of polymeric precursor method to obtain inorganic ceramic pigments. Method that provides quality to obtain the precursor powders of oxides and pigments at the same time, offers time and cost advantages, such as reproducibility, purity and low temperature heat treatment, control of stoichiometry. This work used chromium nitrate and iron nitrate as precursors. The synthesis is based on the dissolution of citric acid as a complexing agent, addition of metal oxides, such as ion chromophores; polymerization with ethylene glycol and doping with titanium oxide. Passing through precalcination, breakdown, thermal treatments at different temperatures of calcination (700 to 1100 oC), resulting in pigments: green for chromium oxide deposited on TiO2 (CrTiO3) and orange for iron oxide deposited on TiO2 ( FeTiO3). Noticing an increase of opacity with increasing temperature. Were performed thermal analysis (TG and ATD) in order to evaluate its thermodecomposition. The powders were also characterized by techniques such as XRD, revealing the formation of crystalline phases such as iron titanate (FeTiO3) and chrome titanate (CrTiO3), SEM, demonstrating formation of rounded particles for both oxides and Spectroscopy in the UV-Visible Region, verifying the potential variation and chromaticity os pigments. Thus, the synthesized oxides were within the requirements to be applied as pigments and shown to be possible to propose its use in ceramic materials

Investigation of microwave dielectric relaxation solid state process in the antiferroelectric phase of NaNbO3 ceramics

This letter reports microwave dielectric measurements performed in the antiferroelectric phase of NaNbO3 ceramics from 100 to 450 K. Remarkable dielectric relaxation was found within the antiferroelectric phase and in the vicinity of the ferroelectric-antiferroelectric phase transition. Such dielectric relaxation process was associated with relaxations of polar nanoregions with strong relaxor-like characteristic. In addition, the microwave dielectric measurements also revealed an unexpected and unusual anomaly in the relaxation strength, which was related to a disruption of the antiferroelectric order induced by a possible AFE-AFE phase transition. (C) 2004 Elsevier Ltd. All rights reserved.

Nucleation kinetics of crystalline phases from a kaolinitic body used in the processing of red ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)