Measurements of stress-optic coefficient and Young's modulus in PMMA fibers drawn under different conditions

We have systematically measured the differential stress-optic coefficient, ΔC, and Young's modulus, E, in a number of PMMA fibers drawn with different stress, ranging from 2 up to 27 MPa. Effect of temperature annealing on those parameters was also investigated. ΔC was determined in transverse illumination by measuring the dependence of birefringence on additional axial stress applied to the fiber. Our results show that ΔC in PMMA fibers has a negative sign and ranges from -4.5 to -1.5×10-12 Pa -1 depending on the drawing stress. Increase of the drawing stress results in greater initial fiber birefringence and lower ΔC. The dependence of ΔC and initial birefringence upon drawing stress is nonlinear and gradually saturates for higher drawing stress. Moreover, we find that ΔC is linearly proportional to initial fiber birefringence and that annealing the fiber has no impact on the slope of this dependence. On the other hand, no clear dependence was observed between the fiber drawing stress and the Young's modulus of the fibers as measured using microscopic digital image correlation with the fibers tensioned using an Instron tension tester. © 2010 SPIE.

Conjunctival epithelial flaps with 18 months of silicone hydrogel contact lens wear

Purpose. To report differences in the incidence of conjunctival epithelial flaps (CEFs) found in a group of neophyte contact wearers using two different silicone hydrogel contact lenses on a daily- and continuous-wear basis during an 18-month period. Methods. Sixty-one subjects were initially examined, and 53 were eligible to participate in the study. Eligible subjects were randomly assigned to wear one of two silicone hydrogel materials, lotrafilcon A or balafilcon A, on a daily- or continuous-wear basis. After an initial screening, subjects were monitored weekly for the first month and then after 3, 6, 12, and IS months. The incidence of CEFs in each of the four contact lens groups was recorded. Results. Five of the 53 subjects enrolled in the study showed bilateral CEFs. A higher incidence of CEFs was found in subjects wearing lotrafilcon A lenses (n = 4) compared to balafilcon A lenses (it = 1) (chi(2) = 4.37, P=0.04). Differences in the incidence of CEFs between subjects wearing lenses on a daily-wear basis (n = 1) versus a continuous-wear basis (it = 4) showed a weak statistical significance (chi(2) = 3.03, P=0.08). Conclusions. Lotrafilcon A lenses were associated with a higher incidence of CEFs than balafilcon A lenses were, and this difference may be attributed to differences in the edge design, material, or modulus of rigidity between the two lens types. Subjects wearing lenses on a daily-wear basis showed fewer adverse events than did subjects wearing lenses on a continuous-wear basis. The longer wearing times of subjects wearing lenses on a continuous-wear basis are likely to exacerbate the incidence of CEFs.

The vibrational spectra of rectangular plates

The wire drive pulse-echo system has been extensively used to excite and measure modes of vibration of thin rectangular plates. The frequency spectra of different modes have been investigated as a function of the material elastic moduli and the plate geometry. Most of the work was carried out on isotropic materials. For square plates a wide selection of materials were used. These were made isotropic in their in-plane dimensions where the displacements are taking place. The range of rnaterials enabled the dependence on Poisson's ratio to be investigated. A method of determining the value of Poisson's ratio resulted from this investigation. Certain modes are controlled principally by the shear modulus. Of these the fundamental has two nodal lines across the plate surface. One of them, which has nodes at the corners, (the Lame mode) is uniquely a pure shear mode where the diagonal is a full wave length. One controlled by the Young's modulus has been found. The precise harmonic relationship of the Lame mode series in square and rectangular plates was established. Use of the Rayleigh-Lamb equation has extended the theoretical support. The low order modes were followed over a wide range of sides ratios. Two fundamental types of modes have been recognised; These are the longitudinal modes where the frequency is controlled by the length of the plate only and the 2~f product has an asymptotic value approaching the rod velocity. The other type is the in-plane flexural modes (in effect a flexurally vibrating bar where the -2/w is the geometrical parameter). Where possible the experimental work was related to theory. Other modes controlled by the width dimension of the plate were followed. Anisotropic materials having rolled sheet elastic symmetry were investigated in terms of the appropriate theory. The work has been extended to examine materials from welds in steel plates.

