Sodium hypochlorite effects on dentin bond strength and acid-base resistant zone formation by adhesive systems

Aim: To evaluate the effects of 10% NaOCl gel application on the dentin bond strengths and morphology of resin-dentin interfaces formed by three adhesives. Methods: Two etch-and-rinse adhesives (One-Step Plus, Bisco Inc. and Clearfil Photo Bond, Kuraray Noritake Dental) and one self-etch adhesive (Clearfil SE Bond, Kuraray Noritake Dental) were applied on dentin according to the manufacturers’ instructions or after the treatment with 10% NaOCl (ED-Gel, Kuraray Noritake Dental) for 60 s. For interfacial analysis, specimens were subjected to acid-base challenge and observed by SEM to identify the formation of the acid-base resistant zone (ABRZ). For microtensile bond strength, the same groups were investigated and the restored teeth were thermocycled (5,000 cycles) or not before testing. Bond strength data were subjected to two-way ANOVA and Tukey’s test (p<0.05). Results: NaOCl application affected the bond strengths for One-Step Plus and Clearfil Photo Bond. Thermocycling reduced the bond strengths for Clearfil Photo Bond and Clearfil SE Bond when used after NaOCl application and One-Step Plus when used as recommended by manufacturer. ABRZ was observed adjacent to the hybrid layer for self-etch primer. The etch-and-rinse systems showed external lesions after acid-base challenge and no ABRZ formation when applied according to manufacturer’s instructions. Conclusions: 10% NaOCl changed the morphology of the bonding interfaces and its use with etch-&-rinse adhesives reduced the dentin bond strength. Formation of ABRZ was material-dependent and the interface morphologies were different among the tested materials.

Adhesives for fixed orthodontic bands

Background: Orthodontic treatment involves using fixed or removable appliances (dental braces) to correct the positions of teeth. It has been shown that the quality of treatment result obtained with fixed appliances is much better than with removable appliances. Fixed appliances are, therefore, favoured by most orthodontists for treatment. The success of a fixed orthodontic appliance depends on the metal attachments (brackets and bands) being attached securely to the teeth so that they do not become loose during treatment. Brackets are usually attached to the front and side teeth, whereas bands (metal rings that go round the teeth) are more commonly used on the back teeth (molars). A number of adhesives are available to attach bands to teeth and it is important to understand which group of adhesives bond most reliably, as well as reducing or preventing dental decay during the treatment period. :Objectives: To evaluate the effectiveness of the adhesives used to attach bands to teeth during fixed appliance treatment, in terms of: (1) how often the bands come off during treatment; and (2) whether they protect the banded teeth against decay during fixed appliance treatment. Search methods: The following electronic databases were searched: Cochrane Oral Health's Trials Register (searched 2 June 2016), Cochrane Central Register of Controlled Trials (CENTRAL; 2016, Issue 5) in the Cochrane Library (searched 2 June 2016), MEDLINE Ovid (1946 to 2 June 2016) and EMBASE Ovid (1980 to 2 June 2016). We searched ClinicalTrials.gov and the World Health Organization International Clinical Trials Registry Platform for ongoing trials. No restrictions were placed on the language or date of publication when searching the electronic databases. Selection criteria: Randomised and controlled clinical trials (RCTs and CCTs) (including split-mouth studies) of adhesives used to attach orthodontic bands to molar teeth were selected. Patients with full arch fixed orthodontic appliance(s) who had bands attached to molars were included. Data collection and analysis: All review authors were involved in study selection, validity assessment and data extraction without blinding to the authors, adhesives used or results obtained. All disagreements were resolved by discussion. Main results: Five RCTs and three CCTs were identified as meeting the review's inclusion criteria. All the included trials were of split-mouth design. Four trials compared chemically cured zinc phosphate and chemically cured glass ionomer; three trials compared chemically cured glass ionomer cement with light cured compomer; one trial compared chemically cured glass ionomer with a chemically cured glass phosphonate. Data analysis was often inappropriate within the studies meeting the inclusion criteria. Authors' conclusions: There is insufficient high quality evidence with regard to the most effective adhesive for attaching orthodontic bands to molar teeth. Further RCTs are required.

