Tubulações de PRFV com adição de areia quartzosa visando sua aplicação na indústria do petróleo

Fillers are often added in composites to enhance performance and/or to reduce cost. Fiberglass pipes must meet performance requirements and industrial sand is frequently added for the pipe to be cost competitive. The sand is added to increase pipe wall thickness, thus increase pipe stiffness. The main goal of the present work is to conduct an experimental investigation between pipes fabricated with and without de addition of sand, to be used in the petroleum industry. Pipes were built using E-glass fibers, polyester resin and siliceous sand. The fabrication process used hand lay up and filament winding and was divided in two different parts: the liner and the structural wall. All tested pipes had the same liner, but different structural wall composition, which is the layer where siliceous sand may be added or not. The comparative investigation was developed considering the results of longitudinal tensile tests, hoop tensile tests, hydrostatic pressure leak tests and parallel-plate loading stiffness tests. SEM was used to analyze if the sand caused any damage to the glass fibers, during the fabrication process, because of the fiber-sand contact. The procedure was also used to verify the composite conditions after the hydrostatic pressure leak test. The results proved that the addition of siliceous sand reduced the leak pressure in about 17 %. In the other hand, this loss in pressure was compensated by a stiffness increment of more than 380 %. MEV analyses show that it is possible to find damage on the fiber-sand contact, but on a very small amount. On most cases, the contact occurs without damage evidences. In summary, the addition of sand filler represented a 27.8 % of cost reduction, when compared to a pipe designed with glass fiber and resin only. This cost reduction combined to the good mechanical tests results make siliceous sand filler suitable for fiberglass pressure pipes

Avaliação mecânica e microestrutural de compósitos de poliéster com adição de cargas minerais e resíduos industriais

With the current growth in consumption of industrialized products and the resulting increase in garbage production, their adequate disposal has become one of the greatest challenges of modern society. The use of industrial solid residues as fillers in composite materials is an idea that emerges aiming at investigating alternatives for reusing these residues, and, at the same time, developing materials with superior properties. In this work, the influence of the addition of sand, diatomite, and industrial residues of polyester and EVA (ethylene vinyl acetate), on the mechanical properties of polymer matrix composites, was studied. The main objective was to evaluate the mechanical properties of the materials with the addition of recycled residue fillers, and compare to those of the pure polyester resin. Composite specimens were fabricated and tested for the evaluation of the flexural properties and Charpy impact resistance. After the mechanical tests, the fracture surface of the specimens was analyzed by scanning electron microscopy (SEM). The results indicate that some of the composites with fillers presented greater Young s modulus than the pure resin; in particular composites made with sand and diatomite, where the increase in modulus was about 168 %. The composites with polyester and EVA presented Young s modulus lower than the resin. Both strength and maximum strain were reduced when fillers were added. The impact resistance was reduced in all composites with fillers when compared to the pure resin, with the exception of the composites with EVA, where an increase of about 6 % was observed. Based on the mechanical tests, microscopy analyses and the compatibility of fillers with the polyester resin, the use of industrial solid residues in composites may be viable, considering that for each type of filler there will be a specific application

Validação de uma metodologia de ensaio de resistência ao cisalhamento para avaliação da aderência de interfaces revestimento metálico-bainha de cimento aplicada a poços de petróleo

Improving the adherence between oilwell metallic casing and cement sheath potentially decrease the number of corrective actions present/y necessary for Northeastern wells submitted to steam injection. In addition to the direct costs involved in the corrective operations, the economic impact of the failure of the primary cementing aIso includes the loss in the production of the well. The adherence between casing and cement is current/y evaluated by a simple shear tests non standardized by the American Petroleum Institute (API). Therefore, the objective of the present is to propose and evaluate a standardized method to assess the adherence of oilwell metallic casing to cement sheath. To that end, a section of a cemented oilwell was simulated and used to test the effect of different parameters on the shear stress of the system. Surface roughness and different cement compositions submitted or not to thermal cycling were evaluated. The results revealed that the test geometry and parameters proposed yielded different values for the shear stress of the system, corresponding to different adherent conditions between metallic casing and cement sheath

Otimização de sistema de bombeamento com energia eólica: sistema de bombeamento de São Gabriel/BA

