Fire protection durability of intumescent coatings after accelerated aging

The most common method of achieve the required fire resistance is by the use of passive fire protection systems, being intumescent coatings the fire protection material frequently used. These are usually considered thin film coatings as they are applied with a dry film thickness (DFT) between 0.3-3 [mm]. The required DFT is obtained by experimental fire resistance tests performed to assess the contribution of this reactive fire protection material to the steel member fire resistance. This tests are done after dry coating and a short time period of atmospheric conditioning, at constant temperature and humidity. As the coatings formulation is mainly made from polymeric basis compounds, it is expected that the environmental factors, such temperature, humidity and UV radiation (UVA and UVB) significantly affect the intumescent coating fire protection performance and its durability. This work presents a research study about the effects of aging on the fire protection performance of intumescent coatings. A commercial water based coating is submitted to an accelerated aging cycle, using a QUV Accelerated Weathering Tester. This tests aim to simulate 10 years of the coating natural aging. The coating durability is tested comparing the fire protection of small steel samples submitted to a radiant heat flux exposure from a cone calorimeter. In total, 28 tests were performed on intumescent coating protected steel specimens, of which 14 specimens were tested before the hydrothermal aging test and other 14 after accelerated aging. The experimental tests results of the steel temperature evolution shows that increasing the intumescent dry coating film thickness, the fire resistance time increases. After the accelerated aging cycles, the coating lose their ability to expand, resulting in an increase of the steel temperature of approximately 200 [ºC], compared to the samples without aging.

Fire behaviour of tabique walls

This paper present a study on the behaviour of tabique walls, concerning its fire resistance. This work is based on the experimental analysis of real scale tabique panels. Such walls were made in pine wood with an earth-based mortar finishing. In order to assess the earth-based mortar thickness effect on the fire resistance of the wall, three specimens were tested with three different mortar thicknesses of 15 mm, 10 mm and 5 mm. The earth-based mortar was previously analysed in the laboratory. The wooden structures were constructed based on traditional tabique technique. The experimental models were tested in a fire-resistance furnace, according to the ISO 834 standard fire. Temperatures were recorded using two data acquisition systems (spot measuring and field measuring). Fire resistance of test elements is expressed as the time during which the appropriate criteria have been satisfied so that one can predict the time before collapse, increasing both people and property safety. The obtained results are of great importance as they allow to improve the knowledge on tabique walls behaviour subjected to fire conditions. Two performance criteria were verified: the integrity criteria and the insulation criteria.