Shear bond strength of resin cements to human dentin

OBJECTIVES: The objectives of this in vitro study were (1) to assess the bond strength of the universal cement RelyX Unicem to dentin and to compare it with three conventional resin cements, (2) to test the influence of aging on their bonding capacity and (3) to test the influence of the operator on bonding quality by performing the same test in two different centers. METHODS: 160 third molars, divided into 80 for tests at the University of Zurich (Z) and 80 for tests at the University of Berne (B), were assigned to 2 x 8 subgroups of 10 teeth each. The specimens were prepared with the corresponding bonding agents and acrylic rods were luted either with RelyX Unicem (U), RelyX ARC (A), Multilink (M) or Panavia 21 (P). All specimens were stored in water for 24h (W) and half of the specimens were subjected to 1500 cycles of thermocycling (5 degrees C and 55 degrees C) (T). Bond strength was measured by means of a shear test. RESULTS: After water storage RelyX Unicem exhibited lowest bond strength (UWZ: 9.2+/-1.6 MPa, UWB: 9.9+/-1.2 MPa, AWZ: 15.3+/-6.0 MPa, AWB: 12.2+/-4.3 MPa, MWZ: 15.6+/-3.3 MPa, MWB: 12.4 MPa+/-2.4, PWZ: 13.4+/-2.9 MPa, PWB: 14.9+/-2.6 MPa). Thermocycling affected the bonding performance of all four cements. However, bond strength of RelyX Unicem was least influenced by thermocycling (UTZ: 9.4+/-2.9 MPa, UTB: 8.6+/-1.3 MPa, ATZ: 11.4+/-6.3 MPa, ATB: 13.3+/-3.7 MPa, MTZ: 15.4+/-3.1 MPa, MTB: 10.3+/-2.4 MPa, PTZ: 11.1+/-2.8 MPa, PTB: 11.3+/-2.8 MPa). SIGNIFICANCE: Although the bond strength of RelyX Unicem to dentin was lower in comparison to RelyX ARC, Multilink and Panavia 21, its bond strength was less sensitive to variations in handling and aging.

Immediate shear bond strengths of a composite, a compomer and a glass ionomer to a ceramic substrate.

PURPOSE To determine the best-performing combination of three core buildup materials and three bonding materials based on their bond strength to ceramic blocks in vitro. MATERIALS AND METHODS The materials used for core buildup were a composite (Tetric EvoCeram), a compomer (Compoglass F), and a glass-ionomer cement (Ketac Fil Plus), and for bonding, a three-step etch-and-rinse adhesive (Syntac), a two-step etch-and-rinse adhesive (ExciTE), and a single-step system (RelyX Unicem). Bond strength to ceramic blocks was determined by shear bond strength testing. Fracture behavior was evaluated by scanning electron microscopy. RESULTS The highest adhesive values between buildup and ceramic were obtained using the materials Compoglass F and Syntac, followed by Compoglass F and ExciTE. Among the two other core buildups, Tetric EvoCeram performed better than Ketac Fil Plus, which was independent of the bonding materials. Adhesive fractures were characteristically observed with Syntac and ExciTE, and cohesive fractures were characteristically observed with RelyX Unicem. CONCLUSION These data show that compomers bonded with a multistep adhesive system achieved statistically significantly higher shear bond strength than composites and glass-ionomer cements. Within the limitations inherent to this in vitro study, the use of compomers for core buildup can be recommended.

Shear bond strengths of three glass ionomer cements to enamel and dentine

OBJECTIVES The shear bond strength of three glass ionomer cements (GIC) to enamel and dentine was evaluated. STUDY DESIGN Sound permanent human molars (n=12) were grinded perpendicular to their axial axes, exposing smooth, flat enamel and dentine surfaces. The teeth were embedded in resin and conditioned with polyacrylic acid (25%; 10s). Twenty four specimens of each GIC: Fuji IX (FJ-GC), Ketac Molar Easymix (KM-3M ESPE) and Maxxion (MX-FGM) were prepared according to the Atraumatic Restorative Treatment (ART) (12 enamel and 12 dentine), in a bonding area of 4.91 mm² and immersed in water (37°C, 24h). The shear bond strength was tested in a universal testing machine. Non-parametric statistical tests (Friedman and post-hoc Wilcoxon Signed Ranks) were carried out (p=0.05). RESULTS The mean (±sd) of shear bond strength (MPa), on enamel and dentine, were: KM (6.4±1.4 and 7.6±1.5), FJ (5.9±1.5 and 6.0±1.9) and MX (4.2±1.5 and 4.9±1.5), respectively. There was a statistically significant difference between the GICs in both groups: enamel (p=0.004) and dentine (p=0.002). The lowest shear bond value for enamel was with MX and the highest for dentine was KM (p<0.05). CONCLUSION It is concluded that KM has the best adhesion to both enamel and dentine, followed by FJ and MX.

