退火对电子束热蒸发193nm Al2O3/MgF2反射膜性能的影响

设计并镀制了193nm Al2O3/MgF2反射膜,对它们在空气中分别进行了250-400℃的高温退火,测量了样品的透射率光谱曲线和绝对反射率光谱曲线.发现样品在高反射区的总的光学损耗随退火温度的升高而下降,而后趋于饱和.采用总积分散射的方法对样品在不同退火温度下的散射损耗进行了分析,发现随着退火温度的升高散射损耗有所增加.因此,总的光学损耗的下降是由于吸收损耗而不是散射损耗起主导作用.对Al2O3材料的单层膜进行了同等条件的退火处理,由它们光学性能的变化推导出它们的折射率和消光系数的变化,从而解释了相应

High-reflectance 193 nm Al2O3/MgF2 mirrors

Thin-film single layers of Al2O3 and MgF2 were deposited upon super polished fused-silica by electron-beam evaporation. The subsequent optical constants n and k were reported for the spectral range of 180-230 nm. High-reflectance dense multilayer coatings for 193 nm were designed on the basis of the evaluated optical constants and produced. The spectra of the reflectance of HR coatings were compared to the theoretical calculations. HR mirrors of 27 layers with a reflectance of more than 98% were reported. (c) 2004 Elsevier B.V. All rights reserved.

Annealing effects on electron-beam evaporated Al2O3 films

The effects of post-deposited annealing on structure and optical properties of electron-beam evaporated Al2O3 single layers were investigated. The films were annealed in air for 1.5 h at different temperatures from 250 to 400 degrees C. The optical constants and cut-off wavelength were deduced. Microstructure of the samples was characterized by X-ray diffraction (XRD). Profile and surface roughness measurement instrument was used to determine the rms surface roughness. It was found that the cut-off wavelength shifted to short wavelength as the annealing temperature increased and the total optical loss decreased. The film structure remained amorphous even after annealing at 400 degrees C temperature and the samples annealed at higher temperature had the higher rms surface roughness. The decreasing total optical loss with annealing temperature was attributed to the reduction of absorption owing to oxidation of the film by annealing. Guidance to reduce the optical loss of excimer laser mirrors was given. (c) 2004 Elsevier B.V. All rights reserved.

高反射率193nm Al2O3／MgF2反射膜的实验研究

用电子束热蒸发方法在熔融石英基底上沉积了Al2O3和MgF2两种材料的单层膜，研究了两种材料的光学特性，采用光度法计算并给出了薄膜材料在180～230nm的折射率n／和消光系数k的色散曲线。以两种材料作为高低折射率材料组合，采用1／4波长规整膜系设计并镀制了193nm的高反射膜，反射膜在退火后的反射率在193nm达到96％以上。结果表明在一定工艺条件下Al2O3和MgF2两种材料能够在193nm获得较好的光学性能，适用于高反射膜的制备。

退火对电子束热蒸发Al2O3薄膜性能影响的实验研究

用电子束热蒸发方法镀制了Al2O3材料的单层膜，对它们在空气中进行了250～400℃的高温退火。对样品的透射率光谱曲线进行了测量，计算了样品的消光系数、折射率和截止波长。通过X射线衍射仪(XRD)测量分析了薄膜的微观结构，采用表面轮廓仪测量了样品的表面均方根粗糙度。结果发现随着退火温度的提高光学损耗下降，薄膜结构在退火温度为400℃时仍然为无定形态，样品的表面粗糙度随退火温度的升高而增加。引起光学损耗下降起主导作用的是吸收而不是散射，吸收损耗的下降主要是由于退火使材料吸收空气中的氧而进一步氧化，从而使薄膜

Al2O3和Cr过渡层对Ag膜光学性质及其附着力的影响

研究了在玻璃基底上镀制Al2O3和Cr过渡层对Ag膜反射率及附着力的影响.分光光度计测试了Ag膜的反射率,结果表明,与Cr过渡层相比,Al2O3过渡层对Ag膜反射率的降低相对较小;而且,随着Al2O3厚度的增加,Ag膜的反射率先增大后减小.XRD与AES测试表明,引入Al2O3或Cr可明显细化Ag晶粒,减弱Ag膜（111）织构;Al2O3作过渡层时,Al原子向Ag层中扩散显著;而Cr作过渡层时,只有少量Cr原子扩散进入Ag层.因此,Al2O3作过渡层能显著增强薄膜与玻璃基体之间的附着力.

Working pressure dependence of properties of Al2O3 thin films prepared by electron beam evaporation

The effects of working pressure on properties of Al2O3 thin films are investigated. Transmittance of the Al2O3 thin film is measured by a Lambda 900 spectrometer. Laser-induced damage threshold (LIDT) is measured by a Nd:YAG laser at 355nm with a pulse width of 7ns. Microdefects were observed under a Nomarski microscope. The samples are characterized by optical properties and defect, as well as LIDT under the 355 nm Nd: YAG laser radiation. It is found that the working pressure has fundamental effect on the LIDT. It is the absorption rather than the microdefect that plays an important role on the LID T of Al2O3 thin film.

Desenvolvimento de revestimentos de óxidos mistos nanoestruturados de TiO2/Al2O3 em substratos metálicos de aço AISI 1020 e estudo das propriedades anticorrosivas

Sóis liofilizados precursores de Al2O3/TiO2, foram preparados via tecnologia sol-gel, com diferentes porcentagens de óxido de titânio (5%, 10%, 15% e 20%, em massa). Os sóis liofilizados foram caracterizados por meio de diversas análises, com o intuito de obter informações sobre o comportamento térmico, fases presentes, tamanho de partícula, composição e uniformidade das amostras. Os resultados obtidos indicam que os sóis apresentam as fases boemita e anatase, com partículas de tamanho nanométrico, tem composições muito similares quando analisadas em pontos distintos, átomos bem dispersos e distribuídos. Após esta etapa, amostras de aço AISI 1020 foram recobertas com estes sóis através do método dip-coating, o comportamento corrosivo foi estudado por meio de ensaios eletroquímicos e a morfologia das camadas, analisadas por meio de microscopias. Observou-se que as camadas eram uniformes e recobriam por completo toda a superfície das amostras, os ensaios de polarização indicaram melhorias no potencial eletroquímico para amostras recobertas, em comparação com amostras de aço sem recobrimento. O monitoramento de circuito aberto apresentou bons ajustes, indicando bom comportamento da camada. Notou-se pelas microscopias a presença de pontos de corrosão em algumas amostras antes dos ensaios, suspeitando-se que os resultados obtidos teriam sido melhores, caso houvesse um maior controle do processo de recobrimento.