Thin film deposition and characterization of pure and iron-doped electron-beam evaporated tungsten oxide for gas sensors

Pure Tungsten Oxide (WO3) and Iron-doped (10 at%) Tungsten Oxide (WO3:Fe) nanostructured thin films were prepared using a dual crucible Electron Beam Evaporation techniques. The films were deposited at room temperature in high vacuum condition on glass substrate and post-heat treated at 300 oC for 1 hour. From the study of X-ray diffraction and Raman the characteristics of the as-deposited WO3 and WO3:Fe films indicated non-crystalline nature. The surface roughness of all the films showed in the order of 2.5 nm as observed using Atomic Force Microscopy (AFM). X-Ray Photoelectron Spectroscopy (XPS) analysis revealed tungsten oxide films with stoichiometry close to WO3. The addition of Fe to WO3 produced a smaller particle size and lower porosity as observed using Transmission Electron Microscopy (TEM). A slight difference in optical band gap energies of 3.22 eV and 3.12 eV were found between the as-deposited WO3 and WO3:Fe films, respectively. However, the difference in the band gap energies of the annealed films were significantly higher having values of 3.12 eV and 2.61 eV for the WO3 and WO3:Fe films, respectively. The heat treated samples were investigated for gas sensing applications using noise spectroscopy and doping of Fe to WO3 reduced the sensitivity to certain gasses. Detailed study of the WO3 and WO3:Fe films gas sensing properties is the subject of another paper.

The rate-limiting mechanism for the heterogeneous burning of cylindrical iron rods

This paper presents the findings of an investigation into the rate-limiting mechanism for the heterogeneous burning in oxygen under normal gravity and microgravity of cylindrical iron rods. The original objective of the work was to determine why the observed melting rate for burning 3.2-mm diameter iron rods is significantly higher in microgravity than in normal gravity. This work, however, also provided fundamental insight into the rate-limiting mechanism for heterogeneous burning. The paper includes a summary of normal-gravity and microgravity experimental results, heat transfer analysis and post-test microanalysis of quenched samples. These results are then used to show that heat transfer across the solid/liquid interface is the rate-limiting mechanism for melting and burning, limited by the interfacial surface area between the molten drop and solid rod. In normal gravity, the work improves the understanding of trends reported during standard flammability testing for metallic materials, such as variations in melting rates between test specimens with the same cross-sectional area but different crosssectional shape. The work also provides insight into the effects of configuration and orientation, leading to an improved application of standard test results in the design of oxygen system components. For microgravity applications, the work enables the development of improved methods for lower cost metallic material flammability testing programs. In these ways, the work provides fundamental insight into the heterogeneous burning process and contributes to improved fire safety for oxygen systems in applications involving both normal-gravity and microgravity environments.

Low-dimensional hydrogen-bonded structures in the 1:1 and 1:2 proton-transfer compounds of 4,5-dichlorophthalic acid with the aliphatic Lewis bases triethylamine, diethylamine, n-butylamine and piperidine

The structures of proton-transfer compounds of 4,5-dichlorophthalic acid (DCPA) with the aliphatic Lewis bases triethylamine, diethylamine, n-butylamine and piperidine, namely triethylaminium 2-carboxy-4,5-dichlorobenzoate C~6~H~16~N^+^ C~8~H~3~Cl~2~O~4~^-^ (I), diethylaminium 2-carboxy-4,5-dichlorobenzoate C~4~H~12~N^+^ C~8~H~3~Cl~2~O~4~^-^ (II), bis(n-butylaminium) 4,5-dichlorophthalate monohydrate 2(C~4~H~12~N^+^) C~8~H~2~Cl~2~O~4~^2-^ . H~2~O (III) and bis(piperidinium) 4,5-dichlorophthalate monohydrate 2(C~5~H~12~N^+^) C~8~H~2~Cl~2~O~4~^2-^ . H~2~O (IV)have been determined at 200 K. All compounds have hydrogen-bonding associations giving in (I) discrete cation-anion units, linear chains in (II) while (III) and (IV) both have two-dimensional structures. In (I) a discrete cation-anion unit is formed through an asymmetric R2/1(4) N+-H...O,O' hydrogen-bonding association whereas in (II), one-dimensional chains are formed through linear N-H...O associations by both aminium H donors. In compounds (III) and (IV) the primary N-H...O linked cation-anion units are extended into a two-dimensional sheet structure via amide N-H...O(carboxyl) and ...O(carbonyl) interactions. In the 1:1 salts [(I) and (II)], the hydrogen 4,5-dichlorophthalate anions are essentially planar with short intramolecular carboxylic acid O-H...O(carboxyl) hydrogen bonds [O...O, 2.4223(14) and 2.388(2)A respectively]. This work provides a further example of the uncommon zero-dimensional hydrogen-bonded DCPA-Lewis base salt and the one-dimensional chain structure type, while even with the hydrate structures of the 1:2 salts with the primary and secondary amines, the low dimensionality generally associated with 1:1 DCPA salts is also found.

