Internal quantum efficiency and tunable colour temperature in monolithic white InGaN/GaN LED

Internal Quantum Efficiency (IQE) of two-colour monolithic white light emitting diode (LED) was measured by temperature dependant electro-luminescence (TDEL) and analysed with modified rate equation based on ABC model. External, internal and injection efficiencies of blue and green quantum wells were analysed separately. Monolithic white LED contained one green InGaN QW and two blue QWs being separated by GaN barrier. This paper reports also the tunable behaviour of correlated colour temperature (CCT) in pulsed operation mode and effect of self-heating on device performance. © 2014 SPIE.

Colour management of InGaN/GaN based monolithic two-wavelength LEDs

The recent advancement in the growth technology of InGaN/GaN has decently positioned InGaN based white LEDs to leap into the area of general or daily lighting. Monolithic white LEDs with multiple QWs were previously demonstrated by Damilano et al. [1] in 2001. However, there are several challenges yet to be overcome for InGaN based monolithic white LEDs to establish themselves as an alternative to other day-to-day lighting sources [2,3]. Alongside the key characteristics of luminous efficacy and EQE, colour rendering index (CRI) and correlated colour temperature (CCT) are important characteristics for these structures [2,4]. Investigated monolithic white structures were similar to that described in [5] and contained blue and green InGaN multiple QWs without short-period superlattice between them and emitting at 440 nm and 530 nm, respectively. The electroluminescence (EL) measurements were done in the CW and pulse current modes. An integration sphere (Labsphere “CDS 600” spectrometer) and a pulse generator (Agilent 8114A) were used to perform the measurements. The CCT and Green/Blue radiant flux ratio were investigated at extended operation currents from 100mA to 2A using current pulses from 100ns to 100μs with a duty cycle varying from 1% to 95%. The strong dependence of the CCT on the duty cycle value, with the CCT value decreasing by more than three times at high duty cycle values (shown at the 300 mA pulse operation current) was demonstrated (Fig. 1). The pulse width variation seems to have a negligible effect on the CCT (Fig. 1). To account for the joule heating, a duty cycle more than 1% was considered as an overheated mode. For the 1% duty cycle it was demonstrated that the CCT was tuneable in three times by modulating input current and pulse width (Fig. 2). It has also been demonstrated that there is a possibility of keeping luminous flux independent of pulse width variation for a constant value of current pulse (Fig. 3).

Correlation between p-GaN growth environment with electrical and optical properties of blue LEDs

Two blue (450 nm) light–emitting diodes (LED), which only differ in top p-GaN layer growth conditions, were comparatively investigated. I-V, C-V, TLM, Electroluminescence (EL) and Photoluminescence (PL) techniques were applied to clarify a correlation between MOCVD carrier gas and internal properties. The A-structure grown in the pure N2 environment demonstrated better parameters than the B-structure grown in the N2/H2 (1:1) gas mixture. The mixed growth atmosphere leaded to an increase of sheet resistances of p-GaN layer. EL and PL measurements confirmed the advantage of the pure N2 utilization, and C(VR) measurement pointed the increase of static charge concentration near the p-GaN interface in the B structure.