Determination of corn stalk fibers' strength through modeling of the mechanical properties of its composites

Worldwide cultivation of corn is expanding, due in part to the increasing production of bioethanol. In consequence, huge amounts of corn stalks residues are been produced. Instead of incineration, we transformed the corn stalks into a semichemical pulp and successfully applied it as reinforcement in polypropylene composites. PP composites reinforced with 40% wt corn stalk single fibers were prepared, and their mechanical properties were evaluated. Through mechanical properties modeling of the composites, the intrinsic tensile strength of the cellulosic fibers that constitute the corn stalk have been determined

Magnetic and transport properties of II-V diluted magnetic semiconductors doped with manganese and nickel

This thesis is devoted to investigations of three typical representatives of the II-V diluted magnetic semiconductors, Zn1-xMnxAs2, (Zn1-xMnx)3As2 and p-CdSb:Ni. When this work started the family of the II-V semiconductors was presented by only the compounds belonging to the subgroup II3-V2, as (Zn1-xMnx)3As2, whereas the rest of the materials mentioned above were not investigated at all. Pronounced low-field magnetic irreversibility, accompanied with a ferromagnetic transition, are observed in Zn1-xMnxAs2 and (Zn1-xMnx)3As2 near 300 K. These features give evidence for presence of MnAs nanosize magnetic clusters, responsible for frustrated ground magnetic state. In addition, (Zn1-xMnx)3As2 demonstrates large paramagnetic response due to considerable amount of single Mn ions and small antiferromagnetic clusters. Similar paramagnetic system existing in Zn1-xMnxAs2 is much weaker. Distinct low-field magnetic irreversibility, accompanied with a rapid saturation of the magnetization with increasing magnetic field, is observed near the room temperature in p- CdSb:Ni, as well. Such behavior is connected to the frustrated magnetic state, determined by Ni-rich magnetic Ni1-xSbx nanoclusters. Their large non-sphericity and preferable orientations are responsible for strong anisotropy of the coercivity and saturation magnetization of p- CdSb:Ni. Parameters of the Ni1-xSbx nanoclusters are estimated. Low-temperature resistivity of p-CdSb:Ni is governed by a hopping mechanism of charge transfer. The variable-range hopping conductivity, observed in zero magnetic field, demonstrates a tendency of transformation into the nearest-neighbor hopping conductivity in non-zero magnetic filed. The Hall effect in p-CdSb:Ni exhibits presence of a positive normal and a negative anomalous contributions to the Hall resistivity. The normal Hall coefficient is governed mainly by holes activated into the valence band, whereas the anomalous Hall effect, attributable to the Ni1-xSbx nanoclusters with ferromagnetically ordered internal spins, exhibits a low-temperature power-law resistivity scaling.

Influence of chloride-mediated oxidation on the electrochemical degradation of the direct black 22 dye using boron-doped diamond and β-PbO2 anodes

The Direct Black 22 dye was electrooxidized at 30 mA cm-2 in a flow cell using a BDD or β-PbO2 anode, varying pH (3, 7, 11), temperature (10, 25, 45 °C), and [NaCl] (0 or 1.5 g L-1). In the presence of NaCl, decolorization rates were similar for all conditions investigated, but much higher than predicted through a theoretical model assuming mass-transport control; similar behavior was observed for COD removal (at pH 7, 25 °C), independently of the anode. With no NaCl, COD removals were also higher than predicted with a theoretical model, which suggests the existence of distinct dye degradation pathways.

A simple square-wave voltammetric method for the determination of scopolamine in pharmaceuticals using a boron-doped diamond electrode

A simple procedure is described for the determination of scopolamine by square-wave voltammetry using a cathodically pretreated boron-doped diamond electrode. Cyclic voltammetry studies indicate that the oxidation of scopolamine is irreversible at a peak potential of 1.59 V (vs. Ag/AgCl (3.0 mol L-1 KCl)) in a 0.50 mol L-1 sulfuric acid solution. Under optimized conditions, the analytical curve obtained was linear (r = 0.9996) for the scopolamine concentration range of 1.0 to 110 µmol L-1, with a detection limit of 0.84 µmol L-1. The method was successfully applied to the determination of scopolamine in pharmaceutical formulations with minimum sample preparation.

