Tunable KIT-6 mesoporous sulfonic acid catalysts for fatty acid esterification

We report the first catalytic application of pore-expanded KIT-6 propylsulfonic acid (PrSO H) silicas, in fatty acid esterification with methanol under mild conditions. As-synthesized PrSO H-KIT-6 exhibits a 40 and 70% enhancement in turnover frequency (TOF) toward propanoic and hexanoic acid esterification, respectively, over a PrSO H-SBA-15 analogue of similar 5 nm pore diameter, reflecting the improved mesopore interconnectivity of KIT-6 over SBA-15. However, pore accessibility becomes rate-limiting in the esterification of longer chain lauric and palmitic acids over both solid acid catalysts. This problem can be overcome via hydrothermal aging protocols which permit expansion of the KIT-6 mesopore to 7 nm, thereby doubling the TOF for lauric and palmitic acid esterification over that achievable with PrSO H-SBA-15. © 2012 American Chemical Society.

Structure-reactivity correlations in sulphated-zirconia catalysts for the isomerisation of α-pinene

A range of mesoporous sulphated zirconias with tuneable structural and catalytic properties have been prepared by direct impregnation. The surface sulphate coverage can be readily varied, achieving a maximum value of ∼0.2 monolayers. High-temperature calcination induces the crystallisation of tetragonal zirconia while suppressing the monoclinic phase and enhances surface acidity. Superacid sites only appear above a critical threshold SO4 coverage of 0.08 mL (corresponding to 0.44 wt% total S). Sulphated zirconias show good activity towards α-pinene isomerisation of under mild conditions. Conversion correlates with the number Brønsted acid sites, while the selectivity towards mono- versus polycyclic products depends on the corresponding acid site strength; superacidity promotes limonene formation over camphene.

Hydrophenylation of internal alkynes with boronic acids catalysed by a Ni–Zn hydroxy double salt-intercalated anionic rhodium(III) complex

[Rh(OH)6]3− intercalated Ni–Zn mixed basic salt (Rh/NiZn) acts as an efficient catalyst for the hydrophenylation of internal alkynes with arylboronic acids under mild conditions. The turnover number per Rh site approached 740 in the reaction between 4-octyne and phenylboronic acid. The catalytic monomeric Rh(III) complex is stabilised within the NiZn interlayers, attributable to a strong electrostatic interaction, promoting its re-use.

Platinum-catalysed cinnamaldehyde hydrogenation in continuous flow

Platinum is one of the most widely used hydrogenation catalysts. Here we describe the translation of batch reactions to continuous flow, affording tunable C=O versus C=C hydrogenation over a Pt/SiO2 catalyst, resulting in high steady state activity and single-pass yields in the selective hydrogenation of cinnamaldehyde to cinnamyl alcohol under mild conditions. Negligible catalyst deactivation occurs under extended flow operation due to removal of reactively-formed poisons from the reaction zone. Process intensification imparts a four-fold enhancement in cinnamyl alcohol productivity.

Support enhanced α-pinene isomerization over HPW/SBA-15

A family of mesoporous SBA-15 supported H3PW12O40 (HPW) catalysts were synthesized by wet-impregnation and compared with fumed silica analogues for the solventless isomerization of α-pinene under mild conditions. Structural and acidic properties of supported HPW materials were characterized by powder XRD, HRTEM, XPS, TGA, N2 porosimetry, DRIFTS, and ammonia and propylamine chemisorption and TPD. The high area, mesoporous SBA-15 architecture facilitates the formation of highly dispersed (isolated or low dimensional) HPW clusters and concomitant high acid site densities (up to 0.54 mmol g−1) relative to fumed silica wherein large HPW crystallites are formed even at low HPW loadings. α-Pinene exhibits a volcano dependence on HPW loading over the SBA-15 support due to competition between the number and accessibility of acid sites to the non-polar reactant, with the superior acid site accessibility for HPW/SBA-15 conferring a 10-fold rate enhancement with respect to HPW/fumed silica and pure HPW. Monocyclic limonene and terpinolene products are favoured over polycyclic camphene and β-pinene by weaker polyoxometallate analogues over SBA-15.