Increment thickness versus dentin bond strength of bulk fill flowables

Objectives: The aim was to investigate the influence of increment thickness on shear bond strength (SBS) to dentin of a conventional and two bulk fill flowable composites. Methods: A total of 135 specimens of ground human dentin were produced (n=15/group; 3 increment thicknesses; 3 flowable composites) and the dentin surfaces were treated with the adhesive system OptiBond FL (Kerr) according to manufacturer’s instructions. Split Teflon molds (inner diameter: 3.6 mm) of 2 mm, 4 mm, or 6 mm height allowing three increment thicknesses were clamped on the dentin surfaces and filled with either the conventional flowable Filtek Supreme XTE ((XTE); 3M ESPE) or the bulk fill flowables Filtek Bulk Fill ((FBF); 3M ESPE) or SDR ((SDR); DENTSPLY Caulk). The flowable composites were light-cured for 20 s (Demi LED; Kerr) and the specimens stored for 24 h (37°C, 100% humidity). Specimens were then subjected to a SBS-test in a universal testing machine at a cross-head speed of 1 mm/min (Zwick Z010; Zwick GmbH & Co.). SBS-values were statistically analysed with a nonparametrical ANOVA followed by exact Wilcoxon rank sum tests (α=0.05). Failure mode of the specimens was determined under a stereomicroscope at 25× magnification. Results: SBS-values (MPa) at 2 mm/4 mm/6 mm increment thicknesses (mean value [standard deviation]) were for XTE: 18.8 [2.6]/17.6 [1.6]/16.7 [3.1], for FBF: 20.6 [2.7]/17.8 [2.7]/18.7 [2.9], and for SDR: 21.7 [2.6]/18.5 [2.6]/20.3 [3.0]. For all three flowable composites, 2 mm increments yielded the highest SBS-values whereas for increments of 4 mm and 6 mm no differences were detected. All specimens presented failure modes involving cohesive failure in dentin. Conclusion: The influence of increment thickness on dentin SBS was less pronounced than expected. However, the high number of cohesive failures in dentin, reflecting the efficiency of the adhesive system, suggests a limited discriminatory power of the SBS-test.

Influence of increment thickness on microhardness and dentin bond strength of bulk fill resin composites

OBJECTIVES To investigate the influence of increment thickness on Vickers microhardness (HV) and shear bond strength (SBS) to dentin of a conventional and four bulk fill resin composites. METHODS HV and SBS were determined on specimens of the conventional resin composite Filtek Supreme XTE (XTE) and the bulk fill resin composites SDR (SDR), Filtek Bulk Fill (FBF), x-tra fil (XFIL), and Tetric EvoCeram Bulk Fill (TEBF) after 24h storage. HV was measured either as profiles at depths up to 6mm or at the bottom of 2mm/4mm/6mm thick resin composite specimens. SBS of 2mm/4mm/6mm thick resin composite increments was measured to dentin surfaces of extracted human molars treated with the adhesive system OptiBond FL, and the failure mode was stereomicroscopically determined at 40× magnification. HV profiles and failure modes were descriptively analysed whereas HV at the bottom of resin composite specimens and SBS were statistically analysed with nonparametric ANOVA followed by Wilcoxon rank sum tests (α=0.05). RESULTS HV profiles (medians at 2mm/4mm/6mm): XTE 105.6/88.8/38.3, SDR 34.0/35.5/36.9, FBF 36.4/38.7/37.1, XFIL 103.4/103.9/101.9, TEBF 63.5/59.7/51.9. HV at the bottom of resin composite specimens (medians at 2mm/4mm/6mm): XTE (p<0.0001) 105.5>85.5>31.1, SDR (p=0.10) 25.8=21.9=26.0, FBF (p=0.16) 26.6=25.3=28.9, XFIL (p=0.18) 110.5=107.2=101.9, TEBF (p<0.0001) 63.0>54.9>48.2. SBS (MPa, medians at 2mm/4mm/6mm): XTE (p<0.0001) 23.9>18.9=16.7, SDR (p=0.26) 24.6=22.7=23.4, FBF (p=0.11) 21.4=20.3=22.0, x-tra fil (p=0.55) 27.0=24.0=23.6, TEBF (p=0.11) 21.0=20.7=19.0. The predominant SBS failure mode was cohesive failure in dentin. SIGNIFICANCE At increasing increment thickness, HV and SBS decreased for the conventional resin composite but generally remained constant for the bulk fill resin composites.

