Embrittlement of electrical steel laminations by nitrogen pick-up during heat treatment

Heat treated electrical steel laminations have shown evidence of low ductility behavior, characterized by a small number of bends till fracture, on repeated bending tests. The laminations were produced using a new grade of electrical steel with much lower aluminum content than usual. The problem happens when the oxygen potential (measured by the dew point of the atmosphere) of the heat treatment atmosphere is abnormally high. Furthermore, ductility can be restored by a low-oxygen potential heat treatment. Although the heat treatment resulted in a loss of ductility, the magnetic properties were not deteriorated. The low ductility samples always show intergranular fracture, whereas the un-treated laminations fracture by cleavage. The low ductility is associated with the formation of silicon manganese nitride precipitates formed at grain boundaries, although they are not the cause of the low ductility. Ductility could be restored by a low dew point heat treatment but the inclusions remained in the grain boundaries. The low ductility and its recovery must be ascribed to the presence of nitrogen atoms segregated to the grain boundaries when the heat treatment atmosphere has a high oxygen potential. The lack of aluminum in the composition of the steel hinders the scavenging effect of this element on nitrogen atoms in solution in the steel. (C) 2009 Elsevier Ltd. All rights reserved.

Life cycle assessment and life cycle cost of sugar plants evaporators

The evaporators of sugar plants in Brazil have used carbon steel intensively because of it is, a low priced material, which possesses inferior corrosion resistance. The materials more indicated for the substitution of carbon steel are stainless steels, however they are considered expensive. The environmental and financial performances of evaporator pipes constructed with carbon steel and with types AISI 304 444 and 439 stainless steel were evaluated. For the environmental evaluation, the Life Cycle Assessment (LCA) methodology Was used and it, revealed that stainless steel is more environmentally efficient than carbon steel. The life cycle costing (LCC) technique was the tool chosen for the financial evaluation and it showed that stainless steel is a better investment option compared to carbon steel. The results also indicate that LCA and LCC methodologies must be used together Therefore, it can he seen that safer environmental products can come to be the most profitable investment options.

Embrittlement of case hardened steel chain link

Various steel chain links presented cracking during their manufacturing process, which includes induction case hardening and electrogalvanizing steps. Fractographic examination of the exposed crack surfaces revealed intergranular cracking with some areas featuring a thin layer of iron oxide, indicating that the cracking took place after the electrogalvanizing step. The location of the cracks coincided with the position of the deepest case hardened layer, suggesting the occurrence of localized overheating during the induction case hardening step. Inductive heating finite element analysis (COSMOS Designstar Software) confirmed that during the case hardening the austenitising temperature reached in the crack region values of approximately 1050 degrees C. The results indicated that intergranular cracking was caused by hydrogen embrittlement. (C) 2009 Elsevier Ltd. All rights reserved.

Study on Iron Formation During the Carbothermic Reduction of Iron Ore in Carbon Composite Pellets in the Temperature Range 1423 K-1623 K

The aim of this work is to study the reaction rate and the morphology of the intermediary reaction products during reduction of iron ore, when iron ore and carbonaceous material are agglomerated together as a carbon composite iron ore pellet. The reaction was performed at high temperatures, and in order to avoid heat transfer constraints small size samples were used. The carbonaceous materials employed were coke breeze and pure graphite. Portland cement was employed as a binder, and the pellets diameter was 5.2 mm. The experimental technique involved the measurement of the pellets weight loss, as well as interruption of the reaction at different stages in order to submit the partially reduced pellet to scanning electron microscopy. It has been observed that above 1523 K there is the formation of liquid slag inside the pellets, which partially dissolves iron oxides. The apparent activation energies obtained were 255 kJ/mol for coke breeze containing pellets, and 230 kJ/mol for those pellets containing graphite. It was possible to avoid heat transfer control of the reaction rate up to 1523 K by employing small composite pellets.

