Bone apposition to a titanium-zirconium alloy implant, as compared to two other titanium-containing implants

Implants made of commercially pure titanium (cpTi) are widely and successfully used in dentistry. For certain indications, diameter-reduced Ti alloy implants with improved mechanical strength are highly desirable. The aim was to compare the osseointegration of titanium-zirconium (TiZr) and cpTi implants with a modified sandblasted and acid-etched (SLActive) surface and with a Ti6Al4V alloy that was sand-blasted and acid-washed. Cylindrical implants with two, 0.75 mm deep, circumferential grooves were placed in the maxilla of miniature pigs and allowed to heal for 1, 2, 4 and 8 weeks. Undecalcified toluidine blue-stained ground sections were produced. Surface topography, area fraction of tissue components, and bone-to-implant contact (BIC) were determined. All materials showed significantly different surface roughness parameters. The amount of new bone within the implant grooves increased over time, without significant differences between materials. However, BIC values were significantly related to the implant material and the healing period. For TiZr and cpTi implants, the BIC increased over time, reaching values of 59.38 % and 76.15 % after 2 weeks, and 74.50 % and 84.67 % after 8 weeks, respectively. In contrast, the BIC for Ti6Al4V implants peaked with 42.29 % after 2 weeks followed by a decline to 28.60 % at 8 weeks. Significantly more surface was covered by multinucleated giant cells on Ti6Al4V implants after 4 and 8 weeks. In conclusion, TiZr and cpTi implants showed faster osseointegration than Ti6Al4V implants. Both chemistry and surface topography might have influenced the results. The use of diameter-reduced TiZr implants in more challenging clinical situations warrants further documentation in long-term clinical studies.

A Double-Blind Randomized Controlled Trial (RCT) of Titanium-13Zirconium versus Titanium Grade IV Small-Diameter Bone Level Implants in Edentulous Mandibles - Results from a 1-Year Observation Period

Background: The use of endosseous dental implants has become common practice for the rehabilitation of edentulous patients, and a two-implant overdenture has been recommended as the standard of care. The use of small-diameter implants may extend treatment options and reduce the necessity for bone augmentation. However, the mechanical strength of titanium is limited, so titanium alloys with greater tensile and fatigue strength may be preferable. Purpose: This randomized, controlled, double-blind, multicenter study investigated in a split-mouth model whether small-diameter implants made from Titanium-13Zirconium alloy (TiZr, Roxolid™) perform at least as well as Titanium Grade IV implants. Methods and Materials: Patients with an edentulous mandible received one TiZr and one Ti Grade IV small-diameter bone level implant (3.3 mm, SLActive®) in the interforaminal region. The site distribution was randomized and double-blinded. Outcome measures included change in radiological peri-implant bone level from surgery to 12 months post-insertion (primary), implant survival, success, soft tissue conditions, and safety (secondary). Results: Of 91 treated patients, 87 were available for the 12-month follow-up. Peri-implant bone level change (-0.3 ± 0.5 mm vs -0.3 ± 0.6 mm), plaque, and sulcus bleeding indices were not significantly different between TiZr and Ti Grade IV implants. Implant survival rates were 98.9 percent and 97.8 percent, success rates were 96.6 percent and 94.4 percent, respectively. Nineteen minor and no serious adverse events were related to the study devices. Conclusion: This study confirms that TiZr small-diameter bone level implants provide at least the same outcomes after 12 months as Ti Grade IV bone level implants. The improved mechanical properties of TiZr implants may extend implant therapy to more challenging clinical situations.

Osseointegration and biocompatibility of different metal implants-a comparative experimental investigation in sheep