Testing for the non-separability of bi-ambiguous compounds

Separability is a concept that is very difficult to define, and yet much of our scientific method is implicitly based upon the assumption that systems can sensibly be reduced to a set of interacting components. This paper examines the notion of separability in the creation of bi-ambiguous compounds that is based upon the CHSH and CH inequalities. It reports results of an experiment showing that violations of the CHSH and CH inequality can occur in human conceptual combination.

Metal Contaminants in Leachate from Sanitary Landfills

The uncontrolled disposal of solid wastes poses an immediate threat to public health and a long term threat to the environmental well being of future generations. Solid waste is waste resulting from human activities that is solid and unwanted (Peavy et al., 1985). If unmanaged, dumped solid wastes generate liquid and gaseous emissions that are detrimental to the environment. This can lead to a serious form of contamination known as metal contamination, which poses a risk to human health and ecosystems. For example, some heavy metals (cadmium, chromium compounds, and nickel tetracarbonyl) are known to be highly toxic, and are aggressive at elevated concentrations. Iron, copper, and manganese can cause staining, and aluminium causes depositions and discolorations. In addition, calcium and magnesium cause hardness in water causing scale deposition and scum formation. Though not a metal but a metalloid, arsenic is poisonous at relatively high concentrations and when diluted at low concentrations causes skin cancer. Normally, metal contaminants are found in a dissolved form in the liquid percolating through landfills. Because average metal concentrations from full-scale landfills, test cells, and laboratory studies have tended to be generally low, metal contamination originating from landfills is not generally considered a major concern (Kjeldsen et al., 2002; Christensen et al., 1999). However, a number of factors make it necessary to take a closer look at metal contaminants from landfills. One of these factors relates to variability. Landfill leachate can have different qualities depending on the weather and operating conditions. Therefore, at one moment in time, metal contaminant concentrations may be quite low, but at a later time these concentrations could be quite high. Also, these conditions relate to the amount of leachate that is being generated. Another factor is biodiversity. It cannot be assumed that a particular metal contaminant is harmless to flora and fauna (including micro organisms) just because it is harmless to human health. This has significant implications for ecosystems and the environment. Finally, there is the moral factor. Because uncertainty surrounds the potential effects of metal contamination, it is appropriate to take precautions to prevent it from taking place. Consequently, it is necessary to have good scientific knowledge (empirically supported) to adequately understand the extent of the problem and improve the way waste is being disposed of

Iron burning in pressurised oxygen under microgravity conditions

An investigation of cylindrical iron rods burning in pressurised oxygen under microgravity conditions is presented. It has been shown that, under similar experimental conditions, the melting rate of a burning, cylindrical iron rod is higher in microgravity than in normal gravity by a factor of 1.8 ± 0.3. This paper presents microanalysis of quenched samples obtained in a microgravity environment in a 2.0 s duration drop tower facility in Brisbane, Australia. These images indicate that the solid/liquid interface is highly convex in reduced gravity, compared to the planar geometry typically observed in normal gravity, which increases the contact area between liquid and solid phases by a factor of 1.7 ± 0.1. Thus, there is good agreement between the proportional increase in solid/liquid interface surface area and melting rate in microgravity. This indicates that the cause of the increased melting rates for cylindrical iron rods burning in microgravity is altered interfacial geometry at the solid/liquid interface.