High Carbon Ferro-Chromium by Self-Reducing Process

This paper discusses the effects of temperature, addition of ferro-silicon and fluxing agents for the production of high carbon ferro-chromium by self-reducing process. The use of self-reducing agglomerates for ferro-alloys production is becoming an emerging processing technology due to lowering the electric energy consumption and improving the metal recovery in comparison with traditional ones. The self-reducing pellets were composed by chromite, petroleum coke, cement and small (0.1% - 2%) addition of ferro-silicon. The slag composition was adjusted by addition of fluxing agents. The reduction of pellets was carried out at 1773K (1500 degrees C), 1823K (1550 degrees C) and 1873K (1600 degrees C) by using induction furnace. The products obtained, containing slag and metallic phases, were analyzed by scanning electron microscopy and chemical analyses (XEDS). By increasing temperature from 1773K to 1823K large effect on the reduction time was observed. It decreased from 30 minutes to 10 minutes, for reaching around 0.98 reduction fraction. No significant effect on reduction time was observed when the reduction temperature was increased from 1823K to 1873K. At 1773K, the addition of 2% of ferro-silicon in the pellet resulted in an increasing reaction rate of around 6 times, in comparison with agglomerate without this addition. The addition of fluxing agents (silica and hydrated lime) has effect on reduction time (inverse relationship) and the pellets become less porous after reduction.

EROSION-CORROSION SYNERGISM OF AN AISI 410 MARTENSITIC STAINLESS STEEL

In this work, the behavior of an AISI 410 martensitic stainless steel under corrosion-erosion conditions is evaluated. Quenched and tempered samples were used for the wear test, using a low velocity jet-like device connected to a potentiostat. Potentiodynamic polarization curves were obtained with the electrolyte in static state, with flow conditions and under corrosion-erosion, adding quartz particles to the electrolyte. In addition, mass loss measurements under erosion and corrosion-erosion conditions were carried out. The topography of the surfaces was examined after the wear tests, using optical and scanning electron microscopy. This information, together with the results of mass losses and the electrochemical tests were used to establish the degradation mechanisms of the stainless steels under different testing conditions. The results showed that synergism is a significant part of the degradation process of this steel (66.5%) and that the mass removal process of steel was controlled by corrosion assisted by erosion.

Mesoscale plasticity anisotropy at the earliest stages of cavitation-erosion damage of a high nitrogen austenitic stainless steel

A high nitrogen austenitic stainless steel (0.9wt% N) and an ordinary 304 austenitic stainless steel were submitted to cavitation-erosion tests in a vibratory apparatus operating at a frequency of 20 kHz. The high nitrogen stainless steel was obtained by high temperature gas nitriding a 1-mm thick strip of an UNS 31803 duplex stainless steel. The 304 austenitic stainless steel was used for comparison purposes. The specimens were characterized by scanning electron microscopy and Electron Back Scatter Diffraction. The surface of the cavitation damaged specimens was analyzed trying to find out the regions where cavitation damage occurred preferentially. The distribution of sites where cavitation inception occurred was extremely heterogeneous, concentrating basically at (i) slip lines inside some grains and (ii) Sigma-3 coincidence site lattice (CSL) boundaries (twin boundaries). Furthermore, it was observed that the CE damage spread faster inside those grains which were more susceptible to damage incubation. The damage heterogeneity was addressed to plasticity anisotropy. Grains in which the crystallographic orientation leads to high resolved shear stress show intense damage at slip lines. Grain boundaries between grains with large differences in resolved shear stress where also intensely damaged. The relationship between crystallite orientation distributions, plasticity anisotropy and CE damage mechanisms are discussed. (C) 2009 Elsevier B.V. All rights reserved.

