H-2-sensing characteristics of nanocrystalline La0.8Pb0.2FeO3 prepared by sol-gel method

Nanocrystalline La0.8Pb0.2FeO3 has been prepared by the sol-gel method. XRD patterns show that the nanocrystalline La0.8Pb0.2FeO3 is a perovskite phase with the orthorhombic structure and its mean crystallite size is about 19 nm. The influence of Pb ions which replaced the La ions on A-sites can be directly observed from the electrical and sensing properties to H-2 gas. The conductance of La0.8Pb0.2FeO3-based sensor is considerably higher than that of LaFeO3-based sensor, and Pb-doping can enhance the sensitivity to H2 gas. An empirical relationship of R = KCH2alpha with alpha = 0.668 was obtained.

Structural role of fluoride in aluminophosphate sol-gel glasses: High-resolution double-resonance NMR studies

The local structure of Na-Al-P-O-F glasses, prepared by a novel sol-gel route, was extensively investigated by advanced solid-state NMR techniques. Al-21{F-19} rotational echo double resonance (REDOR) results indicate that the F incorporated into aluminophosphate glass is preferentially bonded to octahedral Al units and results in a significant increase in the concentration of six-coordinated aluminum. The extent of Al-F and Al-O-P connectivities are quantified consistently by analyzing Al-27{P-31} and Al-21{F-19} REDOR NMR data. Two distinct types of fluorine species were identified and characterized by various F-19{Al-27}, F-19{Na-23}, and F-19{P-31} double resonance experiments, which were able to support peak assignments to bridging (Al-F-Al, -140 ppm) and terminal (Al-F, -170 ppm) units. On the basis of the detailed quantitative dipole-dipole coupling information obtained, a comprehensive structural model for these glasses is presented, detailing the structural speciation as a function of composition.

Effect of water content in sol on optical properties of hybrid sol-gel derived TiO2/SiO2/ormosil film

Sol-gel derived TiO2/SiO2/ormosil hybrid planar waveguides have been deposited on soda-lime glass slides and silicon substrates, films were heat treated at 150 degreesC for 2 h or dried at room temperature. Different amounts of water were added to sols to study their impacts on microstructures and optical properties of films. The samples were characterized by m-line spectroscopy, Fourier transform infrared spectroscopy (FT-IR), UV/VIS/NIR spectrophotometer (UV-vis), atomic force microscopy (AFM), thermal analysis instrument and scattering-detection method. The refractive index was found to have the largest value at the molar ratio H2O/OR = 1 in sol (OR means -OCH3, -OC2H5 and -OC4H9 in the sol), whereas the thickest film appears at H2O/OR = 1/2. The rms surface roughness of all the films is lower than 1.1 nm, and increases with the increase of water content in sol. Higher water content leads to higher attenuation of film. (C) 2004 Elsevier B.V. All rights reserved.

Sol-gel combustion synthesis and luminescent properties of nanocrystalline YAG : Eu3+ phosphors

EU3+ -doped Y3Al5O12 (YAG:Eu3+) phosphors were synthesized by a facile sol-gel combustion method. In this process, citric acid traps the constituent cations and reduces the diffusion length of the precursors. YAG phase is obtained through sintering at 900 degrees C for 2h. There were no intermediate phases such as YAlO3 (YAP) and Y4Al2O9 (YAM) observed. The charge transfer band of nanocrystalline phosphors shows a shift toward the high-energy side, compared with that of amorphous ones due to lower covalency of Eu-O bond for nanocrystalline phosphors. The higher concentration quenching in YAG:EU3+ nanophosphors may be caused by the confinement effect on resonant energy transfer of nanocrystalline. It also indicates that the sol-gel combustion synthesis method provides a good distribution of Eu3+ activators in YAG host. (c) 2005 Elsevier B.V. All rights reserved.

Structural and optical properties of YAG : Ce3+ phosphors by sol-gel combustion method

High-quality Ce3+-doped Y3Al5O12 (YAG:Ce3+) phosphors were synthesized by a facile sol-gel combustion method. In this sol-gel combustion process, citric acid acts as a fuel for combustion, traps the constituent cations and reduces the diffusion length of the precursors. The XRD and FT-IR results show that YAG phase can form through sintering at 900 degrees C for 2 h. This temperature is much lower than that required to synthesize YAG phase via the solid-state reaction method. There were no intermediate phases such as YAlO3 (YAP) and Y4Al2O9 (YAM) observed in the sintering process. The average grain size of the phosphors sintered at 900-1100 degrees C is about 40 nm. With the increasing of sintering temperature, the emission intensity increases due to the improved crystalline and homogeneous distribution of Ce3+ ions. A blue shift has been observed in the Ce3+ emission spectrum of YAG:Ce3+ phosphors with increasing sintering temperatures from 900 to 1200 degrees C. It can be explained that the decrease of lattice constant affects the crystal field around Ce3+ ions. The emission intensity of 0.06Ce-doped YAG phosphors is much higher than that of the 0.04Ce and 0.02Ce ones. The red-shift at higher Ce3+ concentrations may be Ce-Ce interactions or variations in the unit cell parameters between YAG:Ce3+ and YAG. It can be concluded that the sol-gel combustion synthesis method provides a good distribution of Ce3+ activators at the molecular level in YAG matrix. (c) 2005 Elsevier B.V. All rights reserved.