Ba-DOPED ZnO MATERIALS: A DFT SIMULATION TO INVESTIGATE THE DOPING EFFECT ON FERROELECTRICITY

ZnO is a semiconductor material largely employed in the development of several electronic and optical devices due to its unique electronic, optical, piezo-, ferroelectric and structural properties. This study evaluates the properties of Ba-doped wurtzite-ZnO using quantum mechanical simulations based on the Density Functional Theory (DFT) allied to hybrid functional B3LYP. The Ba-doping caused increase in lattice parameters and slight distortions at the unit cell angle in a wurtzite structure. In addition, the doping process presented decrease in the band-gap (Eg) at low percentages suggesting band-gap engineering. For low doping amounts, the wavelength characteristic was observed in the visible range; whereas, for middle and high doping amounts, the wavelength belongs to the Ultraviolet range. The Ba atoms also influence the ferroelectric property, which is improved linearly with the doping amount, except for doping at 100% or wurtzite-BaO. The ferroelectric results indicate the ZnO:Ba is an strong option to replace perovskite materials in ferroelectric and flash-type memory devices.

Utilization of non-wood pulp in different fibers products

The correct utilization of non-wood raw material allows reducing tree cutting and reduces emissions of carbon dioxide from burning of non-wood plants on farmers fields. Also it allows increasing economical situation in regions that non-wood plants are grown and where they are converted into pulp and paper. Also it gives positive effect on population pressure of work by addition of working place. In the literature survey included an overview of the historical meaning of non-wood pulp on developing paper production and structure of non-wood pulps. Moreover, anatomical and chemical composition of straw, reed and bamboo were studied more detailed. Also, an overview of the utilization of non-wood pulp in papermaking was made. Especially tissue, tree-free and release papers were reviewed. In the experimental part the goal was to investigate suitability of non-wood pulp like wheat straw pulp and bamboo pulp for different fiber products. Finally release and tree-free paper products were selected for experimental studies. It was discovered that wheat straw, especially screened wheat straw, showed good results for release paper. Also utilization of wheat straw and bamboo pulp in tree-free paper showed good results and suitability of these non-wood pulps for tree-free paper production. Also it was noticed that addition of wheat straw pulp gave positive effect on initial wet strength for release and tree-free paper.

Synthesis and characterization of activated carbon fibers from Kevlar

Kevlar [poly (p-phenilylene terephtalamide)], was used as a precursor in the preparation of activated carbon fibers. For this intention, physical and chemical activations were carried out. Activated fibers were physically prepared from the carbonization of the Kevlar and its later activation with CO2 and steam of water, by the other hand; the chemically activated fibers were obtained by means of the impregnation of the material with phosphoric acid and their later carbonization. Different conditions were used and preliminary analyses of the precursor were taken into account (TGA-DTA / IR). The resulting fibers were characterized by N2 (77K) adsorption, infrared spectroscopy, SEM, and immersion calorimetry. Yields and Burn off were also evaluated. The results shows that if you want to synthesize activated carbon fibers from Kevlar strong conditions respect to the commonly used such as water steam, high phosphoric acid concentrations and methods of impregnation are the ones who allows the development of optimal surface areas and pore volumes.

Synthesis and characterization of Fe(III)-doped ceramic membranes of titanium dioxide and its application in photoelectrocatalysis of a textile dye

Pure and Fe(III)-doped TiO2 suspensions were prepared by the sol gel method with the use of titanium isopropoxide (Ti(OPri)4) as precursor material. The properties of doped materials were compared to TiO2 properties based on the characterization by thermal analysis (TG-DTA and DSC), X-ray powder diffractometry and spectroscopy measurements (FTIR). Both undoped and doped TiO2 suspensions were used to coat metallic substrate as a mean to make thin-film electrodes. Thermal treatment of the precursors at 400ºC for 2 h in air resulted in the formation of nanocrystalline anatase TiO2. The thin-film electrodes were tested with respect to their photocatalytic performance for degradation of a textile dye in aqueous solution. The plain TiO2 remains as the best catalyst at the conditions used in this report.

