The annealing behavior of Cu nanoparticles in Ar-ion implanted spinel

Magnesium aluminate spinel crystals (MgAl2O4 (1 1 0)) deposited with 30 nm Cu film on surface were implanted with 110 key Ar-ions to a fluence of 1.0 x 10(17) ions/cm(2) at 350 degrees C, and then annealed in vacuum condition at the temperature of 500, 600, 700, 800 and 900 degrees C for 1 h, respectively. Ultraviolet-visible spectrometry (UV-VIS), scanning electron microscopy (SEM), Rutherford backscattering (RBS) and transmission electron microscopy (TEM) were adopted to analyze the specimens. After implantation, the appearance of surface plasmon resonance (SPR) absorbance peak in the UV-VIS spectrum indicated the formation of Cu nanoparticles, and the TEM results for 500 degrees C also confirmed the formation of Cu nanoparticles at near-surface region. In annealing process, The SPR absorbance intensity increased at 500 and 700 degrees C, decreased with a blue shift of the peak position at 600 and 800 degrees C, and the peak disappeared at 900 degrees C. The SPR absorbance intensity evolution with temperature was discussed combined with other measurement results (RBS, SEM and TEM). (C) 2010 Elsevier B.V. All rights reserved.