Enzymatic stabilization of gelatin-based scaffolds

The definitive goal of this research is to develop protein-based scaffolds for use in soft tissue regeneration, particularly in the field of dermal healing. The premise of this investigation was to characterize the mechanical properties of gelatin cross-linked with microbial transglutaminase (mTGase) and to investigate the cytocompatibility of mTGase cross-linked gelatin. Dynamic rheological analysis revealed a significant increase in the storage modulus and thermal stability of gelatin after cross-linking with mTGase. Static, unconfined compression tests showed an increase in Young's modulus of gelatin gels after mTGase cross-linking. A comparable increase in gel strength was observed with 0.03% mTGase and 0.25% glutaraldehyde cross-linked gelatin gels. In vitro studies using 3T3 fibroblasts indicated cytotoxicity at a concentration of 0.05% mTGase after 72 h. However, no significant inhibition of cell proliferation was seen with cells grown on lower concentrations of mTGase cross-linked gelatin substrates. The mechanical improvement and cytocompatibility of mTGase cross-linked gelatin suggests mTGase has potential for use in stabilizing gelatin gels for tissue-engineering applications.

Improving the solubility and dissolution of poorly soluble drugs by salt formation and the consequent effect on mechanical properties

The bioavailability of BCS II compounds may be improved by an enhanced solubility and dissolution rate. Four carboxylic acid drugs were selected, which were flurbiprofen, etodolac, ibuprofen and gemfibrozil. The drugs were chosen because they are weak acids with poor aqueous solubility and should readily form salts. The counterions used for salt formation were: butylamine, pentylamine, hexylamine, octylamine, benzylamine, cyclohexylamine, tert-butylamine, 2-amino-2-methylpropan­2-ol, 2-amino-2-methyl propan-1,3-ol and tromethamine. Solubility was partially controlled by the saturated solution pH with the butylamine counterion increasing the solution pH and solubility and dissolution to the greatest extent. As the chain length increased, solubility was reduced due to the increasing lipophilic nature of the counterion. The benzylamine and cyclohexylamine counterions produced crystalline, stable salts but did not improve solubility and dissolution significantly compared to the parent compound. The substitution of hydroxyl groups to tert-butylamine counterions produced an increase in solubility and dissolution. AMP2 resulted in the most enhanced solubility and dissolution compared to the parent drug but using the tris salt did not further improve solubility due to a very stable crystal lattice structure. The parent drugs were very difficult to compress due to orientation effects and lamination. Compacts were prepared of each parent drug and salt and their modulus of elasticity values were measured using a three-point bend (Young’s modulus, E0) were extrapolated to zero porosity and compared. Compressibility and E0 were improved with the butylamine, tert-butylamine, cyclohexylamine and AMP2 counterions. The most significant improvement in compression and E0 was with the AMP2 salts. Mechanical properties were related to the hydrogen bonding within the crystal lattice structure for the gemfibrozil salt series.

Local and systemic delivery of a novel group of inhibitors of transglutaminase enzyme: A potential approach for treating of catheter-related complications and liver fibrosis