Anhydrous 1:1 proton-transfer compounds of isonipecotamide with picric acid and 3,5-dinitrosalicylic acid: 4-carbamoylpiperidinium 2,4,6-trinitrophenolate and two polymorphs of 4-carbamoylpiperidinium 2-carboxy-4,6-dinitrophenolate

The structures of the anhydrous 1:1 proton-transfer compounds of isonipecotamide (4-carbamoylpiperidine) with picric acid and 3,5-dinitrosalicylic acid, namely 4-carbamoylpiperidinium 2,4,6-trinitrophenolate, C6H13N2O8+ C6H2N3O7- (I) and 4-carbamoylpiperidinium 2-carboxy-4,6-dinitrophenolate, C6H13N2O8+ C7H3N2O7-: two forms, the monoclinic alpha-polymorph (II) and the triclinic beta-polymorph (III) have been determined at 200 K. All compounds form hydrogen-bonded structures, one-dimensional in (II), two-dimensional in (I) and three-dimensional in (III). In (I), the cations form centrosymmetric cyclic head-to-tail hydrogen-bonded homodimers [graph set R2/2(14)] through lateral duplex piperidinium N---H...O(amide) interactions. These dimers are extended into a two-dimensional network structure through further interactions with anion phenolate-O and nitro-O acceptors, including a direct symmetric piperidinium N-H...O(phenol),O(nitro) cation--anion association [graph set R2/1(6)]. The monoclinic polymorph (II) has a similar R2/1(6) cation-anion hydrogen-bonding interaction to (I) but with an additional conjoint symmetrical R1/2(4) interaction as well as head-to-tail piperidinium N-H...O(amide) O hydrogen bonds and amide N-H...O(carboxyl) hydrogen bonds, give a network structure which include large R3/4(20) rings. The hydrogen bonding in the triclinic polymorph (III) is markedly different from that of monoclinic (II). The asymmetric unit contains two independent cation-anion pairs which associate through cyclic piperidinium N-H...O,O'(carboxyl) interactions [graph set R2/1(4)]. The cations also show the zig-zag head-to-tail piperidinium N-H...O(amide) hydrogen-bonded chain substructures found in (II) but in addition feature amide N-H...O(nitro) and O(phenolate) and amide N-H...O(nitro) associations. As well there is a centrosymmetric double-amide N-H...O(carboxyl) bridged bis(cation-anion) ring system [graph set R2/4(8)] in the three-dimensional framework. The structures reported here demonstrate the utility of the isonipecotamide cation as a synthon with previously unrecognized potential for structure assembly applications. Furthermore, the structures of the two polymorphic 3,5-dinitrosalicylic acid salts show an unusual dissimilarity in hydrogen-bonding characteristics, considering that both were obtained from identical solvent systems.

Hydrogen bonding in the anhydrous 1:1 proton-transfer compounds of isonipecotamide with nitro-substituted benzoic acids: the salts of the three isomeric mononitrobenzoic acids and of 3,5-dinitrobenzoic acid

