The influence of sulfuric environments on concretes elaborated with sulfate resistant cements and mineral admixtures. Part 2: Concrete exposed to Magnesium Sulfate (MgSO4) = Estudio de la influencia de los medios con presencia de sulfatos en hormigones con cementos sulforresistentes y adiciones minerales. Parte 2.Hormigones expuestos a sulfato magnésico (MgSO4)

The present work studies the resistant of the concrete against magnesium sulfate (MgSO4) and compare the results with values obtained previously of the same concretes exposed to sodium sulfate (Na2SO4). Thus, it is possible analyze the influence of the cation type. To that end, four different concrete mixes were made with sulfur resistant cement and mineral admixtures (silica fume, fly ash and blast furnace slag). The concretes were submerged for different period in magnesium sulfate (MgSO4). After that, different tests were carried out to define mechanical and microstructural properties. The results obtained were compared with reference values of concretes cured in calcium hydroxide [Ca(OH)2]. According to the results, the concrete with blast furnace slag presented the best behavior front MgSO4, meanwhile the concretes with silica fume and fly ash were the most susceptible. The resistance of the concrete with blast furnace slag could be attributed to the characteristics of the hydrated silicates formed during the hydration time, which include aluminum in the chemical chain that hinder its chemical decomposition during the attack of magnesium. The magnesium sulfate solution was most aggressive than sodium sulfate solution. El presente trabajo estudia la resistencia de hormigones al ataque de sulfatos provenientes de sulfato magnésico (MgSO4) y compara estos valores con resultados previos de los mismos hormigones atacados con sulfato sódico (Na2SO4). De esta manera se estudia la interacción del catión que acompaña al ion sulfato durante su afectación a la matriz cementicia. Para lo anterior, se diseñaron cuatro dosificaciones empleando cementos sulforresistentes y adiciones minerales (humo de sílice, ceniza volante y escoria de alto horno). Los hormigones se sumergieron, por distintos periodos de tiempo, en disolución de sulfato magnésico (MgSO4) de concentración 1M, para después realizarles ensayos mecánicos y a nivel microestructural. Los valores obtenidos se compararon con los obtenidos en el hormigón de referencia curado en hidróxido cálcico. El hormigón con escoria de alto horno presentó el mejor comportamiento frente a MgSO4, siendo las mezclas de humo de sílice y ceniza volante las más susceptibles. La resistencia del hormigón con escoria se atribuye a las características de los silicatos hidratados formados durante la hidratación, los cuales incorporan aluminio en las cadenas impidiendo su descomposición ante un ataque por magnesio. El medio con sulfato magnésico mostro una mayor agresividad que el medio con sulfato sódico.

Mechanical behavior of alkali-cement as function of the temperature.

This investigation reports on a comparative study of the mechanical behavior at different temperatures of three different alkali-activated fly ash pastes chemically activated using sodium silicate. A control Portland cement (OPC) was used as a reference. In an attempt to simulate the conditions prevailing in the event of accidental fire, post-thermal mechanical tests were performed to determine the residual strength. It has therefore been established that FA based cements can be fabricated for construction purposes and these materials have great potential for fire resistance applications.

Estudio de la utilización de las cenizas de cenicero de centrales termoeléctricas de carbón como adición del cemento portland : análisis comparativo con las cenizas volantes