Bond–slip models for double strap joints strengthened by CFRP

This paper presents the results of a series of tension tests on CFRP bonded steel plate double strap joints. The main aim of this research is to provide detailed understanding of bond characteristics using experimental and numerical analysis of strengthened double strap joints under tension. A parametric study has been performed by numerical modelling with the variables of CFRP bond lengths, adhesive maximum strain and adhesive layer thicknesses. Finally, bond-slip models are proposed for three different types of adhesives within the range of the parametric study.

Microscale study of electrical characteristics of epoxy-multiwall carbon nanotube nanocomposites

Epoxy-multiwall carbon nanotube nanocomposite thin films were prepared by spin casting. High power air plasma was used to preferentially etch a coating of epoxy and expose the underlying carbon nanotube network. Scanning electron microscopy (SEM) examination revealed well distributed and spatially connected carbon nanotube network in both the longitudinal direction (plasma etched surface) and traverse direction (through-thickness fractured surface). Topographical examination and conductive mode imaging of the plasma etched surface using atomic force microscope (AFM) in the contact mode enabled direct imaging of topography and current maps of the embedded carbon nanotube network. Bundles consisting of at least three single carbon nanotubes form part of the percolating network observed under high resolution current maps. Predominantly non-ohmic response is obtained in this study; behaviour attributed to less than effective polymer material removal when using air plasma etching.

Investigations of the physical origins of etching LiNbO3 during Ti in-diffusion

We investigate the physical origins of etching observed during Ti diffusion. The relationship between observed etch depth and water vapor content in the annealing environment is quantified. The dynamics of the etching process are also identified. It is discovered that water vapor content is essential for etching and that there is a characteristic delay before etching is observed. From these observations we can conclude that the process is electrochemical in nature with ionic defects diffusing into the Ti strip from the lithium niobate and these defects catalyzing the dissociation of water into reactive ions.

Cyanoacrylate glue as an alternative mounting medium for resin-embedded semithin sections

Commercially available generic Superglue (cyanoacrylate glue) can be used as an alternative mounting medium for stained resin-embedded semithin sections. It is colourless and contains a volatile, quick-setting solvent that produces permanent mounts of semithin sections for immediate inspection under the light microscope. Here, we compare the use of cyanoacrylate glue for mounting semithin sections with classical dibutyl phthalate xylene (DPX) in terms of practical usefulness, effectiveness and the quality of the final microscopic image.

Effects of joint thickness, adhesion and web shells to the face shell bedded concrete masonry loaded in compression

The Australian masonry standard allows either prism tests or correction factors based on the block height and mortar thickness to evaluate masonry compressive strength. The correction factor helps the taller units with conventional 10 mm mortar being not disadvantaged due to size effect. In recent times, 2-4 mm thick, high-adhesive mortars and H blocks with only the mid-web shell are used in masonry construction. H blocks and thinner and higher adhesive mortars have renewed interest of the compression behaviour of hollow concrete masonry and hence is revisited in this paper. This paper presents an experimental study carried out to examine the effects of the thickness of mortar joints, the type of mortar adhesives and the presence of web shells in the hollow concrete masonry prisms under axial compression. A non-contact digital image correlation technique was used to measure the deformation of the prisms and was found adequate for the determination of strain fi eld of the loaded face shells subjected to axial compression. It is found that the absence of end web shells lowers the compressive strength and stiffness of the prisms and the thinner and higher adhesive mortars increase the compressive strength and stiffness, while lowering the Poisson's ratio. © Institution of Engineers Australia, 2013.

Development of polymers for Non-CAR resists for EUV lithography

Three strategies for approaching the design and synthesis of non-chemically amplified resists (non-CARs) are presented. These are linear polycarbonates, star polyester-blk-poly(methyl methacrylate) and comb polymers with polysulfone backbones. The linear polycarbonates were designed to cleave when irradiated with 92 eV photons and high Tg alicyclic groups were incorporated into the backbone to increase Tg and etch resistance. The star block copolymers were designed to have a core that is sensitive to 92 eV photons and arms that have the potential to provide properties such as high Tg and etch resistance. Similarly the polysulfone comb polymers were designed to have an easily degradable polymer backbone and comb-arms that impart favorable physical properties. Initial patterning results are presented for a number of the systems.

