Diffusion of Zn into GaAs and AlGaAs from isothermal Liquid-phase epitaxy solutions

In this work we present results of zinc diffusion in GaAs using the liquid phase epitaxy technique from liquid solutions of Ga‐As‐Zn and Ga‐As‐Al‐Zn. Using silicon‐doped n‐GaAs substrates, working at a diffusion temperature of 850 °C, and introducing a dopant concentration ranging 1018–1019 cm−3, the most important findings regarding the diffusion properties are as follows: (a) zinc concentration in the solid depends on the square root of zinc atomic fraction in the liquid; (b) the diffusion is dominated by the interstitial‐substitutional process; (c) the diffusivity D varies as about C3 in the form D=2.9×10−67C3.05; (d) aluminum plays the role of the catalyst of the diffusion process, if it is introduced in the liquid solution, since it is found that D varies as (γAsXlAs)−1; (e) the zinc interstitial is mainly doubly ionized (Zn++i); (f) the zinc diffusion coefficient in Al0.85 Ga0.15 As is about four times greater than in GaAs; (g) by means of all these results, it is possible to control zinc diffusion processes in order to obtain optimized depth junctions and doping levels in semiconductor device fabrication.

Limiting efficiencies of GaAs solar cells

The limiting efficiencies of GaAs solar cells when used under concentrated sunlight are calculated. The benefits to be expected from applying techniques which restrict the angle of acceptance of the cell are determined. It is concluded that when the acceptance angle is restricted the emission of the luminescent photons and therefore the associated current loss are reduced. A limiting efficiency close to 39% results for concentration ratios of about 1000 suns AM1.5 direct. For lower concentration ratios, the limiting efficiency decreases if Auger recombination is also taken into account

Back contacted emitter GaAs solar cells

A new device structure to improve the performance of concentrator GaAs solar cells is described and the first experimental results are reported. The reason for such an improvement relies on a drastic reduction of the shadowing and series resistance losses based on the possibility of back contacting the emitter region of the solar cell. The experimental results obtained with devices of these types, with a simplified structure, fabricated by liquid phase epitaxy, demonstrate the feasibility and correct operation of the proposed back contact of the emitter of the cells.

Performance analysis of AlGaAs/GaAs tunnel junctions for ultra-high concentration photovoltaics

An n(++)-GaAs/p(++)-AlGaAs tunnel junction with a peak current density of 10 100Acm(-2) is developed. This device is a tunnel junction for multijunction solar cells, grown lattice-matched on standard GaAs or Ge substrates, with the highest peak current density ever reported. The voltage drop for a current density equivalent to the operation of the multijunction solar cell up to 10 000 suns is below 5 mV. Trap-assisted tunnelling is proposed to be behind this performance, which cannot be justified by simple band-to-band tunnelling. The metal-organic vapour-phase epitaxy growth conditions, which are in the limits of the transport-limited regime, and the heavy tellurium doping levels are the proposed origins of the defects enabling trap-assisted tunnelling. The hypothesis of trap-assisted tunnelling is supported by the observed annealing behaviour of the tunnel junctions, which cannot be explained in terms of dopant diffusion or passivation. For the integration of these tunnel junctions into a triple-junction solar cell, AlGaAs barrier layers are introduced to suppress the formation of parasitic junctions, but this is found to significantly degrade the performance of the tunnel junctions. However, the annealed tunnel junctions with barrier layers still exhibit a peak current density higher than 2500Acm(-2) and a voltage drop at 10 000 suns of around 20 mV, which are excellent properties for tunnel junctions and mean they can serve as low-loss interconnections in multijunction solar cells working at ultra-high concentrations.

Analysis of the modified optical properties and band structure of GaAs12xSbx-capped InAs/GaAs quantum dots

