Interface effect on emission properties of Er-doped Si nanoclusters embedded in SiO2 prepared by magnetron sputtering

Er-doped Si nanoclusters embedded in SiO2 (NCSO) films were prepared by radio frequency magnetron sputtering on either silicon or quartz substrates. A 1.16 mu m (1.08 eV) photoluminescence (PL) peak was observed from an Er-doped NCSO film deposited on a Si substrate. This 1.16 mu m peak is attributed to misfit dislocations at the NCSO/Si interface. The emission properties of the 1.16 mu m peak and its correlation with the Er3+ emission (1.54 mu m) have been studied in detail. The observed behavior suggests that the excitation mechanism of the 1.16 mu m PL is in a fashion similar to that shown for Er-doped Si nanoclusters embedded in a SiO2 matrix. (C) 2006 American Institute of Physics.

Electroluminescence afterglow from indium tin oxide/Si-rich SiO2/p-Si structure

Indium tin oxide/Si-rich SiO2/p-Si structured devices are fabricated to study the electroluminescence (EL) of the Si-rich SiO2 (SRO) material. The obvious peaks at similar to 1050nm and similar to 1260nm in the EL are ascribed to localized state transitions of amorphous Si (alpha-Si) clusters. The EL afterglow associated with alpha-Si clusters is observed from this structure at room temperature, while the afterglow is absent in the case of optical pumping. It is believed that carrier-induced defects act as trap centres in the alpha-Si clusters, resulting in the EL afterglow. The phenomenon of the EL afterglow indicates the limits of EL performance and electrical modulation of the SRO material with a larger fraction of alpha-Si clusters.

Photoluminesfcence of Er-doped SiO2 films containing Si nanocrystals and Er

Correlations between Si nanocrystal (nc-Si) related photoluminescence (PL), Er3+ emission and nonradiative defects in the Er-doped SiO2 films containing nc-Si (SRSO) are studied. Upon 514.5 nm laser excitation the erbium-doped SRSO samples exhibit PL peaks at around 0.8 and 1.54 mum, which can be assigned to the electron-hole recombination in nc-Si and the intra-4f transition in Er3+, respectively. With increasing Er3+ content in the films, Er3+ emission becomes intense while the PL at 0.8 mum decreases, suggesting a strong coupling of nc-Si and Er 31 ions. Hydrogen plasma treatment for the samples improve the PL intensities of the 0.8 and 1.54 mum bands, indicating H passivation for the nonradiative defects existing in the samples. Further-more, from the effect of hydrogen treatment for the samples, we observe variation of the number of nonradiative defects with annealing temperatures. (C) 2003 Elsevier Science B.V. All rights reserved.

The plasmon resonance absorption of Ag/SiO2 nanocomposite films

The plasmon resonance absorption of the Ag/SiO2 nanocomposite film is investigated. The measured absorption spectra are compared with those calculated by the Mie theory. The results indicate that the Mie theory on the basis of classical electrodynamics can only partially explain the optical absorption spectra of the Ag/SiO2 nanocomposite film. We believe that the plasmon resonance absorption is mainly an intrinsic quality of the metal particle, and can be explained only with the electronic structure of the metal particle. In the latter, surface resonance state is introduced to systematically discuss the optical absorption spectra of the Ag/SiO2 nanocomposite film. (C) 2003 Elsevier Science B.V. All rights reserved.

Influence of coupling between Er3+, nc-Si and nonradiative centers on photoluminescence from Er3+-doped nc-Si/SiO2 films

Con-elation between nc-Si, Er3+ and nonradiative defects in Er-doped nc-Si/SiO2 films is studied. Upon the 514.5 run laser excitation, the samples exhibit a nanocrystal-related spectrum centered at around 750 nm and an Er3+ luminescence line at 1.54mum. With increasing Er3+ content in the films,the Er3+ emission becomes intense while the photoluminescence at 750 nm decreases. Hydrogen passivation of the samples is shown to result in increases of the two luminescence peaks. However, the effect of hydrogen treatment is different for the samples annealed at different temperatures. The experimental results show that the coupling between Er3+, nc-Si and noradiative centers has a great influence on photoluminescence from nc-Si/SiO2 < Er > films.