El empleo de nuevas adiciones en el cemento se plantea como una vía para que éste sea un material más sostenible. En este contexto, las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón actualmente se están llevando a vertederos creando un problema medioambiental o se están empleando con usos minoritarios. Sin embargo, la presente Tesis doctoral demuestra cómo este material puede ser empleado como un componente principal de los cementos portland mezclado en una proporción optimizada con las cenizas volantes o solo. Por tanto, este estudio se puede considerar como un trabajo prenormativo que cubre las demandas de la sociedad tanto económicas como ambientales. Se han estudiado las propiedades químicas, físicas y mecánicas de las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón como una adición potencial de los cementos portland (con adiciones) en comparación con los cementos portland con cenizas volantes. En consecuencia, el objeto de la presente Tesis Doctoral es el análisis de las prestaciones de morteros elaborados con clínkeres de cemento portland y cenizas de fondo o cenicero con cenizas volantes de las centrales termoeléctricas de carbón en unos porcentajes similares a los correspondientes a los CEM II/A-V, CEM II/B-V y CEM IV/A (V) de la UNE-EN 197-1:2011. La caracterización de las cenizas de fondo o cenicero y de las cenizas volantes de las centrales termoeléctricas de carbón se ha realizado mediante las técnicas analíticas de FRX, ICP, análisis químicos, DRX, densidad, granulometría láser, superficie específica Blaine, ATD, TG, puzolanicidad, MEB y EDX; mientras que la caracterización de las mezclas se ha realizado mediante análisis químico (análisis químico, FRX e ICP y), DRX, MIP, granulometría láser, puzolanicidad, MEB y EDX, agua de consistencia normal, inicio y final de fraguado, estabilidad de volumen, colorimetría, calor de hidratación, DTA y TG, asícomo ensayos de resistencia; resistencia a flexión y compresión y ensayos de durabilidad (carbonatación natural, resistencia al hielo-deshielo, resistencia a la acción de los sulfatos y resistencia a la reacción árido-álcali). Finalmente, se han comprobado las propiedades de las cenizas de cenicero y cenizas volantes en hormigones, realizando ensayos de resistencia a compresión y resistividad. Los resultados obtenidos indican que la sustitución parcial o completa de las cenizas volantes por las de cenicero no tiene un efecto tecnológicamente importante en las propiedades ni mecánicas ni durables, incluso los mejora en determinados aspectos. Por tanto, se recomienda la normalización de las cenizas de fondo o cenicero de las centrales termoeléctricas de carbón como componente principal de los cementos portland comunes de la UNE-EN 197-1:2011. Actualmente, la mayoría de las cenizas de fondo se consideran como un residuo que no tiene un posible uso. Sólo se han encontrado algunos datos relativos a la aplicación de este material combinado con cenizas volantes como un componente principal de los cementos portland. Por tanto, la realización de un estudio integrado considerando aspectos que van desde la caracterización de las cenizas hasta las mezclas de conglomerante y la hidratación de éstas, desarrollo de resistencias y demás prestaciones y durabilidad (carbonatación natural, resistencia al hielo-deshielo, resistencia a la acción de los sulfatos y resistencia a la reacción árido-álcali), así como los ensayos de resistencia en hormigón es totalmente novedoso. Como resultado final se propone incorporar estas nuevas adiciones en aplicaciones particulares y en la norma más apropiada para ello. Los resultados han demostrado que la sustitución completa o parcial de las cenizas volantes por cenizas de fondo o cenicero de las centrales termoeléctricas de carbón en cementos de los tipos CEM II/A-V, CEM II/B-V y CEM IV/A no afecta de forma significativa en la resistencia a compresión a 1, 3 ,7, 28 ni 90 días ni a la durabilidad. En parte esto se debe a que la composición química de ambas cenizas es muy similar en la mayoría de los elementos tales como Fe2O3, TiO2, P2O5, SrO2, aunque en algún caso, como en el ZnO, se encuentra alguna ligera diferencia. Por tanto, se pueden esperar unas ligeras diferencias en el mecanismo de hidratación de las diferentes mezclas estudiadas. La presencia de los óxidos mencionados afectará a la composición de la fase acuosa y, en consecuencia, podrían ser elementos lixiviables. Asimismo, influyen de distinta manera en propiedades tales como los tiempos de fraguado y en la durabilidad. New additions to the cement are needed to achieve a more sustainable construction material. Within this context, bottom ashes produced in coal-fired power stations are currently wastes which are dumped provoking an environmental problem. Only in few cases are being used in minor applications. However, the present PhD Thesis shows how this material can be used as a main constituent of Portland cement when it is mixed in an optimised proportion with fly ashes or added to the Portland clinker alone. Therefore, this study may also be considered as a pre-standardization work which covers both the environmental and economic demands of society. Chemical, physical and mechanical characteristics of pulverized coal combustion bottom ash used as a potential constituent of Portland cements (with additions) are studied in comparison to Portland cements with fly ashes. Therefore, the aim of this experimental PhD Thesis is the analysis of the performance of mortars made of clinker of Portland cement and bottom and/or fly ashes in similar proportions to those of CEM II/A-V, CEM II/B-V and CEM IV/A (V) according to EN 197-1:2011. Characterisation of bottom and fly ashes has been done by XRF, ICP, chemical analyses, XRD, density, laser granulometry, Blaine, ATD, TG, pozzolanity, SEM and EDS. Characterisation of bottom and fly ashes mixes has been perform by chemical analyses, XRF, ICP, XRD, MIP, laser granulometry, pozzolanity, SEM, EDS, setting time, soundness, colorimetric test, heat of hydration, ATD, TG, compressive strength, and durability tests (natural carbonation, frost-thaw resistance, sulphate resistance and silica-alkali resistance). In conclusion, it can be established that partial or complete replacement of fly ash by bottom ash has neither significant effect on mechanical nor durability properties. Even, they are improved in several aspects. Therefore, it is recommended to standardise the bottom ash as a main cement constituent of the European standard EN 197-1:2011. Nowadays, most bottom ashes are considered as waste without any potential re-use. Only a few papers deal with the study of this material and its use mixed with fly ashes to be employed as a main constituent of Portland cement. Therefore, the execution of an integrated study considering together aspects from the initial characterization of the ashes and blinder mixes to the hydration steps, strength achievement, leading behaviour and durability (natural carbonation, sulphate attack, aggregate-alcali reaction and freeze-thaw resistance) is totally new. As result, it is proposed to include this new addition for particular applications in the appropriate cement standard. The results have shown that with regard to the compressive strength at 1, 3, 7, 28 and 90 days, partial or complete replacement of fly ash by bottom ash in CEM II/A-V, CEM II/B-V and CEM IV/A has no more significant effects. Partially, this can be explained because the bottom ash contains a similar amount of most of the elements, Fe2O3, TiO2, P2O5, SrO2, and so on, instead of ZnO. Therefore, slight hydration differences are expected. The presence of such oxides might have a significant effect on pore solution concentration and so will be leachable constituents. They will also play an important role in the cement properties such as setting times and durability.

Comportamiento frente a la durabilidad de morteros de reparación de cemento modificados con polímeros