Sol-gel combustion synthesis and luminescence Of Y4Al2O9 : Eu3+ nanocrystal

Y4Al2O9:EU3+ phosphor was synthesized through a sol-gel combustion method. The Y4Al2O9 phase can form through sintering at 800 degrees C. This temperature is much lower than that required via the solid state reaction method. The average grain size of the phosphor was about 30 run. Compared with the amorphous phosphor, the charge transfer band of crystalline phosphor shows a blue shift. The emission Of Y4Al2O9:Eu3+ indicates the existence of two luminescent centers, in agreement with the crystal structure of Y4Al2O9. Higher doping concentration could be realized in Y4Al2O9 nanocrystal host lattice. This indicates that the sol-gel combustion synthesis method can increase emission intensity and quenching concentration due to a good distribution of EU3+ activators in Y4Al2O9 host. (c) 2005 Elsevier B.V. All rights reserved.

Synthesis of CaCu3Ti4O12 ceramic via a sol-gel method

The novel nano-ultrafine powders for the preparation of CaCu3Ti4O12 ceramic were prepared by the sol-gel method and citrate auto-ignition method. The obtained precursor powders were pressed, sintered at 1000 degrees C to fabricate microcrystal CaCu3Ti4O12 ceramic. The microcrystalline phase of CaCu3Ti4O12 was confirmed by X-ray powder diffraction (XRD). The morphology and size of the grains of the powders and ceramics under different heat treatments were observed using scanning electron microscopy (SEM). The relative dielectric constant of the ceramic sintered at 1000 degrees C was measured with a magnitude of more than 10(4) at room temperature, which was approaching to those of Pb-containing complex perovskite ceramics, and the loss tangent was less than 0.20 in a broad frequency region. The relative dielectric constant and loss tangent were also compared with that of CaCu3Ti4O12 ceramic prepared by other reported methods. (c) 2006 Elsevier B.V. All rights reserved.

Sol-Gel法制备生物玻璃／Ti涂层参数的确定

采用溶胶-凝胶（Sol-Gel）法在已经预涂了一层过渡层的纯钛基体上制备生物玻璃（BG）涂层。试验以正硅酸乙酯（TEOS）、硝酸钙（Ca（NO3）2·4H2O）、氯化镁（MgCl2·6H2O）等为原料，并采用正交试验设计，所得涂层均通过SEM和EDS进行分析，并利用空间几何模型折算绝对偏差，从而确定出最优的试验参数为：[Si]=1M，水酯比（Rω）=4，pH=4．5，浸涂粘度（η）为3．55mPa·s。

Comparison of TiO2 and ZrO2 films deposited by electron-beam evaporation and by sol-gel process

TiO2 and ZrO2 films are deposited by electron-beam (EB) evaporation and by sol-gel process. The film properties are characterized by visible and Fourier-transform infrared spectrometry, x-ray diffraction analysis, surface roughness measure, absorption and laser-induced damage threshold (LIDT) test. It is found that the sol-gel Elms have lower refractive index, packing density and roughness than EB deposited films due to their amorphous structure and high OH group concentration in the film. The high LIDT of sol-gel films is mainly due to their amorphous and porous structure, and low absorption. LIDT of EB deposited film is considerably affected by defects in the Elm, and LIDT of sol-gel deposited film is mainly effected by residual organic impurities and solvent trapped in the film.