Detemplation of soft mesoporous silica nanoparticles with structural preservation

A mild protocol that allows the template removal of soft un-aged silica nanoparticles was investigated. After oxidizing the organic template by Fenton chemistry, a good structural preservation is only achieved when the material is equilibrated and dried in a low-surface tension solvent. This avoids excessive capillary stress induced by the high surface tension of water, a major component in the Fenton reaction medium. The Fenton reaction should be carried out under mild conditions as well; otherwise the sample deteriorates by extensive hydrolysis, and capillary stress, and the structural ordering diminishes severely. We propose employing 10 ppm Fe concentration at 70 °C for 24 h for the cetyltrimethylammonium bromide template. The proposed protocol involves 2 steps resulting in an overall significantly higher pore volume attributed to the wider pores and limited particle agglomeration, while the calcined counterpart evidences aggregation and loss of the hexagonal ordering. n-BuOH exchange is unnecessary when the mesophase is stabilized by ageing, as the structure resists the water capillary stress. © The Royal Society of Chemistry 2013.

Asymmetric syntheses of analogs of kainic acid

Kainic acid has been used for nearly 50 years as a tool in neuroscience due to its pronounced neuroexcitatory properties. However, the significant price increase of kainic acid resulting from the disruption in the supply from its natural source, the alga Digenea Simplex, as well as inefficient synthesis of kainic acid, call for the exploration of functional mimics of kainic acid that can be synthesized in a simpler way. Aza kainoids analog could be one of them. The unsubstituted aza analog of kainoids has demonstrates its ability as an ionotropic glutamate receptor agonist and showed affinity in the chloride dependent glutamate (GluCl) binding site. This opened a question of the importance of the presence of one nitrogen or both nitrogens in the aza kainoid analogs for binding to glutamate receptors. Therefore, two different pyrrolidine analogs of kainic acid, trans -4-(carboxymethyl)pyrrolidine-3-carboxylic acid and trans -2-carboxy-3-pyrrolidineacetic acid, were synthesized through multi-step sequences. The lack of the affinity of both pyrrolidine analogs in GluCl binding site indicated that both nitrogens in aza kainoid analogs are involved in hydrogen bonding with receptors, significantly enhancing their affinity in GluCl binding site. Another potential functional mimic of kainic acid is isoxazolidine analogs of kainoids whose skeleton can be constituted directly via a 1, 3 dipolar cycloaddition as the key step. The difficulty in synthesizing N-unsubstituted isoxazolidines when applying such common protecting groups as alkyl, phenyl and benzyl groups, and the requirement of a desired enantioselectivity due to the three chiral ceneters in kainic acid, pose great challenges. Hence, several different protected nitrones were studied to establish that diphenylmethine nitrone may be a good candidate as the dipole in that the generated isoxazolidines can be deprotected in mild conditions with high yields. Our investigations also indicated that the exo/endo selectivity of the 1, 3 dipolar cycloaddition can be controlled by Lewis acids, and that the application of a directing group in dipolarophiles can accomplish a satisfied enantioselectivity. Those results demonstrated the synthesis of isoxazoldines analogs of kainic acid is very promising.

Dinocyst assemblages of site HM52-43

Past sea-surface conditions over the northern North Atlantic during the last glacial maximum were examined from the study of 61 deep-sea cores. The last glacial maximum time slice studied here corresponds to an interval between Heinrich layers H2 and H1, and spanning about 20-16 ka on a 14C time scale. Transfer functions based on dinocyst assemblages were used to reconstruct sea-surface temperature, salinity, and sea-ice cover. The results illustrate extensive sea-ice cover along the eastern Canadian margins and sea-ice spreading, only during winter, over most of the northern North Atlantic. On the whole, much colder winter prevailed, despite relatively mild conditions in August (10-15°C at most offshore sites), thus suggesting a larger seasonal contrast of temperatures than today. Lower salinity than at present is reconstructed, especially along the eastern Canadian and Scandinavian margins, likely because of meltwater supply from the surrounding ice sheets. These reconstructions contrast with those established by CLIMAP on the basis of planktonic foraminifera. These differences are discussed with reference to the stratigraphical frame of the last glacial maximum, which was not the coldest phase of the last glacial stage. The respective significance of dinocyst and foraminifer records is also examined in terms of the thermohaline characteristics of surface waters and the vertical structure of upper water masses, which was apparently much more stratified than at present in the northern North Atlantic, thus preventing deep-water formation.