Background In the present study, 4 different metallic implant materials, either partly coated or polished, were tested for their osseointegration and biocompatibility in a pelvic implantation model in sheep. Methods Materials to be evaluated were: Cobalt-Chrome (CC), Cobalt-Chrome/Titanium coating (CCTC), Cobalt-Chrome/Zirconium/Titanium coating (CCZTC), Pure Titanium Standard (PTST), Steel, TAN Standard (TANST) and TAN new finish (TANNEW). Surgery was performed on 7 sheep, with 18 implants per sheep, for a total of 63 implants. After 8 weeks, the specimens were harvested and evaluated macroscopically, radiologically, biomechanically (removal torque), histomorphometrically and histologically. Results Cobalt-Chrome screws showed significantly (p = 0.031) lower removal torque values than pure titanium screws and also a tendency towards lower values compared to the other materials, except for steel. Steel screws showed no significant differences, in comparison to cobalt-chrome and TANST, however also a trend towards lower torque values than the remaining materials. The results of the fluorescence sections agreed with those of the biomechanical test. Histomorphometrically, there were no significant differences of bone area between the groups. The BIC (bone-to-implant-contact), used for the assessment of the osseointegration, was significantly lower for cobalt-chrome, compared to steel (p = 0.001). Steel again showed a lower ratio (p = 0.0001) compared to the other materials. Conclusion This study demonstrated that cobalt-chrome and steel show less osseointegration than the other metals and metal-alloys. However, osseointegration of cobalt-chrome was improved by zirconium and/or titanium based coatings (CCTC, TANST, TAN, TANNEW) being similar as pure titanium in their osseointegrative behavior.

Experimental peri-implant mucositis at different implant surfaces

OBJECTIVES To histologically and immunologically assess experimental peri-implant mucositis at surface enhanced modified (mod) hydrophilic titanium implants. MATERIALS AND METHODS In a split-mouth design (n = 6 foxhounds), four different implants were inserted on each side of the maxilla: three titanium-zirconium alloy implants (TiZr) with either modSLA (sand-blasted, acid etched and chemically mod), modMA (machined, acid etched and chemically mod), or M (machined) surfaces in the transmucosal portion, and one titanium implant with a machined transmucosal portion (TiM). Experimental mucositis was induced at one randomly assigned side (NPC), whereas the contra-lateral maxillary side received mechanical plaque removal three times per week (PC). At 16 weeks, tissue biopsies were processed for histological (primary outcome: apical extension of the inflammatory cell infiltrate measured from the mucosal margin - PM-aICT) and immunohistochemical (CD68 antigen reactivity) analyses. Peri-implant sulcus fluid was analysed for interleukin (IL)-1β, IL-8, matrix metalloproteinase (MMP)-8 and myeloperoxidase (MPO). RESULTS Mean PM-aICT values varied between 1.86 (TiZrmodSLA) and 3.40 mm (TiM) in the UPC group, and between 0.88 (TiZrmodSLA) and 2.08 mm (TiZrM) in the PC group. Mean CD68, IL-1β, IL-8, MMP-8 and MPO values were equally distributed between mod- and control implants in both NPC and PC groups. CONCLUSIONS The progression of experimental mucositis was comparable at all implant surfaces investigated.

In vitro adhesion of fibroblastic cells to titanium alloy discs treated with sodium hydroxide.

OBJECTIVE Adhesion of osteogenic cells on titanium surfaces is a prerequisite for osseointegration. Alkali treatment can increase the hydrophilicity of titanium implant surfaces, thereby supporting the adhesion of blood components. However, it is unclear if alkali treatment also supports the adhesion of cells with a fibroblastic morphology to titanium. MATERIALS AND METHODS Here, we have used a titanium alloy (Ti-6AL-4V) processed by alkali treatment to demonstrate the impact of hydrophilicity on the adhesion of primary human gingival fibroblast and bone cells. Also included were the osteosarcoma and fibroblastoma cell lines, MG63 and L929, respectively. Cell adhesion was determined by scanning electron microscopy. We also measured viability, proliferation, and protein synthesis of the adherent cells. RESULTS Alkali treatment increased the adhesion of gingival fibroblasts, bone cells, and the two cell lines when seeded onto the titanium alloy surface for 1 h. At 3 h, no significant changes in cell adhesion were observed. Cells grown for 1 day on the titanium alloy surfaces processed by alkali treatment behave similarly to untreated controls with regard to viability, proliferation, and protein synthesis. CONCLUSION Based on these preliminary In vitro findings, we conclude that alkali treatment can support the early adhesion of cells with fibroblastic characteristics to a titanium alloy surface.