Dentin Bond Strength of Two Recent CAD/CAM-Materials after Storage

Purpose: To investigate the bond strength to dentin of two recent resin-ceramic materials for computer-aided design/computer-aided manufacturing (CAD/CAM) after 24 hours and after six months storage. Methods and Materials: Ninety cylinders were milled out of Lava Ultimate (3M ESPE) and 90 cylinders out of VITA ENAMIC (VITA Zahnfabrik) (dimension of cylinders: ∅=3.6 mm, h=2 mm). All Lava Ultimate cylinders were sandblasted (aluminium oxide, grain size: 27 μm) and cleaned with ethanol, whereas all VITA ENAMIC cylinders were acid-etched (5% hydrofluoric acid) and cleaned with water-spray. According to the three groups of cements used, the cylinders (n=30/resin-ceramic material) were further pretreated with 1) Scotchbond Universal for RelyX Ultimate (3M ESPE), 2) CLEARFIL Ceramic Primer for PANAVIA F2.0 (Kuraray), or 3) no further pretreatment for Ketac Cem Plus (3M ESPE). The cylinders were then bonded to ground human dentin specimens with 1) Scotchbond Universal and RelyX Ultimate (light-cured), 2) ED PRIMER II and PANAVIA F2.0 (light-cured), or 3) no adhesive system; Ketac Cem Plus (self-cured). Shear bond strength (SBS) was measured after 24 hours for 15 specimens/group and after six months (37°C, 100% humidity) for the other 15 specimens/group. SBS-values were statistically analysed with nonparametric ANOVA followed by exact Wilcoxon rank sum tests (α=0.05). Results: SBS of the two resin-ceramic materials and the three cements after 24 hours and after six months storage are shown in Figure 1. The statistical analysis showed that the duration of storage had a significant effect on SBS of Lava Ultimate for all three cements but had no significant effect on SBS of VITA ENAMIC. For Lava Ultimate SBS-values were (MPa; medians after 24 hours/six months): 13.5/22.5 (p=0.04) for RelyX Ultimate, 11.4/5.8 (p=0.0006) for PANAVIA F2.0, and 0.34/0.09 (p=0.04) for Ketac Cem Plus (Fig. 1). For VITA ENAMIC SBS-values were (MPa; medians after 24 hours/six months): 16.0/21.2 (p=0.10) for RelyX Ultimate, 11.4/14.4 (p=0.06) for PANAVIA F2.0, and 0.43/0.41 (p=0.32) for Ketac Cem Plus (Fig. 1). After 24 hours, there was no significant difference in SBS between Lava Ultimate and VITA ENAMIC for all three cements (p≥0.37). After six months, there was no significant difference in SBS between Lava Ultimate and VITA ENAMIC for RelyX Ultimate and Ketac Cem Plus (p≥0.07) whereas for PANAVIA F2.0, SBS was significantly lower for Lava Ultimate than for VITA ENAMIC (p<0.0001). Conclusion: SBS of Lava Ultimate was more affected by six months storage and by the cement used than was VITA ENAMIC.

Salivary Contamination and Decontamination: Bond Strength to Dentin of Primary and Permanent Teeth

Aim: To evaluate the effects of salivary contamination and decontamination on bond strength of two one-step adhesives to primary and permanent dentin. Methods: Dentin specimens were prepared from extracted primary and permanent molars (210 of each) and were distributed to seven groups (n=15/group/molar type) for each adhesive (Xeno V+ and Scotchbond Universal): no saliva contamination (control); saliva contamination before or after light-curing of the adhesives followed either by air-drying, by rinsing with water and air-drying, or by rinsing with water, air-drying and reapplication of the adhesives. Resin composite was applied and the specimens were stored for 24h (37°C, 100% humidity). Then, shear bond strength (SBS) was measured and data analyzed with nonparametric ANOVA and Wilcoxon rank sum tests. Results: Saliva contamination reduced SBS of Xeno V+, the reduction being more pronounced when contamination occurred before light-curing than after. In both situations, decontamination involving reapplication of the adhesive restored SBS. Saliva contamination had no significant effect on Scotchbond Universal. There were no differences in SBS between primary and permanent teeth. Conclusion: Saliva contamination reduced SBS of Xeno V+, but not of Scotchbond Universal. SBS was restored when contaminated dentin was rinsed with water and air-dried followed by reapplication of the adhesive.

