Palladium-supported catalysts in methane combustion: comparison of alumina and zirconia supports

Palladium catalysts supported on alumina and zirconia were prepared by the impregnation method and calcined at 600 and 1000 ºC. Catalysts were characterized by BET measurements, XRD, XPS, O2-TPD and tested in methane combustion through temperature programmed surface reaction. Alumina supported catalysts were slightly more active than zirconia supported catalysts, but after initial heat treatment at 1000 ºC, zirconia supported palladium catalyst showed better performance above 500 ºC A pattern between temperature interval stability of PdOx species and activity was observed, where better PdOx stability was associated with more active catalysts.

Isomerization-cracking of n-octane on catalysts based on heteropolyacid H3Pw12O40 and heteropolyacid supported on zirconia and promoted with Pt and Cs

Isomerization - cracking of n-octane was studied using H3PW12O40 (HPA) and HPA supported on zirconia and promoted with Pt and Cs. The addition of Pt and Cs to the supported HPA did not modify the Keggin structure. The Pt addition to the supported HPA did not substantially modify the total acidity; however, the Brönsted acidity increased significantly. Cs increased the total acidity and Brönsted acidity. A linear relation was observed between the n-C8 total conversion and Brönsted acidity. The most adequate catalysts for performing isomerization and cracking to yield high research octane number (RON) are those with higher values of Brönsted acidity.

Solubilidade do SrO em NaCl-Kcl fundido a 727ºC

The solubility product value of SrO has been found to be equal to 10-4,2 (molality scale) in molten equimolar mixture of NaCl and KCl at 727ºC, using a potentiometric method involving a calcia stabilized zirconia membrane electrode. This value, which is in a logical agreement with other alkaline-earth oxide determined solubilities, is compared to those of 10-5,8, 10-3,0 and 10-3,08 (molality scale) found in the litterature 33, 22 and 5 years ago, respectively. Such discrepencies have called the attention of the authors, their possible reasons (methodology, titrating agent) are analyzed and a theoretical discussion, for considering the authors' value as more reliable, is given in this paper.

Estudo de algumas reações oxoacidobásicas no solvente NaCl fundido entre 1100K e 1200K

Equilibrium constants (K) of some oxoacidbasic reactions in molten NaCl in the temperature range of 1100K to 1200K, have been measured potentiometrically with a calcia stabilized zirconia oxide ion (O2-) indicator electrode. In molten NaCl at 1100K the pKs values (in molality scale) for HCl/H2O and HO-/H2O are respectively 11.0 ± 0.3; 1.6 ± 0.3 and the pKs for CaO is 4.3 ± 0.3. The results have been compared with those determined previously by Combes for the molten equimolar NaCl-KCl mixture and are in good agreement with literature data and gives some qualitative explanation of the comparison of oxoacidbasic properties between molten NaCl and NaCl-KCl.

Síntese de membranas cerâmicas via método sol-gel utilizando TEOS e N,N-dimetilformamida

In this work we obtained microporous and mesoporous silica membranes by sol-gel processing. Tetraethylortosilicate (TEOS) was used as precursor. Nitric acid was used as catalyst. In order to study the affect of N,N-dimethylformamide (NDF) as drying additive, we used a molar ratio TEOS/NDF of 1/3. The performance of N,N-dimethylformamide was evaluated through monolithicity measurements. The structural evolutions occurring during the sol-gel transition and in the interconnected network of the membranes during thermal treatment were monitored by Fourier transform infrared spectroscopy (FTIR), thermogravimetric analyses and nitrogen sorption. We noted that in the presence of N,N-dimethylformamide, polymerization goes through a temporary stabilization of oligomers. The Si-O(H) bonds are stronger and belong to a more cross-linked structure for the N,N-dimethylformamide containing sol. The membranes obtained in the presence of N,N-dimethylformamide have larger surface area and its pore structure is in the range of mesoporous. The membranes obtained without additive have pore structure in the range of microporous.

Dióxido de estanho nanoestruturado: síntese e crescimento de nanocristais e nanofitas

The objectives of this work are to supply a basic background on nanostructured materials and also to report about the obtaining of nanoparticles, mainly, tin dioxide nanocrystalline particles (obtained by using the polymeric precursor method) presenting a high stability against particle growth due to the usage of a metastable solid solution. The synthesis and growth of SnO2 nanoribbons by a carbothermal reduction process are also discussed.

Efeito do cromo nas propriedades catalíticas da MCM-41

The effect of chromium on the catalytic properties of MCM-41 was evaluated in order to develop new catalysts for the trimethylbenzene transalkylation with benzene to produce ethylbenzene, a high-value aromatic in the industry. It was found that chromium decreases the specific surface area but increases the acidity, turning MCM-41 into an active and selective catalyst for ethylbenzene and toluene production. The coke produced on the catalyst is hydrogenated and mainly located outside the pores and thus can be easily removed. The catalyst is more active and selective than mordenite, a commercial catalyst, and thus more promising for commercial applications.