The origin of the modified optical properties of InAs/GaAs quantum dots (QD) capped with a thin GaAs1−xSbx layer is analyzed in terms of the band structure. To do so, the size, shape, and composition of the QDs and capping layer are determined through cross-sectional scanning tunnelling microscopy and used as input parameters in an 8 × 8 k·p model. As the Sb content is increased, there are two competing effects determining carrier confinement and the oscillator strength: the increased QD height and reduced strain on one side and the reduced QD-capping layer valence band offset on the other. Nevertheless, the observed evolution of the photoluminescence (PL) intensity with Sb cannot be explained in terms of the oscillator strength between ground states, which decreases dramatically for Sb > 16%, where the band alignment becomes type II with the hole wavefunction localized outside the QD in the capping layer. Contrary to this behaviour, the PL intensity in the type II QDs is similar (at 15 K) or even larger (at room temperature) than in the type I Sb-free reference QDs. This indicates that the PL efficiency is dominated by carrier dynamics, which is altered by the presence of the GaAsSb capping layer. In particular, the presence of Sb leads to an enhanced PL thermal stability. From the comparison between the activation energies for thermal quenching of the PL and the modelled band structure, the main carrier escape mechanisms are suggested. In standard GaAs-capped QDs, escape of both electrons and holes to the GaAs barrier is the main PL quenching mechanism. For small-moderate Sb (<16%) for which the type I band alignment is kept, electrons escape to the GaAs barrier and holes escape to the GaAsSb capping layer, where redistribution and retraping processes can take place. For Sb contents above 16% (type-II region), holes remain in the GaAsSb layer and the escape of electrons from the QD to the GaAs barrier is most likely the dominant PL quenching mechanism. This means that electrons and holes behave dynamically as uncorrelated pairs in both the type-I and type-II structures.

ARXPS analysis of a GaAs/GaInP heterointerface with application in III-V multijunction solar cells

In this contribution, angle-resolved X-ray photoelectron spectroscopy is used to explore the extension and nature of a GaAs/GaInP heterointerface. This bilayer structure constitutes a very common interface in a multilayered III-V solar cell. Our results show a wide indium penetration into the GaAs layer, while phosphorous diffusion is much less important. The physico-chemical nature of such interface and its depth could deleteriously impact the solar cell performance. Our results probe the formation of spurious phases which may profoundly affect the interface behavior.

Evaluation of the reliability of high concentrator GaAs solar cells by means of temperature accelerated aging tests

ABSTRACT Evaluating the reliability, warranty period, and power degradation of high concentration solar cells is crucial to introducing this new technology to the market. The reliability of high concentration GaAs solar cells, as measured in temperature accelerated life tests, is described in this paper. GaAs cells were tested under high thermal accelerated conditions that emulated operation under 700 or 1050 suns over a period exceeding 10 000 h. Progressive power degradation was observed, although no catastrophic failures occurred. An Arrhenius activation energy of 1.02 eV was determined from these tests. The solar cell reliability [R(t)] under working conditions of 65°C was evaluated for different failure limits (1–10% power loss). From this reliability function, the mean time to failure and the warranty time were evaluated. Solar cell temperature appeared to be the primary determinant of reliability and warranty period, with concentration being the secondary determinant. A 30-year warranty for these 1 mm2-sized GaAs cells (manufactured according to a light emitting diode-like approach) may be offered for both cell concentrations (700 and 1050 suns) if the solar cell is operated at a working temperature of 65°C.

High-Power High-Efficiency Laser Power Transmission at 100m Using Optimized Multi-Cell GaAs Converter

A high-power high-efficiency laser power transmission system at 100m based on an optimized multi-cell GaAs converter capable of supplying 9.7W of electricity is demonstrated. An I-V testing system integrated with a data acquisition circuit and an analysis software is designed to measure the efficiency and the I-V characteristics of the laser power converter (LPC). The dependencies of the converter’s efficiency with respect to wavelength, laser intensity and temperature are analyzed. A diode laser with 793nm of wavelength and 24W of power is used to test the LPC and the software. The maximum efficiency of the LPC is 48.4% at an input laser power of 8W at room temperature. When the input laser power is 24W (laser intensity of 60000W/m2), the efficiency is 40.4% and the output voltage is 4 V. The overall efficiency from electricity to electricity is 11.6%.

The feasibility of high-efficiency InAs/GaAs quantum dot intermediate band solar cells

In recent years, all the operating principles of intermediate band behaviour have been demonstrated in InAs/GaAs quantum dot (QD) solar cells. Having passed this hurdle, a new stage of research is underway, whose goal is to deliver QD solar cells with efficiencies above those of state-of-the-art single-gap devices. In this work, we demonstrate that this is possible, using the present InAs/GaAs QD system, if the QDs are made to be radiatively dominated, and if absorption enhancements are achieved by a combination of increasing the number of QDs and light trapping. A quantitative prediction is also made of the absorption enhancements required, suggesting that a 30 fold increase in the number of QDs and a light trapping enhancement of 10 are sufficient. Finally, insight is given into the relative merits of absorption enhancement via increasing QD numbers and via light trapping.

AlGaAs/GaAs photovoltaic converters for high power narrowband radiation

AlGaAs/GaAs-based laser power PV converters intended for operation with high-power (up to 100 W/cm(2)) radiation were fabricated by LPE and MOCVD techniques. Monochromatic (lambda = 809 nm) conversion efficiency up to 60% was measured at cells with back surface field and low (x = 0.2) Al concentration 'window'. Modules with a voltage of 4 V and the efficiency of 56% were designed and fabricated.