Bending fatigue of stainless steel shear pins belonging to a hydroelectric plant

Coaracy Nunes was the first hydroelectric power plant in the Amazon region, being located in Araguari River, Amapa State, Brazil. The plant operates since 1976, presenting now a nominal capacity of 78 MW. The shear pins, which are installed in the turbine hydraulic arms to control the wicket gate and regulate the water flow into the turbine blades, suffered several breakdowns since 2004. These shear pins are made of an ASTM 410 stainless steel and were designed to break by a shear overload of 120 kN. Fractographic investigation of the pins, however, revealed two types of fracture topographies: a region of stable crack propagation area, with non-pronounced striation and secondary cracks; and a region of unstable propagation, featuring elongated dimples. These results indicated that the stable crack propagation occurred by fatigue (bidirectional bending), which was nucleated at machining marks under high nominal load. Finite element analysis was carried out using two loading conditions (pure shear and a combination of shear and bending) and the results indicated that the presence of a bending stress strongly increased the stress concentration factor (85% rise in the shear stress and 130% rise in the Von Mises stress). Misalignment during shear pins assembly associated with vibration might have promoted the premature failure of the shear by bending fatigue. (C) 2008 Elsevier Ltd. All rights reserved.

ANNEALING EFFECTS ON THE MICROSTRUCTURE OF FERRITIC-MARTENSITIC ODS-EUROFER STEEL

Oxide dispersion strengthened (ODS) ferritic/martensitic (FM) steels are promising candidates for structural applications in future fusion power reactors. In order to evaluate the thermal stability of 80% cold-rolled ODS-EUROFER, samples were annealed for 1 h at temperatures up to about 0.9 T(m), where T(m) is the absolute melting point. The characterization of the annealed samples was performed using transmission electron microscopy and electron backscatter diffraction. Results show that static recovery is the main softening mechanism of this steel when annealed below 800 degrees C. The volume fraction of recrystallized grains is quite small (below 0.10). Above 900 degrees C, martensitic transformation takes place causing pronounced hardening. Large M(23)C(6) particles are found at the grain boundaries after tempering at 750 degrees C for 2 h.

Fretting fatigue in overhead conductors: Rig design and failure analysis of a Grosbeak aluminium cable steel reinforced conductor

The performance optimisation of overhead conductors depends on the systematic investigation of the fretting fatigue mechanisms in the conductor/clamping system. As a consequence, a fretting fatigue rig was designed and a limited range of fatigue tests was carried out at the middle high cycle fatigue regime in order to access an exploratory S-N curve for a Grosbeak conductor, which was mounted on a mono-articulated aluminium clamping system. Subsequent to these preliminary fatigue tests, the components of the conductor/clamping system, such as ACSR conductor, upper and lower clamps, bolt and nuts, were subjected to a failure analysis procedure in order to investigate the metallurgical free variables interfering on the fatigue test results, aiming at the optimisation of the testing reproducibility. The results indicated that the rupture of the planar fracture surfaces observed in the external At strands of the conductor tested under lower bending amplitude (0.9 mm) occurred by fatigue cracking (I mm deep), followed by shear overload. The V-type fracture surfaces observed in some At strands of the conductor tested under higher bending amplitude (1.3 mm) were also produced by fatigue cracking (approximately 400 mu m deep), followed by shear overload. Shear overload fracture (45 degrees fracture surface) was also observed on the remaining At wires of the conductor tested under higher bending amplitude (1.3 mm). Additionally, the upper and lower Al-cast clamps presented microstructure-sensitive cracking, which was folowed by particle detachment and formation of abrasive debris on the clamp/conductor tribo-interface, promoting even further the fretting mechanism. The detrimental formation of abrasive debris might be inhibited by the selection of a more suitable class of as-cast At alloy for the production of clamps. Finally, the bolt/nut system showed intense degradation of the carbon steel nut (fabricated in ferritic-pearlitic carbon steel, featuring machined threads with 190 HV), with intense plastic deformation and loss of material. Proper selection of both the bolt and nut materials and the finishing processing might prevent the loss in the clamping pressure during the fretting testing. It is important to control the specification of these components (clamps, bolt and nuts) prior to the start of large scale fretting fatigue testing of the overhead conductors in order to increase the reproducibility of this assessment. (c) 2008 Elsevier Ltd. All rights reserved.