Biochemical Modification of Thermomechanical Pulp Fibers

The first objective of this study was to find out reliable laboratory methods to predict the effect of enzymes on specific energy consumption and fiber properties of TMP pulp. The second one was to find with interactive software called “Knowledge discovery in databases” enzymes or other additives that can be used in finding a solution to reduce energy consumption of TMP pulp. The chemical composition of wood and enzymes, which have activity on main wood components were presented in the literature part of the work. The results of previous research in energy reduction of TMP process with enzymes were also highlighted. The main principles of knowledge discovery have been included in literature part too. The experimental part of the work contains the methods description in which the standard size chip, crushed chip and fiberized spruce chip (fiberized pulp) were used. Different types of enzymatic treatment with different dosages and time were tested during the experiments and showed. Pectinase, endoglucanase and mixture of enzymes were used for evaluation of method reliability. The fines content and fiber length of pulp was measured and used as evidence of enzymes' effect. The refining method with “Bauer” laboratory disc refiner was evaluated as not highly reliable. It was not able to provide high repeatability of results, because of uncontrolled feeding capacity and refining consistency. The refining method with Valley refiner did not have a lot of variables and showed stable and repeatable results in energy saving. The results of experiments showed that efficient enzymes impregnation is probably the main target with enzymes application for energy saving. During the work the fiberized pulp showed high accessibility to enzymatic treatment and liquid penetration without special impregnating equipment. The reason was that fiberized pulp has larger wood surface area and thereby the contact area between the enzymatic solution and wood is also larger. Standard size chip and crushed chip treatment without special impregnator of enzymatic solution was evaluated as not efficient and did not show visible, repeatable results in energy consumption decrease. Thereby it was concluded that using of fiberized pulp and Valley refiner for measurements of enzymes' effectiveness in SEC decrease is more suitable than normal size chip and crushed chip with “Bauer” refiner. Endoglucanase with 5 kg/t dosage showed about 20% energy consumption decrease. Mixture of enzymes with 1.5 kg/t dosage showed about 15% decrease of energy consumption during the refining. Pectinase at different dosages and treatment times did not show significant effect on energy consumption. Results of knowledge discovery in databases showed the xylanase, cellulase and pectinase blend as most promising for energy reduction in TMP process. Surfactants were determined as effective additives for energy saving with enzymes.

Growth, magnetic and transport properties of InSb and II-IV-As2 semiconductors doped with manganese

This thesis is devoted to growth and investigations of Mn-doped InSb and II-IV-As2 semiconductors, including Cd1-xZnxGeAs2:Mn, ZnSiAs2:Mn bulk crystals, ZnSiAs2:Mn/Si heterostructures. Bulk crystals were grown by direct melting of starting components followed by fast cooling. Mn-doped ZnSiAs2/Si heterostructures were grown by vacuum-thermal deposition of ZnAs2 and Mn layers on Si substrates followed by annealing. The compositional and structural properties of samples were investigated by different methods. The samples consist of micro- and nano- sizes clusters of an additional ferromagnetic Mn-X phases (X = Sb or As). Influence of magnetic precipitations on magnetic and electrical properties of the investigated materials was examined. With relatively high Mn concentration the main contribution to magnetization of samples is by MnSb or MnAs clusters. These clusters are responsible for high temperature behavior of magnetization and relatively high Curie temperature: up to 350 K for Mn-doped II-IV-As2 and about 600 K for InMnSb. The low-field magnetic properties of Mn-doped II-IV-As2 semiconductors and ZnSiAs2:Mn/Si heterostructures are connected to the nanosize MnAs particles. Also influence of nanosized MnSb clusters on low-field magnetic properties of InMnSb have been observed. The contribution of paramagnetic phase to magnetization rises at low temperatures or in samples with low Mn concentration. Source of this contribution is not only isolated Mn ions, but also small complexes, mainly dimmers and trimmers formed by Mn ions, substituting cation positions in crystal lattice. Resistivity, magnetoresistance and Hall resistivity properties in bulk Mn-doped II-IV-As2 and InSb crystals was analyzed. The interaction between delocalized holes and 3d shells of the Mn ions together with giant Zeeman splitting near the cluster interface are respond for negative magnetoresistance. Additionally to high temperature critical pointthe low-temperature ferromagnetic transition was observed Anomalous Hall effect was observed in Mn doped samples and analyzed for InMnSb. It was found that MnX clusters influence significantly on magnetic scattering of carriers.

Positron measurements in Mg-doped GaN and development of digital Doppler broadening spectroscopy

In this work parameters of Mg-doped GaN samples were studied using positron annihilation spectroscopy and analyzed. It is shown that gallium vacancies exist in an unintentionally doped sample. Next, the sample with higher concentration of Mg and low growth temperature contains vacancy clusters. In case of low concentration of Mg the growth temperature does not affect the formation of defects. Analog electronics can be replaced by a modern digital device. While promising a high quantity of benefits, the performance of these digitizers requires thorough adjustment. A 14-bit two channel digitizer has been tested in order to achieve better performance than the one of a traditional analog setup, and the adjustment process is described. It has been shown that the digital device is unable to achieve better energy resolution, but it is quite close to the corresponding attribute of the available analog system, which had been used for measurements in Mg-doped GaN.

Bovine serum albumin potentiates caffeine- or ATP-induced tension in human skinned skeletal muscle fibers

Human skinned muscle fibers were used to investigate the effects of bovine serum albumin (BSA) on the tension/pCa relationship and on the functional properties of the Ca2+-release channel of the sarcoplasmic reticulum (SR). In both fast- and slow-type fibers, identified by their tension response to pSr 5.0, BSA (0.7-15 µM) had no effect on the Ca2+ affinity of the contractile proteins and elicited no tension per se in Ca2+-loaded fibers. In contrast, BSA (>1.0 µM) potentiated the caffeine-induced tension in Ca2+-loaded fibers, this effect being more intense in slow-type fibers. Thus, BSA reduced the threshold caffeine concentration required for eliciting detectable tension, and increased the amplitude, the rate of rise and the area under the curve of caffeine-induced tension. BSA also potentiated the tension elicited in Ca2+-loaded fibers by low-Mgv solutions containing 1.0 mM free ATP. These results suggest that BSA modulates the response of the human skeletal muscle SR Ca2+-release channel to activators such as caffeine and ATP.