El auge que ha surgido en los últimos años por la reparación de edificios y estructuras construidas con hormigón ha llevado al desarrollo de morteros de reparación cada vez más tecnológicos. En el desarrollo de estos morteros por parte de los fabricantes, surge la disyuntiva en el uso de los polímeros en sus formulaciones, por no encontrarse justificado en ocasiones el trinomio prestaciones/precio/aplicación. En esta tesis se ha realizado un estudio exhaustivo para la justificación de la utilización de estos morteros como morteros de reparación estructural como respuesta a la demanda actual disponiéndolo en tres partes: En la primera parte se realizó un estudio del arte de los morteros y sus constituyentes. El uso de los morteros se remonta a la antigüedad, utilizándose como componentes yeso y cal fundamentalmente. Los griegos y romanos desarrollaron el concepto de morteros de cal, introduciendo componentes como las puzolanas, cales hidraúlicas y áridos de polvo de mármol dando origen a morteros muy parecidos a los hormigones actuales. En la edad media y renacimiento se perdió la tecnología desarrollada por los romanos debido al extenso uso de la piedra en las construcciones civiles, defensivas y religiosas. Hubo que esperar hasta el siglo XIX para que J. Aspdin descubriese el actual cemento como el principal compuesto hidraúlico. Por último y ya en el siglo XX con la aparición de moléculas tales como estireno, melanina, cloruro de vinilo y poliésteres se comenzó a desarrollar la industria de los polímeros que se añadieron a los morteros dando lugar a los “composites”. El uso de polímeros en matrices cementantes dotan al mortero de propiedades tales como: adherencia, flexibilidad y trabajabilidad, como ya se tiene constancia desde los años 30 con el uso de caucho naturales. En la actualidad el uso de polímeros de síntesis (polivinialacetato, estireno-butadieno, viniacrílico y resinas epoxi) hacen que principalmente el mortero tenga mayor resistencia al ataque del agua y por lo tanto aumente su durabilidad ya que se minimizan todas las reacciones de deterioro (hielo, humedad, ataque biológico,…). En el presente estudio el polímero que se utilizó fue en estado polvo: polímero redispersable. Estos polímeros están encapsulados y cuando se ponen en contacto con el agua se liberan de la cápsula formando de nuevo el gel. En los morteros de reparación el único compuesto hidraúlico que hay es el cemento y es el principal constituyente hoy en día de los materiales de construcción. El cemento se obtiene por molienda conjunta de Clínker y yeso. El Clínker se obtiene por cocción de una mezcla de arcillas y calizas hasta una temperatura de 1450-1500º C por reacción en estado fundente. Para esta reacción se deben premachacar y homogeneizar las materias primas extraídas de la cantera. Son dosificadas en el horno con unas proporciones tales que cumplan con unas relación de óxidos tales que permitan formar las fases anhidras del Clínker C3S, C2S, C3A y C4AF. De la hidratación de las fases se obtiene el gel CSH que es el que proporciona al cemento de sus propiedades. Existe una norma (UNE-EN 197-1) que establece la composición, especificaciones y tipos de cementos que se fabrican en España. La tendencia actual en la fabricación del cemento pasa por el uso de cementos con mayores contenidos de adiciones (cal, puzolana, cenizas volantes, humo de sílice,…) con el objeto de obtener cementos más sostenibles. Otros componentes que influyen en las características de los morteros son: - Áridos. En el desarrollo de los morteros se suelen usar naturales, bien calizos o silícicos. Hacen la función de relleno y de cohesionantes de la matriz cementante. Deben ser inertes - Aditivos. Son aquellos componentes del mortero que son dosificados en una proporción menor al 5%. Los más usados son los superplastificantes por su acción de reductores de agua que revierte en una mayor durabilidad del mortero. Una vez analizada la composición de los morteros, la mejora tecnológica de los mismos está orientada al aumento de la durabilidad de su vida en obra. La durabilidad se define como la capacidad que éste tiene de resistir a la acción del ambiente, ataques químicos, físicos, biológicos o cualquier proceso que tienda a su destrucción. Estos procesos dependen de factores tales como la porosidad del hormigón y de la exposición al ambiente. En cuanto a la porosidad hay que tener en cuenta la distribución de macroporos, mesoporos y microporos de la estructura del hormigón, ya que no todos son susceptibles de que se produzca el transporte de agentes deteriorantes, provocando tensiones internas en las paredes de los mismos y destruyendo la matriz cementante Por otro lado los procesos de deterioro están relacionados con la acción del agua bien como agente directo o como vehículo de transporte del agente deteriorante. Un ambiente que resulta muy agresivo para los hormigones es el marino. En este caso los procesos de deterioro están relacionados con la presencia de cloruros y de sulfatos tanto en el agua de mar como en la atmosfera que en combinación con el CO2 y O2 forman la sal de Friedel. El deterioro de las estructuras en ambientes marinos se produce por la debilitación de la matriz cementante y posterior corrosión de las armaduras que provocan un aumento de volumen en el interior y rotura de la matriz cementante por tensiones capilares. Otras reacciones que pueden producir estos efectos son árido-álcali y difusión de iones cloruro. La durabilidad de un hormigón también depende del tipo de cemento y su composición química (cementos con altos contenidos de adición son más resistentes), relación agua/cemento y contenido de cemento. La Norma UNE-EN 1504 que consta de 10 partes, define los productos para la protección y reparación de estructuras de hormigón, el control de calidad de los productos, propiedades físico-químicas y durables que deben cumplir. En esta Norma se referencian otras 65 normas que ofrecen los métodos de ensayo para la evaluación de los sistemas de reparación. En la segunda parte de esta Tesis se hizo un diseño de experimentos con diferentes morteros poliméricos (con concentraciones de polímero entre 0 y 25%), tomando como referencia un mortero control sin polímero, y se estudiaron sus propiedades físico-químicas, mecánicas y durables. Para mortero con baja proporción de polímero se recurre a sistemas monocomponentes y para concentraciones altas bicomponentes en la que el polímero está en dispersión acuosa. Las propiedades mecánicas medidas fueron: resistencia a compresión, resistencia a flexión, módulo de elasticidad, adherencia por tracción directa y expansión-retracción, todas ellas bajo normas UNE. Como ensayos de caracterización de la durabilidad: absorción capilar, resistencia a carbonatación y adherencia a tracción después de ciclos hielo-deshielo. El objeto de este estudio es seleccionar el mortero con mejor resultado general para posteriormente hacer una comparativa entre un mortero con polímero (cantidad optimizada) y un mortero sin polímero. Para seleccionar esa cantidad óptima de polímero a usar se han tenido en cuenta los siguientes criterios: el mortero debe tener una clasificación R4 en cuanto a prestaciones mecánicas al igual que para evaluar sus propiedades durables frente a los ciclos realizados, siempre teniendo en cuenta que la adición de polímero no puede ser elevada para hacer el mortero competitivo. De este estudio se obtuvieron las siguientes conclusiones generales: - Un mortero normalizado no cumple con propiedades para ser clasificado como R3 o R4. - Sin necesidad de polímero se puede obtener un mortero que cumpliría con R4 para gran parte de las características medidas - Es necesario usar relaciones a:c< 0.5 para conseguir morteros R4, - La adición de polímero mejora siempre la adherencia, abrasión, absorción capilar y resistencia a carbonatación - Las diferentes proporciones de polímero usadas siempre suponen una mejora tecnológica en propiedades mecánicas y de durabilidad. - El polímero no influye sobre la expansión y retracción del mortero. - La adherencia se mejora notablemente con el uso del polímero. - La presencia de polímero en los morteros mejoran las propiedades relacionadas con la acción del agua, por aumento del poder cementante y por lo tanto de la cohesión. El poder cementante disminuye la porosidad. Como consecuencia final de este estudio se determinó que la cantidad óptima de polímero para la segunda parte del estudio es 2.0-3.5%. La tercera parte consistió en el estudio comparativo de dos morteros: uno sin polímero (mortero A) y otro con la cantidad optimizada de polímero, concluida en la parte anterior (mortero B). Una vez definido el porcentaje de polímeros que mejor se adapta a los resultados, se plantea un nuevo esqueleto granular mejorado, tomando una nueva dosificación de tamaños de áridos, tanto para el mortero de referencia, como para el mortero con polímeros, y se procede a realizar los ensayos para su caracterización física, microestructural y de durabilidad, realizándose, además de los ensayos de la parte 1, mediciones de las propiedades microestructurales que se estudiaron a través de las técnicas de porosimetría de mercurio y microscopia electrónica de barrido (SEM); así como propiedades del mortero en estado fresco (consistencia, contenido de aire ocluido y tiempo final de fraguado). El uso del polímero frente a la no incorporación en la formulación del mortero, proporcionó al mismo de las siguientes ventajas: - Respecto a sus propiedades en estado fresco: El mortero B presentó mayor consistencia y menor cantidad de aire ocluido lo cual hace un mortero más trabajable y más dúctil al igual que