Materiales laminares pilareados: preparación y propiedades

The structure of several types of layered materials will be described. These include clays, layered double hydroxides, group IV metal phosphates and other layered materials. The preparation of the pillared materials and pillaring agents will be presented along with a description of the properties and applications of the products.

Análise por difração de raios x de filmes de óxidos cerâmicos compostos por IrO2/TiO2/CeO2

Independent of the sample form (powder or film), XRD analysis of Ir0,3Ti(0,7-x)Ce xO2, (nominal) mixtures, for x=0, shows the formation of a solid solution phase between IrO2 and TiO2, as well as the rutile phases of IrO2 and TiO2. The presence of the anatase phase of TiO2 is also confirmed. The introduction of 30 mol% CeO2 in the mixture reveals the presence of the CeO2 and Ce2O3 phases, besides the already mentioned ones, in the powder. In the film form, however, an amorphous phase is identified. When all of the TiO2 is substituded by CeO2, for both sample forms, the only phases found are IrO2, CeO2 and Ce2O3. This result suggests cerium oxides are not capable of forming solid solutions with either IrO2 or (Ir,Ti)O2 acting solely as a dispersant matrix for these phases. These results are consistent with the much higher electrochemically active surface area when CeO2 is introduced in the binary Ti/Ir0,3Ti0,7O2 mixture. It was possible to establish a relationship between the electrochemical stability of the supported films and their crystalline structure. The unexpected presence of TiO2 and Ti2O3 in the Ti/Ir0,3Ce0,7O2 (film sample) is attributed to oxidation of the Ti support during the calcination step.

Preparação e caracterização de pós cerâmicos de aluminatos de lítio

The preparation of gamma-LiAlO2 by coprecipitation and sol-gel synthesis was investigated. Ceramic powders obtained by coprecipitation synthesis were prepared from aqueous solutions of aluminum and lithium nitrates using sodium hydroxide as precipitant agent. By sol-gel synthesis, the ceramic powders were prepared from hydrolysis of aluminum isopropoxide. The materials obtained by two routes of synthesis were dried at 80ºC and calcined at 550, 750, 950 and 1150ºC. The characterization was done by X-ray diffraction, infrared spectroscopy, emission and absorption atomic spectrometry, helium picnometry, specific surface area (BET method) and scanning electronic microscopy. Mixtures of crystalline phases were obtained by coprecipitation synthesis: 80ºC- LiAl2(OH)7.2H2O + Al(OH)3; 550 and 750ºC- alpha-LiAlO2 + eta-Al2O3; 950 and 1150ºC- gamma-LiAlO2 + LiAl5O8. Chemical analysis showed molar ration Al/Li @ 3. Crystalline single-phases were obtained by sol-gel synthesis above 550ºC: 550ºC-alpha-LiAlO2; 750, 950 and 1150ºC-gamma-LiAlO2. These powders presented molar ration Al/Li @ 1. Thus, gamma-LiAlO2 crystalline phase was obtained at 750ºC by sol-gel synthesis while by coprecipitation synthesis, a mixture of crystalline phases was obtained. These results showed the superiority of the sol-gel synthesis for the preparation of pure gamma-LiAlO2.

Resistência química de vitro-cerâmicos pertencentes a sistemas Li2O-ZrO2-BaO-SiO2 frente ao tratamento com soluções ácidas e básicas

The chemical durability of the Li2O-ZrO2-BaO-SiO2 system was examined by determination of the Vickers hardness. The dependence of hardness and of the chemical resistance with BaO addition was investigated. The experimental results indicate that the hardness increases with the BaO content. The samples surface's morphology submitted to the chemical treatment in acidic (H2SO4) and basic (KOH) solution was accompanied by scanning electron microscopy. The chemical durability of the materials with BaO showed better than the glass ceramic without this content. These materials treated with H2SO4 solution showed a preferential attack to the silica rich sites.

Evaluación de la estructura porosa de los materiales MCM-22, MCM-36 e ITQ-2 empleando el test catalitico del n-decano

The void structure of zeolites MCM-22, MCM-36 and ITQ-2 were discussed on the bases of catalytic reaction tests. The hydromerization of n-decane on bifunctional Pt/Zeolite Catalysts have been used as model reactions. Beta and ZSM-5 zeolites were used for comparison. It is concluded that all materials show features of 10MR zeolites and have also pores bigger than 12MR in this order MCM-22

Nanocompósitos cerâmicos a partir do processo de moagem mecânica de alta energia

Pb/Ti, Sn and Mg-based nanocomposite materials were prepared by the high-energy mechanical milling of commercial powders. The surface of these ceramic compounds was strongly influenced by the doping, diameter of the milling spheres and time of the mechanical milling (amorphization process). Such milling leads to the formation of nanocrystalline materials. The mechanical processing parameters of these compounds were investigated through Brunauer, Emmett and Teller isotherms, wide angle X-ray diffraction, transmission electron microscopy and CO2 adsorption.

Desenvolvimento e avaliação de um porta-amostra de baixo custo para caracterização elétrica de materiais cerâmicos

Conventional sample holder cells used to the electric characterization of ceramics at high temperature consists of an alumina tube and platinum wires and plates using a complex design. The high cost materials used in the conventional sampler holder cell were replaced by stainless steel and conventional ceramics. The sample holder was validated by characterizing yttria-stabilized-zirconia in a temperature range of 25 to 700 ºC. The results do not present variations, discontinuity or unusual noise in the electric signals. Several samples were characterized without maintenance, which demonstrates that the sample holder is electric and mechanic adequate to be used to electrical characterization of ceramics up to 700 ºC.