Getting high-efficiency photoluminescence from Si nanocrystals in SiO2 matrix

Silicon nanocrystals in SiO2 matrix are fabricated by plasma enhanced chemical vapor deposition followed by thermal annealing. The structure and photoluminescence (PL) of the resulting films is investigated as a function of deposition temperature. Drastic improvement of PL efficiency up to 12% is achieved when the deposition temperature is reduced from 250 degreesC to room temperature. Low-temperature deposition is found to result in a high quality final structure of the films in which the silicon nanocrystals are nearly strain-free, and the Si/SiO2 interface sharp. The demonstration of the superior structural and optical properties of the films represents an important step towards the development of silicon-based light emitters. (C) 2002 American Institute of Physics.

SiO2/Ta interface reaction in magnetic multilayers and its influence on Ta buffer layers

Ta is often used as a buffer layer in magnetic multilayers. In this study, Ta/Ni81Fe19/Ta multilayers were deposited by magnetron sputtering on sing-crystal Si with a 300-nm-thick SiO2 film. The composition and chemical states at the interface region of SiO2/Ta were studied using the X-ray photoelectron spectroscopy (XPS) and peak decomposition technique. The results show that there is an 'inter-mixing layer" at the SiO2/Ta interface due to a thermodynamically favorable reaction: 15 SiO2 + 37 Ta = 6 Ta2O5 + 5 Ta5Si3. Therefore, the Ta buffer layer thickness used to induce NiFe (111) texture increases.

Electroluminescence from Au/(SiO2/Si/SiO2) nanometer double barrier/p-Si structures and its mechanism

SiO2/Si/SiO2 nanometer double barriers (SSSNDB) with Si layers of twenty-seven different thicknesses in a range of 1-5 nm with an interval of 0.2 nm have been deposited on p-Si substrates using two-target alternative magnetron sputtering. Electroluminescence (EL) from the semitransparent Au film/SSSNDB/p-Si diodes and from a control diode without any Si layer have been observed under forward bias. Each EL spectrum of all these diodes can be fitted by two Gaussian bands with peak energies of 1.82 and 2.25 eV, and full widths at half maximum of 0.38 and 0.69 eV, respectively. It is found that the current, EL peak wavelength and intensities of the two Gaussian bands of the Au/SSSNDB/p-Si structure oscillate synchronously with increasing Si layer thickness with a period corresponding to half a de Broglie wavelength of the carriers. The experimental results strongly indicate that the EL originates mainly from two types of luminescence centres with energies of 1.82 and 2.25 eV in the SiO2 barriers, rather than from the nanometer Si well in the SSSNDB. The EL mechanism is discussed in detail.

Effects of rapid thermal annealing and SiO2 encapsulation on GaNAs/GaAs single quantum wells grown by plasma-assisted molecular-beam epitaxy

Effects of rapid thermal annealing and SiO2 encapsulation on GaNAs/GaAs single quantum wells grown by plasma-assisted molecular-beam epitaxy were studied. Photoluminescence measurements on a series of samples with different well widths and N compositions were used to evaluate the effects. The intermixing of GaNAs and GaAs layers was clearly enhanced by the presence of a SiO2-cap layer. However, it was strongly dependent on the N composition. After annealing at 900 degreesC for 30 s, a blueshift up to 62 meV was observed for the SiO2-capped region of the sample with N composition of 1.5%, whereas only a small blueshift of 26 meV was exhibited for the bare region. For the sample with the N composition of 3.1%, nearly identical photoluminescence peak energy shift for both the SiO2-capped region and the bare region was observed. It is suggested that the enhanced intermixing is mainly dominated by SiO2-capped layer induced defects-assisted diffusion for the sample with smaller N composition, while with increasing N composition, the diffusion assisted by interior defects become predominant. (C) 2001 American Institute of Physics.

