Electrodeposition of Ni-B and Ni-Co-B Alloys by Using Boric Acid as Boron Source

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Silver ion release from electrodes of nanotubes of TiO2 impregnated with Ag nanoparticles applied in photoelectrocatalytic disinfection

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Estudo da corrosão em ligas de alumínio utilizadas na indústria aeronáutica

A resistência e o mecanismo de corrosão das ligas de alumínio 2024, 7010, 7050 e 7475 foram estudados em solução de NaCl. Os efeitos do tratamento térmico nas ligas, concentração de oxigênio, pH, adição de oxi-ânions e temperatura do meio constituem algumas das variáveis estudadas. Primeiramente, procedeu-se à caracterização físicoquímica dos materiais através de análise química e metalográfica, mediante microscopia eletrônica de varredura e espectroscopia de energia dispersiva. As ligas 2024, 7010, 7050 e 7475 como recebidas, recozidas e envelhecidas, revelaram a existência de partículas ternárias e quaternárias, constituídas por Al:Cu:Fe e Mg ou Zn. Também foi observado um maior número de partículas pequenas de composição variável situando-se, preferencialmente, nos contornos dos grãos. Os resultados dos ensaios de corrosão em meios aerados e desaerados indicam que o cromato é efetivo como inibidor da corrosão localizada em ambas ligas e que o molibdato somente na liga 7050. O efeito inibidor do tungstato se revela em meio desaerado e é comparativamente menor daquele observado com os outros oxi-ânions. As análises quantitativas de superfície das ligas após os ensaios de imersão indicam que ainda na presença de inibidor, se pites foram nucleados, eles crescem.

Thermal behavior of Ca2+ and Cu2+ oxalates obtained by precipitation in homogeneous solution from dimethyl oxalate hydrolysis

Mixed calcium and copper oxalates, with different proportions of Ca2+ and Cu2+ ions, were precipitated by dimethyl oxalate hydrolysis in homogeneous solution. The compounds were evaluated by means of scanning electron microscopy, energy dispersive X-ray spectroscopy, thermogravimetry (TG), and differential thermal analysis (DTA). The results suggested quantitative precipitation without solid solution formation. From the TG and DTA curves, it was possible to evaluate the Ca2+ ion proportion in the solid phase and to confirm the precipitation of the individual species.

Controlled Synthesis of Layered Sn3O4 Nanobelts by Carbothermal Reduction Method and Their Gas Sensor Properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Processo de reparo ósseo diante de três tipos de superfície de titânio: análise histomorfométrica e por microscopia eletrônica de varredura associada ao EDS: estudo experimental

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Electrical properties of highly conducting Sno2:Sb nanocrystals synthesized using a nonaqueous sol gel method

This work describes the synthesis of highly conducting antimony-doped tin oxide (ATO) nanocrystals prepared via a nonaqueous sol–gel route in the size range of 4–6 nm and provides insights into its electrical properties. The antimony composition was varied from 1 to 18 mol% and the lowest resistivity (4.0 × 10−4Ω·cm) was observed at room temperature in the SnO2:8.8 mol% Sb composition. The samples were evaluated by X-ray diffraction, high-resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy, and scanning electron microscope, and resistivity measurements were taken in the four-probe mode in the temperature range of 13–300 K. The results show highly crystalline nanoparticles in a monodisperse colloidal system, dependence on the shape of ATO nanoparticles as a function of Sb distribution, low resistivity, and semiconductor–metal transition.

SnO2 dense ceramic microwave sintered with low resistivity

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Laser irradiation and thermal treatment inducing selective crystallization in Sb2O3-Sb2S3 glassy films

The influence of both thermal treatment and laser irradiation on the structural and optical properties of films in the Sb 2 O 3 –Sb 2 S 3 system was investigated. The films were prepared by RF-sputtering using glass compositions as raw materials. Irreversible photodarkening effect was observed after exposure the films to a 458nm solid state laser. It is shown, for the first time, the use of holographic technique to measure “in situ”, simultaneously and independently, the phase and amplitude modulations in glassy films. The films were also photo-crystallized and analysed “in situ” using a laser coupled to a micro-Raman equipment. Results showed that Sb 2 S 3 crystalline phase was obtained after irradiation. The effect of thermal annealing on the structure of the films was carried out. Different from the result obtained by irradiation, thermal annealing induces the crystallization of the Sb 2 O 3 phase. Photo and thermal induced effects on films were studied using UV–Vis and Raman spectroscopy, atomic force microscopy (AFM), thermal analysis (DSC), X-ray diffraction, scanning electron microscopy (MEV) and energy-dispersive X-ray spectroscopy (EDX).

Ciprofloxacin Release Using Natural Rubber Latex Membranes as Carrier

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Análise estrutural e bioquímica da hidroxiapatita submetida ao tratamento com fluoreto e polifosfatos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito do trimetafosfato de sódio e do fluoreto sobre a solubilidade da hidroxiapatita: estudo in vitro

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito da administração de alendronato, a longo prazo, sobre as propriedades mecânicas do tecido ósseo, sua reparação e mineralização ao redor de implantes osseointegráveis. Estudo em ratas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of surface treatments on the shear bond strength of luting cements to Y-TZP ceramic

Statement of problem Because zirconia is a glass-free material, alternative surface treatments such as airborne-particle abrasion or silica coating should be used for long-term bonding. However, these surface treatments in combination with different bonding agents and luting cements have not yet been studied. Purpose The purpose of the study was to evaluate the effect of surface treatments on the shear bond strength (SBS) of luting cements to Y-TZP ceramic. Material and methods Zirconia disks (N=240) were airborne-particle abraded with the following particles (n=48): 50 μm Al2O3; 120 μm Al2O3; 30 μm silica-coated Al2O3 (Rocatec Soft); 120 μm Al2O3+110 μm silica-coated Al2O3 (Rocatec Plus); and Rocatec Plus. After silanization of the zirconia surface, composite resin disks were bonded with (n=12) RelyX Luting 2; RelyX ARC; RelyX U100; and Panavia F. The bonded specimens were thermocycled (10 000 cycles) and tested for SBS. Failure mode was determined with a stereomicroscope (×20). The morphology and elemental composition of airborne-particle abraded surfaces were evaluated with scanning electron microscopy (×500) and energy-dispersive x-ray spectroscopy (×50). Results Surface treatments, cements, and their interaction were significant (P<.001). For RelyX ARC, Rocatec Soft and Rocatec Plus provided the highest SBS. In general, surface treatments did not influence the SBS of RelyX U100 and Panavia F. Regardless of the cement, no significant difference was found between 50 μm and 120 μm Al2O3 particles, between Rocatec Soft and Rocatec Plus, or between Rocatec Plus and 120 μm Al2O3 particles+Rocatec Plus. All groups showed adhesive failures. Different particle sizes provided differences in morphological patterns. The elemental composition comprised Al and Al/Si for alumina and silica-abraded zirconia. Conclusions Particle size did not influence the SBS of the groups abraded exclusively with alumina or silica-coated particles. RelyX ARC was more surface-treatment dependent than RelyX U100 or Panavia F.

Mineral Loss and Morphological Changes in Dental Enamel Induced by a 16% Carbamide Peroxide Bleaching Gel

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)