Synthesis of nucleoside phosphoroselenolates via the efficient Michaelis-Arbuzov reaction of selenocyanates

The Michaelis-Arbuzov reactions of benzylselenocyanate and 5′-deoxythymidine-5′-selenocyanate with thymidine H-phosphonate proceeded rapidly in the presence of a neutral silylating agent and 2,6-lutidine to give the corresponding Se-alkyl phosphoroselenolate triesters. Deprotection under mild conditions enabled the isolation of phosphoroselenolate diesters which were fully characterised.

Catalytic reactions with palladium supported on mesocellular foam : Applications in hydrogenation, isomerization, and C-C bond forming reactions

The major part of this thesis concerns the development of catalytic methodologies based on palladium nanoparticles immobilized on aminopropyl-functionalized siliceous mesocellular foam (Pd0-AmP-MCF). The catalytic activity of the precursor to the nanocatalyst, PdII-AmP-MCF is also covered by this work. In the first part the application of Pd0-AmP-MCF in Suzuki-Miyaura cross-coupling reactions and transfer hydrogenation of alkenes under microwave irradiation is described. Excellent reactivity was observed and a broad range of substrates were tolerated for both transformations. The Pd0-AmP-MCF exhibited high recyclability as well as low metal leaching in both cases. The aim of the second part was to evaluate the catalytic efficiency of the closely related PdII-AmP-MCF for cycloisomerization of various acetylenic acids. The catalyst was able to promote formation of lactones under mild conditions using catalyst loadings of 0.3 - 0.5 mol% at temperatures of up to 50 oC in the presence of Et3N. By adding 1,4-benzoquinone to the reaction, the catalyst could be recycled four times without any observable decrease in the activity. The selective arylation of indoles at the C-2 position using Pd-AmP-MCF and symmetric diaryliodonium salts is presented in the third part. These studies revealed that Pd0-AmP-MCF was more effective than PdII-AmP-MCF for this transformation. Variously substituted indoles as well as diaryliodonium salts were tolerated, giving arylated indoles in high yields within 15 h at 20 - 50 oC in H2O. Only very small amounts of Pd leaching were observed and in this case the catalyst exhibited moderate recyclability. The final part of the thesis describes the selective hydrogenation of the C=C in different α,β-unsaturated systems. The double bond was efficiently hydrogenated in high yields both under batch and continuous-flow conditions. High recyclability and low metal leaching were observed in both cases.

Sustainable Catalysis : Rational Pd Loading on MIL-101Cr-NH2 for More Efficient and Recyclable Suzuki-Miyaura Reactions

Palladium nanoparticles have been immobilized into an amino-functionalized metal-organic framework (MOF), MIL-101Cr-NH2, to form Pd@MIL-101Cr-NH2. Four materials with different loadings of palladium have been prepared (denoted as 4-, 8-, 12-, and 16wt%Pd@MIL-101Cr-NH2). The effects of catalyst loading and the size and distribution of the Pd nanoparticles on the catalytic performance have been studied. The catalysts were characterized by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier-transform infrared (FTIR) spectroscopy, powder X-ray diffraction (PXRD), N-2-sorption isotherms, elemental analysis, and thermogravimetric analysis (TGA). To better characterize the palladium nanoparticles and their distribution in MIL-101Cr-NH2, electron tomography was employed to reconstruct the 3D volume of 8wt%Pd@MIL-101Cr-NH2 particles. The pair distribution functions (PDFs) of the samples were extracted from total scattering experiments using high-energy X-rays (60keV). The catalytic activity of the four MOF materials with different loadings of palladium nanoparticles was studied in the Suzuki-Miyaura cross-coupling reaction. The best catalytic performance was obtained with the MOF that contained 8wt% palladium nanoparticles. The metallic palladium nanoparticles were homogeneously distributed, with an average size of 2.6nm. Excellent yields were obtained for a wide scope of substrates under remarkably mild conditions (water, aerobic conditions, room temperature, catalyst loading as low as 0.15mol%). The material can be recycled at least 10times without alteration of its catalytic properties.