Effect of Salivary Contamination and Decontamination on Bond Strength of Two One-Step Self-Etching Adhesives to Dentin of Primary and Permanent Teeth

Purpose: To evaluate the effects of human saliva contamination and two decontamination procedures at different stages of the bonding procedure on the bond strength of two one-step self-etching adhesives to primary and permanent dentin. Materials and Methods: Extracted human primary and permanent molars (210 of each) were ground to mid-coronal dentin. The dentin specimens were randomly divided into 7 groups (n = 15/group/molar type) for each adhesive (Xeno V+ and Scotchbond Universal): no saliva contamination (control); saliva contamination before or after light curing of the adhesives followed by air drying, rinsing with water spray/air drying, or by rinsing with water spray/air drying/reapplication of the adhesives. Resin composite (Filtek Z250) was applied on the treated dentin surfaces. The specimens were stored at 37°C and 100% humidity for 24 h. After storage, shear bond strength (SBS) was measured and data analyzed with nonparametric ANOVA followed by exact Wilcoxon rank sum tests. Results: Xeno V+ generated significantly higher SBS than Scotchbond Universal when no saliva contamination occurred. Saliva contamination reduced SBS of Xeno V+, with the reduction being more pronounced when contamination occurred before light curing than after. In both situations, decontamination involving reapplication of the adhesive restored SBS. Saliva contamination had no significant effect on Scotchbond Universal. There were no differences in SBS between primary and permanent teeth. Conclusion: Rinsing with water and air drying followed by reapplication of the adhesive restored bond strength to saliva-contaminated dentin.

Bond Strength of Resin Composite to Dentin with Different Adhesive Systems: Influence of Relative Humidity and Application Time.

PURPOSE To investigate the influence of relative humidity and application time on bond strength to dentin of different classes of adhesive systems. MATERIALS AND METHODS A total of 360 extracted human molars were ground to mid-coronal dentin. The dentin specimens were treated with one of six adhesive systems (Syntac Classic, OptiBond FL, Clearfil SE Bond, AdheSE, Xeno Select, or Scotchbond Universal), and resin composite (Filtek Z250) was applied to the treated dentin surface under four experimental conditions (45% relative humidity/application time according to manufacturers' instructions; 45% relative humidity/reduced application time; 85% relative humidity/application time according to manufacturers' instructions; 85% relative humidity/reduced application time). After storage (37°C, 100% humidity, 24 h), shear bond strength (SBS) was measured and data analyzed with nonparametric ANOVA followed by Kruskal-Wallis tests and Mann-Whitney U-tests with Bonferroni-Holm correction for multiple testing (level of significance: α = 0.05). RESULTS Increased relative humidity and reduced application time had no effect on SBS for Clearfil SE Bond and Scotchbond Universal (p = 1.00). For Syntac Classic, OptiBond FL, AdheSE, and Xeno Select there was no effect on SBS of reduced application time of the adhesive system (p ≥ 0.403). However, increased relative humidity significantly reduced SBS for Syntac Classic, OptiBond FL, and Xeno Select irrespective of application time (p ≤ 0.003), whereas for AdheSE, increased relative humidity significantly reduced SBS at recommended application time only (p = 0.002). CONCLUSION Generally, increased relative humidity had a detrimental effect on SBS to dentin, but reduced application time had no effect.