After the Protocol of Kyoto and of the ECHO 92 - Rio de Janeiro, the attentions of the world focus to the preservation of the environment and of the maintainable use of the natural resources. People were looking for preserving environment for the future generations. Ever since, solutions are looked for the supply of energy in its more acquaintances forms and the substitution of the use of fossil fuels for the such alternative forms as: Photovoltaics, solar heat systems for water, wind , bio-diesel, etc. and in this context the Company of Engineering of the State of Bahia - Cerb changed a diesel pumping system by an wind one, It´s the first community system of this nature in Bahia. Facing problems with the model, a Cerb involved the academic segment of the Federal Center of Technological Education of Bahia Cefetba looking for a solution. This work intends to demonstrate the possibilities of optimization of the pumping communit system that supply water to approximately 50 people in the place of Romão, municipal district of São Gabriel-Ba. Technical reports were published in AGRENERGD2004-Unicamp SP and Scientific Magazine ETC,Cefetba, 2005. A simulation of the increase of energy is presented for heights of 15 and 20m, considering the eletromecanical balance from the pumping energy to the wind turbine. From the accomplished bibliographical revision, we emphasized the mechanical aspects of the engineering once in UFRN, those studies concentrate on the Department of Mechanical Engineering while, in others eletroelectronic are more emphasized. Finally, documents that we judged important were enclosed for the perfect understanding of this work

Utilização de um secador solar para desintoxicação da torta de mamona

It´s been motivating motivated by the current rulers as an energy solution the use of the biodiesel as source of energy, that doesn't damage the environment and promotes the development of the areas where the base plant are grown. The process of production of the biodiesel, starting from the castor oil plant and its derivers, generates a known product as castor oil plant pie that has been used as fertilizer. Once disintoxicated, it can serve as animal ration, because it contains high content of proteins, presenting larger joined value. The disintoxication process, can be obtained through the process of drying the pie with the construction and use of models of dryers capable to elevate the temperature of the castor oil plant pie to approximately 60ºC.In this temperature the product tends to eliminate the ricina, with the aid of an aqueous solution of hydroxide of calcium, or still reach higher temperatures to make the disintoxication without a chemical treatment. It was made a bibliographical research about known processes of disintoxication of the castor oil plant pie from the autoclave use to the drying direct exposure to the sun. Starting from the state of the art and identification of the object, it was chosen solar dryers to eliminate the ricina. It was applied two types of solar dryers: the one of solar direct exposure, and the one with concentrador. The castor oil plant pie was separated in samples, with measurement of its initial mass, codified and placed in the dryers. The results were presented in graphs and tables forms, with the values of temperatures noticed. It was noticed the variations of temperature and the relationships analyzed related with the ricina content eliminated from the pie. The analysis of the ricina content was accomplished by Embrapa - Campina Grande, by eletroforese method. The analysis of the result of considering the content of ricina of the samples. It was observed that, we obtained lower rate of ricina in samples that had larger drying time and average value temperature above 60ºC. Comparing with the ones submitted to higher temperatures and in a shorter period of time. It was possible to evaluate the efficiency of the dryers in the desintoxication process of the samples, as well as the type of more appropriate dryer for the drying pie process. Finally, it was concluded that the solar dryer with concentrador presents higher values temperatures than the direct exposure one. So, it´s being more opportune applied in the castor oil plant pie drying process. However, more than one hour for drying time is needed

Avaliação dos impactos ambientais gerados por uma industria cerâmica típica da Região do Seridó/RN

The present work deals with an evaluation of the environmental impacts arised from a typical ceramics industry located in the Seridó region of Rio Grande do Norte State. That region contains the largest State s producing basin of red ceramics. The district of Parelhas stands out as the largest producing nucleus. The studied company is located in the rural zone of Parelhas, it was selected as study object because it possesses a great part of the representative characteristics of the Region s ceramics park as a whole. Impacts produced at the implantation and operation phases of the Company had been evaluated, being this last phase subdivided in stages of the productive process. Among found adverse impacts, they are distinguished: losses in air quality, undesirable noises, microclimatic alterations, impoverishment of the ground, elimination of the vegetal covering, agricultural exodus, crisis in cattle agriculture and, superficial and underground water contamination, beyond risks ocupational diseases and industrial accidents. The Leopold s interactive matrix, that summarizes results of the work, was presented in form of 15 (fifteen) tables that display impacts classified in qualitative and quantitative way. Totally, 175 (one hundred and seventy-five) significant impacts produced by this Company had been identified, being 114 (one hundred and fourteen) negative, 38 (thirty-eight) positive and 23 (twenty-three) among mixed, indefinite and inert ones. In the work, before the evaluation of impacts properly said, it was constructed a diagnostic table of the ambient situation at a previous moment to implantation of the Company, elaborated on basis of inferences and historical researches. It was proposed still, mitigative steps for adverse impacts identified, as also elaborated a program to accompaniment and observing that the fulfilment of indicated mitigative steps guarantees. The final part of the work contemplates conclusions and suggestions that aim to influence positively the presented sight in terms of environmental management