NIR-Vis Up-Conversion Luminescence in the Yb3+,Er3+ Doped Y2O2S, ZrO2, and NaYF4 Nanomaterials

Since the discovery of the up-conversion phenomenon, there has been an ever increasing interest in up-converting phosphors in which the absorption of two or more low energy photons is followed by emission of a higher energy photon. Most up-conversion luminescence materials operate by using a combination of a trivalent rare earth (lanthanide) sensitizer (e.g. Yb or Er) and an activator (e.g. Er, Ho, Tm or Pr) ion in a crystal lattice. Up-converting phosphors have a variety of potential applications as lasers and displays as well as inks for security printing (e.g. bank notes and bonds). One of the most sophisticated applications of lanthanide up-conversion luminescence is probably in medical diagnostics. However, there are some major problems in the use of photoluminescence based on the direct UV excitation in immunoassays. Human blood absorbs strongly UV radiation as well as the emission of the phosphor in the visible. A promising way to overcome the problems arising from the blood absorption is to use a long wavelength excitation and benefit from the up-conversion luminescence. Since there is practically no absorption by the whole-blood in the near IR region, it has no capability for up-conversion in the excitation wavelength region of the conventional up-converting phosphor based on the Yb3+ (sensitizer) and Er3+ (activator) combination. The aim of this work was to prepare nanocrystalline materials with high red (and green) up-conversion luminescence efficiency for use in quantitative whole-blood immunoassays. For coupling to biological compounds, nanometer-sized (crystallite size below 50 nm) up-converting phosphor particles are required. The nanocrystalline ZrO2:Yb3+,Er3+, Y2O2S:Yb3+,Er3+, NaYF4:Yb3+,Er3+ and NaRF4-NaR’F4 (R: Y, Yb, Er) materials, prepared with the combustion, sol-gel, flux, co-precipitation and solvothermal synthesis, were studied using the thermal analysis, FT-IR spectroscopy, transmission electron microscopy, EDX spectroscopy, XANES/EXAFS measurements, absorption spectroscopy, X-ray powder diffraction, as well as up-conversion and thermoluminescence spectroscopies. The effect of the impurities of the phosphors, crystallite size, as well as the crystal structure on the up-conversion luminescence intensity was analyzed. Finally, a new phenomenon, persistent up-conversion luminescence was introduced and discussed. For efficient use in bioassays, more work is needed to yield nanomaterials with smaller and more uniform crystallite sizes. Surface modifications need to be studied to improve the dispersion in water. On the other hand, further work must be carried out to optimize the persistent up-conversion luminescence of the nanomaterials to allow for their use as efficient immunoassay nanomaterials combining the advantages of both up-conversion and persistent luminescence.

Impaired regeneration of dystrophin-deficient muscle fibers is caused by exhaustion of myogenic cells

Duchenne muscular dystrophy is one of the most devastating myopathies. Muscle fibers undergo necrosis and lose their ability to regenerate, and this may be related to increased interstitial fibrosis or the exhaustion of satellite cells. In this study, we used mdx mice, an animal model of Duchenne muscular dystrophy, to assess whether muscle fibers lose their ability to regenerate after repeated cycles of degeneration-regeneration and to establish the role of interstitial fibrosis or exhaustion of satellite cells in this process. Repeated degenerative-regenerative cycles were induced by the injection of bupivacaine (33 mg/kg), a myotoxic agent. Bupivacaine was injected weekly into the right tibialis anterior muscle of male, 8-week-old mdx (N = 20) and C57Bl/10 (control, N = 10) mice for 20 and 50 weeks. Three weeks after the last injection, the mice were killed and the proportion of regenerated fibers was counted and reported as a fibrosis index. Twenty weekly bupivacaine injections did not change the ability of mdx muscle to regenerate. However, after 50 weekly bupivacaine injections, there was a significant decrease in the regenerative response. There was no correlation between the inability to regenerate and the increase in interstitial fibrosis. These results show that after prolonged repeated cycles of degeneration-regeneration, mdx muscle loses its ability to regenerate because of the exhaustion of satellite cells, rather than because of an increase in interstitial fibrosis. This finding may be relevant to cell and gene therapy in the treatment of Duchenne muscular dystrophy.