Effect of 4% titanium tetrafluoride solution on the erosion of permanent and deciduous human enamel: an in situ/ex vivo study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Cross-Sectional Microhardness of Human Enamel Subjected to Erosive, Cariogenic or Combined Erosive/Cariogenic Challenges

This in situ study evaluated the interaction between caries and erosion processes. In the first phase, enamel specimens were subjected to erosion without dental plaque (EO) or to erosion with plaque (EP); in the second phase, they were subjected to erosion plus cariogenic challenge (EC) or cariogenic challenge (CO), both with plaque accumulation. Cross-sectional hardness data (10-330 mu m depth) were tested using ANOVA (alpha = 0.05). EO and EP showed surface softening to 10 mu m depth. CO and EC produced subsurface lesions, of similar depth (up to 220 mu m), with CO showing higher integrated loss of hardness than EC, indicating that cariogenic and erosive challenges did not have an additive effect. Copyright (C) 2010 S. Karger AG, Basel

Roughness of Human Enamel Surface Submitted to Different Prophylaxis Methods

The purpose of this in vitro study was to evaluate alterations in the surface roughness and micromorphology of human enamel submitted to three prophylaxis methods. Sixty-nine caries-free molars with exposed labial surfaces were divided into three groups. Group I was treated with a rotary instrument set at a low speed, rubber clip and a mixture of water and pumice; group II with a rotary instrument set at a low speed, rubber cup and prophylaxis paste Herjos-F (Vigodent S/A Industria e Comercio, Rio de Janeiro, Brazil); and group III with sodium bicarbonate spray Profi II Ceramic (Dabi A dante Indtistrias Medico Odontologicas Ltda, Ribeirao Preto, Brazil). All procedures were performed by the same operator for 10 s, and samples were rinsed and stored in distilled water. Pre and post-treatment surface evaluation was completed using a surface profilometer (Perthometer S8P Marh, Perthen, Germany) in 54 samples. In addition, the other samples were coated with gold and examined in a scanning electron microscope (SEM). The results of this study were statistically analyzed with the paired t-test (Student), the Kruskal-Wallis test and the Dunn (5%) test. The sodium bicarbonate spray led to significantly rougher surfaces than the pumice paste. The use of prophylaxis paste showed no statistically significant difference when compared with the other methods. Based on SEM analysis, the sodium bicarbonate spray presented an irregular surface with granular material and erosions. Based on this study, it can be concluded that there was an increased enamel stuface roughness when teeth were treated with sodium bicarbonate spray when compared with teeth treated with pumice paste.

Caries resistance of lased human enamel with Er : YAG laser - morphological and ratio Ca/P analysis

Objective: In vitro analysis of caries resistance of dental enamel under caries simulation after irradiation with Er:YAG laser. Background Data: More susceptible to caries development spots at adjacent hard tissues from cavity preparations of dental tissues using burrs or lasers are quite common. Methods: Thirteen caries-free third permanent human molars were distributed as follows: G1: sound control and caries control; G2: Er:YAG 100, 200, 300, or 400 mJ/ 10 Hz/ 3 sec.; G3: the same parameters of G2 followed by artificial caries simulation, through dynamic model of demineralization and remineralization (DE/RE). Caries resistance analysis was evaluated through scanning electron microscopy (SEM) and Ca/P rate (X-Rays spectroscopy - EDX). Results: Photomicrographs showed that the Er:YAG laser created craters with rough aspect which became more evident as the energy per pulse was increased, but without change of regular morphology of enamel prisms. Significant statistical changes among the irradiated and control groups was observed considering the Ca/P ratio. Conclusion: Irradiated groups showed higher caries resistance than control groups. However, it is not possible to affirm that the enamel surface accidental irradiation could be a benefit to caries resistance for other situations can be considered, as biofilm deposit, which could increase the caries susceptibility.

Influence of fluoride dentifrice on brushing abrasion of eroded human enamel: An in situ/ex vivo study

This in situ/ex vivo study assessed the effect of fluoride dentifrice on eroded enamel subjected to brushing abrasion. In a crossover study performed in 2 phases, 10 volunteers wore acrylic palatal appliances, each containing 3 human enamel blocks. Dentifrice was used to brush the volunteers' teeth and the specimens subjected to abrasion. In phases A and B the dentifrices used had the same formulation, except for the absence or presence of fluoride, respectively. The blocks were subjected to erosion by immersion of the appliances in a cola drink for 5 min, 4 times a day. Then the blocks were brushed, and the appliance was replaced into the mouth. Enamel alterations were determined using profilometry and percentage change in surface microhardness (%SMHC) tests. The data were tested using the paired t test. The mean wear values (+/- SD, mu m) were: group A 6.84 +/- 1.72 and group B 5.38 +/- 1.21 (p = 0.04). The mean %SMHC values (+/- SD) were: group A 54.6 +/- 16.2 and group B 45.7 +/- 6.8 (p = 0.04). Fluoride dentifrice had a protective effect on eroded enamel subjected to brushing abrasion. Copyright (c) 2007 S. Karger AG, Basel.