[Titanium-alloy vs. CoCr-alloy in removable prosthodontics--a clinical study]

Different types of titanium-alloys instead of CoCr-alloys have been tested as material for the framework of removable partial dentures (RPD). Adequate casting and processing techniques have been developed which enable to fabricate frameworks of complex designs and the problem limits porosity. This opened new possibilities for the use of titanium-alloys with improved properties (E-module). The aim of this study was to summarise the use of titanium in removable prosthodontics and to evaluate prospectively the use of the Ti6A17Nb-alloy for RPDs in a small group of patients. Two identically designed RPDs from CoCr-alloy (remanium GM 800+) and Ti6A17Nb-alloy (girotan L) were produced for ten patients. They had to wear each RPD during six months, first the CoCr-RPD and then the Ti6A17Nb-RPD. A questionnaire (visual analogue scale = VAS) was completed by the patients after one, three and six months of function for each RPD. Prosthetic complications and service needed were recorded. After the end of the entire observation period of twelve months, the patients remained with the Ti6A17Nb-RPD and answered the questionnaire after another six months. All parameters regarding the design of the RPDs were positively estimated by the dentist. Minimal, not significant differences were noted by the patients concerning comfort, stability and retention (VAS). Clinically, no differences in technical aspects or regarding biological complications were observed after six-months periods. The Ti6A17Nb-alloy (girotan L) for the framework of RPDs was judged by patients and professionals to be equivalent to RPDs made from CoCr-alloy. No differences in material aspects could objectively be observed. The Ti6A17Nb-alloy can be beneficial for patients with allergies or incompatibility with one or several components of the CoCr-alloy.

Small-diameter titanium grade IV and titanium-zirconium implants in edentulous mandibles: five-year results from a double-blind, randomized controlled trial.

BACKGROUND The aim of this study was to compare the 5-year survival and success rates of 3.3 mm dental implants either made from titanium-zirconium (TiZr) alloy or from Grade IV titanium (Ti Grade IV) in mandibular implant-based removable overdentures. METHODS The core study had a follow-up period of 36 months and was designed as a randomized, controlled, double-blind, split-mouth multicenter clinical trial. Patients with edentulous mandibles received two Straumann Bone Level implants (diameter 3.3 mm, SLActive®), one of TiZr (test) and one of Ti Grade IV (control), in the interforaminal region. This follow-up study recruited patients from the core study and evaluated the plaque and sulcus bleeding indices, radiographic crestal bone level, as well as implant survival and success 60 months after implant placement. RESULTS Of the 91 patients who initially received implants, 75 completed the 36 month follow-up and 49 were available for the 60 month examination. Two patients were excluded so that a total of 47 patients with an average age of 72 ± 8 years were analysed. The characteristics and 36-month performance of the present study cohort did not differ from the non-included initial participants (p > 0.05). In the period since the 36-month follow-up examination, no implant was lost. The cumulative implant survival rate was 98.9 % for the TiZr group and 97.8 % for the Ti Grade IV group. Crestal bone level changes at 60 months were not different in the test and control group (TiZr -0.60 ± 0.69 mm and Ti Grade IV -0.61 ± 0.83 mm; p = 0.96). The cumulative implant success rate after 60 months was 95.8 and 92.6 % for TiZr and Ti Grade IV, respectively. CONCLUSIONS After 60 months, the positive outcomes of the 36 month results for TiZr and Ti Grade IV implants were confirmed, with no significant differences with regard to crestal bone level change, clinical parameters and survival or success rates. TiZr implants performed equally well compared to conventional Ti Grade IV 3.3 mm diameter-reduced implants for mandibular removable overdentures. TRIAL REGISTRATION Registered on www.clinicaltrials.gov: NCT01878331.

Early loading after 21 days of healing of nonsubmerged titanium implants with a chemically modified sandblasted and acid-etched surface: two-year results of a prospective two-center study