más resistente porque al endurecer dejará menos huecos en su estructura interna y aumentará su durabilidad. Al tener también mayor tiempo de fraguado, pero no excesivo permite que la manejabilidad para puesta en obra sea mayor, - Respecto a sus propiedades mecánicas: Destacar la mejora en la adherencia. Es una de las principales propiedades que confiere el polímero a los morteros. Esta mayor adherencia revierte en una mejora de la adherencia al soporte, minimización de las posibles reacciones en la interfase hormigón-mortero y por lo tanto un aumento en la durabilidad de la reparación ejecutada con el mortero y por consecuencia del hormigón. - Respecto a propiedades microestructurales: la porosidad del mortero con polímero es menor y menor tamaño de poro critico susceptible de ser atacado por agentes externos causantes de deterioro. De los datos obtenidos por SEM no se observaron grandes diferencias - En cuanto a abrasión y absorción capilar el mortero B presentó mejor comportamiento como consecuencia de su menor porosidad y su estructura microscópica. - Por último el comportamiento frente al ataque de sulfatos y agua de mar, así como al frente de carbonatación, fue más resistente en el mortero con polímero por su menor permeabilidad y su menor porosidad. Para completar el estudio de esta tesis, y debido a la gran importancia que están tomando en la actualidad factores como la sostenibilidad se ha realizado un análisis de ciclo de vida de los dos morteros objeto de estudio de la segunda parte experimental.In recent years, the extended use of repair materials for buildings and structures made the development of repair mortars more and more technical. In the development of these mortars by producers, the use of polymers in the formulations is a key point, because sometimes this use is not justified when looking to the performance/price/application as a whole. This thesis is an exhaustive study to justify the use of these mortars as a response to the current growing demand for structural repair. The thesis is classified in three parts:The first part is the study of the state of the art of mortars and their constituents.In ancient times, widely used mortars were based on lime and gypsum. The Greeks and Romans developed the concept of lime mortars, introducing components such as pozzolans, hydraulic limes and marble dust as aggregates, giving very similar concrete mortars to the ones used currently. In the middle Age and Renaissance, the technology developed by the Romans was lost, due to the extensive use of stone in the civil, religious and defensive constructions. It was not until the 19th century, when J. Aspdin discovered the current cement as the main hydraulic compound. Finally in the 20th century, with the appearance of molecules such as styrene, melanin, vinyl chloride and polyester, the industry began to develop polymers which were added to the binder to form special "composites".The use of polymers in cementitious matrixes give properties to the mortar such as adhesion, Currently, the result of the polymer synthesis (polivynilacetate, styrene-butadiene, vynilacrylic and epoxy resins) is that mortars have increased resistance to water attack and therefore, they increase their durability since all reactions of deterioration are minimised (ice, humidity, biological attack,...). In the present study the polymer used was redispersible polymer powder. These polymers are encapsulated and when in contact with water, they are released from the capsule forming a gel.In the repair mortars, the only hydraulic compound is the cement and nowadays, this is the main constituent of building materials. The current trend is centered in the use of higher contents of additions (lime, pozzolana, fly ash, silica, silica fume...) in order to obtain more sustainable cements. Once the composition of mortars is analyzed, the technological improvement is centred in increasing the durability of the working life. Durability is defined as the ability to resist the action of the environment, chemical, physical, and biological attacks or any process that tends to its destruction. These processes depend on factors such as the concrete porosity and the environmental exposure. In terms of porosity, it be considered, the distribution of Macropores and mesopores and pores of the concrete structure, since not all of them are capable of causing the transportation of damaging agents, causing internal stresses on the same walls and destroying the cementing matrix.In general, deterioration processes are related to the action of water, either as direct agent or as a transport vehicle. Concrete durability also depends on the type of cement and its chemical composition (cement with high addition amounts are more resistant), water/cement ratio and cement content. The standard UNE-EN 1504 consists of 10 parts and defines the products for the protection and repair of concrete, the quality control of products, physical-chemical properties and durability. Other 65 standards that provide the test methods for the evaluation of repair systems are referenced in this standard. In the second part of this thesis there is a design of experiments with different polymer mortars (with concentrations of polymer between 0 and 25%), taking a control mortar without polymer as a reference and its physico-chemical, mechanical and durable properties were studied. For mortars with low proportion of polymer, 1 component systems are used (powder polymer) and for high polymer concentrations, water dispersion polymers are used. The mechanical properties measured were: compressive strength, flexural strength, modulus of elasticity, adhesion by direct traction and expansion-shrinkage, all of them under standards UNE. As a characterization of the durability, following tests are carried out: capillary absorption, resistance to carbonation and pull out adhesion after freeze-thaw cycles. The target of this study is to select the best mortar to make a comparison between mortars with polymer (optimized amount) and mortars without polymer. To select the optimum amount of polymer the following criteria have been considered: the mortar must have a classification R4 in terms of mechanical performance as well as in durability properties against the performed cycles, always bearing in mind that the addition of polymer cannot be too high to make the mortar competitive in price. The following general conclusions were obtained from this study: - A standard mortar does not fulfill the properties to be classified as R3 or R4 - Without polymer, a mortar may fulfill R4 for most of the measured characteristics. - It is necessary to use relations w/c ratio < 0.5 to get R4 mortars - The addition of polymer always improves adhesion, abrasion, capillary absorption and carbonation resistance - The different proportions of polymer used always improve the mechanical properties and durability. - The polymer has no influence on the expansion and shrinkage of the mortar - Adhesion is improved significantly with the use of polymer. - The presence of polymer in mortars improves the properties related to the action of the water, by the increase of the cement power and therefore the cohesion. The cementitious properties decrease the porosity. As final result of this study, it was determined that the optimum amount of polymer for the second part of the study is 2.0 - 3.5%. The third part is the comparative study between two mortars: one without polymer (A mortar) and another with the optimized amount of polymer, completed in the previous part (mortar B). Once the percentage of polymer is defined, a new granular skeleton is defined, with a new dosing of aggregate sizes, for both the reference mortar, the mortar with polymers, and the tests for physical, microstructural characterization and durability, are performed, as well as trials of part 1, measurements of the microstructural properties that were studied by scanning electron microscopy (SEM) and mercury porosimetry techniques; as well as properties of the mortar in fresh State (consistency, content of entrained air and final setting time). The use of polymer versus non polymer mortar, provided the following advantages: - In fresh state: mortar with polymer presented higher consistency and least amount of entrained air, which makes a mortar more workable and more ductile as well as more resistant because hardening will leave fewer gaps in its internal structure and increase its durability. Also allow it allows a better workability because of the longer (not excessive) setting time. - Regarding the mechanical properties: improvement in adhesion. It is one of the main properties which give the polymer to mortars. This higher adhesion results in an improvement of adhesion to the substrate, minimization of possible reactions at the concrete-mortar interface and therefore an increase in the durability of the repair carried out with mortar and concrete. - Respect to microstructural properties: the porosity of mortar with polymer is less and with smaller pore size, critical to be attacked by external agents causing deterioration. No major differences were observed from the data obtained by SEM - In terms of abrasion and capillary absorption, polymer mortar presented better performance as a result of its lower porosity and its microscopic structure. - Finally behavior against attack by sulfates and seawater, as well as to carbonation, was better in the mortar with polymer because of its lower permeability and its lower porosity. To complete the study, due to the great importance of sustainability for future market facts, the life cycle of the two mortars studied was analysed.