Desenvolvimento e avaliação de padrão de torque para calibração de torquímetros em três faixas de medição

The continuous development of instruments and equipment used as tools or torque measurement in the industry is demanding more accurate techniques in the use of this kind instrumentation, including development of metrological characteristics in torque measurement. The same happens with the needs in calibration services. There is a diversity of methods of hand torque tools in the market with different measuring range but without complaining with technical standards in terms of requirements of quality and reliability. However, actually there is no choice of a torque measuring standard that fulfils, with low cost, the needs for the calibration of hand torque tools in a large number of ranges. The objective of this thesis is to show the development and evaluation of a torque measuring standard device with a conception to allow the calibration of hand torque tools with three levels of torque with an single instrument, promoting reduction of costs and time in the calibration, also offering reliability for the evaluation of torque measuring instrument. To attend the demand in the calibration of hand torque tools it is necessary that the calibration laboratories have a big collection of torque measuring standards, to fulfills the needs of the costumer, what is very costly. The development of this type of torque measuring standard revealed a viable technique and economically making possible the calibration of hand torque tools in different nominal ranges through a single measurement system versatile, efficient and of easy operation

Desenvolvimento de microcápsulas contendo as antocianinas presentes no corante do extrato do jambo por polimerização interfacial

The industries of food, medicine and cosmetic apply microencapsulation for many reasons, among them, stabilize the active, control the release of encapsulated and separate incompatible components of the formulation. In this context, microencapsulation techniques have been used in the food industry to provide stable liquid and solid ingredients. Anthocyanins have high antioxidant potential, but they are photodegradable. The challenges are therefore directed to the research for techniques that could make this potential remaining active and bioavailable and could be used as a vehicle for the delivery release of bioactive and micronutrients in appropriate conditions and levels. This work has as main objective to propose a method to encapsulate the anthocyanins in the extract of mountain apple using the interfacial polymerization technique. As well as to define the ideal conditions of temperature and agitation system for this procedure. The microparticles were characterized for size, morphology, active distribution, surface charge, degradation, composition and stability. The results, like particle diameter of 5.94 μm and Zeta potential of 7.03 mV, showed that the technique used to obtain these microparticles was satisfactory and has potential for application in cosmetics and food

Estudo do comportamento mecânico de estruturas de solo-cimento reforçado com fibras de coco e hastes de bambu

In this work the use of coconut fiber (coir) and bamboo shafts as reinforcement of soil-cement was studied, in order to obtain an alternative material to make stakes for fences in rural properties. The main objective was to study the effect of the addition of reinforcement to the soil-cement matrix. The effect of humidity on the mechanical properties was also analyzed. The soil-cement mortar was composed by a mixture, in equal parts, of soil and river sand, 14% in weight of cement and 10 % in weight of water. As reinforcement, different combinations of (a) coconut fiber with 15 mm mean length (0,3 %, 0,6 % and 1,2 % in weight) and (b) bamboo shafts, also in crescent quantities (2, 4 and 8 shafts per specimen) were used. For each combination 6 specimens were made and these were submitted to three point flexural test after 28 days of cure. In order to evaluate the effect of humidity, 1 specimen from each of the coconut fiber reinforced combination was immersed in water 24 hours prior to flexural test. The results of the tests carried out indicated that the addition of the reinforcement affected negatively the mechanical resistance and, on the other hand, increased the tenacity and the ductility of the material.