PURPOSE: The aim of this two-center study was to evaluate screw-type titanium implants with a chemically modified, sandblasted and acid-etched surface when placed in the posterior maxilla or mandible, and loaded 21 days after placement. MATERIAL AND METHODS: All 56 patients met strict inclusion criteria and provided informed consent. Each patient displayed either a single-tooth gap, an extended edentulous space, or a distal extension situation in the posterior mandible or maxilla. Eighty-nine dental implants (SLActive, Institut Straumann AG, Basel, Switzerland) were inserted according to an established nonsubmerged protocol and underwent undisturbed healing for a period of 21 days. Where appropriate, the implants were loaded after 21 days of healing with provisional restorations in full occlusion. Definitive metal ceramic restorations were fabricated and positioned on each implant after 6 months of healing. Clinical measurements regarding soft tissue parameters and radiographs were obtained at different time points up to 24 months after implant placement. RESULTS: Of the 89 inserted implants, two (2.2%) implants failed to integrate and were removed during healing, and two (2.2%) additional implants required a prolonged healing time. A total of 85 (95.6%) implants were therefore loaded without incident after 21 days of healing. No additional implant was lost throughout the study period, whereas one implant was lost to follow-up and therefore left unaccounted for further analysis. The remaining 86 implants all exhibited favorable radiographic and clinical findings. Based on strict success criteria, these implants were considered successfully integrated 2 years after insertion, resulting in a 2-year success rate of 97.7%. CONCLUSION: The results of this prospective two-center study demonstrate that titanium implants with a modified SLA surface can predictably achieve successful tissue integration when loaded in full occlusion 21 days after placement. Integration could be maintained without incident for at least 2 years of follow-up.

Bioengineered periodontal tissue formed on titanium dental implants

The ability to use autologous dental progenitor cells (DPCs) to form organized periodontal tissues on titanium implants would be a significant improvement over current implant therapies. Based on prior experimental results, we hypothesized that rat periodontal ligament (PDL)-derived DPCs can be used to bioengineer PDL tissues on titanium implants in a novel, in vivo rat maxillary molar implant model. Analyses of recovered implants revealed organized PDL tissues surrounding titanium implant surfaces in PDL-cell-seeded, and not in unseeded control, implants. Rat PDL DPCs also exhibited differentiative potential characteristic of stem cells. These proof-of-principle findings suggest that PDL DPCs can organize periodontal tissues in the jaw, at the site of previously lost teeth, indicating that this method holds potential as an alternative approach to osseointegrated dental implants. Further refinement of this approach will facilitate the development of clinically relevant methods for autologous PDL regeneration on titanium implants in humans.

A pilot study to evaluate the success and survival rate of titanium-zirconium implants in partially edentulous patients: results after 24 months of follow-up

Implants made from a new titanium-zirconium (TiZr) alloy (Roxolid) have shown good osseointegration with no adverse effects in animal studies. This single-cohort pilot study was performed to evaluate the performance and safe use of reduced-diameter implants made from this new TiZr alloy for the first time in human subjects, in a prospective case-controlled series.

The role of macrophages in the clearance of inhaled ultrafine titanium dioxide particles

The role of macrophages in the clearance of particles with diameters less than 100 nm (ultrafine or nanoparticles) is not well established, although these particles deposit highly efficiently in peripheral lungs, where particle phagocytosis by macrophages is the primary clearance mechanism. To investigate the uptake of nanoparticles by lung phagocytes, we analyzed the distribution of titanium dioxide particles of 20 nm count median diameter in macrophages obtained by bronchoalveolar lavage at 1 hour and 24 hours after a 1-hour aerosol inhalation. Differential cell counts revealing greater than 96% macrophages and less than 1% neutrophils and lymphocytes excluded inflammatory cell responses. Employing energy-filtering transmission electron microscopy (EFTEM) for elemental microanalysis, we examined 1,594 macrophage profiles in the 1-hour group (n = 6) and 1,609 in the 24-hour group (n = 6). We found 4 particles in 3 macrophage profiles at 1 hour and 47 particles in 27 macrophage profiles at 24 hours. Model-based data analysis revealed an uptake of 0.06 to 0.12% ultrafine titanium-dioxide particles by lung-surface macrophages within 24 hours. Mean (SD) particle diameters were 31 (8) nm at 1 hour and 34 (10) nm at 24 hours. Particles were localized adjacent (within 13-83 nm) to the membrane in vesicles with mean (SD) diameters of 592 (375) nm at 1 hour and 414 (309) nm at 24 hours, containing other material like surfactant. Additional screening of macrophage profiles by conventional TEM revealed no evidence for agglomerated nanoparticles. These results give evidence for a sporadic and rather unspecific uptake of TiO(2)-nanoparticles by lung-surface macrophages within 24 hours after their deposition, and hence for an insufficient role of the key clearance mechanism in peripheral lungs.