Aroylhydrazone Cu(II) complexes in keto form: structural characterization and catalytic cctivity towards cyclohexane oxidation

The reaction of the Schiff base (3,5-di-tert-butyl-2-hydroxybenzylidene)-2-hydroxybenzohydrazide (H3L) with a copper(II) salt of a base of a strong acid, i.e., nitrate, chloride or sulphate, yielded the mononuclear complexes [Cu(H2L)(NO3)(H2O)] (1), [Cu(H2L)Cl]center dot 2MeOH (2) and the binuclear complex [{Cu(H2L)}(2)(mu-SO4)]center dot 2MeOH (3), respectively, with H2L- in the keto form. Compounds 1-3 were characterized by elemental analysis, Infrared (IR) spectroscopy, Electrospray Ionisation-Mass Spectrometry (ESI-MS) and single crystal X-ray crystallography. All compounds act as efficient catalysts towards the peroxidative oxidation of cyclohexane to cyclohexyl hydroperoxide, cyclohexanol and cyclohexanone, under mild conditions. In the presence of an acid promoter, overall yields (based on the alkane) up to 25% and a turnover number (TON) of 250 (TOF of 42 h(-1)) after 6 h, were achieved.

Purificação de C-ficocianina e sua incorporação em nanofibras

C-ficocianina (C-FC) é uma ficobiliproteína, de cor natural azul, com diversas aplicações na indústria alimentícia, farmacêutica e biomédica, dependendo do seu grau específico de pureza, que pode variar de 0,7 a 4,0, com respectivo aumento de seu valor comercial. Essa pureza é alcançada através de diversas técnicas de purificação, que podem ser aplicadas em diferentes sequências. Um destes processos de purificação de proteínas baseia-se na cromatografia de troca iônica, que utiliza trocadores que adsorvem as proteínas como resultado de interações iônicas entre a superfície da proteína e o trocador. Resinas e colunas de leito expandido podem ser utilizadas para aumentar a produtividade dessa técnica. É fundamental conhecer o perfil do processo de adsorção, para melhor aplicá-lo como ferramenta para o design e otimização de parâmetros operacionais. Outra tecnologia para o tratamento de biomoléculas é a ultrafiltração. Esta técnica é aplicável em larga escala, apresenta baixa complexidade de aplicação e pode ser realizada em condições brandas, minimizando o dano para o produto. Para aumentar a estabilidade da C-FC, e facilitar a sua aplicação, podem ser avaliadas técnicas recentes, não exploradas para este fim, como as nanofibras obtidas através do processo de electrospinning. Estas fibras possuem uma área superficial específica extremamente elevada devido a seu pequeno diâmetro. O objetivo deste trabalho foi avaliar parâmetros de adsorção e diferentes técnicas para purificação de C-ficocianina de Spirulina platensis e obter nanofibras poliméricas incorporadas de C-ficocianina. O trabalho foi dividido em quatro artigos. No primeiro artigo, foram avaliados os parâmetros e as isotermas de adsorção de C-ficocianina em resina de troca iônica para leito expandido Streamline® DEAE. Verificou-se que o maior coeficiente de partição foi obtido em pH 7,5, nas temperaturas de 15 e 25 °C. As isotermas de adsorção da Cficocianina foram bem representadas pelos modelos de Langmuir, de Freundlich e de Langmuir-Freundlich, sendo os valores estimados para Qm e Kd obtidos pela isoterma de Langmuir foram, respectivamente, 33,92 mg.mL-1 e 0,123 mg.mL-1, respectivamente. No segundo artigo foi avaliada a purificação de C-FC até grau alimentar, utilizando ultrafiltração (UF). Com a membrana de 50 kDa, identificou-se que somente a temperatura e a aplicação de diferentes ciclos de diafiltração (DF) causaram influência significativa sobre a purificação e recuperação da C-ficocianina. Foram então aplicados o aumento gradativo da quantidade de ciclos, e a diafiltração previamente à ultrafiltração (DF/UF), onde obteve-se um extrato de Cficocianina com pureza de 0,95. No terceiro artigo foram propostos processos de purificação, envolvendo a utilização das diferentes técnicas para obtenção de C-FC com diferentes purezas. Determinou-se que a partir de cromatografia de troca iônica em leito fixo seguido de DF/UF, obtém-se C-FC para uso em cosméticos e a partir de precipitação com sulfato de amônio, e DF/UF obtém-se C-FC para uso em biomarcadores. Com uma sequência de precipitação com sulfato de amônio, DF/UF e cromatografia de troca iônica em leito fixo chega-se a C-FC de grau analítico. No último artigo, C-FC foi incorporada a nanofibras de óxido de polietileno (PEO) através de processo de electrospinning. Foram determinadas a condutividade da solução de C-FC/PEO, a estrutura e comportamento termogravimétrico das nanofibras formadas. Soluções de polímeros com concentração de 6 e 8% proporcionaram a formação de nanofibras com diâmetro médio inferior a 800 nm, homogêneas, sem a presença de gotas. A análise termogravimétrica identificou aumento na resistência térmica da C-FC incorporada nas fibras.

