Electromechanical properties of calcium bismuth titanate films: A potential candidate for lead-free thin-film piezoelectrics

CaBi4Ti4O15 (CBTi144) thin films were evaluated for use as lead-free thin-film piezoelectrics in microelectromechanical systems. The films were grown by the polymeric precursor method on (100)Pt/Ti/SiO2/Si substrates. The a/b-axis orientation of the ferroelectric film is considered to be associated with the preferred orientation of the Pt bottom electrode. The P-r and E-c were 14 mu C/cm(2) and 64 kV/cm, respectively, for a maximum applied field of 400 kV/cm. The domain structure was investigated by piezoresponse force microscopy. The film has a piezoelectric coefficient, d(33), equal to 60 pm/V and a current density of 0.7 mA/cm(2).

Ferroelectric and piezoelectric properties of bismuth titanate thin films grown on different bottom electrodes by soft chemical solution and microwave annealing

Bismuth titanate (Bi4Ti3O12, BIT) films were evaluated for use as lead-free piezoelectric thin films in micro-electromechanical systems. The films were grown by the polymeric precursor method on LaNiO3/SiO2/Si (1 0 0) (LNO), RuO2/SiO2/Si (1 0 0) (RuO2) and Pt/Ti/SiO2/Si (1 0 0) (Pt) bottom electrodes in a microwave furnace at 700 degrees C for 10 min. The domain structure was investigated by piezoresponse force microscopy (PFM). Although the converse piezoelectric coefficient, d(33), regardless of bottom electrode is around (similar to 40 pm/V), those over RuO2 and LNO exhibit better ferroelectric properties, higher remanent polarization (15 and 10 mu C/cm(2)), lower drive voltages (2.6 and 1.3 V) and are fatigue-free. The experimental results demonstrated that the combination of the polymeric precursor method assisted with a microwave furnace is a promising technique to obtain films with good qualities for applications in ferroelectric and piezoelectric devices. (c) 2006 Elsevier Ltd. All rights reserved.

Luminescence in semi-crystalline zirconium titanate doped with lanthanum

This paper aims to describe the synthesis of the semi-crystalline and crystalline powder of lanthanum doped with zirconium titanate (65/35), LZT through Pechini method. The analysis done by Raman demonstrated that semi-crystalline phase at 550 degrees C and crystalline phase after 600 degrees C were formed. The XRD pattern shows the ZrTiO4 phase formation demonstrating that La substitutions into the lattice take place. The calcined powder at different temperatures shows a semi-crystalline phase presenting photoluminescence effect when processed at low temperatures. From 300 to 400 degrees C a broadband is observed at 563 nm and 568 nm, respectively. Defects creation such as: Zr3+ center dot Vo(center dot center dot) and Ti3+ - V-O(center dot center dot), Zr and Ti replaced by La with vacancy formation, impurities and imperfections contributed to the photoluminescence effect. However, the main emission is due to a reverse Ti4+ -> O2- or/and Zr4+ -> O2- transition that occur within a regular titanate or zirconate eight-fold coordination [BO8-delta], B = Zr4+, Ti4+. (c) 2006 Elsevier B.V. All rights reserved.

Characterization of bismuth titanate ceramics derived by mechanochemical synthesis

Bismuth titanate, Bi(4)Ti(3)O(12) (BIT) nanosized powders have been successfully synthesized via high energy mechanochemical activation. The phase formation of BIT, crystal structure, microstructure, crystallite size and specific surface area were followed by XRD, scanning electron microscopy (SEM) and the BET specific surface area measurements. The BIT milled 2 h shows the orthorhombic crystalline structure with small amount of amorphous phase. The microstructure of Bi(4)Ti(3)O(12) ceramics sintered at 1000 degrees C for 12h exhibit plate-like grain structure.

Structural and electrical characterization of semiconducting barium-lead-titanate ceramics

BaTiO3 is usually doped to achieve the temperature stability required by device applications, as well as to obtain a large positive temperature coefficient anomaly of resistivity (PTCR). Uniform distribution of dopants among the submicron dielectric particles is the key for optimal control of grain size and microstructure to maintain a high reliability. The system Ba0.84Pb0.16TiO3 was synthesized from high purity BaCO3, TiO2, PbO oxide powders as raw materials. Sb2O3, MnSO4 and ZnO were used as dopants and Al2O3, TiO2 and SiO2 as grain growth controllers. Phase composition was analyzed by using XRD and the microstructure was investigated by SEM. EDS attached to SEM was used to analyze phase composition specially related to abnormal grain growth. Electrical resistivities were measured as a function of temperature and the PTCR effect characterized by an abrupt increase on resistivity.