Sínteses e caracterizações de TiO2 puro, dopado e co-dopado pelo método sol-gel e suas atividades fotocatalíticas

Nanopartículas de dióxido de titânio vêm sendo extensamente empregadas como fotocatalisa-dores, já que são eficientes na degradação de diversos poluentes. Visando a obtenção de titâ-nias com diferentes propriedades, realizaram-se sínteses através do método sol-gel, a partir da hidrólise do tetraisopropóxido de titânio (IV) TIPP e seguindo-se os princípios da Química Verde, dispensando-se temperaturas e pressões elevadas. Foi estudada a influência de dife-rentes parâmetros, como: pH, solvente, razão molar álcool/TIPP e ordem de adição dos rea-gentes. Foram obtidas titânias na forma cristalina anatásio, nanométricas, com elevadas áreas superficiais específicas e predominantemente mesoporosas. Visando-se obter titânias com melhores propriedades óticas, isto é, capazes de sofrer a fotoativação pela luz visível, foram sintetizadas titânias dopadas e co-dopadas com os metais ferro e rutênio (Fe3+ e Ru3+) e o a-metal N (N3). A síntese desses materiais também foi realizada através do método sol-gel, sendo a dopagem realizada durante o processo de hidrólise. As amostras foram caracterizadas na forma de pó por difração de raios-X, adsorção-dessorção de nitrogênio, microscopia ele-trônica de varredura e espectroscopia de refletância difusa no UV-Visível. A titânia pura a-presentou como única fase cristalina o anatásio, quando calcinada até 400 C, com a presença de traços de brookita. A partir de 600 C, observou-se o aparecimento da fase rutilo, que em 900C foi a única fase encontrada na titânia. A dopagem com Ru3+dificultou a transformação de fase anatásio para rutilo, ao contrário da dopagem com Fe3+. O processo de co-dopagem acelerou a formação de rutilo, que se apresentou como única fase nas amostras calcinadas a 600 C. As titânias dopadas apresentaram uma leve diminuição na energia de bandgap, sendo os dopantes capazes de deslocar a absorção para o vermelho. Foram realizados testes fotoca-talíticos visando à degradação do azocorante Reactive Yellow 145 com lâmpada de vapor de mercúrio de 125 W a fim de se comparar as atividades fotocatalíticas das titânias puras, dopa-das e co-dopadas, calcinadas a 300C. De todas as titânias sintetizadas, a titânia pura foi a que melhor degradou o corante, tendo um desempenho semelhante ao do TiO2 P25, da Evo-nik

Trapped charge dynamics in a sol-gel based TiO(2) high- k gate dielectric silicon metal-oxide-semiconductor field effect transistor.

We have studied the response of a sol-gel based TiO(2), high k dielectric field effect transistor structure to microwave radiation. Under fixed bias conditions the transistor shows frequency dependent current fluctuations when exposed to continuous wave microwave radiation. Some of these fluctuations take the form of high Q resonances. The time dependent characteristics of these responses were studied by modulating the microwaves with a pulse signal. The measurements show that there is a shift in the centre frequency of these high Q resonances when the pulse time is varied. The measured lifetime of these resonances is high enough to be useful for non-classical information processing.

YBa2Cu3O7 tapes prepared by sol-gel deposition techniques: Microstructure and structural characterizations

We report on the preparation conditions of YBa2Cu3O7 polycrystalline superconducting tapes by a sol-gel deposition technique. We present some discussion on the compatibility between the nature of the substrate, the use of a buffer layer, and the conditions used to prepare appropriate superconducting YBa2Cu3O7 materials. We report also on the microstructural characterizations performed in order to evaluate the crystallites size, degree of orientation and connectivity. © 2002 Elsevier Science B.V. All rights reserved.

Realization of MMI power splitter by UV-light imprinting technique using hybrid sol-gel SiO2 materials

An efficient fabrication scheme of buried ridge waveguide devices is demonstrated by UV-light imprinting technique using organic-in organic hybrid sol-gel Zr-doped SiO2 materials. The refractive indices of a guiding layer and a cladding layer for the buried ridge waveguide structure are 1.537 and 1.492 measured at 1550 nm, respectively. The tested results show more circular mode profiles clue to existence of the cladding layer. A buried ridge single-mode waveguide operating at 1550 nm has a low propagation loss (0.088 dB/cm) and the 1 x 2 MMI power splitter exhibits uniform outputs, with a very low splitting loss of 0.029 dB at 1549 nm.

Fabrication of 1.55-mu m Si-based resonant cavity enhanced photodetectors using sol-gel bonding

In this work, a novel bonding method using silicate gel as the bonding medium was developed to fabricate an InGaAs narrow-band response resonant cavity enhanced photodetector on a silicon substrate. The bonding was performed at a low temperature of 350 degreesC without any special treatment on bonding surfaces and a Si-based narrow-band response InGaAs photodetector was successfully fabricated, with a quantum efficiency of 34.4% at the resonance wavelength of 1.54 mum, and a full-width at half-maximum of about 27 nm. The photodetector has a linear photoresponse up to 4-mW optical power under 1.5 V or higher reverse bias. The low temperature wafer bonding process demonstrates a great potential in device fabrication.