Bonding of restorative materials to dentin with various luting agents

The aim was to compare eight types of luting agents when used to bond six indirect, laboratory restorative materials to dentin. Cylinders of the six restorative materials (Esteticor Avenir [gold alloy], Tritan [titanium], NobelRondo [feldspathic porcelain], Finesse All-Ceramic [leucite-glass ceramic], Lava [zirconia], and Sinfony [resin composite]) were ground and air-abraded. Cylinders of feldspathic porcelain and glass ceramic were additionally etched with hydrofluoric acid and were silane-treated. The cylinders were luted to ground human dentin with eight luting agents (DeTrey Zinc [zinc phosphate cement], Fuji I [conventional glass ionomer cement], Fuji Plus [resin-modified glass ionomer cement], Variolink II [conventional etch-and-rinse resin cement], Panavia F2.0 and Multilink [self-etch resin cements], and RelyX Unicem Aplicap and Maxcem [self-adhesive resin cements]). After water storage at 37°C for one week, the shear bond strength of the specimens (n=8/group) was measured, and the fracture mode was stereomicroscopically examined. Bond strength data were analyzed with two-factorial analysis of variance (ANOVA) followed by Newman-Keuls' Multiple Range Test (?=0.05). Both the restorative material and the luting agent had a significant effect on bond strength, and significant interaction was noted between the two variables. Zinc phosphate cement and glass ionomer cements produced the lowest bond strengths, whereas the highest bond strengths were found with the two self-etch and one of the self-adhesive resin cements. Generally, the fracture mode varied markedly with the restorative material. The luting agents had a bigger influence on bond strength between restorative materials and dentin than was seen with the restorative material.

Dentinhaftung von Zementen. Der Haftverbund von Zementen mit Dentin in Kombination mit verschiedenen indirekten Restaurationsmaterialien

Einleitung: Die Anzahl zahnärztlicher Zemente sowie Restaurationsmaterialien steigt stetig. Die richtige Zementwahl für einen zuverlässigen Haftverbund zwischen Restaurationsmaterial und Zahnsubstanz ist von Interesse für den Kliniker. Ziel der vorliegenden in vitro-Studie war es daher, den Dentinhaftverbund von verschiedenen Zementen in Kombination mit verschiedenen indirekten Restaurationsmaterialien zu untersuchen. Material und Methoden: Zylindrische Probekörper aus sechs Restaurationsmaterialien (Goldlegierung, Titan, Feldspat-Keramik, Leuzit-Glaskeramik, Zirkon sowie Komposit) wurden an einem Ende plangeschliffen und sandgestrahlt. Die Zylinder aus Feldspat-Keramik und Leuzit-Glaskeramik wurden zusätzlich mit Flusssäure geätzt und silanisiert. Die Zylinder wurden anschliessend mit acht Zementen auf plangeschliffenes Dentin extrahierter menschlicher Zähne zementiert (ein Zink-Phosphatzement (DeTrey Zinc), ein konventioneller Glasionomerzement (Fuji I), ein kunststoffmodifizierter Glasionomerzement (Fuji Plus), ein "etch-&-rinse" Kompositzement (Variolink II), zwei "self-etch" Kompositzemente (Panavia F2.0 und Multilink) und zwei "self-adhesive" Kompositzemente (RelyX Unicem Aplicap und Maxcem)). Nach einwöchiger Wasserlagerung bei 37°C wurden die Dentinhaftwerte der Zylinder (n=8 pro Gruppe) mittels Scherkraft-Test gemessen. Zusätzlich wurde das Frakturmuster unter dem Lichtmikroskop bestimmt. Die Haftwerte wurden mittels zweifaktorieller ANOVA und einem post hoc-Test analysiert (Signifikanzniveau α = 0.05). Resultate: Sowohl das Restaurationsmaterial wie auch der Zement hatten einen statistisch signifikanten Effekt auf den Haftverbund. Der Zink-Phosphatzement sowie beide Glasionomerzemente zeigten die niedrigsten Haftwerte. Die höchsten Haftwerte wurden mit beiden "self-etch" und einem der zwei "self-adhesive" Kompositzementen erzielt. Im Allgemeinen variierte das Frakturmuster deutlich je nach Zement und Restaurationsmaterial. Schlussfolgerungen: Der Dentinhaftverbund wurde stärker vom Zement beeinflusst als vom Restaurationsmaterial. Die Kompositzemente erzielten im Grossen und Ganzen die höchsten Haftwerte.

Long-term storage affects adhesion between titanium and zirconia using resin cements.