Size effect on structure and dielectric properties of Nb-doped barium titanate

It is known that the dielectric properties of BaTiO3 (BT) are strongly dependent on its grain size. Coarse-grained ceramics of pure BT showed lower dielectric constant at room temperature then fine grained. Many authors considered that when the grain size is lower than 700 nm, the lattice of BT changes from tetragonal to pseudocubic, and the dielectric constant value is very low. In the doped BT this effect is more complex, because it is necessary to consider also the influence of dopants. The grain size effect on the structure and dielectric properties of niobium-doped barium titanate was investigated. Niobium-doped barium titanate was prepared from powders obtained by doping of commercial barium titanate and from organometallic complex using citrates as precursors (Pechini procedure). The crystal and microstructure of sintered niobium-doped barium titanate were determined. Dielectric constant and dissipation factor were measured. The observation confirmed that the structure and properties are strongly dependent on grain size. (C) 2003 Elsevier B.V. B.V. All rights reserved.

Ferroelectric and dielectric properties of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration of 0.75 was grown on Pt/Ti/SiO2/Si substrates by using the polymeric precursor solution and spin-coating method. The scanning electron microscopy (SEM) showed rounded grains, which is not typical for these system. The BLT films showed well-saturated polarization-electric field curve which 2P(r) = 41.4 muC/cm(2) and V-c = 0.99 V. The capacitance dependence on the voltage is strongly nonlinear, confirming the ferroelectric properties of the film resulting from the domains switching. These properties make BLT a promising material for FERAM applications.

Experimental and theoretical study of the ferroelectric and piezoelectric behavior of strontium-doped PZT

Theoretical data using ab initio perturbed ion calculation were compared with ferroelectric and piezoelectric experimental data of strontium doped PZT. Various concentrations of SrO in PZT at constant temperature and sintering time were carried out. Experimental results, such as the remanent polarization, P-R of 6.9-8.9 muC/Cm-2, the coercive field, E-C of 6.6-7.8 kVcm, and the planar coupling factor, Kp of 0.45-0.53, were compared with the energy of Zr4+ and Ti4+ ion dislocation and the lattice interaction energy which show that strontium increment in PZT alter the energies and increase the values of piezoelectric and ferroelectric variables. Calculations of lattice energy of the rhombohedral phase show that a phase non-stability is coincident with increasing experimental values of the P-R, E-C and Kp. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Electrical characterization of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration ranging from 0 to 0.75 were grown on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution and spin-coating method. The scanning electron microscopy shows a change of morphology with increasing the lanthanum concentration. The BLT films show well-saturated polarization-electric field curves whit remnant polarizations of 14.7, 20.5, 21.5, and 20.4 muC/cm(2) for x = 0, 0.25, 0.50 and 0.75, respectively. The dielectric constant of BLT (x = 0.75 mol% La) is equal to 158 while dielectric loss remain low (tandelta = 0.0018).

Use of strontium in the activation of bovine oocytes reconstructed by somatic cell nuclear transfer

As an important step in the nuclear transfer (NT) procedure, we evaluated the effect of three different treatments for oocyte activation on the in vitro and in vivo developmental capacity of bovine reconstructed embryos: (1) strontium, which has been successfully used in mice but not yet tested in cattle; (2) ionomycin and 6-dimethylammopurine (6-DMAP), a standard treatment used in cattle; (3) ionomycin and strontium, in place of 6-DMAP. As regards NT blastocyst development, no difference was observed when strontium (20.1%) or ionomycin/6-DMAP (14.4%) were used. However, when 6-DMAP was substituted by strontium (3), the blastocyst rate (34.8%) was superior to that in the other activation groups (p < 0.05). Results of in vivo development showed the possibility of pregnancies when NT embryos activated in strontium were transferred to recipient cows (16.6%). A live female calf was obtained when ionomycin/strontium were used, but it died 30 days after birth. Our findings show that strontium can be used as an activation agent in bovine cloning procedures and that activation with a combination of strontium and ionomycin increased the in vitro developmental capacity of reconstructed embryos. This is the first report of a calf produced by adult somatic cell NT in Latin America.

An approach to analyzing synthesis, structure and properties of bismuth titanate ceramics

The family of bismuth titanate, Bi(4)Ti(3)O(12) (BIT) layered-structured ferroelectrics materials is attractive from the viewpoint of such as their application as electronic materials dielectrics, piezoelectrics and pyroelectrics, because they are characterized by good stability of piezoelectric properties, a high Curie temperature and a good resistance vs temperature. Bismuth titanate (Bi(4)Ti(3)O(12)) powders can be prepared using different methods, depending if the creation will be film coating or ceramics. The structure and properties of bismuth titanate materials show a significance dependence on the applied synthesis method. In this review paper, we made an attempt to give an approach to analyszing the structure, synthesis methods and properties of bismuth titanate ferroelectrics materials.