Potential of chemically modified hydrophilic surface characteristics to support tissue integration of titanium dental implants

In the past, several modifications of specific surface properties such as topography, structure, chemistry, surface charge, and wettability have been investigated to predictably improve the osseointegration of titanium implants. The aim of the present review was to evaluate, based on the currently available evidence, the impact of hydrophilic surface modifications of titanium for dental implants. A surface treatment was performed to produce hydroxylated/hydrated titanium surfaces with identical microstructure to either acid-etched, or sand-blasted, large grit and acid-etched substrates, but with hydrophilic character. Preliminary in vitro studies have indicated that the specific properties noted for hydrophilic titanium surfaces have a significant influence on cell differentiation and growth factor production. Animal experiments have pointed out that hydrophilic surfaces improve early stages of soft tissue and hard tissue integration of either nonsubmerged or submerged titanium implants. This data was also corroborated by the results from preliminary clinical studies. In conclusion, the present review has pointed to a potential of hydrophilic surface modifications to support tissue integration of titanium dental implants.

Early loading of nonsubmerged titanium implants with a chemically modified sand-blasted and acid-etched surface: 6-month results of a prospective case series study in the posterior mandible focusing on peri-implant crestal bone changes and implant stability quotient (ISQ) values

PURPOSE: The aim of this prospective case series study was to evaluate the short-term success rates of titanium screw-type implants with a chemically modified sand-blasted and acid-etched (mod SLA) surface after 3 weeks of healing. MATERIAL AND METHODS: A total of 56 implants were inserted in the posterior mandible of 40 partially edentulous patients exhibiting bone densities of class I to III. After a healing period of 3 weeks, all implants were functionally loaded with a screw-retained crown or fixed dental prosthesis. The patients were recalled at weeks 4, 7, 12, and 26 for monitoring and assessment of clinical and radiological parameters, including implant stability quotient (ISQ) measurements. RESULTS: None of the implants failed to integrate. However, two implants were considered "spinners" at day 21 and left unloaded for an extended period. Therefore, 96.4% of the inserted implants were loaded according to the protocol tested. All 56 implants including the "spinners" showed favorable clinical and radiographic findings at the 6-month follow-up examination. The ISQ values increased steadily throughout the follow-up period. At the time of implant placement, the range of ISQ values exhibited a mean of 74.33, and by week 26, a mean value of 83.82 was recorded. Based on strict criteria, all 56 implants were considered successfully integrated, resulting in a 6-month survival and success rate of 100.0%. CONCLUSION: This prospective study using an early-loading protocol after 3 weeks of healing demonstrated that titanium implants with the modified SLA surface can achieve and maintain successful tissue integration over a period of at least 6 months. The ISQ method seems feasible to monitor implant stability during the initial wound-healing period.

Long-term outcomes of dental implants with a titanium plasma-sprayed surface: a 20-year prospective case series study in partially edentulous patients

BACKGROUND Long-term studies of ≥10 years are important milestones to get a better understanding of potential factors causing implant failures or complications. PURPOSE The present study investigated the long-term outcomes of titanium dental implants with a rough, microporous surface (titanium plasma sprayed [TPS]) and the associated biologic and technical complications in partially edentulous patients with fixed dental prostheses over a 20-year follow-up period. MATERIALS AND METHODS Sixty-seven patients, who received 95 implants in the 1980s, were examined with well-established clinical and radiographic parameters. Based on these findings, each implant was classified as either successful, surviving, or failed. RESULTS Ten implants in nine patients were lost during the observation period, resulting in an implant survival rate of 89.5%. Radiographically, 92% of the implants exhibited crestal bone loss below 1 mm between the 1- and 20-year follow-up examinations. Only 8% yielded peri-implant bone loss of >1 mm and none exhibited severe bone loss of more than 1.8 mm. During the observation period, 19 implants (20%) experienced a biologic complication with suppuration. Of these 19 implants, 13 implants (13.7%) had been treated and were successfully maintained over the 20-year follow-up period. Therefore, the 20-year implant success rate was 75.8 or 89.5% depending on the different success criteria. Technical complications were observed in 32%. CONCLUSION The present study is the first to report satisfactory success rates after 20 years of function of dental implants with a TPS surface in partially edentulous patients.