PURPOSE To determine the impact of long-term storage on adhesion between titanium and zirconia using resin cements. MATERIALS AND METHODS Titanium grade 4 blocks were adhesively fixed onto zirconia disks with four resin cements: Panavia F 2.0 (Kuraray Europe), GC G-Cem (GC Europe), RelyX Unicem (3M ESPE), and SmartCem 2 (Dentsply DeguDent). Shear bond strength was determined after storage in a water bath for 24 h, 16, 90, and 150 days at 37°C, and after 6000 cycles between 5°C and 55°C. Fracture behavior was evaluated using scanning electron microscopy. RESULTS After storage for at least 90 days and after thermocycling, GC G-Cem (16.9 MPa and 15.1 MPa, respectively) and RelyX Unicem (10.8 MPa and 15.7 MPa, respectively) achieved higher shear bond strength compared to SmartCem 2 (7.1 MPa and 4.0 MPa, respectively) and Panavia F2 (4.1 MPa and 7.4 MPa, respectively). At day 150, GC G-Cem and RelyX Unicem caused exclusively mixed fractures. SmartCem 2 and Panavia F2 showed adhesive fractures in one-third of the cases; all other fractures were of mixed type. After 24 h (GC G-Cem: 26.0, RelyX Unicem: 20.5 MPa, SmartCem 2: 16.1 MPa, Panavia F2: 23.6 MPa) and 16 days (GC G-Cem: 12.8, RelyX Unicem: 14.2 MPa, SmartCem 2: 9.8 MPa, Panavia F2: 14.7 MPa) of storage, shear bond strength was similar among the four cements. CONCLUSION Long-term storage and thermocycling differentially affects the bonding of resin cement between titanium and zirconia.

Airborne-particle Abrasion Is a Minimally Invasive Method to Pre-Treat Sclerotic, Non-Carious Cervical Dentin

Objectives: To investigate substance loss and bond strength capacity of sclerotic, non-carious cervical dentin after airborne-particle abrasion or diamond bur preparation. Methods: Fifteen non-sclerotic dentin specimens were made from crowns of extracted human incisors of which the labial surfaces had been ground with silicon carbide papers (non-sclerotic control; Group 1). Forty-five sclerotic dentin specimens (n=15/group) were made from the labial, non-carious cervical root part of extracted human incisors and underwent either no pre-treatment (sclerotic control; Group 2), pre-treatment with airborne-particle abrasion (CoJet Prep [3M ESPE] and 50 µm aluminium oxide; Group 3), or with diamond bur preparation (40 µm grit size; Group 4). Substance loss after pre-treatment was measured in Groups 3 and 4. Subsequently, Scotchbond Universal (3M ESPE) and resin composite (CeramX [DENTSPLY DeTrey]) were applied on the treated dentin surfaces. The specimens were stored at 37°C and 100% humidity for 24 h. After storage, shear bond strength (SBS) was measured and data analyzed with nonparametric ANOVA followed by Wilcoxon rank sum tests. Results: Substance loss (medians) was 19 µm in Group 3 and 113 µm in Group 4. SBS-values (MPa; medians) in Group 2 (9.24) were significantly lower than in Group 1 (13.15; p=0.0069), Group 3 (13.05; p=0.01), and Group 4 (13.02; p=0.0142). There were no significant differences in SBS between Groups 1, 3, and 4 (p≥0.8063). Conclusion: Airborne-particle abrasion and diamond bur preparation restored bond strength of Scotchbond Universal to sclerotic dentin to the level of non-sclerotic dentin, with airborne-particle abrasion being less invasive than diamond bur preparation.

Effect of zirconia surface treatments on the shear strength of zirconia/veneering ceramic composites

Aim of the investigation was to assess the effect of different surface treatments on the bond strength of veneering ceramics to zirconia. In a shear test, the influences of polishing, sandblasting, and silica-coating of the zirconia surface on bonding were assessed with five different veneering ceramics. In addition the effect of liner application was examined. With one veneering ceramic, the impact of regeneration firing of zirconia was also evaluated. Statistical analysis was performed with one-way ANOVA and post hoc Scheffé's test. Failure in every case occurred in the veneering ceramic adjacent to the interface with a thin layer of ceramic remaining on the zirconia surface, indicating that bond strength was higher than the cohesive strength of the veneering ceramic. Shear strength ranged from 23.5 +/- 3.4 MPa to 33.0 +/- 6.8 MPa without explicit correlation to the respective surface treatment. Regeneration firing significantly decreased the shear strength of both polished and sandblasted surfaces. Findings of this study revealed that bonding between veneering ceramics and zirconia might be based on chemical bonds. On this note, sandblasting was not a necessary surface pretreatment to enhance bond strength and that regeneration firing was not recommended.