The present thesis investigates targeted (locally and systemically) delivery of a novel group of inhibitors of enzyme transglutaminases (TGs). TGs are a widely distributed group of enzymes that catalyse the formation of isopeptide bonds between the y-carboxamide group of protein-bound glutamines and the a-amino group of protein-bound lysines or polyamines. The first group of the novel inhibitors tested were the tluorescently labelled inhibitors of Factor XIIIa (FXIIIa). These small, non-toxic inhibitors have the potential to prevent stabilisation of thrombi by FXIIIa and consequently increase the natural rate of thrombolysis, in addition it reduces staphylococcal colonisation of catheters by inhibiting their FXIIIa¬mediated cross-linking to blood clot proteins on the central venous catheter (CVCs) surface. The aim of this work was to incorporate the FXIIIa inhibitor either within coating of polyurethane (PU) catheters or to integrate it into silicone catheters, so as to reduce the incidence of thrombotic occlusion and associated bacterial infection in CVCs. The initial work focused on the incorporation of FXIIIa inhibitors within polymeric coatings of PU catheters. After defining the key characteristics desired for an effective polymeric-coating, polyvinylpyrrolidone (PVP), poly(lactic-co-glycolic acid) (PLGA) or their combination were studies as polymers of choice for coating of the catheters_ The coating was conducted by dip-coating method in a polymer solution containing the inhibitor. Upon incubation of the inhibitor-and polymer-coated strips in buffer, PVP was dissolved instantly, generating fast and significant drug release, whilst PLGA did not dissolve, yielding a slow and an insufficient amount of drug release. Nevertheless, the drug release profile was enhanced upon employing a blend solution of PVP and PLGA. The second part of the study was to incorporate the FXIIIa inhibitor into a silicone elastomer; results demonstrated that FXIIIa inhibitor can be incorporated and released from silicone by using citric acid (CA) and sodium bicarbonate (SB) as additives and the drug release rate can be controlled by the amount of incorporated additives in the silicone matrix. Furthermore, it was deemed that the inhibitor was still biologically active subsequent to being released from the silicone elastomer strips. Morphological analysis confirmed the formation of channels and cracks inside the specimens upon the addition of CA and SB. Nevertheless, the tensile strength, in addition to Young's modulus of silicone elastomer strips, decreased constantly with an increasing amount of amalgamated CA/ SB in the formulations. According to our results, incorporation of FXIIIa inhibitor into catheters and other medical implant devices could offer new perspectives in preventing bio-material associated infections and thrombosis. The use of tissue transglutaminase (T02) inhibitor for treating of liver fibrosis was also investigated. Liver fibrosis is characterized by increased synthesis and decreased degradation of the extracellular matrix (ECM). Transglutaminase-mediated covalent cross-linking is involved in the stabilization of ECM in human liver fibrosis. Thus, TG2 inhibitors may be used to counteract the decreased degradation of the ECM. The potential of a liposome based drug delivery system for site specific delivery of the fluorescent TG2 inhibitor into the liver was investigated; results indicated that the TG2 inhibitor can be successfully integrated into liposomes and delivered to the liver, therefore demonstrating that liposomes can be employed for site-specific delivery of TG2 inhibitors into the liver and TG2 inhibitor incorporating liposomes could offer a new approach in treating liver fibrosis and its end stage disease cirrhosis.

Structural behaviour of glass reinforced plastics

The aim of this research is to promote the use of G.R.P. as a structural material. In the past, the use of G.R.P. has been confined to non-load carrying applications. Such uses are still rapidly increasing but in addition significant changes have been made during the last decade in the development of semi-structural and now even fully structural applications. Glass-reinforced plastic is characterized by a high strength but a relatively low modulus of elasticity. For this reasona G.R.P. structure can expect to show large deformations as a result of which the individual structural members will fail under load due to a loss of stability rather than approaching the ultimate strength of the material. For this reason the selection of the geometrical shapes of G.R.P. structural elements is considered to be an important factor in designing G.R.P. structures. The first chapter of this thesis deals with a general review of the theoretical and experimental methods used to describe the structural properties of G.R.P. The research programme includes five stages dealing with the structural behaviour of G.R.P. The first stage (Chapter 2) begins with selecting and designing an optimum box beam cross-section which gives the maximum flexural and torsional rigidity. The second stage of investigation (Chapter 3) deals with beam to beam connections. A joint was designed and manufactured with different types of fasteners used to connect two beam units. A suitable fastener was selected and the research extended to cover the behaviour of long span beams using multiple joints. The third part of the investigation includes a study of the behaviour of box beams subjected to combined bending, shear and torsion. A special torque rig was developed to perform the tests. Creep deformation of 6 m span G.R.P. was investigated as the fourth stage under a range of loading conditions. As a result of the phenomenon of post buckling behaviour exhibited in the compression flange during testing of box beams during earlier stages of the investigation it was decided to consider this phenomenon in more detail in the final stage of the investigation. G.R.P. plates with different fibre orientation were subjected to uniaxial compression and tested up to failure. In all stages of the investigation theoretical predictions and experimental results were compared and generally good correlation between theory and experimental data was observed.