Scanning electron microscopy evaluation of the effect of etching agents on human enamel surface

Acid etching promotes microporosities on enamel surface, which provide a better bonding surface to adhesive materials. The purpose of this study was to comparatively analyze the microstructure of enamel surface after etching with 37% phosphoric acid or with two self-etching primers, Non-rinse conditioner (NRC) and Clearfil SE Bond (CSEB) using scanning electron microscopy. Thirty sound premolars were divided into 3 groups with ten teeth each: Group 1: the buccal surface was etched with 37% phosphoric acid for 15 seconds; Group 2: the buccal surface was etched with NRC for 20 seconds; Group 3: the buccal surface was etched with CSEB for 20 seconds. Teeth from Group 1 were rinsed with water; teeth from all groups were air-dried for 15 seconds. After that, all specimens were processed for scanning electron microscopy and analyzed in a Jeol 6100 SEM. The results showed deeper etching when the enamel surface was etched with 37% phosphoric acid, followed by NRC and CSEB. It is concluded that 37% phosphoric acid is still the best agent for a most effective enamel etching.

Correlation between pH and surface structural changes on human enamel submitted to different tooth whitening agents

The intense valuation of an esthetic pleasant smile guided the dentistry to bleached tooth due the popularity of whitening treatments. The consequence of it is an increasing interest in searching the effect of peroxides in hard dental tissues. The aim of this work was to analyze qualitatively in vitro the human enamel after three different bleaching treatments: Opalescence PF 10%, White Class 7.5% and Opalescence Xtra Boost 38%, correlating the structural changes in the surface of the enamel with its respective pH. A total of 40 sound human pre-molars were randomly divided into four groups of 10 elements, which had been immersed in artificial saliva during all the experiment. Bleaching protocols followed the recommendations of the respective manufacturers. Each bleached sample and control group were submitted to a scanning electronic microscopy analysis and compared with one another. Bleaching agents used in this experiment had modified the morphologic aspect of the surface of the dental enamel; however, it did not have correlation between the degrees of severity of the alterations and pH. There is a correlation between hydrogen peroxide concentration and changes in the enamel, where G4 showed more severe alterations, followed for G3 and G2.

Evaluation of the bleached human enamel by scanning electron microscopy

Since bleaching has become a popular procedure, the effect of peroxides on dental hard tissues is of great interest in research. Purpose: The aim of this in vitro study was to perform a qualitative analysis of the human enamel after the application of in-office bleaching agents, using Scanning Electron Microscopy (SEM). Materials and Methods: Twenty intact human third molars extracted for orthodontic reasons were randomly divided into four groups (n=5) treated as follows: G1- storage in artificial saliva (control group); G2- four 30-minute applications of 35% carbamide peroxide (total exposure: 2h); G3- four 2-hour exposures to 35% carbamide peroxide (total exposure: 8h); G4- two applications of 35% hydrogen peroxide, which was light-activated with halogen lamp at 700mW/cm2 during 7min and remained in contact with enamel for 20min (total exposure: 40min). All bleaching treatments adopted in this study followed the application protocols advised by manufacturers. Evaluation of groups submitted to 35% carbamide peroxide was carried out after two time intervals (30 minutes and 2 hours per session), following the extreme situations recommended by the manufacturer. Specimens were prepared for SEM analysis performing gold sputter coating under vacuum and were examined using 15kV at 500x and 2000x magnification. Results: Morphological alterations on the enamel surface were similarly detected after bleaching with either 35% carbamide peroxide or 35% hydrogen peroxide. Surface porosities were characteristic of an erosive process that took place on human enamel. Depression areas, including the formation of craters, and exposure of enamel rods could also be detected. Conclusion: Bleaching effects on enamel morphology were randomly distributed throughout enamel surface and various degrees of enamel damage could be noticed. Clinical significance: In-office bleaching materials may adversely affect enamel morphology and therefore should be used with caution.

Effect of Er:YAG laser on CaF2 formation and its anticariogenic action on human enamel: An in vitro study

Objective: The objective of this study was to evaluate the effect of Er: YAG laser on the formation of CaF2, after the application of acidulated phosphate fluoride (APF), and its influence on the anti-cariogenic action in human dental enamel. Background Data: Er:YAG laser was designed to promote ablation of the enamel. However, the possibility of using this energy to increase the enamel's resistance to caries has hardly been explored, and neither has its interaction with the use of fluorides. Materials and Methods: One hundred and twenty blocks of enamel were allocated to four groups of 30 blocks each: (1) C, control group; (2) Er:YAG, laser; (3) APF; and (4) Er:YAG+APF. Of these, 80 blocks were submitted to pH cycling for 14 days. In the other 40 blocks, fluoride (CaF2) was measured before cycling. After pH cycling, surface microhardness (SMH), microhardness in cross-section (converted to mineral contents % vol. min.), and fluoride after cycling (40 blocks) were also determined. Results: SMH decreased in all groups. The control group showed the highest decrease, and Er:YAG+APF showed the lowest decrease (p < 0.05). Groups APF and Er:YAG showed the same results (p > 0.05). Mineral content at depths 10, 20, and 40 μm was lower in the control and Er:YAG groups, and higher in groups APF and Er:YAG+APF. CaF2 (μgF/cm2) deposited before pH cycling was higher in the APF group when compared to the Er:YAG+APF group. Control and Er:YAG groups showed the lowest values (p > 0.05). Conclusion: It was concluded that Er:YAG laser influenced the deposition of CaF2 on the enamel and showed a superficial anti-cariogenic action, but not in depth.