An Assessment of Novel Biodegradable Magnesium Alloys for Endovascular Biomaterial Applications

Magnesium alloys have been widely explored as potential biomaterials, but several limitations to using these materials have prevented their widespread use, such as uncontrollable degradation kinetics which alter their mechanical properties. In an attempt to further the applicability of magnesium and its alloys for biomedical purposes, two novel magnesium alloys Mg-Zn-Cu and Mg-Zn-Se were developed with the expectation of improving upon the unfavorable qualities shown by similar magnesium based materials that have previously been explored. The overall performance of these novel magnesium alloys has been assessesed in three distinct phases of research: 1) analysing the mechanical properties of the as-cast magnesium alloys, 2) evaluating the biocompatibility of the as-cast magnesium alloys through the use of in-vitro cellular studies, and 3) profiling the degradation kinetics of the as-cast magnesium alloys through the use of electrochemical potentiodynamic polarization techqnique as well as gravimetric weight-loss methods. As compared to currently available shape memory alloys and degradable as-cast alloys, these experimental alloys possess superior as-cast mechanical properties with elongation at failure values of 12% and 13% for the Mg-Zn-Se and Mg-Zn-Se alloys, respectively. This is substantially higher than other as-cast magnesium alloys that have elongation at failure values that range from 7-10%. Biocompatibility tests revealed that both the Mg-Zn-Se and Mg-Zn-Cu alloys exhibit low cytotoxicity levels which are suitable for biomaterial applications. Gravimetric and electrochemical testing was indicative of the weight loss and initial corrosion behavior of the alloys once immersed within a simulated body fluid. The development of these novel as-cast magnesium alloys provide an advancement to the field of degradable metallic materials, while experimental results indicate their potential as cost-effective medical devices.

Circadian rhythm disruption and post-surgical recovery

Circadian rhythms, patterns of each twenty-four hour period, are found in most bodily functions. The biological cycles of between 20 and 28 hours have a profound effect on an individual's mood, level of performance, and physical well being. Loss of synchrony of these biological rhythms occurs with hospitalization, surgery and anesthesia. The purpose of this comparative, correlational study was to determine the effects of circadian rhythm disruption in post-surgical recovery. Data were collected during the pre-operative and post-operative periods in the following indices: body temperature, blood pressure, heart rate, urine cortisol level and locomotor activity. The data were analyzed by cosinor analysis for evidence of circadian rhythmicity and disruptions throughout the six day study period which encompassed two days pre-operatively, two days post-operatively, and two days after hospital discharge. The sample consisted of five men and five women who served as their own pre-surgical control. The surgical procedures were varied. Findings showed evidence of circadian disruptions in all subjects post-operatively, lending support for the hypotheses.