Characterization of tin oxide based sol-gel coatings on borosilicate glasses by X-ray reflectivity

The X-ray reflectivity technique was applied in the study of tin oxide films deposited by sol-gel dip-coating on borosilicate glasses. The influence of the withdrawal speed and temperature of thermal treatment on the film structure was analyzed. We have compared the thermal evolution of the density and the shrinkage of the films with these properties measured for the monolithic xerogel by helium picnometry and thermomechanical analysis. In agreement with the Landau-Levich model, the layer thickness increases by increasing the withdrawal speed. Nevertheless, it decreases with the increase of the thermal treatment temperature, due to the densification process. The values of apparent density are smaller than the skeletal density, which shows that the films are porous. The comparison between the film and the monolith indicates that shrinkage during firing is anisotropic, occurring essentially perpendicular to the coating surface.

Platinum surface modification with cerium species and the effect against the methanol anodic reaction

Spontaneous deposition and electrochemical deposition by potential perturbation programs were used to place cerium-containing species on platinum surfaces in acid solution. Cyclic voltammetric profiles of cerium-modified platinum surfaces obtained after potentiostatic or potentiodynamic procedures (applied in the true hydrogen evolution region) differ from those recorded after spontaneous methods. However, the catalytic effects are nearly the same on these cerium-modified platinum surfaces for methanol electrooxidation, i.e. lower onset potential values for the anodic reaction. Besides, a different electrocatalytic effect was observed at large positive potentials on methanol oxidation due to the cerium oxide capability of oxygen storage. This effect is observed on platinum modified by a drastic potentiostatic procedure (by applying -2.0 V) in cerium(IV) acid solution. (C) 2008 Elsevier B.V. All rights reserved.

Controlled growth of anodic aluminium oxide films with hexagonal array of nanometer-sized pores filled with textured copper nanowires

Anodic aluminium oxide (AAO) films exhibiting a homogeneous morphology of parallel pores perpendicular to the surface were prepared in a two-step anodization process and filled with copper by electrochemical deposition. The optimum growth conditions for the formation of freestanding AAO films with hexagonal compact array of cylindrical pores were studied by field emission scanning electron microscopy and small angle X-ray scattering. The results show well-defined periodic structures with uniform pores size distribution for films with pore diameters between 40 and 70 nm prepared using different voltages and temperatures during the second anodization step. X-ray photoelectron spectroscopy and X-ray diffraction analysis of AAO films filled with copper show the formation of nanowires with high structural order, exhibiting a preferential crystalline orientation along the (2 2 0) axis and only small fraction of copper oxides. The best results for textured Cu nanowires were obtained at a reduction potential of -300 mV. (C) 2009 Elsevier Ltd. All rights reserved.

Developments in hot-filament metal oxide deposition (HFMOD)

Hot-filament metal oxide deposition (HFMOD) is a variant of conventional hot-filament chemical vapor deposition (HFCVD) recently developed in our laboratory and successfully used to obtain high-quality, uniform films of MOx WOx and VOx. The method employs the controlled oxidation of a filament of a transition metal heated to 1000 degrees C or more in a rarefied oxygen atmosphere (typically, of about 1 Pa). Metal oxide vapor formed on the surface of the filament is transported a few centimetres to deposit on a suitable substrate. Key system parameters include the choice of filament material and diameter, the applied current and the partial pressures of oxygen in the chamber. Relatively high film deposition rates, such as 31 nm min(-1) for MoOx, are obtained. The film stoichiometry depends on the exact deposition conditions. MoOx films, for example, present a mixture of MoO2 and MoO3 phases, as revealed by XPS. As determined by Li+ intercalation using an electrochemical cell, these films also show a colouration efficiency of 19.5 cm(2) C-1 at a wavelength of 700 nm. MOx and WOx films are promising in applications involving electrochromism and characteristics of their colouring/bleaching cycles are presented. The chemical composition and structure of VOx films examined using IRRAS (infrared reflection-absorption spectroscopy), RBS (Rutherford backscattering spectrometry) and XPS (X-ray photoelectron spectrometry) are also presented. (c) 2007 Elsevier B.V. All rights reserved.