Obtenção e caracterização de filmes SnO2 depositados em vidro borosilicato por silk-screen modificado: SnCl2.2H2O como precursor

O presente trabalho tem como objetivo investigar as características de filmes de SnO2 depositados em substrato de vidro borosilicato por um processo de silk-screen modificado para obtenção de espessura fina compatível com a aplicação em células solares policristalinas de baixo custo. O filme de SnO2 é um dos mais apropriados para obtenção de vidro TCO (transparent conductive oxide) para uso em células solares devido a sua baixa resistividade elétrica e alta transmitância, sendo quimicamente inerte, mecanicamente duro e tem resistência a altas temperaturas, o que facilita então a calcinação das amostras entre 500º C a 550º C. Os filmes foram obtidos a partir de uma solução precursora básica, preparada pela dissolução de SnCl2.2H2O em Etanol (99,5 %). Foi realizado um planejamento fatorial 2(3-1) para analisar a influência dos parâmetros concentração da solução precursora (CETN), temperatura de calcinação (TC) e taxa de aquecimento (tX) na calcinação, sendo a concentração CETN o parâmetro que apresentou maior efeito sobre os parâmetros de respostas investigados: espessura do filme (ω), resistividade de superfície (ρ) e a transmitância relativa (θ). Foi possível obter com a metodologia utilizada, filmes com espessuras da ordem de 1 Nm com resistividade de superfície de 10 / e transmitância relativa entre 70 e 80 %.

Estabilização de órbitas periódicas instáveis utilizando controle por modos deslizantes com compensação adaptativa

The chaotic behavior has been widely observed in nature, from physical and chemical phenomena to biological systems, present in many engineering applications and found in both simple mechanical oscillators and advanced communication systems. With regard to mechanical systems, the effects of nonlinearities on the dynamic behavior of the system are often of undesirable character, which has motivated the development of compensation strategies. However, it has been recently found that there are situations in which the richness of nonlinear dynamics becomes attractive. Due to their parametric sensitivity, chaotic systems can suffer considerable changes by small variations on the value of their parameters, which is extremely favorable when we want to give greater flexibility to the controlled system. Hence, we analyze in this work the parametric sensitivity of Duffing oscillator, in particular its unstable periodic orbits and Poincar´e section due to changes in nominal value of the parameter that multiplies the cubic term. Since the amount of energy needed to stabilize Unstable Periodic Orbits is minimum, we analyze the control action needed to control and stabilize such orbits which belong to different versions of the Duffing oscillator. For that we will use a smoothed sliding mode controller with an adaptive compensation term based on Fourier series.

Desenvolvimento de bionanocompósitos: nano e microcristais de celulose com poli (álcool vinílico) e poli (ácido lático)

This work has the main objective to obtain nano and microcrystals of cellulose, extracted from the pineapple leaf fibres (PALF), as reinforcement for the manufacture of biocomposite films with polymeric matrices of Poly(vinyl alcohol) (PVA) and Poly(lactic acid) (PLA). The polymer matrices and the nano and microcrystals of cellulose were characterised by means of TGA, FTIR and DSC. The analysis was performed on the pineapple leaves to identify the macro and micronutrients. The fibers of the leaves of the pineapple were extracted in a desfibradeira mechanical. The PALF extracted were washed to remove washable impurities and subsequently treated with sodium hydroxide (NaOH) and sodium hypochlorite (NaClO) in the removal of impurities, such as fat, grease, pectates, pectin and lignin. The processed PALF fibers were hydrolysed in sulfuric acid (H2SO4) at a concentration of 13.5 %, to obtain nano and microcrystals of cellulose. In the manufacture of biocomposite films, concentrations of cellulose, 0 %, 1 %, 3 %, 6 %, 9% and 12% were used as reinforcement to the matrices of PVA and PLA. The PVA was dissolved in distilled water at 80 ± 5 oC and the PLA was dissolved in dichloromethane at room temperature. The manufacture of biocompósitos in the form of films was carried out by "casting". Tests were carried out to study the water absorption by the films and mechanical test of resistance to traction according to ASTM D638-10 with a velocity of 50 mm/min.. Chi-square statistical test was used to check for the existence of significant differences in the level of 0.05: the lengths of the PALF, lengths of the nano and microcrystals of cellulose and the procedures used for the filtration using filter syringe of 0.2 μm or filtration and centrifugation. The hydrophilicity of biocompósitos was analysed by measuring the contact angle and the thickness of biocompósitos were compared as well as the results of tests of traction. Statistical T test - Student was also applied with the significance level (0.05). In biodegradation, Sturm test of standard D5209 was used. Nano and microcrystals of cellulose with lengths ranging from 7.33 nm to 186.17 nm were found. The PVA films showed average thicknesses of 0.153 μm and PLA 0.210 μm. There is a strong linear correlation directly proportional between the traction of the films of PVA and the concentration of cellulose in the films (composite) (0,7336), while the thickness of the film was correlated in 0.1404. Nano and microcrystals of cellulose and thickness together, correlated to 0.8740. While the correlation between the cellulose content and tensile strength was weak and inversely proportional (- 0,0057) and thickness in -0.2602, totaling -0,2659 in PLA films. This can be attributed to the nano and microcrystals of cellulose not fully adsorbed to the PLA matrix. In the comparison of the results of the traction of the two polymer matrices, the nano and microcrystals have helped in reducing the traction of the films (composite) of PLA. There was still the degradation of the film of PVA, within a period of 20 days, which was not seen in the PLA film, on the other hand, the observations made in the literature, the average time to start the degradation is above 60 days. What can be said that the films are biodegradable composites, with hydrophilicity and the nano and microcrystals of cellulose, contribute positively in the improvement of the results of polymer matrices used.