Stacked GaAs(Sb)(N)-capped InAs/GaAs quantum dots for enhanced solar cell efficiency

Different approaches have arisen aiming to exceed the Shockley-Queisser efficiency limit of solar cells. Particularly, stacking QD layers allows exploiting their unique properties, not only for intermediate-band solar cells or multiple exciton generation, but also for tandem cells in which the tunability of QD properties through the capping layer (CL) could be very useful.

Stacked GaAsSbN-capped InAs/GaAs quantum dots for enhanced solar cell efficiency

Different approaches have recently arisen aiming to exceed the Shockley-Queisser efficiency limit. Particularly, the use of self-organized quantum dots (QD) has been recently proposed in order to introduce new states within the barrier material, which enhances the subband gap absorption yielding a photocurrent increase. Stacking QD layers allows exploiting their unique properties for intermediate-band solar cells (SC) or tandem cells.In all these cases, tuning the QD properties by modifying the capping layer (CL) can be very useful.

3-D modeling of perimeter recombination in GaAs diodes and its influence on concentrator solar cells

This paper describes a complete modelling of the perimeter recombination of GaAs diodes which solves most unknowns and suppresses the limitations of previous models. Because of the three dimensional nature of the implemented model, it is able to simulate real devices. GaAs diodes on two epiwafers with different base doping levels, sizes and geometries, namely square and circular are manufactured. The validation of the model is achieved by fitting the experimental measurements of the dark IV curve of the manufactured GaAs diodes. A comprehensive 3-D description of the occurring phenomena affecting the perimeter recombination is supplied with the help of the model. Finally, the model is applied to concentrator GaAs solar cells to assess the impact of their doping level, size and geometry on the perimeter recombination.

Ti/Pd/Ag Contacts to n-Type GaAs for High Current Density Devices

The metallization stack Ti/Pd/Ag on n-type Si has been readily used in solar cells due to its low metal/semiconductor specific contact resistance, very high sheet conductance, bondability, long-term durability, and cost-effectiveness. In this study, the use of Ti/Pd/Ag metallization on n-type GaAs is examined, targeting electronic devices that need to handle high current densities and with grid-like contacts with limited surface coverage (i.e., solar cells, lasers, or light emitting diodes). Ti/Pd/Ag (50 nm/50 nm/1000 nm) metal layers were deposited on n-type GaAs by electron beam evaporation and the contact quality was assessed for different doping levels (from 1.3 × 1018 cm−3 to 1.6 × 1019 cm−3) and annealing temperatures (from 300°C to 750°C). The metal/semiconductor specific contact resistance, metal resistivity, and the morphology of the contacts were studied. The results show that samples doped in the range of 1018 cm−3 had Schottky-like I–V characteristics and only samples doped 1.6 × 1019 cm−3 exhibited ohmic behavior even before annealing. For the ohmic contacts, increasing annealing temperature causes a decrease in the specific contact resistance (ρ c,Ti/Pd/Ag ~ 5 × 10−4 Ω cm2). In regard to the metal resistivity, Ti/Pd/Ag metallization presents a very good metal conductivity for samples treated below 500°C (ρ M,Ti/Pd/Ag ~ 2.3 × 10−6 Ω cm); however, for samples treated at 750°C, metal resistivity is strongly degraded due to morphological degradation and contamination in the silver overlayer. As compared to the classic AuGe/Ni/Au metal system, the Ti/Pd/Ag system shows higher metal/semiconductor specific contact resistance and one order of magnitude lower metal resistivity.

Analysis of perimeter recombination in the subcells of GaInP/GaAs/Ge triple-junction solar cells

This paper studies the recombination at the perimeter in the subcells that constitute a GaInP/GaAs/Ge lattice-matched triple-junction solar cell. For that, diodes of different sizes and consequently different perimeter/area ratios have been manufactured in single-junction solar cells resembling the subcells in a triple-junction solar cell. It has been found that neither in GaInP nor in Ge solar cells the recombination at the perimeter is significant in devices as small as 500 μm × 500μm(2.5 ⋅ 10 − 3 cm2) in GaInP and 250μm  × 250μm (6.25 ⋅ 10 − 4cm2) in Ge. However, in GaAs, the recombination at the perimeter is not negligible at low voltages even in devices as large as 1cm2, and it is the main limiting recombination factor in the open circuit voltage even at high concentrations in solar cells of 250 μm  × 250μm (6.25 ⋅ 10 − 4 cm2) or smaller. Therefore, the recombination at the perimeter in GaAs should be taken into account when optimizing triple-junction solar cells.