Effect of temperature on glass-ceramic films prepared by impregnation of commercial float glass surfaces with oxide powders under pressure

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Changes on iron electrode surface during hydrogen permeation in borate buffer solution

Hydrogen interaction with oxide films grown on iron electrodes at open circuit potential (E-oc) and in the passive region (+0.30 V-ECS) was studied by chronopotentiometry, chronoamperometry and electrochemical impedance spectroscopy techniques. The results were obtained in deaerated 0.3 mol L-1 H3BO3 + 0.075 mol L-1 Na2B4O7 (BB, pH 8.4) solution before, during and after hydrogen permeation. The iron oxide film modification was also investigated by means of in situ X-ray absorption near-edge spectroscopy (XANES) and scanning electrochemical microscopy (SECM) before and during hydrogen permeation. The main conclusion was that the passive film is reduced during the hydrogen diffusion. The hydrogen permeation stabilizes the iron surface at a potential close to the thermodynamic water stability line where hydrogen evolution can occur. The stationary condition required for the determination of the permeation parameters cannot be easily attained on iron surface during hydrogen permeation. Moreover, additional attention must be paid when obtaining the transport parameters using the classical permeation cell. (c) 2007 Elsevier Ltd. All rights reserved.

Thermo-reversible sol-gel transition of TiO2 nanoparticles with surface modified by p-toluene sulfonic acid

In this paper an unprecedent thermo-reversible sol-gel transition for titania nanoparticles dispersed in a solution of p-toluene sulfonic acid (PTSH) in isopropanol is reported. The sol formed by the thermo-hydrolysis at 60 degrees C of titanium tetraisopropoxide (Ti((OPr)-Pr-i)(4)) reversibly changes into a turbid gel upon cooling to room temperature. Turbidimetric measurements performed for samples containing different nominal acidity ratios (A = [PTSH]/[Ti]) have evidenced that the gel transformation temperature increases from 20 to 35 degrees C as the [PTSH]/[Ti] ratio increases from 0.2 to 2.0. SAXS results indicate that the thermo-reversible gelation is associated to a reversible aggregation of a monodisperse set of titania nanoparticles with average gyration radius of approximate to 2 nm. From the different PTSH species evidenced by Raman spectroscopy and TG/DTA of dried gels we proposed that the then-no-reversible gelation in this systems is induced by the formation of a supramolecular network, in which the protonated surface of nanoparticles is interconnected through cooperative hydrogen bonds between -SO3 groups of p-toluene sulfonic acid. (C) 2009 Elsevier Ltd. All rights reserved.

Heterogeneous Fenton reactants: a study of the behavior of iron oxide nanoparticles obtained by the polymeric precursor method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of the surfactant nature on the thermo-stability of surface modified SnO2 nanoparticles

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Theory of electrical characteristics for metal-oxide-insulator Schottky barrier and metal-insulator-metal structures

The metal-insulator or metal-amorphous semiconductor blocking contact is still not well understood. Here, the intimate metal-insulator and metal-oxide-insulator contact are discussed. Further, the steady-state characteristics of metal-oxide-insulator-metal structures are also discussed. Oxide is an insulator with wider energy band gap (about 50 Å thick). A uniform energetic distribution of impurities is considered in addition to impurities at a single energy level inside the surface charge region at the oxide-insulator interface. Analytical expressions are presented for electrical potential, field, thickness of the depletion region, capacitance, and charge accumulated in the surface charge region. The electrical characteristics are compared with reference to relative densities of two types of impurities. ln I is proportional to the square root of applied potential if energetically distributed impurities are relatively important. However, distribution of the electrical potential is quite complicated. In general energetically distributed impurities can considerably change the electrical characteristics of these structures.

Effect of dentine surface treatment on leakage of root fillings with a glass ionomer sealer.