Comparative durability study of CFRP strengthened tubular steel members under cold weather

In strengthening systems, the CFRP (Carbon Fibre Reinforced Polymer) materials typically have excellent resistance against environmental conditions; however, the performance of adhesives between CFRP and steel is generally affected by various environmental conditions such as marine environment, cold and hot weather. This paper presents the comparative durability study of CFRP strengthened tubular steel structures by using two different adhesives such as MBrace saturant and Araldite K630 under four-point bending. The program consisted of testing twelve CFRP strengthened specimens having treated with epoxy based adhesion promoter, untreated surface and one unstrengthened specimen and conditioned under cold weather for 3 and 6 months to determine the environmental durability. The beams were then loaded to failure in quasi-static manner under four-point bending. The structural responses of CFRP strengthened tubular steel beams were compared in terms of failure load, stiffness and modes of failure. The research findings show that the cold weather immersion had adversely affected the durability of CFRP strengthened steel members. Design factor is also proposed to address the short-terms durability performance under cold weather.

Concentrations of phthalates and DINCH metabolites in pooled urine from Queensland, Australia

Dialkyl phthalate esters (phthalates) are ubiquitous chemicals used extensively as plasticizers, solvents and adhesives in a range of industrial and consumer products. 1,2-Cyclohexane dicarboxylic acid, diisononyl ester (DINCH) is a phthalate alternative introduced due to a more favourable toxicological profile, but exposure is largely uncharacterised. The aim of this study was to provide the first assessment of exposure to phthalates and DINCH in the general Australian population. De-identified urine specimens stratified by age and sex were obtained from a community-based pathology laboratory and pooled (n = 24 pools of 100). Concentrations of free and total species were measured using online solid phase extraction isotope dilution high performance liquid chromatography tandem mass spectrometry. Concentrations ranged from 2.4 to 71.9 ng/mL for metabolites of di(2-ethylhexyl)phthalate, and from < 0.5 to 775 ng/mL for all other metabolites. Our data suggest that phthalate metabolites concentrations in Australia were at least two times higher than in the United States and Germany; and may be related to legislative differences among countries. DINCH metabolite concentrations were comparatively low and consistent with the limited data available. Ongoing biomonitoring among the general Australian population may help assess temporal trends in exposure and assess the effectiveness of actions aimed at reducing exposures.

Copper Diffusion Barrier Deposition on Integrated Circuit Devices by Atomic Layer Deposition Technique

Transfer from aluminum to copper metallization and decreasing feature size of integrated circuit devices generated a need for new diffusion barrier process. Copper metallization comprised entirely new process flow with new materials such as low-k insulators and etch stoppers, which made the diffusion barrier integration demanding. Atomic Layer Deposition technique was seen as one of the most promising techniques to deposit copper diffusion barrier for future devices. Atomic Layer Deposition technique was utilized to deposit titanium nitride, tungsten nitride, and tungsten nitride carbide diffusion barriers. Titanium nitride was deposited with a conventional process, and also with new in situ reduction process where titanium metal was used as a reducing agent. Tungsten nitride was deposited with a well-known process from tungsten hexafluoride and ammonia, but tungsten nitride carbide as a new material required a new process chemistry. In addition to material properties, the process integration for the copper metallization was studied making compatibility experiments on different surface materials. Based on these studies, titanium nitride and tungsten nitride processes were found to be incompatible with copper metal. However, tungsten nitride carbide film was compatible with copper and exhibited the most promising properties to be integrated for the copper metallization scheme. The process scale-up on 300 mm wafer comprised extensive film uniformity studies, which improved understanding of non-uniformity sources of the ALD growth and the process-specific requirements for the ALD reactor design. Based on these studies, it was discovered that the TiN process from titanium tetrachloride and ammonia required the reactor design of perpendicular flow for successful scale-up. The copper metallization scheme also includes process steps of the copper oxide reduction prior to the barrier deposition and the copper seed deposition prior to the copper metal deposition. Easy and simple copper oxide reduction process was developed, where the substrate was exposed gaseous reducing agent under vacuum and at elevated temperature. Because the reduction was observed efficient enough to reduce thick copper oxide film, the process was considered also as an alternative method to make the copper seed film via copper oxide reduction.