Contaminantes orgánicos (PAHs) derivados de la escombrera de la Central Térmica de Aliaga (Teruel)

The aim of this study was to determine if the soils, waters and plants from the Aliaga dump contained polycyclic aromatic hydrocarbons (PAHs) and their quantification.The results showed that PAHs concentrations in soils are in general higher than the reference levels from the Spanish legislation. Waters and plants contained PAHs but in low concentrations. The possible actions for remediation (photodegradation and bioremediation) seem to be unviable here because of the large volume of materials involved, although its use as an additive for the cement industry and derivatives can be considered. It is proposed that fluorantene in waters, and phenanthrene and benzo[ghi]perilene in soils be considered as pollutants as well as to study the incorporation of PAHs to plants. Key-words: Polycyclic aromatic hydrocarbons, soil, plant and water contamination, fly- ash, power plant. RESUMEN: El objetivo de este estudio fue determinar y cuantificar los hidrocarburos policíclicos aromáticos (PAHs) en los suelos, plantas y aguas de la Escombrera de Aliaga. La concentración de PAHs en las cenizas supera, en general, los valores establecidos en la legislación española.Las aguas y plantas contienen PAHs, aunque en concentraciones bajas. La remoción de los materiales para someterlos a fotodegradación y biorremediación es inviable debido al gran volumen de la escombrera, aunque se plantea su uso como aditivo en la fabricación de productos derivados del cemento. Se propone incluir el fenantreno y benzo[ghi]perileno en la normativa de suelos, así como el naftaleno en la de aguas y la elaboración de una legislación sobre la incorporación de estos compuestos a las plantas.