The purpose of this study was to observe the quality of seal of the glass ionomer cement, Ketac-Endo, after treatment of the root canal wall. The root canals of 140 extracted human teeth were prepared biomechanically. The root canals were treated with either EDTA or received an intracanal dressing of calcium hydroxide or camphorated paramonochlorphenol. The root canals were filled by the lateral condensation technique with gutta-percha points and the sealer Ketac-Endo, or zinc oxide-eugenol cement or Sealapex. The teeth were placed into a 2% methylene blue dye solution inside a flask, which was attached to a vacuum pump. Leakage was measured linearly. Sealapex exhibited significantly less leakage than Ketac-Endo or zinc oxide-eugenol cement (P<0.01). The use of EDTA and intermediary dressings reduced significantly (P<0.01) the leakage observed with the zinc oxide-eugenol sealer and Ketac-Endo.

pH changes at the surface of root dentin when using root canal sealers containing calcium hydroxide

The purpose of this study was to investigate long-term pH changes in cavities prepared in root surface dentin of extracted teeth after obturation of the root canal with gutta-percha and a variety of sealers containing calcium hydroxide. After cleaning and shaping, root canals in 50 recently extracted, human single-rooted teeth were divided into five groups. Each of four groups was obturated with gutta-percha and either Sealapex, Sealer 26, Apexit, or CRCS, all of which contain calcium hydroxide. The remaining group served as the control and was not obturated with gutta-percha or sealer. Cavities were prepared in the facial surface of the roots in the cervical and middle regions. The pH was measured in these dentinal cavities at the initiation of the experiment, and 3, 7, 14, 21, 28, 45, 60, 90, and 120 days after obturation. Results indicate that the pH at the surface of the root does not become alkaline when calcium hydroxide cements are used as root canal sealers. Regardless of the sealer used, the observed pattern of pH change was not different from that seen in the control group of roots that were not treated with sealer. It is concluded that calcium hydroxide-containing cements, although suitable for use as root canal sealants, do not produce an alkaline pH at the root surface. If such a pH change is related to treatment of root resorption, these sealants do not contribute to this treatment. Copyright © 1996 by The American Association of Endodontists.

Surface finishing of glass ionomer

Purpose: To evaluate the surface roughness and staining of a glass ionomer cement when subjected to different finishing procedures. Materials and Methods: Sixty-four discs of Chem-Fil II glass ionomer cement were submitted to staining test with methylene blue by spectrophotometry and roughness test by profilometry. Four groups were evaluated: Mylar matrix (control), Sof-Lex discs, Enhance points, and diamond bur. Results: Staining and roughness test, analyzed by ANOVA and Tukey's test, showed that the best surface was obtained when the material cured in contact with the Mylar matrix strip or when treated with Sof-Lex discs. The poorest results were obtained after using the diamond bur.

Model for zinc oxide varistor

Zinc oxide varistors are very complex systems, and the dominant mechanism of voltage barrier formation in these systems has not been well established. Yet the MNDO quantum mechanical theoretical calculation was used in this work to determine the most probable defect type at the surface of a ZnO cluster. The proposed model represents well the semiconducting nature as well as the defects at the ZnO bulk and surface. The model also shows that the main adsorption species that provide stability at the ZnO surface are O-, O2 -, and O2.

Effect of atmosphere on the sintering and grain growth of tin oxide

High purity SnO 2 powder (>99.9%) was compacted in cylindrical pellets and sintered in atmospheres of dry argon, argon with water vapor, oxygen and CO 2 using 10 °C/min up to 1200 °C or isotherms in the range of 1000 to 1200 °C. Time, temperature and sintering atmosphere have large influence on grain growth and low influence on densification of this oxide. Surface diffusion is the dominant mechanism up to 1200 °C and evaporation-condensation is dominant above 1200 °C. The maximum linear shrinkage observed was about 2.0% and attributed to structural rearrangement of particles due to high capillary stresses developed with neighboring particles. © 1999 Trans Tech Publications.