Study of Co-based hydrotalcite-derived mixed metal oxides partially modified with silver as potential catalysts for N2O decomposition

Co-Al-Ox mixed metal oxides partially modified with Cu or Mg, as well as Ag were successfully prepared, characterized and evaluated as potential catalysts for the N2O decomposition. The materials were characterized by the following techniques: X-Ray Diffraction, Thermogravimetric Analysis (TGA), N2 Physisorption, Hydrogen Temperature-Programmed Reduction (H2-TPR), and X-ray photoelectron spectroscopy (XPS). Ag-modified HT-derived mixed oxides showed enhanced activity compared to the undoped materials, the optimum composition was found for (1 wt.% Ag)CHT-Co3Al. The catalyst characterization studies suggested that the improved catalytic activity of Ag-promoted catalysts were mainly because of the altered redox properties of the materials.

I. Nickel-Exchanged Zincosilicate Catalysts for the Oligomerization of Propylene and II. Organic SDA-Free Catalysts for the Methanol-to-Olefins Reaction

Nickel-containing catalysts are developed to oligomerize light olefins. Two nickel-containing zincosilicates (Ni-CIT-6 and Ni-Zn-MCM-41) and two nickel-containing aluminosilicates (Ni-HiAl-BEA and Ni-USY) are synthesized as catalysts to oligomerize propylene into C_3n (C₆ and C₉) products. All catalysts oligomerize propylene, with the zincosilicates demonstrating higher average selectivities to C_3n products, likely due to the reduced acidity of the Zn heteroatom.

To test whether light alkanes can be incorporated into this oligomerization reaction, a supported homogeneous catalyst is combined with Ni-containing zincosilicates. The homogeneous catalyst is included to provide dehydrogenation/hydrogenation functions. When this tandem catalyst system is evaluated using a propylene/n-butane feed, no significant integration of alkanes are observed.

Ni-containing zincosilicates are reacted with 1-butene and an equimolar propylene/1-butene mixture to study other olefinic feeds. Further, other divalent metal cations such as Mn²⁺, Co²⁺, Cu²⁺, and Zn²⁺ are exchanged onto CIT-6 samples to investigate stability and potential use for other reactions. Co-CIT-6 oligomerizes propylene, albeit less effectively than Ni-CIT-6. The other M-CIT-6 samples, while not able to oligomerize light olefins, may be useful for other reactions, such as deNO_x.

Molecular sieves are synthesized, characterized, and used to catalyze the methanol-to-olefins (MTO) reaction. The Al concentration in SSZ-13 samples is varied to investigate the effect of Al number on MTO reactivity when compared to a SAPO-34 sample with only isolated Si Brønsted acid sites. These SSZ-13 samples display reduced transient selectivity behavior and extended reaction lifetimes as Si/Al increases; attributable to fewer paired Al sites. MTO reactivity for the higher Si/Al SSZ-13s resembles the SAPO-34 sample, suggesting that both catalysts owe their stable reaction behavior to isolated Brønsted acid sites.

Zeolites CHA and RHO are prepared without the use of organic structure-directing agents (OSDAs), dealuminated by steam treatments (500°C-800°C), and evaluated as catalysts for the MTO reaction. The effects of temperature and steam partial pressure during steaming are investigated. X-ray diffraction (XRD) and Ar physisorption show that steaming causes partial structural collapse of the zeolite, with degradation increasing with steaming temperature. ²⁷Al MAS NMR spectra of steamed materials reveal the presence of tetrahedral, pentacoordinate, and hexacoordinate aluminum.

Proton forms of as-synthesized CHA (Si/Al=2.4) and RHO (Si/Al=2.8) rapidly deactivate under MTO testing conditions (400°C, atmospheric pressure). CHA samples steamed at 600°C performed best among samples tested, showing increased olefin selectivities and catalyst lifetime. Acid washing these steamed samples further improved activity. Reaction results for RHO were similar to CHA, with the RHO sample steamed at 800°C producing the highest light olefin selectivities. Catalyst lifetime and C₂-C₃ olefin selectivities increase with increasing reaction temperature for both CHA-type and RHO-type steamed samples.

