Structural, morphological and optical properties of ZnO thin films grown on gamma-LiAlO2 substrate by pulsed laser deposition

ZnO thin films were deposited on the substrates of (100) gamma-LiAlO2 at 400, 550 and 700 degrees C using pulsed laser deposition (PLD) with the fixed oxygen pressure of 20 Pa, respectively. When the substrate temperature is 400 degrees C, the grain size of the film is less than 1 mu m observed by Leitz microscope and measured by X-ray diffraction (XRD). As the substrate temperature increases to 550 degrees C, highly-preferred c-orientation and high-quality ZnO film can be attained. While the substrate temperature rises to 700 degrees C, more defects appears on the surface of film and the ZnO films become polycrystalline again possibly because more Li of the substrate diffused into the ZnO film at high substrate temperature. The photoluminescence (PL) spectra of ZnO films at room temperature show the blue emission peaks centered at 430 nm. We suggest that the blue emission corresponds to the electron transition from the level of interstitial Zn to the valence band. Meanwhile, the films grown on gamma-LiAlO2 (LAO) exhibit green emission centered at 540 nm, which seemed to be ascribed to excess zinc and/or oxygen vacancy in the ZnO films caused by diffusion of Li. from the substrates into the films during the deposition.

Influence of SiO2 additional layers on the laser induced damage threshold of Ta2O5 films

A series or Ta2O5 films with different SiO2 additional layers including overcoat, undercoat and interlayer was prepared by electron beam evaporation under the same deposition process. Absorption of samples was measured using the surface thermal lensing (STL) technique. The electric field distributions of the samples were theoretical predicted using thin film design software (TFCalc). The laser induced damage threshold (LIDT) was assessed using an Nd:YAG laser operating at 1064 nm with a pulse length of 12 ns. It was found that SiO2 additional layers resulted in a slight increase of the absorption, whereas they exerted little influence on the microdefects. The electric field distribution among the samples was unchanged by adding an SiO2 overcoat and undercoat, yet was changed by adding an interlayer. SiO2 undercoat. The interlayer improved the LIDT greatly, whereas the SiO2 overcoat had little effect on the LIDT. (C) 2007 Elsevier Ltd. All rights reserved.

Optimizing the Curie temperature of pseudo-binary RxR2-x ' Fe-17 (R, R ' = rare earth) for magnetic refrigeration

Several pseudo-binary RxR2-x'Fe-17 alloys (with R = Y, Ce, Pr, Gd and Dy) were synthesized with rhombohedral Th2Zn17-type crystal structure determined from x-ray and neutron powder diffraction. The choice of compositions was done with the aim of tuning the Curie temperature (T-C) in the 270 +/- 20 K temperature range, in order to obtain the maximum magneto-caloric effect around room temperature. The investigated compounds exhibit broad isothermal magnetic entropy changes, Delta S-M(T), with moderate values of the refrigerant capacity, even though the values of Delta S-M(Peak) are relatively low compared with those of the R2Fe17 compounds with R = Pr or Nd. The reduction on the Delta S-M(Peak) is explained in terms of the diminution in the saturation magnetization value. Furthermore, the Delta S-M(T) curves exhibit a similar caret-like behavior, suggesting that the magneto-caloric effect is mainly governed by the Fe-sublattice. A single master curve for Delta S-M/Delta S-M(Peak)(T) under different values of the magnetic field change are obtained for each compound by rescaling of the temperature axis.

Arte medioambiental y ecología. Paradigmas de comprensión, interpretación y valoración de las relaciones entre arte y ecología (1960-2015)

549 pp. (Bibliogr. pp. 501-522) (Conclusiones pp. 467-483/ Conclusions pp. 484-497)

The relationships between fish assemblages and the amount of bottom horizontal beam exposed at California oil platforms: fish habitat preferences at man-made platforms and (by inference) at natural reefs

Between 1995 and 2002, we surveyed fish assemblages at seven oil platforms off southern and central California using the manned research submersible Delta. At each platform, there is a large horizontal beam situated at or near the sea floor. In some instances, shells and sediment have buried this beam and in other instances it is partially or completely exposed. We found that fish species responded in various ways to the amount of exposure of the beam. A few species, such as blackeye goby (Rhinogobiops nicholsii), greenstriped rockfish (Sebastes elongatus), and pink seaperch (Zalembius rosaceus) tended to avoid the beam. However, many species that typically associate with natural rocky outcrops, such as bocaccio (S. paucispinis), cowcod (S. levis), copper (S. caurinus), greenblotched (S. rosenblatti), pinkrose (S. simulator) and vermilion (S. miniatus) rockfishes, were found most often where the beam was exposed. In particular, a group of species (e.g., bocaccio, cowcod, blue (Sebastes mystinus), and vermilion rockfishes) called here the “sheltering habitat” guild, lived primarily where the beam was exposed and formed a crevice. This work demonstrates that the presence of sheltering sites is important in determining the species composition of man-made reefs and, likely, natural reefs. This research also indicates that adding structures that form sheltering sites in and around decommissioned platforms will likely lead to higher densities of many species typical of hard and complex structure.