Influence of adhesive non-linearities on the performance and optimal length of adhesive bonded joints

An analytical study for the static strength of adhesive lap joints is presented. The earlier solutions of Volkersen [i], DeBruyne[2] and others were limited to linear adhesives. The influence of adhesive non-linearity was first considered by Grimes' et al[3] and Dickson et al [4]. Recently Hart-Smith[5] successfully introduced elastic-plastic behaviour of the adhesive. In the present study the problem is formulated for general non-linear adhesive behaviour and an efficient numerical algorithm is written for the solution. Bilinear and trilinear models for the nonlinearity yield closed form analytical solutions.

Behaviour of Bi-adhesive Joints

The use of relatively low modulus adhesive at the ends of overlap in a bi-adhesive bondline of a bonded joint can reduce the stress concentration significantly and, therefore, potentially lead to higher strength of the joint. This study presents the two-dimensional and three-dimensional nonlinear (geometric and material) finite element analyses of adhesively bonded single lap joints having modulus-graded bondline under monotonic loading conditions. The adhesives were modelled as an elasto-plastic multi-linear material, while the substrates were regarded as both linear elastic and bi-linear elasto-plastic material. The computational simulations have been performed to investigate the bondline behaviour by studying the stress and strain distributions both at the mid-plane as well as at the interface of the bondline. It has been observed that the static strength is higher for joints with bi-adhesive bondlines compared to those with single adhesives in bondline. Higher joint strength has also been observed for optimum bi-adhesive bondline ratio through parametric studies. Effects of load level, and bondline thickness on stress distribution in the bi-adhesive bondline have also been studied. 3D analysis results reveal the existence of complex multi-axial stress/strain state at the ends of the overlap in the bondline which cannot be observed in 2D plane strain analysis. About 1/3rd of the width of the joint from the free edge in the width direction has 3D stress state, especially in the compliant adhesive of the bondline. Magnitudes of longitudinal and lateral stress/strain components are comparable to peel stress/strain components. It has also been analytically shown that the in-plane global stiffness of the joint remains unaffected by modulus gradation of the bondline adhesive. (C) Koninklijke Brill NV, Leiden, 2010.

Effect of √-irradiation on the structure and dynamics of domains in triglycine selenate

A comparative study of the switching properties of pure and √-irradiated TGSe crystals has been carried out to see the effect of irradiation on the structure and dynamics of domains. The switching behaviour of √-irradiated TGSe has been found to be qualitatively similar to that of unirradiated crystal and this has been interpreted in terms of structural inhibition caused by the formation of radiolysis products as well as the difference between the domain structures of the unirradiated and irradiated samples. Confirmation of this has been obtained by studying the domain patterns using the etch method.

Influence of viscoelastic nature on the intermittent peel-front dynamics of adhesive tape

We investigate the influence of viscoelastic nature of the adhesive on the intermittent peel front dynamics by extending a recently introduced model for peeling of an adhesive tape. As time and rate-dependent deformation of the adhesives are measured in stationary conditions, a crucial step in incorporating the viscoelastic effects applicable to unstable intermittent peel dynamics is the introduction of a dynamization scheme that eliminates the explicit time dependence in terms of dynamical variables. We find contrasting influences of viscoelastic contribution in different regions of tape mass, roller inertia, and pull velocity. As the model acoustic energy dissipated depends on the nature of the peel front and its dynamical evolution, the combined effect of the roller inertia and pull velocity makes the acoustic energy noisier for small tape mass and low-pull velocity while it is burstlike for low-tape mass, intermediate values of the roller inertia and high-pull velocity. The changes are quantified by calculating the largest Lyapunov exponent and analyzing the statistical distributions of the amplitudes and durations of the model acoustic energy signals. Both single and two stage power-law distributions are observed. Scaling relations between the exponents are derived which show that the exponents corresponding to large values of event sizes and durations are completely determined by those for small values. Th scaling relations are found to be satisfied in all cases studied. Interestingly, we find only five types of model acoustic emission signals among multitude of possibilities of the peel front configurations.