Desarrollo de conglomerados con la incorporación de cenizas volantes procedentes de la incineración de residuos sólidos urbanos

Esta tesis presenta los resultados de la investigación realizada sobre la inertización de cenizas volantes procedentes de residuos sólidos urbanos y su posterior encapsulación en distintas matrices de mortero. Durante el proceso de inertización, se ha logrado la inertización de éste residuo tóxico y peligroso (RTP) y también su valorización como subproducto. De esta forma se dispone de nueva “materia prima” a bajo coste y la eliminación de un residuo tóxico y peligroso con la consiguiente conservación de recursos naturales alternativos. La caracterización química de las cenizas analizadas refleja que éstas presentan altas concentraciones de cloruros, Zn y Pb. Durante la investigación se ha desarrollado un proceso de inertización de las cenizas volantes con bicarbonato sódico (NaHCO3) que reduce en un 99% el contenido en cloruros y mantiene el pH en valores óptimos para que la concentración de los metales pesados en el lixiviado sea mínima debido a su estabilización en forma de carbonatos insolubles. Se han elaborado morteros con cuatro tipos distintos de cementos (CEM-I, CEM-II, CAC y CSA) incorporando cenizas volantes inertizadas en una proporción igual a un 10% en peso del árido utilizado. Los morteros ensayados abarcan distintas dosificaciones tanto en la utilización de áridos con distintos diámetros (0/2 y 0/4), como en la relación cemento/árido (1/1 y 1/3). Se han obtenido las propiedades físicas y mecánicas de estos morteros mediante ensayos de Trabajabilidad, Estabilidad Dimensional, Carbonatación, Porosidad y Resistencias Mecánicas. De igual forma, se presentan resultados de ensayos de lixiviación de Zn, Pb, Cu y Cd, sobre probetas monolíticas de los morteros con los mejores comportamientos físico/mecánicos, donde se ha analizado el contenido en iones de dichos metales pesados lixiviados mediante determinación voltamperométrica de redisolución anódica Se concluye que todos los morteros ensayados son técnicamente aceptables, siendo los más favorables los elaborados con Cemento de Sulfoaluminato de Calcio (CSA) y con Cemento de Aluminato de Calcio (CAC). En este último caso, se mejoran las resistencias a compresión de los morteros de referencia en más de un 48%, y las resistencias a flexión en más de un 67%. De igual forma, los ensayos de lixiviado revelan la completa encapsulación de los iones de Zn y la mitigación en el lixiviado de los iones de Pb. Ambos morteros podrían ser perfectamente validos en actuaciones en las que se necesitase un producto de fraguado rápido, altas resistencias iniciales y compensación de las retracciones con una elevada estabilidad dimensional. En base a esto, el material podría ser utilizado como mortero de reparación en viales y pavimentos que requiriesen altas prestaciones, tales como: soleras industriales, pistas de aterrizaje, aparcamientos, etc. O bien, para la confección de elementos prefabricados sin armaduras estructurales, dada su elevada resistencia a flexión. ABSTRACT This dissertation presents the results of a research on inerting fly ash from urban solid waste and its subsequent encapsulation in mortar matrixes. The inerting of this hazardous toxic waste, as well as its valorization as a by-product has been achieved. In this way, a new "raw material" is available through a simple process and the toxic and hazardous waste is eliminated, and consequently, conservation of alternative natural resources is strengthened. Chemical analysis of the ashes analyzed shows high concentrations of soluble chlorides, Zn and Pb. An inerting process of fly ash with sodium bicarbonate (NaHCO3) has been developed which reduces 99% the content of chlorides and maintains pH at optimal values, so that the concentration of heavy metals in the leachate is minimum, due to its stabilization in the form of insoluble carbonates. Mortars with four different types of cements (CEM-I, CEM-II, CAC and CSA) have been developed by the addition of inertized fly ash in the form of carbonates, in the proportion of 10% in weight of the aggregates used. The samples tested include different proportions in the use of aggregates with different sizes (0/2 and 0/4), and in the cement/aggregate ratio (1/1 and 1/3). Physical/mechanical properties of these mortars have been studied through workability, dimensional stability, carbonation, porosity and mechanic strength tests. Leaching tests of Zn, Pb, Cu and Cd ions are also being performed on monolithic samples of the best behavioral mortars. The content in leachated heavy metal ions is being analyzed through stripping voltammetry determination. Conclusions drawn are that the tested CAC and CSA cement mortars present much better behavior than those of CEM-I and CEM-II cement. The results are especially remarkable for the CAC cement mortars, improving reference mortars compression strengths in more than 48%, and also bending strengths in more than 67%. Leaching tests confirm that the encapsulation of Zn and Pb is achieved and leachate of both ions is mitigated within the mortar matrixes. For the above stated reasons, it might be concluded that mortars made with calcium aluminate cements or calcium sulfoaluminate with the incorporation of treated fly ash, may be perfectly valid for uses in which a fast-curing product, with high initial strength and drying shrinkage compensation with a high dimensional stability is required. Based on this, the material could be used as repair mortar for structures, roads and industrial pavements requiring high performance, such as: industrial floorings, landing tracks, parking lots, etc. Alternatively, it could also be used in the manufacture of prefabricated elements without structural reinforcement, given its high bending strength.