The transition from Eu3+ to Eu2+ in SiO2(Eu) thin films prepared by ion implantation and co-sputtering

Eu ions doped SiO2 thin films, SiO2( Eu), were prepared by co-sputtering of SiO2 and Eu2O3 and Eu ion implantation into thermally grown SiO2 films. The Eu-L-3-edge X-ray absorption near edge structure (XANES) spectra of SiO2(Eu) films show a doublet absorption peak structure with energy difference of 7 eV, which indicates the conversion of Eu3+ to Eu2+ at high annealing temperature in N-2. The strong blue luminescence of SiO2(Eu) films prepared by ions implantation after films annealed above 1100 degreesC confirms the above argument.

Photoluminescence and Raman scattering of silicon nanocrystals prepared by silicon ion implantion into SiO2 films

Photoluminescence (PL) and Raman spectra of silicon nanocrystals prepared by Si ion implantion into SiO2 layers on Si substrate have been measured at room temperature. Their dependence on annealing temperature was investigated in detail. The PL peaks observed in the as-implanted sample originate from the defects in SiO2 layers caused by ion implantation. They actually disappear after thermal annealing at 800 degrees C. The PL peak from silicon nanocrystals was observed when thermal annealing temperatures are higher than 900 degrees C. The PL peak is redshifted to 1.7 eV and the intensity reaches maximum at the thermal annealing temperature of 1100 degrees C. The characterized Raman scattering peak of silicon nanocrystals was observed by using a right angle scattering configuration. The Raman signal related to the silicon nanocrystals appears only in the samples annealed at temperature above 900 degrees C. It further proves the formation of silicon nanocrystals in these samples. (C) 2000 American Institute of Physics. [S0021-8979(00)00215-2].

The fabrication of thick SiO2 layer by anodization

Silicon-based silica waveguide (SiO2/Si) devices have huge applications in optical telecommunication. SiO2 up to 25-mu m thick is necessary for some passive SiO2/Si waveguide devices. Oxidizing porous silicon to obtain thick SiO2 as cladding layer is presented. The experimental results of porous layer and oxidized porous layer formation were given. The relationship between cracking of SiO2 and temperature varying rate was given experimentally. Such conclusions are drawn: oxidation rate of porous silicon is several orders faster than that of bulk silicon; appropriate temperature variation rate during oxidation can prevent SiO2 on silicon substrates from cracking, and 25 mu m thick silicon dioxide layer has been obtained. (C) 2000 Elsevier Science B.V. All rights reserved.

Thick SiO2 layer produced by anodisation

A method for oxidising porous silicon to obtain thick SiO2 as the cladding layer of silicon-based silica waveguides is presented. The experimental results of oxidation are given. The following conclusions are drawn: the oxidation rate of porous silicon is several orders higher than that of bulk silicon, the appropriate temperature variation rate during oxidation combined with proper porosity can prevent SiO2 on silicon substrates from cracking. and a 25 mu M thick silicon dioxide layer has been obtained.

Raman scattering of nanocrystalline silicon embedded in SiO2

Raman scattering of nanocrystalline silicon embedded in SiO2 matrix is systematically investigated. It is found that the Raman spectra can be well fitted by 5 Lorentzian lines in the Raman shift range of 100-600 cm(-1). The two-phonon scattering is also observed in the range of 600-1100 cm(-1) The experimental results indicate that the silicon crystallites in the films consist of nanocrystalline phase and amorphous phase; both can contribute to the Raman scattering. Besides the red-shift of the first order optical phonon modes with the decreasing size of silicon nanocrystallites, we have also found an enhancement effect on the second order Raman scattering, and the size effect on their Raman shift.

Absorption spectra of nanocrystalline silicon embedded in SiO2 matrix

Nanocrystalline silicon (nc-Si) embedded SiO2 matrix has been formed by annealing the SiOx films fabricated by plasma-enhanced chemical vapor deposition (PECVD) technique. Absorption coefficient and photoluminescence of the films have been measured at room temperature. The experimental results show that there is an "aUrbach-like" b exponential absorption in the spectral range of 2.0-3.0 eV. The relationship of (alpha hv)(1/2) proportional to(hv - E-g) demonstrates that the luminescent nc-Si have an indirect band structure. The existence of Stokes shift between photoluminescence and absorption edge indicates that radiative combination can take place not only between electron states and hole states but also between shallow trap states of electrons and holes. (C) 2000 Elsevier Science B.V. All rights reserved.