Sustained release of TGF-β1 from biodegradable microparticles prepared by a new green process in CO2 medium

International audience

Degradação de Ocratoxina a: estudo de processo e toxicidade

A ocratoxina A (OTA), micotoxina encontrada em diferentes níveis e em diversas matrizes, apresenta efeitos carcinogênicos, nefrotóxicos e teratogênicos. O desenvolvimento de métodos capazes de diminuir esta contaminação a níveis permitidos pela legislação é incentivado e os processos biológicos utilizados envolvem o uso de enzimas e/ou microrganismos para degradação da OTA e são preferenciais pela especificidade, bem como pelas condições brandas para a detoxificação. O objetivo do trabalho foi estudar a ação de carboxipeptidase A nos níveis e na toxicidade de OTA, visando aplicar a técnica para detoxificar farinhas de trigo. Primeiramente foi estimado o risco de exposição à ocratoxina A pelo consumo de farinhas de trigo. Para isso foram estabelecidas condições de determinação de OTA em farinhas de trigo, empregando técnicas de estatística multivariada para definir os principais interferentes na extração de OTA pelo método de QuEChERS e detecção em CLAE-FL. O método validado permitiu a avaliação da ocorrência natural em 20 amostras de farinha de trigo, estando estas contaminadas na faixa de 0,22 a 0,85 µg.kg-1 , apresentando um valor de ingestão diária de 0,08 ngOTA.dia-1 .kgmassacorpórea -1 e uma disponibilidade de 94,4%. Em seguida foi realizada a padronização da extração de carboxipeptidase A em biomassa de Rhizopus oryzae que consistiu em agitação ultrassônica durante 30 minutos numa potencia fixa de 150 W e 40 kHz e a triagem de agentes biológicos para degradação de OTA. Para o estudo da degradação in vitro de OTA, método de extração e detecção de OTA e OTα em CLAEFL foi validado e o processo de degradação foi realizado com Rhizopus oryzae e Trichoderma reesei, obtendo-se uma redução máxima de 63,5% e 57,7%, respectivamente. A degradação apresentou uma correlação alta (R>0,9) e significativa (p<0,05) com a produção de Otα, indicando que ocorreu a produção de enzimas capazes de hidrolisar a micotoxina, por exemplo, a carboxipeptidase A. O estudo da toxicidade de OTA e seu metabólito OTα foi realizado em neutrófilos humanos, onde foi observado a ausência de efeito tóxico de OTα. Também foi determinado o mecanismo de toxicidade de OTA pelo aumento de Ca2+ intracelular pela liberação a partir das reservas internas. Esta liberação, subsequentemente, provoca uma cascata de eventos, nomeadamente: a produção de espécies reativas, depleção de ATP, perda de ΔΨm, levando à morte por necrose. Para reduzir o risco de exposição à micotoxina pela ingestão de matéria prima contaminada, carboxipeptidase A extraída de diferentes fontes foi aplicada na hidrólise de OTA em farinha de trigo para posterior determinação do conteúdo residual de OTA e OTα, empregando método validado. O estudo mostrou uma redução de OTA entre 16,8 e 78,5% e produção de OTα entre 2 a 8,2 ng.g-1 . As carboxipeptidases mais promissoras para degradação foram as provenientes de Rhizopus e Trichoderma e a carboxipeptidase comercial. Ficou demonstrado que se pode recomendar a aplicação de enzimas proteolíticas, tipo carboxipeptidase, para reduzir o risco de exposição à micotoxina quando utilizada matéria prima contaminada, por exemplo, farinha de trigo para diferentes processos. A transformação de OTA para OTα e seus efeitos na redução da toxicidade da micotoxina corroboram com esta afirmação.