Corrosión de armaduras en el hormigón armado en ambiente marino aéreo

La presente tesis doctoral surge ante la necesidad de completar el estudio sobre la corrosión en el hormigón armado expuesto al ambiente marino iniciado por D. Miguel Ángel Bermúdez Odriozola en 2007 con la tesis doctoral con título “Corrosión de las armaduras del hormigón armado en ambiente marino: zona de carrera de mareas y zona sumergida”. Una vez realizado el estudio bibliográfico, se ha planteado un estudio experimental en el que se analizan cuatro muelles de distintas edades y localizados en distintos lugares de la geografía española. Uno de ellos contiene adiciones en el hormigón. Una vez inspeccionados, se extraen testigos de cada uno de ellos con el fin de realizar ensayos de caracterización y se analizan sus resultados en paralelo con los coeficientes de difusión. Uno se los objetivos ha sido comprobar el mejor método de ensayo que permita controlar la durabilidad del hormigón en ambiente IIIa. La tesis que se presenta ha demostrado la efectividad del ensayo de penetración de agua para discriminar los hormigones que presentarán un buen comportamiento frente a la difusión de cloruros y por tanto para predecir la vida útil de la estructura. Asimismo, otro objetivo ha sido valorar el uso de adiciones en el hormigón y cómo afectan a la mejora del comportamiento del hormigón expuesto al ambiente marino. Se han obtenido valores del coeficiente de eficacia de cenizas volantes y humo de sílice frente a la difusión de cloruros, muy superiores a los actualmente considerados en términos de resistencia. El ambiente marino aéreo engloba estructuras situadas en primera línea de costa así como aquellas que se sitúan hasta 5km de distancia de la línea del mar. La investigación realizada ha demostrado la necesidad de establecer una nueva subdivisión en este ambiente introduciendo la zona Spray, siguiendo criterios internacionales, que permita diferenciar la zona más desfavorable del mismo que comprende las estructuras ubicadas sobre el nivel del mar tal como los tableros de pantalanes portuarios estudiados. Se han analizado en profundidad los valores del contenido de cloruros en superficie de hormigón en los diferentes tipos de ambiente marino recogidos por la Instrucción EHE- 08 contrastando los requisitos normativos. Como conclusión se han hecho nuevas propuestas normativas que afectan al ambiente sumergido y al ambiente marino aéreo (zona spray). Asimismo se ha realizado un análisis en profundidad de la concentración crítica de cloruros recogida por la Instrucción EHE-08, a partir de los datos obtenidos en estructuras reales. Se ha evaluado el ensayo de resistividad para estimar el valor del coeficiente de difusión de cloruros. Este ensayo ha demostrado su efectividad para discriminar hormigones con adiciones y con muy baja penetración de agua, si bien no resulta sensible para detectar hormigones con elevada permeabilidad. Finalmente en la tesis se ha obtenido un modelo de difusión de cloruros (a/c-D) en ambiente marino aéreo a fin de poder estimar la difusión de cloruros en el hormigón a partir de un requisito normativo como es la relación a/c. This Thesis is focussed to complete the previous study on the corrosion of reinforced concrete exposed to marine environment, carried out by Dr. Miguel Ángel Bermúdez Odrizola in 2007. That Thesis title was “Corrosion of concrete reinforcement located in marine environment: tidal zone and submerged zone”. After the literature review presented in the State of the Art, an experimental programme was carried out. Four docks of different ages and locations have been studied, one of them was a fly ash concrete. The structures were inspected on site and several cores extracted in order to develop characterization tests and obtain diffusion profiles at the laboratory. One of the objectives has been to check the best laboratory test method to control concrete durability when exposed to atmospheric marine environment. This Thesis has proven the effectiveness of the water penetration test to differentiate concretes well behaved against chloride diffusion and also to predict the structure service life. Another objective has been to study the effect of mineral additions in concrete and how they improve the durability of concrete in this environment. Efficiency factors have been obtained for fly ashes and silica fume, much higher than those consider for strength. According to the Spanish Concrete Code EHE 08, the atmospheric marine environment includes structures located at the cost, from the sea line up to 5km inland. The research conducted has shown the need to consider a spray zone which is the most unfavourable area of the atmospheric environment, affecting structures over the sea level as the decks of the wharves here studied. Surface chloride contents of structures in the different marine environments have been deeply analysed, checking the actual standard limits. As a conclusion, new normative values have been proposed for submerged and atmospheric zone (spray zone). A complete analysis of the chloride threshold concentration from the data obtained in real structures has also been performed. It has been evaluated the resistivity test as a tool to estimate the chloride diffusion coefficient. This test has proven effectiveness to discriminate concrete with mineral additions and low water penetration values, while it is not sensitive to detect concretes with high permeability. Finally, a chloride diffusion model (w/c) has been obtained in atmospheric marine environment in order to estimate the chloride diffusion of the concrete knowing a normative requirement as w/c.

Washcoated Pd/Al2O3 monoliths for the liquid phase hydrodechlorination of dioxins

The catalytic activity and durability of 2 wt.% Pd/Al2O3 in powder and washcoated on cordierite monoliths were examined for the liquid phase hydrodechlorination (LPHDC) of polychlorinated dibenzo-p-dioxins/polychlorinated dibenzofurans (PCDD/Fs), also known as dioxins. NaOH was employed as a neutralizing agent, and 2-propanol was used as a hydrogen donor and a solvent. Fresh and spent powder and monolith samples were characterized by elemental analysis, surface area, hydrogen chemisorption, scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDX), and transmission electron microscopy/energy dispersive X-ray spectroscopy (TEM/EDX). Three reactor configurations were compared including the slurry and monolith batch reactors as well as the bubble loop column resulting in 100, 70, and 72% sample toxicity reduction, respectively, after 5 h of reaction. However, the slurry and monolith batch reactors lead to catalyst sample loss via a filtration process (slurry) and washcoat erosion (monolith batch), as well as rapid deactivation of the powder catalyst samples. The monolith employed in the bubble loop column remained stable and active after four reaction runs. Three preemptive regeneration methods were evaluated on spent monolith catalyst including 2-propanol washing, oxidation/reduction, and reduction. All three procedures reactivated the spent catalyst samples, but the combustion methods proved to be more efficient at eliminating the more stable poisons.