The structural properties of glassfibre reinforced plastics

The research work described in this thesis is concerned with the development of glassfibre reinforced plastics for structural uses in Civil Engineering construction. The first stage was primarily concerned with the design of GRP lamintes with structura1 properties and method of manufacture suitable for use with relatively large structural components. A cold setting, pressure moulding technique was developed which proved to be efficient in reducing the void content in the composite and minimising the exothermic effect due to curing. The effect of fibre content and fibre arrangement on strength and stiffness of the cornposite was studied and the maximum amount of' fibre content that could be reached by the adopted type of moulding technique was determined. The second stage of the project was concerned with the introduction of steel-wire "sheets" into the GRP cornposites, to take advantage of the high modulus of steel wire to improve the GRP stiffness and to reduce deformation. The experimental observations agreed reasonably well with theoretical predictions in both first and second stages of the work. The third stage was concerned with studying the stability of GRP flat rectangular plates subjected to uniaxial compression or pure shear, to simulate compression flanges or shear webs respectively. The investigation was concentrated on the effect of fibre arrangement in the plate on buckling load. The effect of the introduction of steel-wire sheets on the plate stability in compression was also investigated. The boundary conditions were chosen to be close to those usually assumed in built-up box-sections for both compression flanges and webs. The orthotropic plate and the mid-plane symmetric were used successfully in predicting the buckling load theoretically. In determining the buckling load experimentally, two methods were used. The Southwell plot method and electrical strain gauge method. The latter proved to be more reliable in predicting the buckling load than the former, especially for plates under uniaxial compression. Sample design charts for GRP plates that yield and buckle simultaneously under compression are also presented in the thesis. The final stage of the work dealt with the design and test of GRP beams. The investigation began by finding the optimum cross-section for a GRP beam. The cross-section which was developed was a thin walled corrugated section which showed higher stiffness than other cross-sections for the same cross-sectional area (i.e. box, I, and rectangular sections). A cold setting, hand layings technique was used in manufacturing these beams wbich were of nine types depending on the type of glass reinforcement employed and the arrangement of layers in the beam. The simple bending theory was used in the beam design and proved to be satisfactory in predicting the stresses and deflections. A factor of safety of 4 was chosen for design purposes and considered to be suitable for long term use under static load. Because of its relatively low modulus, GRP beams allowable deflection was limited to 1/120th of the span which was found to be adequate for design purposes. A general discussion of the behaviour of GRP composites and their place relative to the more conventional structural material was also presented in the thesis.

Effects of fibre reinforcement on the mechanical properties of brushite cement

In this study the effect of structure and amount of polyglactin fibre incorporation into a brushite forming calcium phosphate cement system and the effect of mechanical compaction on the fibre modified system were investigated. In comparison the effect of resorbable polycaprolactone surface coating of cement specimens was investigated. The results showed that, apart from the mechanical properties of the reinforcing material, the structure of the incorporated fibres, regular or random, is crucial for the resulting flexural strength and modulus of elasticity. Fibre reinforcement could also be combined with mechanical compaction of the cement/fibre composite paste leading to a possible 7-fold increase in flexural strength or an almost 5-fold increase in modulus of elasticity. Reinforcement of the tensile surface of cement grafts may ultimately improve strength where required, especially in conjunction with bone fixation devices. © 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effect of microstructure upon elastic behaviour of human tooth enamel