The structures of the anhydrous 1:1 proton-transfer compounds of isonipecotamide (piperidine-4-carboxamide) with the three isomeric mononitro-substituted benzoic acids and 3,5-dinitrobenzoic acid, namely 4-carbamoylpiperidinium 2-nitrobenzoate (I), 4-carbamoylpiperidinium 3-nitrobenzoate (II), 4-carbamoylpiperidinium 4-nitrobenzoate (III), (C6H13N2O+ C7H4NO4-) and 4-carbamoylpiperidinium 3,5-dinitrobenzoate (IV) (C6H13N2O+ C7H5N2O6-)respectively, have been determined at 200 K. All salts form hydrogen-bonded structures: three-dimensional in (I), two-dimensional in (II) and (III) and one-dimensional in (IV). Featured in the hydrogen bonding of three of these [(I), (II) and (IV)] is the cyclic head-to-head amide--amide homodimer motif [graph set R2/2~(8)] through a duplex N---H...O association, the dimer then giving structure extension via either piperidinium or amide H-donors and carboxylate-O and in some examples [(II) and (IV)], nitro-O atom acceptors. In (I), the centrosymmetric amide-amide homodimers are expanded laterally through N-H...O hydrogen bonds via cyclic R2/4(8) interactions forming ribbons which extend along the c cell direction. These ribbons incorporate the 2-nitrobenzoate cations through centrosymmetric cyclic piperidine N-H...O(carboxyl) associations [graph set R4/4(12)], giving inter-connected sheets in the three-dimensional structure. In (II) in which no amide-amide homodimer is present, duplex piperidinium N-H...O(amide) hydrogen-bonding homomolecular associations [graph set R2/2(14)] give centrosymmetric head-to-tail dimers. Structure extension occurs through hydrogen-bonding associations between both the amide H-donors and carboxyl and nitro O-acceptors as well as a three-centre piperidinium N-H...O,O'(carboxyl) cyclic R2/1(4) association giving the two-dimensional network structure. In (III), the centrosymmetric amide-amide dimers are linked through the two carboxyl O-atom acceptors of the anions via bridging piperidinium and amide N-H...O,O'...H-N(amide) hydrogen bonds giving the two-dimensional sheet structure which features centrosymmetric cyclic R4/4(12) associations. In (IV), the amide-amide dimer is also centrosymmetric with the dimers linked to the anions through amide N-H...O(nitro) interactions. The piperidinium groups extend the structure into one-dimensional ribbons via N-H...O(carboxyl) hydrogen bonds. The structures reported here further demonstrate the utility of the isonipecotamide cation in molecular assembly and highlight the efficacy of the cyclic R2/2(8) amide-amide hydrogen-bonding homodimer motif in this process and provide an additional homodimer motif type in the head-to-tail R2/2(14) association.

Hydrogen bonding in proton-transfer compounds of 5-sulfosalicylic acid with a series of aliphatic nitrogen Lewis bases

The crystal structures of the proton-transfer compounds of 5-sulfosalicylic acid (3-carboxy-4-hydroxybenzenesulfonic acid) with the aliphatic nitrogen Lewis bases, hydroxylamine, triethylamine, pyrrolidine, morpholine, N-methylmorpholine and piperazine, viz. hydroxyammonium 3-carboxy-4-hydroxybenzenesulfonate (1), triethylaminium 3-carboxy-4-hydroxybenzenesulfonate (2), pyrrolidinium 3-carboxy-4-hydroxybenzenesulfonate monohydrate (3), morpholinium 3-carboxy-4-hydroxybenzenesulfonate monohydrate (4), N-methylmorpholinium 3-carboxy-4-hydroxybenzenesulfonate monohydrate (5) and piperazine-1,4-diium bis(3-carboxy-4-hydroxybenzenesulfonate) hexahydrate (6) have been determined and their comparative structural features and hydrogen-bonding patterns described. Crystals of 4 are triclinic, space group P-1 while the remainder are monoclinic with space group either P21/c (1 - 3) or P21/n (5, 6). Unit cell dimensions and contents are: for 1, a = 5.0156(3), b = 10.5738(6), c = 18.4785(9) Å, β = 96.412(5)o, Z = 4; for 2, a = 8.4998(4), b = 12.3832(6), c = 15.4875(9) Å, β = 102.411(5)o, Z = 4; for 3, a = 6.8755(2), b = 15.5217(4), c = 12.8335(3) Å, β = 92.074(2)o, Z = 4; for 4, a = 6.8397(2), b = 12.9756(5), c = 15.8216(6) Å, α = 90.833(3), β = 95.949(3), γ = 92.505(3)o, Z = 4; for 5, a = 7.0529(3), b = 13.8487(7), c = 15.6448(6) Å, β = 90.190(6)o, Z = 4; for 6, a = 7.0561(2), b = 15.9311(4), c = 12.2102(3) Å, β = 100.858(3)o, Z = 2. The hydrogen bonding generates structures which are either two-dimensional (2 and 5) or three-dimensional (1, 3, 4 and 6). Compound 6 represents the third reported structure of a salt of 5-sulfosalicylic acid having a dicationic piperazine species.