In vitro biocompatibility of a novel membrane of the composite poly(vinylidene-trifluoroethylene)/barium titanate

This study was aimed at investigating the in vitro biocompatibility of a novel membrane of the composite poly(vinylidene-trifluoroethylene)/barium titanate (P(VDF-TrFE)/BT). Osteoblastic cells were obtained from human alveolar bone fragments and cultured under standard osteogenic condition until subconfluence. First passaged cells were cultured on P(VDF-TrFE)/BT and expanded polytetrafluoroethylene (e-PTFE - control) membranes in 24-well plates. Cell adhesion and spreading were evaluated at 30 min, and 4 and 24 h. For proliferation assay, cells were cultured for 1, 7, and 10 days. Cell viability was detected by trypan blue at 7 and 10 days. Total protein content and alkaline phosphatase (ALP) activity were measured at 7, 14, and 21 days. Cultures were stained with Alizarin red at 21 days, for detection of mineralized matrix. Data were compared by ANOVA and Student t test. Cell attachment (p = 0.001), cell number (p = 0.001), and ALP activity (p = 0.0001) were greater on P(VDF-TrFE)/BT. Additionally, doubling time was greater on P(VDF-TrFE)/BT (p = 0.03), indicating a decreased proliferation rate. Bone-like nodule formation took place only on P(VDF-TrFE)/BT. The present results showed that both membranes are biocompatible. However, P(VDF-TrFE)/BT presented a better in vitro biocompatibility and allowed bone-like nodule formation. Therefore, P(VDF-TrFE)/BT could be an alternative membrane to be used in guided tissue regeneration. (c) 2006 Wiley Periodicals, Inc.

The effect of microwave annealing on the electrical characteristics of lanthanum doped bismuth titanate films obtained by the polymeric precursor method

Lanthanum doped bismuth titanate thin films (Bi3.25La0.75Ti3O12-BLT) were produced by the polymeric precursor method and crystallized in a domestic microwave oven and in conventional furnace. Using platinum coated silicon substrates configuration, ferroelectric properties of the films were determined with remanent polarization P-r and a coercive field E-c of 3.9 mu C/cm(2) and 70 kV/cm for the film annealed in the microwave oven and 20 mu C/cm(2) and 52 kV/cm for the film annealed in conventional furnace, respectively. The films annealed in conventional furnace exhibited excellent retention-free characteristics at low infant periods indicating that BLT thin films can be a promise material for use in nonvolatile memories. on the other hand, the pinning of domains wall causes a strong decay at low infant periods for the films annealed in the microwave furnace which makes undesireable the application for future FeRAMS memories. (c) 2005 Elsevier B.V. All rights reserved.

Mechanochemical synthesis of barium titanate

A powder mixture of BaO and TiO2, was mechanochemically treated in a planetary ball mill in an air atmosphere for up to 4 h, using zirconium oxide vial and zirconium oxide balls as the milling medium. Mechanochemical reaction leads to the gradual formation of BaTiO3 phase. Phase evolution during synthesis and changes in powder size and morphology were monitored by XRD, DSC, IR and TEM analysis and it was shown that the formation of BaTiO3 phase was initiated after 60 min. Extended time of milling directed to formation of higher amount of BaTiO3 perovskite phase. Barium titanate with good crystallinity was formed after 240 min sintering without pre-calcination step was performed at 1330 degrees C for 2 It within heating rate 10 degrees C/min. (c) 2005 Elsevier Ltd. All rights reserved.

Use of strontium for bovine oocyte activation

Strontium efficiently activates mouse oocytes, however, there is limited information on its use in cattle. Thus, the objective of this study was to establish a suitable protocol for activating bovine oocyte with strontium. For pronuclear development, the absence of calcium and magnesium in the activation medium (TALP) with 10 and 50mM strontium (34.4 and 53.1%, respectively) was superior to the complete TALP (6.5 and 19.4%, respectively). In all activation media, better results were observed with 25 and 50 mM strontium (21.9-53.1 and 19.4-53.1%, respectively). Incubation for 4 h promoted similar results in all strontium concentrations. However, strontium at 15, 20, and 25 mM for 6 and 8 h (40.7, 46.7, and 48.3%, and 29.3, 48.3, and 40.7%, respectively) were superior to control (15.5 and 10%, respectively). After in vitro maturation for 26 h, strontium (S; 20 mM in Ca2+ and Mg2+-free TALP for 6 h), ionomycin + strontium (IS), and strontium + ionomycin (SI) (60, 63.3, and 65%, respectively) were similar in pronuclear development and superior to ionomycin (I; 5 mu M for 5 min; 36.7%). In treatments S and I, only 1 PN zygotes were observed. In treatment S, most of them had 1 and 2 PB (35.7 and 60.7%, respectively), and in treatment I, 0, 1, and 2 PB (14.3, 57.1, and 28.6%, respectively). Most of the zygotes in treatment IS and SI were 1 PN 2 PB (77.4 and 61.6%, respectively). The number of oocytes with clusters of cortical granules was similar in all treated groups (11-29%). Cortical granule exocytosis in treatment IS (68%) was similar to S (54%) and superior to 1, SI, and control (27, 45, and 5.0%, respectively). Cleavage and blastocyst rates were similar for S, I, IS, and SI treatments (61.7-76.7, and 8.3-13.3%, respectively) and the same was observed for ICM, TE, and total cell number, and ICM/total cell ratio (22-25, 64-69, and 86-95, and 0.26-0.27). In conclusion, strontium may be efficiently applied for bovine oocyte activation at 20 mM in Ca2+-and Mg2+-free TALP medium for 6 h.