Hardness and structure characterization of Ti(6)Al(4)V films produced by reactive magnetron sputtering on a conventional austenitic stainless steel

Ti(6)Al(4)V thin films were grown by magnetron sputtering on a conventional austenitic stainless steel. Five deposition conditions varying both the deposition chamber pressure and the plasma power were studied. Highly textured thin films were obtained, their crystallite size (C) 2008 Elsevier Ltd. All rights reserved.

Magnetic losses evolution of a semi-processed steel during forced aging treatments

An ultra-low carbon steel (30 ppm after decarburization) containing Al and Si was aged for distinct soaking times at 210 degrees C. The core loss increased continuously until around 24 h. After that, only slight changes were verified. It was found that only the hysteresis loss component changed during the aging treatment. By internal friction test and transmission electron microscopy it was seen that carbon precipitation caused the magnetic aging. By scanning electron microscopy it could be concluded that the increase of aging index was attributed to the high number of carbides larger than 0.1 mu m. (C) 2008 Elsevier B. V. All rights reserved.

Effect of rolling on the residual stresses and magnetic properties of a 0.5% Si electrical steel

Cold-rolled (0-19% of reduction) 0.5% Si electrical steel sheets were studied in detail, including macro and micro residual stress measurements, crystallographic texture, dc-hysteresis curves and iron losses. Even for the smallest deformation, losses increase significantly, with large increase of the hysteresis losses, whereas the anomalous losses reduce slightly. The residual microstresses are similar to 150-350 MPa, whereas residual macrostresses are compressive, similar to 50 MPa. The large increase of the hysteresis losses is attributed to the residual microstresses. The dislocation density estimated by X-ray diffraction is in reasonable agreement with that predicted from the Sablik et al. model for effect of plastic deformation on hysteresis. The intensity of the texture fibers {1 1 1}< u v w > and < 110 >//RD (RD = rolling direction) increases with the reduction. (C) 2008 Elsevier B.V. All rights reserved.

Investigation on the intergranular corrosion resistance of the AISI 316L(N) stainless steel after long time creep testing at 600 degrees C

The effect of precipitation on the corrosion resistance of AISI 316L(N) stainless steel previously exposed to creep tests at 600 degrees C for periods of up to 10 years, has been studied. The corrosion resistance was investigated in 2 M H(2)SO(4)+0.5 M NaCl+0.01 M KSCN solution at 30 degrees C by electrochemical methods. The results showed that the susceptibility to intergranular corrosion was highly affected by aging at 600 degrees C and creep testing time. The intergranular corrosion resistance decreased by more than twenty times when the creep testing time increased from 7500 h to 85,000 h. The tendency to passivation decreased and less protective films were formed on the creep tested samples. All tested samples also showed susceptibility to pitting. Grain boundary M(23)C(6) carbides were not found after long-term exposure at 600 degrees C and the corrosion behavior of the creep tested samples was attributed to intermetallic phases (mainly sigma phase) precipitation. (C) 2007 Elsevier Inc. All rights reserved.

Precipitation of Laves phase in a 28%Cr-4%Ni-2%Mo-Nb superferritic stainless steel

The main objective of the present work was to study the precipitation of the Laves phase in the X1 CrNiMoNb 28 4 2 (Werkstoff-Nr. DIN 1.4575) superferritic stainless steel employing several complementary techniques of microstructural analysis. The phase that precipitated in largest quantity in the DIN 1.4575 steel was the sigma (sigma) phase. However, along grain boundaries, after aging at 850 degrees C, a Laves phase of the MgZn2 type, with a hexagonal C14 crystal structure and chemical composition (Fe,Cr,Ni)(2)(Nb,Mo,Si), was also identified. Growth of the Laves phase is curtailed by exhaustion of niobium of the matrix and by the presence of the sigma phase, which also precipitates in the vicinity of the grain boundaries, however in larger amounts. No chi (chi) or austenite phases were detected in the temperature range studied. (C) 2007 Elsevier Inc. All rights reserved.