Influence of the metal precursor on the catalytic behavior of Pt/Ceria catalysts in the preferential oxidation of CO in the presence of H2 (PROX)

The effect of the metal precursor (presence or absence of chlorine) on the preferential oxidation of CO in the presence of H2 over Pt/CeO2 catalysts has been studied. The catalysts are prepared using (Pt(NH3)4)(NO3)2 and H2PtCl6, as precursors, in order to ascertain the effect of the chlorine species on the chemical properties of the support and on the catalytic behavior of these systems in the PROX reaction. The results show that chloride species exert an important effect on the redox properties of the oxide support due to surface chlorination. Consequently, the chlorinated catalyst exhibits a poorer catalytic activity at low temperatures compared with the chlorine-free catalyst, and this is accompanied by a higher selectivity to CO2 even at high reaction temperatures. It is proposed that the CO oxidation mechanism follows different pathways on each catalyst.

Selective hydrogenation by novel composite supported Pd egg-shell catalysts

Two organic–inorganic mixed phase supports were prepared, comprising an alumina filler and polymers of different chemical nature. Four low loaded Pd catalysts were prepared. Good activities and selectivities were obtained during the hydrogenations of styrene, 1-heptyne and 2,3-butanedione. The catalysts were found to have excellent mechanical properties and could be used in applications needing high attrition resistance and crushing strength. In this sense, processes for fine chemicals using slurry reactors or processes for commodities using long packed beds could advantageously use them.

High performance of Cu/CeO2-Nb2O5 catalysts for preferential CO oxidation and total combustion of toluene

Copper-based catalysts supported on niobium-doped ceria have been prepared and tested in the preferential oxidation of CO in excess of H2 (PROX) and in total oxidation of toluene. Supports and catalysts have been characterized by several techniques: N2 adsorption, ICP-OES, XRF, XRD, Raman Spectroscopy, SEM, TEM, H2-TPR and XPS, and their catalytic performance has been measured in PROX, with an ideal gas mixture (CO, O2 and H2) with or without CO2 and H2O, and in total oxidation of toluene. The effects of the copper loading and the amount of niobium in the supports have been evaluated. Remarkably, the addition of niobia to the catalysts may improve the catalytic performance in total oxidation of toluene. It allows us to prepare cheaper catalysts (niobia it is far cheaper than ceria) with improved catalytic performance.

Green synthesis of polypyrrole-supported metal catalysts: application to nitrate removal in water

Pt and Pt/Sn catalysts supported on polypyrrole (PPy) have been prepared using Ar plasma to reduce the metal precursors dispersed on the polymer. The PPy support was synthesized by chemical polymerization of pyrrole with FeCl3·6H2O, this leading to the conducting form of the polymer (conductimetric measurements). The Ar plasma treatment produced a partial reduction of platinum ions, anchored as platinum chloro-complexes to the PPy chain, into metallic platinum. A homogeneous distribution of Pt and Sn nanoparticles was observed by TEM. Activity of the PPy-supported catalysts was evaluated in the reduction of aqueous nitrate with H2 at room temperature. Nitrate concentration in water below the maximum acceptable level of 50 mg L−1 was achieved with all catalysts. However, considering not only efficiency in nitrate reduction, but also minimized concentrations of undesired nitrite and ammonium, the monometallic Pt catalyst seems to be the most promising one.

Active oxygen by Ce–Pr mixed oxide nanoparticles outperform diesel soot combustion Pt catalysts

A Ce0.5Pr0.5O2 mixed oxide has been prepared with the highest surface area and smallest particle size ever reported (125 m2/g and 7 nm, respectively), also being the most active diesel soot combustion catalyst ever tested under realistic conditions if catalysts forming highly volatile species are ruled out. This Ce–Pr mixed oxide is even more active than a reference platinum-based commercial catalyst. This study provides an example of the efficient participation of oxygen species released by a ceria catalyst in a heterogeneous catalysis reaction where both the catalyst and one of the reactants (soot) are solids. It has been concluded that both the ceria-based catalyst composition (nature and amount of dopant) and the particle size play key roles in the combustion of soot through the active oxygen-based mechanism. The composition determines the production of active oxygen and the particle size the transfer of such active oxygen species from catalyst to soot.

