Evaluation of fatigue behavior on repaired carbon fiber/epoxy composites

The continuous use of structural polymer composites in aeronautical industry has required the development of repairing techniques of damages found in different types of laminates. The most usually adopted procedure to investigate the repair of composite laminates has been by repairing damages simulated in laminated composite specimens. This work shows the influence of structural repair technique on mechanical properties of a typical carbon fiber/epoxy laminate used in aerospace industry. When analyzed by tensile test, the laminates with and without repair present tensile strength values of 670 and 892 MPa, respectively, and tensile modulus of 53.0 and 67.2 GPa, respectively. By this result, it is possible to observe a decrease of the measured mechanical properties of the repaired composites. When submitted to fatigue test, it is observed that in loads higher than 250 MPa, this laminate presents a low life cycle (lower than 400,000 cycles). The fatigue performance of both laminates is comparable, but the non-repaired laminate presented higher tensile and fatigue resistance when compared with the repaired laminate.

Improvement in the fatigue strength of chromium electroplated AISI 4340 steel by shot peening

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

PREPARATION and CHARACTERIZATION of CELLULOSE/HYDROUS NIOBIUM PHOSPHATE HYBRID

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

SUGARCANE BAGASSE PULPING and BLEACHING: THERMAL and CHEMICAL CHARACTERIZATION

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

CHEMICAL MODIFICATION EFFECT on THE MECHANICAL PROPERTIES of HIPS/COCONUT FIBER COMPOSITES

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

The surface treatment influence on the fatigue crack propagation of Al 7050-T7451 alloy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Sugarcane bagasse cellulose/HDPE composites obtained by extrusion

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Cure Kinetic of Castor Oil-Based Polyurethane

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Considerations on corrosion and weld repair effects on the fatigue strength of a steel structure critical to the flight-safety

The aim of this study is to analyze the effects of corrosion and successive tungsten inert gas (TIC) welding repairs on the reverse bending fatigue strength of AISI 4130 steel used in components critical to the flight-safety. The tests were performed on hot-rolled steel plate specimens, 1.10 mm and 1.60 mm thick, by means of a SCHENK PWS equipment, with load ratio R = -1, constant amplitude, 30 Hz frequency and room temperature. It was observed that the reverse bending fatigue strength of AISI 4130 steel decreases due to the corrosion and the TIC welding and re-welding processes. (C) 2010 Elsevier Ltd. All rights reserved.

Repair Welding Effects on the Bending Fatigue Strength of AISI 4130 Aeronautical Steel used in a Critical to the Flight-Safety Structure

The aim of this study was to analyze the effect of successive TIG (tungsten inert gas) welding repairs on the reverse bending fatigue strength of AISI 4130 steel, which is widely used in components critical to the flight-safety. In order to simulate the abrupt maneuvers, wind bursts, motor vibration and helixes efforts, which generate cyclic bending loadings at the welded joints of a specific aircraft component called motor cradle, experimental reverse bending fatigue tests were carried out on specimens made from hot-rolled steel plate, 1.10 mm (0.043 in) thick, by mean of a SCHENK PWS equipment, with load ratio R = -1, under constant amplitude, at 30 Hz frequency and room temperature. It was observed that the bending fatigue strength decreases after the TIG (Tungsten Inert Gas) welding process application on AISI 4130 steel, with subsequent decrease due to re-welding sequence as well. Microstructural analyses and microhardness measurements on the base material, heat-affected zone (HAZ) and weld metal, as well as the effects of the weld bead geometry on the obtained results, have complemented this study.

Quantitative microscopy characterization of hydrous niobium phosphate into bleached cellulose

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of WC-10%Co-4%Cr coating on the Ti-6Al-4V alloy fatigue strength

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Fractography analysis and fatigue strength of carbon fiber/RTM6 laminates

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Thermal and mechanical behaviour of sisal/phenolic composites

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effects of several TIG weld repairs on the axial fatigue strength of AISI 4130 aeronautical steel-welded joints

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)