Produção de estrutura com gradiente de porosidade a partir da sinterização por plasma da mistura de pós Ti-Nb-Sn

Porous structures are being widely investigated for use in biomedical implants, aiming to mechanically integrate and functionally the implant inside the bone tissue. Moreover, this structure is also important for drugs that can be stored and can induce and accelerate the process of osseointegration. With the purpose to investigate this effect, Ti, Nb and Sn metal powders, were sintered by plasma using a hollow cathode discharge. Sintering was performed in argon plasma set at 4 mbar pressure and temperatures of 500 ° C, 600 ° C and 700 ° C. Samples were also sintered in the electrical resistance furnace at 1200 ° C in order to compare plasma sintering with the conventional method. It was observed that plasma samples sintered with the hollow cathode configuration showed a gradient in porosity, while the samples sintered in the resistive furnace did not. Furthermore, differences in the microstructure of the samples were found, were a surface with higher porosity and ales porous core were obtained at different temperatures. The percolation profile of distilled water and the chemical compositions of the porous layers of the plasma treated samples were the main results obtained. Based on these results, we can conclude that this structure is particularly important for application in the biomedical field such as scaffolds for drug delivery and implants

Avaliação das propriedades das fibras de algodões coloridos naturalmente e ecologicamente corretas cultivados nos assentamentos do município de Guamaré/RN

In this work evaluate the technical characteristics of the fibers grown in settlements Guamaré, colored cotton seeds were donated existing in the Germplasm Bank of Embrapa Cotton. We sought through the breeding program, raising the resistance, fineness, length and uniformity of cotton fibers, as well as stabilize the staining of fibers in the BRS Topaz, BRS Brown and BRS Green shades and raise their productivity in the field. First, the individual selections to test progeny seeds, and thereafter the hybridization method followed by family selection to obtain variations in the color tones were performed. The BRS Topaz, BRS Brown and BRS Green varieties were produced, analyzed and compared with existing cottons in the region which is the White cotton. The properties amount of impurities and neps, length, length uniformity, short fiber content, fineness and tensile strength of the fibers were sized in Classifiber, NATI, Pressley and Micronaire devices. 10 trials each with 10 tests for all four fiber types were carried out. The White and Topaz fibers showed greater length (32-34mm) and greater resistance (7.94 lb/mg and 7.97 lb/mg respectively) and showed finesse with lower micronaire index 3,71μg/inch and 3, 73μg/inch and a low rate of short fibers. The results were very promising for the use of genetically improved cotton in the manufacturing of fabric and yarn in the textile industry. The fibers were brown colored cotton used in the manufacture of a composite fiber with thermoplastic resin

Análise da formulação em Monte Carlo dos pacotes de energia multiespectrais aplicada a meios constituídos por vapor d'água

The Monte Carlo method is accurate and is relatively simple to implement for the solution of problems involving complex geometries and anisotropic scattering of radiation as compared with other numerical techniques. In addition, differently of what happens for most of numerical techniques, for which the associated simulations computational time tends to increase exponentially with the complexity of the problems, in the Monte Carlo the increase of the computational time tends to be linear. Nevertheless, the Monte Carlo solution is highly computer time consuming for most of the interest problems. The Multispectral Energy Bundle model allows the reduction of the computational time associated to the Monte Carlo solution. The referred model is here analyzed for applications in media constituted for nonparticipating species and water vapor, which is an important emitting species formed during the combustion of hydrocarbon fuels. Aspects related to computer time optimization are investigated the model solutions are compared with benchmark line-by-line solutions