Tooth enamel is the stiffest tissue in the human body with a well-organized microstructure. Developmental diseases, such as enamel hypomineralisation, have been reported to cause marked reduction in the elastic modulus of enamel and consequently impair dental function. We produce evidence, using site-specific transmission electron microscopy (TEM), of difference in microstructure between sound and hypomineralised enamel. Built upon that, we develop a mechanical model to explore the relationship of the elastic modulus of the mineral-protein composite structure of enamel with the thickness of protein layers and the direction of mechanical loading. We conclude that when subject to complex mechanical loading conditions, sound enamel exhibits consistently high stiffness, which is essential for dental function. A marked decrease in stiffness of hypomineralised enamel is caused primarily by an increase in the thickness of protein layers between apatite crystals and to a lesser extent by an increase in the effective crystal orientation angle. © 2009 Elsevier Ltd. All rights reserved.

Grewia gum 1:some mechanical and swelling properties of compact and film

Purpose: To study the mechanical and dynamic swelling properties of grewia gum, evaluate its compression behaviour and determine the effect of drying methods on its properties. Methods: Compacts (500 mg) of both freeze-dried and air-dried grewia gum were separately prepared by compression on a potassium bromide (KBr) press at different pressures and subjected to Heckel analysis. Swelling studies were performed using 200 mg compacts of the gum (freeze-dried or air-dried) compressed on a KBr press. The mechanical properties of the films of the gum prepared by casting 1 % dispersions of the gum were evaluated using Hounsfield tensiometer. The mechanical properties of grewia gum films were compared with films of pullulan and guar gum which were similarly prepared. The effect of temperature on the water uptake of the compacts was studied and the data subjected to Schott's analysis. Results: Drying conditions had no effect on the yield pressure of the gum compacts as both air-dried and freeze-dried fractions had a yield pressure of 322.6 MPa. The plots based on Schott's equation for the grewia gum samples showed that both samples (freeze-dried and air-dried) exhibited long swelling times. Grewia gum film had a tensile strength of 19.22±3.61 MPa which was similar to that of pullulan films (p > 0.05). It had an elastic modulus of 2.13±0.12 N/mm2 which was significantly lower (p < 0.05) than those of pullulan and guar gum with elastic moduli of 3.33±0.00 and 2.86±0.00 N/mm2, respectively. Conclusion: The type of drying method used does not have any effect on the degree of plasticity of grewia gum compacts. Grewia gum obtained by either drying method exhibited extended swelling duration. Matrix tablet formulations of the gum will likely swell slowly and promote sustained release of drug. © Pharmacotherapy Group, Faculty of Pharmacy, University of Benin, Benin City.

Performance analysis of polymer optical fibre based Fabry-Perot sensor formed by two uniform Bragg gratings

The stress sensitivity of polymer optical fibre (POF) based Fabry-Perot sensors formed by two uniform Bragg gratings with finite dimensions is investigated. POF has received high interest in recent years due to its different material properties compared to its silica counterpart. Biocompatibility, a higher failure strain and the highly elastic nature of POF are some of the main advantages. The much lower Young’s modulus of polymer materials compared to silica offers enhanced stress sensitivity to POF based sensors which renders them great candidates for acoustic wave receivers and any kind of force detection. The main drawback in POF technology is perhaps the high fibre loss. In a lossless fibre the sensitivity of an interferometer is proportional to its cavity length. However, the presence of the attenuation along the optical path can significantly reduce the finesse of the Fabry-Perot interferometer and it can negatively affect its sensitivity at some point. The reflectivity of the two gratings used to form the interferometer can be also reduced as the fibre loss increases. In this work, a numerical model is developed to study the performance of POF based Fabry-Perot sensors formed by two uniform Bragg gratings with finite dimensions. Various optical and physical properties are considered such as grating physical length, grating effective length which indicates the point where the light is effectively reflected, refractive index modulation of the grating, cavity length of the interferometer, attenuation and operating wavelength. Using this model, we are able to identify the regimes in which the PMMA based sensor offer enhanced stress sensitivity compared to silica based one.