Aplicação catalítica de peneiras moleculares básicas micro e mesoporosas

Catalysis by solid acids has received much attention due to its importance in petroleum refining and petrochemical processes. Relatively few studies have focused on catalysis by bases and even les on using basic molecular sieves. This paper deals with the potential application of micro and mesoporous molecular sieves in base catalysis reactions. The paper is divided in two parts, the first one dedicated to the design of the catalysts and the second to some relevant examples of catalytic reactions, which find a huge field of applications essentially in the synthesis of fine chemicals. Here, recent developments in catalysis by basic molecular sieves and the perspectives of applications in correlated catalytic processes are described.

Nanocompósitos cerâmicos a partir do processo de moagem mecânica de alta energia

Pb/Ti, Sn and Mg-based nanocomposite materials were prepared by the high-energy mechanical milling of commercial powders. The surface of these ceramic compounds was strongly influenced by the doping, diameter of the milling spheres and time of the mechanical milling (amorphization process). Such milling leads to the formation of nanocrystalline materials. The mechanical processing parameters of these compounds were investigated through Brunauer, Emmett and Teller isotherms, wide angle X-ray diffraction, transmission electron microscopy and CO2 adsorption.

Obtenção de filmes finos de TiO2 nanoestruturado pelo método dos precursores poliméricos

This work focuses in optimizing setup for obtaining TiO2 thin films by polymeric precursor route due to its advantages on stoichiometric and morphological control. Precursor stoichiometry, synthesis pH, solids concentration and rotation speed at deposition were optimized evaluating thin films morphology and thickness. Thermogravimetry and RMN were applied for precursor's characterization and AFM, XRD and ellipsometry for thin films evaluation. Results showed successful attainment of homogeneous nanocrystalline anatase TiO2 thin films with outstanding control over morphological characteristics, mean grain size of 17 nm, packing densities between 57 and 75%, estimated surface areas of 90 m²/g and monolayers thickness within 20 and 128 nm.

Desenvolvimento e avaliação de um porta-amostra de baixo custo para caracterização elétrica de materiais cerâmicos

Conventional sample holder cells used to the electric characterization of ceramics at high temperature consists of an alumina tube and platinum wires and plates using a complex design. The high cost materials used in the conventional sampler holder cell were replaced by stainless steel and conventional ceramics. The sample holder was validated by characterizing yttria-stabilized-zirconia in a temperature range of 25 to 700 ºC. The results do not present variations, discontinuity or unusual noise in the electric signals. Several samples were characterized without maintenance, which demonstrates that the sample holder is electric and mechanic adequate to be used to electrical characterization of ceramics up to 700 ºC.

Diesel/biodiesel soot oxidation with ceo2 and ceo2-zro2-modified cordierites: a facile way of accounting for their catalytic ability in fuel combustion processes

CeO2 and mixed CeO2-ZrO2 nanopowders were synthesized and efficiently deposited onto cordierite substrates, with the evaluation of their morphologic and structural properties through XRD, SEM, and FTIR. The modified substrates were employed as outer heterogeneous catalysts for reducing the soot originated from the diesel and diesel/biodiesel blends incomplete combustion. Their activity was evaluated in a diesel stationary motor, and a comparative analysis of the soot emission was carried out through diffuse reflectance spectroscopy. The analyses have shown that the catalyst-impregnated cordierite samples are very efficient for soot oxidation, being capable of reducing the soot emission in more than 60%.

Esterificação de ácidos graxos utilizando zircônia sulfatada e compósitos carvão ativado/zircônia sulfatada como catalisadores

In this work sulfated zirconia (SZr) and activated carbon/SZr composites produced by impregnation method with or without heating treatment step (CABC/SZr-I and CABC/SZr-I SC) and by the method of synthesis of SZr on the carbon (CABC/SZr-S) was used as catalysts in the esterification reactions of fatty acids. The SZr presented very active, conversions higher than 90% were obtained after 2 h of reaction. The activity of the composite CABC/SZr-I20%SC was up to 92%, however, this was directly related to time and temperature reactions. CABC/SZr-I and CABC/SZr-S were less active in esterification reactions, what could be attributed to its low acidity

Nanocompósitos magnéticos: potencialidades de aplicações em Biomedicina

The synthesis of magnetic materials such as nanostructured iron oxide has been intensively researched due to their broad applications in biomedicine. As these nanoparticles have high specific surface area, they are very reactive and can aggregate easily, and biodegrade when exposed to biological systems. Mesoporous silica is often employed as support matrix to protect the magnetic functional component, avoiding undesirable effects. In this context, this review describes various syntheses of silica-coated iron oxide nanoparticles, and their use in applications such as bioseparation, magnetic resonance imaging, hyperthermia and drug delivery systems showing the growing interest of these materials in biological area.

Iodeto de potássio suportado em peneiras moleculares mesoporosas (SBA-15 e MCM-41) como catalisador básico para síntese de biodiesel

Iodide potassium incorporated on mesoporous molecular sieves (SBA-15 and MCM-41) was used as heterogeneous catalysts in the transesterification of sunflower oil under different conditions of reaction time and ratio catalyst/oil (w/w). The results have showed that the system supported in SBA-15 has been more active than the supported in MCM-41, promoting a conversion to methyl esters of 84.98%.