In situ characterization of porous VPO catalysts with fibrous structure: Identifying the redox behavior and the stability of active sites

Two VPO materials with fibrillar morphology have been prepared by the aid of electrospinning technique. One is a VPO carbon-supported material (VCF200) with fibrous morphology and very high surface area that is stable under oxidizing conditions up to 350C. The other material is a bulk mixed VPO oxide (VPO500) with fibrous structure obtained after optimizing the calcination of the carbon support in VCF200. Despite it is a bulk oxide material, this material exhibits a high surface area (> 60 m2/g). The redox behavior of both samples was monitored by in situ Raman spectroscopy under oxidation/reduction cycles. For the dehydrated supported sample (VCF200), the pyrophosphate phase (VO)2P2O7 (Raman ~930 cm-1) is detected, which has been described as the active phase (see Figure (a) below). This phase is quite stable since it does not disappear upon subsequent oxidation/reduction cycles. Under reduction conditions at 125C, in consecutive cycles, additional Raman bands appear at ~1090 cm-1 that are characteristic of the αII-VOPO4 phase. On the other hand, the bulk phases show a reversible behavior under redox cycles (Figure (b)). Under reducing conditions, a Raman band appears at ~980 cm-1 (β-VPO phase), whereas under oxidation conditions some segregation to VOx oxides occurs. Nevertheless, this segregation is reversible and the β-VPO phase forms again under reducing conditions. Thus, these results demonstrate that the active VPO phases of these fibrous catalysts are quite stable, and that their structure is reversible under several redox cycles, which make them suitable as oxidation catalysts.

Niobic acid nanoparticle catalysts for the aqueous phase transformation of glucose and fructose to 5-hydroxymethylfurfural

A family of bulk and SBA-15 supported peroxo niobic acid sols were prepared by peptisation of niobic acid precipitates with H2O2 as heterogeneous catalysts for aqueous phase glucose and fructose conversion to 5-hydroxymethylfurfural (5-HMF). Niobic acid nanoparticles possess a high density of Brønsted and Lewis acid sites, conferring good activity towards glucose and fructose conversion, albeit with modest 5-HMF yields under mild reaction conditions (100 °C). Thermally-induced niobia crystallisation suppresses solid acidity and activity. Nanoparticulate niobic acid dispersed over SBA-15 exhibits pure Brønsted acidity and an enhanced Turnover Frequency for fructose dehydration.

Octyl co-grafted PrSO3H/SBA-15:tunable hydrophobic solid acid catalysts for acetic acid esterification

Propylsulfonic acid (PrSO3H) derivatised solid acid catalysts have been prepared by post modification of mesoporous SBA-15 silica with mercaptopropyltrimethoxysilane (MPTMS), with the impact of co-derivatisation with octyltrimethoxysilane (OTMS) groups to impart hydrophobicity to the catalyst investigated. Turn over frequencies (TOF) for acetic acid esterification with methanol increase with PrSO3H surface coverage across both families suggesting a cooperative effect of adjacent acid sites at high acid site densities. Esterification activity is further promoted upon co-functionalisation with hydrophobic octyl chains, with inverse gas chromatography (iGC) measurements indicating increased activity correlates with decreased surface polarity or increased hydrophobicity.

Efficient removal of paracetamol using LaCu1-xMxO3 (M=Mn, Ti) perovskites as heterogeneous Fenton-like catalysts

A series of perovskite-like oxides LaCu1-xMxO3 (M=Mn, Ti; 0.0 ⩽ x ⩽ 0.8) was prepared by amorphous citrate decomposition and characterized by XRD, ICP-OES and XPS techniques. The catalysts were tested in the Fenton-like degradation of paracetamol with H2O2, under mild reaction conditions, 25 °C and nearly neutral pH. Values of decomposition of paracetamol between 80 and 97% at 300 min were achieved for most of samples. The presence of the Cu2+/Cu+ pair at the surface of the catalysts is necessary to carry out the reaction and the catalysts containing higher amount of copper at the surface, resulted to be more active. The leaching of metals was less than 1%, which discards the contribution of the homogenous Fenton-like reaction and remarks the high stability of the metals into the mixed oxide network. The catalytic activity of LaCu0.8Mn0.2O3 was maintained after three cycles of reaction, which proves the stability and reusability of the catalyst.