Comparative physical, mechanical and crystallographic properties of a series of gemfibrozil salts

Objectives Understanding the impact of the counterion on the properties of an acidic or basic drug may influence the choice of salt form, especially for less potent drugs with a high drug load per unit dose. The aim of this work was to determine the influence of the hydrogen bonding potential of the counterion on the crystal structure of salts of the poorly soluble, poorly compressible, acidic drug gemfibrozil and to correlate these with mechanical properties. Methods Compacts of the parent drug and the salts were used to determine Young's modulus of elasticity using beam bending tests. Crystal structures were determined previously from X-ray powder diffraction data. Key findings The free acid, tert-butylamine, 2-amino-2-methylpropan-1-ol and 2-amino-2-methylpropan-1, 3-diol salts had a common crystal packing motif of infinite hydrogen-bonded chains with cross-linking between pairs of adjacent chains. The tromethamine (trsi) salt, with different mechanical properties, had a two-dimensional sheet-like network of hydrogen bonds, with slip planes, forming a stiffer compact. Conclusions The type of counter ion is important in determining mechanical properties and could be selected to afford slip and plastic deformation. © 2010 Royal Pharmaceutical Society of Great Britain.

Osmotic dehydration in plant tissues

The primary aim of the thesis is to provide a comprehensive investigation of the osmotic dehydration processes in plant tissue. Effort has been concentrated on the modelling for simulating the processes. Two mathematical models for simulating the mass transfer during osmotic dehydration processes in plant tissues are developed and verified using existing experimental data. Both models are based on the mechanism of diffusion and convection of any mobile material that can transport in plant tissues. The mass balance equation for the transport of each constituent is established separately for intracellular and extra-cellular volumes with taking into account the mass transfer across the cell membrane the intracellular and extra-cellular volumes and the shrinkage of the whole tissue. The contribution from turgor pressure is considered in both models. Model two uses Darcy’s law to build the relation between shrinkage velocity and hydrostatic pressure in each volume because the plant tissue can be considered as the porous medium. Moreover, it has been extended to solve the multi-dimensional problems. A lot of efforts have been made to the parameter study and the sensitivity analyses. The parameters investigated including the concentration of the osmotic solution, diffusion coefficient, permeability of the cell membrane, elastic modulus of the cell wall, critical cell volume etc. The models allow us to quantitatively simulate the time evolution of intracellular and extra-cellular volumes as well as the time evolution of concentrations in each cross-section.

Ocular response to silicone-hydrogel contact lenses

The thesis investigates the ocular response to silicone-hydrogel (SiH) contact lens wear, a relatively new contact lens material that has a higher modulus of rigidity and different surface coating than used in conventional hydrogel materials. The properties of SiH materials differ significantly from conventional hydrogels and, using subjective and objective means of assessment, the thesis examines how these properties affect reflection and biometry, ocular physiology, tear film characteristics, symptomatology, adverse events and complications. A range of standard and newly designed investigative techniques were employed, and latter involving novel imaging techniques, for the objective assessment of physiological changes which occur with contact lens wear. The study is the first to combine these techniques with biochemical analyses of the tear film composition. Forty-seven subjects were fitted with SiH lenses and randomly allocated to one of the two materials currently on the market (Lotrafilcon A or Balafilcon A) on an either daily or continuous wear basis. An additional control group of 14 age-matched non-contact lens wearers were monitored over the same period. Measurements were taken before and 1, 3, 6, 12 and 18 months after initial fitting. The findings reported in this thesis will enable contact lens practitioners and manufacturers to understand further the optical, physiological and biochemical nature of the ocular response to SiH contact lenses and hence facilitate the development of this important generation of contact lens material.