Radiological impact of cement, concrete and admixtures in Spain

It has been analyzed samples of portland cement (PC) with and without admixtures, samples of calcium aluminate cement (CAC) with different content of Al2O3 and specimens of concrete made with PC and CAC using High Resolution Gamma Spectrometry. The activity concentration index (I) is much less than 0.5 mSv y-1 for all the concrete specimens according to the Radiation protection document 112 of the European Commission. The PC without admixtures (CEM I 52,5 R) and the PC with addition of limestone (CEM II/BL 32,5 N) also have an I value much lower than 0.5 and the PC with the addition of fly ash and blast furnace slag (CEM IV/B (V) 32,5 N and III/A 42.5 N/SR) have an I value close to 0.6. The I value of the CAC used in the manufacture of structural precast concrete is of the order of 1 mSv y-1. Some of the CAC used in refractory concrete reaches a value close to 2 mSv y-1.

Influencia de diferentes condiciones de curado en la estructura porosa y en las propiedades a edades tempranas de morteros que contienen ceniza volante y escoria de alto horno

En este trabajo se ha estudiado la evolución de la microestructura, propiedades de durabilidad y resistencias mecánicas de morteros preparados con cementos comerciales, que contienen ceniza volante (entre un 21% y un 35%) y escoria de alto horno (entre un 66% y un 80%), expuestos a tres ambientes, un ambiente óptimo de laboratorio, y dos ambientes representativos del clima Atlántico y Mediterráneo respectivamente. Como referencia de comportamiento, también se ensayaron morteros de cemento Portland. La microestructura se caracterizó mediante porosimetría de intrusión de mercurio. En lo referente a la durabilidad, se estudiaron los coeficientes de absorción capilar y de migración de cloruros en estado no estacionario. También se determinó la resistencia a compresión de los morteros. Los ensayos se realizaron a 7, 28 y 90 días. La principal conclusión alcanzada es que los cementos con cenizas y escorias expuestos a condiciones ambientales representativas de los climas Atlántico y Mediterráneo, pueden desarrollar unas propiedades en servicio adecuadas al cabo de tres meses.

Blending of industrial waste from different sources as partial substitution of Portland cement in pastes and mortars

Binary and ternary combinations of sewage sludge ash (SSA) with marble dust (MD), fly ash (FA) and rice husk ash (RHA) as replacement in Portland cement pastes, were assessed. Several tests were carried out at different curing ages: thermogravimetry, density, water absorption, ultrasonic pulse velocity and mechanical strengths. Pozzolanic effects of the mineral admixtures, densities similar to control sample and improved absorptions when combining waste materials were identified. In general, the compressive strength reaches or exceeds the cement strength class, and blending SSA, FA and RHA (30% cement replacement) increase of strength by 9%, compared to the control sample, was achieved.

Valorización de cenizas de lodo de depuradora como componente de hormigones para prefabricados

Se plantea la combinación binaria y ternaria de cenizas de lodo de depuradora (CLD) con ceniza volante, polvo de mármol y ceniza de cáscara de arroz, como sustitución parcial o como adición respecto al cemento Portland en hormigones, con una dosificación similar a la utilizada en la prefabricación de bloques (consistencia muy seca). Se llevaron a cabo ensayos físico-mecánicos sobre probetas de mortero y hormigón con edades de curado de 28 y 90 días: densidad, absorción y resistencia a compresión. Se comprueba que la sustitución de cemento por CLD supone una disminución de la densidad y de la resistencia respecto a la muestra patrón, sin embargo, las combinaciones con otros residuos mejoran notablemente las características de los materiales cementantes. La adición de CLD proporcionó densidades y resistencias similares a la muestra de control y reduce significativamente la absorción de agua.

Stability of Cs-Ionsiv in Portland cement blends for radioactive waste disposal

The suitability of Portland cement blends for encapsulation of Cs-Ionsiv in a monolithic wasteform was investigated. No evidence of reaction or dissolution of the Cs-Ionsiv in the cementitious environment was found by scanning electron microscopy and X-ray diffraction. However, a small fraction (≤1.6 wt%) of the Cs inventory was released from the encapsulated Ionsiv during leaching experiments carried out on hydrated samples. Cs release was enhanced by exchange of K and Na present in the cementitious pore water. Cement systems lower in K and Na, such as slag based blends, showed lower Cs release than the fly ash based analogues. © 2010 Materials Research Society.

Spray dryer spent sorbent hazardous waste fixating and cementitious properties /

"HWRIC project no. 86-103."

Update : New Jersey Zinc/Mobil Chemical Superfund Site, DePue, Illinois = U ltimos acontecimientos : Sitio Superfund New Jersey Zinc/Mobil Chemical, Depue, Illinois.

The potentially responsible parties (PRPs) have removed the beaver dams and have collected the sediment samples they need for treatability studies. The treatability studies will establish the correct silt fence to minimize releases of sediment during the actual dredging to occur this fall. The studies will also determine the types and amounts of materials (lime, kiln dust, fly ash, etc.) required to stabilize the sediment, chemically tie up the metals and insure the sediment mixture will bear the weight of the cap on the Interim Storage Cell where the sediment will be placed. The Illinois Environmental Protection Agency (Illinois EPA) anticipates work to be completed by late fall or early winter 2004, if lake and river levels that affect the South Ditch are at their normal seasonal levels.