Stability of clay-based catalysts in contact with water vapour

The search for cleaner processes is one of the major challenges in modern chemical industries. In this context clay derived materials are environmentally friendly catalysts that can be easily tailored to optimize their catalytic activity for a precise reaction of interest. Furthermore, clay-based catalysts can be easily separated, recovered and reused and their versatility, low cost, high catalytic activity and/or selectivity render them very attractive materials. Considering that the stability towards water vapour is a crucial aspect for catalytic performance and reuse of the catalysts, we present a study of the pore structure stability, in the presence of water vapour, of clay catalysts prepared by acid activation with HCl solutions and ion-exchange with sodium, aluminium and iron, from a natural clay collected at Serra de Dentro (Porto Santo Island, Portugal) [1]. For elucidating the influence of water vapour on the pore structure stability, water vapour adsorption- -desorption isotherm, at 298 K, was determined on each sample by gravimetric method as well as n-pentane adsorption−desorption isotherms, at 298 K, which were determined before and after the corresponding water adsorption-desorption isotherms. Prior to the measurements, the samples were outgassed during 5 h at 473 K and the adsorptives were outgassed by repeated freeze–thaw cycles. The results to be reported in the communication allow us to state that, upon contact with water vapour, the less acid activated catalysts suffered some reduction in pore volume reflecting changes in the pore structure, while the more acid activated catalysts and those prepared by ion-exchange presented excellent stability upon one cycle of water vapour adsorption-desorption. The results are corroborated by nitrogen adsorption-desorption isotherms determined, at 77 K, before and after the water and n-pentane adsorption-desorption measurements.

Orals ain't orals : how instruction and assessment practices affect delivery choices with prepared student oral presentations.

Despite an ostensibly technology-driven society, the ability to communicate orally is still seen as an essential ability for students at school and university, as it is for graduates in the workplace. The need to develop effective oral communication skills is often tied to future work-related tasks. One tangible way that educators have assessed proficiency in this area is through prepared oral presentations. While some use the terms oral communication and oral presentation interchangeably, other writers question the role more formal presentations play in the overall development of oral communication skills. Adding to the discussion, this paper is part of a larger study examining the knowledge and skills students bring into the academy from previous educational experiences. The study examines some of the teaching and assessment methods used in secondary schools to develop oral communication skills through the use of formal oral presentations. Specifically, it will look at assessment models and how these are used as a form of instruction as well as how they contribute to an accurate evaluation of student abilities. The purpose of this paper is to explore key terms and identify tensions between expectations and practice. Placing the emphasis on the ‘oral’ aspect of this form of communication this paper will particularly look at the ‘delivery’ element of the process.

Polyurethane (PU) scaffolds prepared by solvent casting/particulate leaching (SCPL) combined with centrifugation

This article reports an enhanced solvent casting/particulate (salt) leaching (SCPL) method developed for preparing three-dimensional porous polyurethane (PU) scaffolds for cardiac tissue engineering. The solvent for the preparation of the PU scaffolds was a mixture of dimethylformamide (DFM) and tetrahydrofuran (THF). The enhanced method involved the combination of a conventional SCPL method and a step of centrifugation, with the centrifugation being employed to improve the pore uniformity and the pore interconnectivity of scaffolds. Highly porous three-dimensional scaffolds with a well interconnected porous structure could be achieved at the polymer solution concentration of up to 20% by air or vacuum drying to remove the solvent. When the salt particle sizes of 212-295, 295-425, or 425-531 µm and a 15% w/v polymer solution concentration were used, the porosity of the scaffolds was between 83-92% and the compression moduli of the scaffolds were between 13 kPa and 28 kPa. Type I collagen acidic solution was introduced into the pores of a PU scaffold to coat the collagen onto the pore walls throughout the whole PU scaffold. The human aortic endothelial cells (HAECs) cultured in the collagen-coated PU scaffold for 2 weeks were observed by scanning electron microscopy (SEM). It was shown that the enhanced SCPL method and the collagen coating resulted in a spatially uniform distribution of cells throughout the collagen-coated PU scaffold.