Formation of Au nanoparticles in sapphire by using Ar ion implantation and thermal annealing

In this paper, we present results of the synthesis of gold nanoclusters in sapphire, using Ar ion implantation and annealing in air. Unlike the conventional method of Au implantation followed by thermal annealing, Au was deposited on the surface of m- and a- cut sapphire single crystal samples including those pre-implanted with Ar ions. Au atoms were brought into the substrate by subsequent implantation of Ar ions to form Au nanoparticles. Samples were finally annealed stepwisely in air at temperatures ranging from 400 to 800 C and then studied using UV–vis absorption spectrometry, transmission electron microscopy and Rutherford backscattered spectrometry. Evidence of the formation Au nanoparticles...

The annealing behavior of Cu nanoparticles in Ar-ion implanted spinel

Magnesium aluminate spinel crystals (MgAl2O4 (1 1 0)) deposited with 30 nm Cu film on surface were implanted with 110 key Ar-ions to a fluence of 1.0 x 10(17) ions/cm(2) at 350 degrees C, and then annealed in vacuum condition at the temperature of 500, 600, 700, 800 and 900 degrees C for 1 h, respectively. Ultraviolet-visible spectrometry (UV-VIS), scanning electron microscopy (SEM), Rutherford backscattering (RBS) and transmission electron microscopy (TEM) were adopted to analyze the specimens. After implantation, the appearance of surface plasmon resonance (SPR) absorbance peak in the UV-VIS spectrum indicated the formation of Cu nanoparticles, and the TEM results for 500 degrees C also confirmed the formation of Cu nanoparticles at near-surface region. In annealing process, The SPR absorbance intensity increased at 500 and 700 degrees C, decreased with a blue shift of the peak position at 600 and 800 degrees C, and the peak disappeared at 900 degrees C. The SPR absorbance intensity evolution with temperature was discussed combined with other measurement results (RBS, SEM and TEM). (C) 2010 Elsevier B.V. All rights reserved.

Heavy Metals in Soil and Crops of an Intensively Farmed Area: A Case Study in Yucheng City, Shandong Province, China

lThe study was supported by the Knowledge Innovation Foundation of the institute of Geographical Sciences and Natural Resource, Chinese Academy of Sciences (Grant No. 200906002) and Key Directional Project of Knowledge Innovation of Chinese Academy of Sciences (Grant No. KSCX2-YW-N-46-01). The authors would like to thank to Luke Driskell for his kind help and hard work on English language polishing of the article.

Effects of soil pH and organic matter on distribution of thorium fractions in soil contaminated by rare-earth industries

The labilities of thorium fractions including mobility and bioavailability vary significantly with soil properties. The effects of soil pH and soil organic matter on the distribution and transfer of thorium fractions defined by a sequential extraction procedure were investigated. Decrease of soil pH could enhance the phytoavailability and the potential availability of thorium in soil. Increase of organic matter reduced the phytoavailability of thorium, but enhanced the potential availability of it.

Selective hydrogenation of citral catalyzed with palladium nanoparticles in CO2-in-water emulsion

CO2-in-Water (C/W) emulsion was formed by using a nonionic surfactant of poly (ethylene oxide)-poly (propylene oxide)-poly (ethylene oxide) (P123), and palladium nanoparticles were synthesized in situ in the present work. The catalytic performance of Pd nanoparticles in the C/W emulsion has been discussed for a selective hydrogenation of citral. Much higher activity with a turnover frequency (TOF) of 6313 h(-1) has been obtained in this unique C/W emulsion compared to that in the W/C microemulsion (TOF, 23 h(-1)), since the reaction was taking place not only in the surfactant shell but also on the inner surface of the CO2 core in the C/W emulsion. Moreover, citronellal was obtained with a higher selectivity for that it was extracted to a supercritical carbon dioxide (scCO(2)) phase as formed and thus its further hydrogenation was prohibited. The Pd nanoparticles could be recycled several times and still retain the same selectivity, but it showed a little aggregation leading to a slight decrease in conversion.

Design of polymeric stabilizers for size-controlled synthesis of monodisperse gold nanoparticles in water

A new methodology is described for the one-step aqueous preparation of highly monodisperse gold nanoparticles with diameters below 5 nm using thioether- and thiol-functionalized polymer ligands. The particle size and size distribution was controlled by subtle variation of the polymer structure. It was shown that poly(acrylic acid) (PAA) and poly(methacrylic acid) (PMAA) were the most effective stabilizing polymers in the group studied and that relatively low molar mass ligands (similar to 2500 g/mol) gave rise to the narrowest particle size distributions. Particle uniformity and colloidal stability to changes in ionic strength and pH were strongly affected by the hydrophobicity of the ligand end group. "Multidentate" thiol-terminated ligands were produced by employing dithiols and tetrathiols as chain-transfer agents, and these ligands gave rise to particles with unprecedented control over particle size and enhanced colloidal stability. It was found throughout that dynamic light scattering (DLS) is a very useful corroboratory technique for characterization of these gold nanoparticles in addition to optical spectroscopy and TEM.

Synthesis of chitosan-stabilized gold nanoparticles in the absence/presence of tripolyphosphate

Gold nanoparticles were prepared by reducing gold salt with a polysaccharide, chitosan, in the absence/ presence of tripolyphosphate (TPP). Here, chitosan acted as a reducing/stabilizing agent. The obtained gold nanoparticles were characterized with UV-vis spectroscopy and transmission electron microscopy. The results indicated that the shape and size distribution of gold nanoparticles changed with the molecular weight and concentration of chitosan. More interestingly, the gelation of chitosan upon contacting with polyanion (TPP) can also affect the shape and size distribution of gold nanoparticles. By adding TPP to chitosan solution before the reduction of gold salt, gold nanoparticles have a bimodal size distribution, and at the same time, polygonal gold particles were obtained in addition to spherical gold nanoparticles.