Retention of Root Canal Posts: Effect of Cement Film Thickness, Luting Cement, and Post Pretreatment.

The aim of this study was to investigate the effect of the cement film thickness of a zinc phosphate or a resin cement on retention of untreated and pretreated root canal posts. Prefabricated zirconia posts (CosmoPost: 1.4 mm) and two types of luting cements (a zinc phosphate cement [DeTrey Zinc] and a self-etch adhesive resin cement [Panavia F2.0]) were used. After removal of the crowns of 360 extracted premolars, canines, or incisors, the root canals were prepared with a parallel-sided drill system to three different final diameters. Half the posts did not receive any pretreatment. The other half received tribochemical silicate coating according to the manufacturer's instructions. Posts were then luted in the prepared root canals (n=30 per group). Following water storage at 37°C for seven days, retention of the posts was determined by the pull-out method. Irrespective of the luting cement, pretreatment with tribochemical silicate coating significantly increased retention of the posts. Increased cement film thickness resulted in decreased retention of untreated posts and of pretreated posts luted with zinc phosphate cement. Increased cement film thickness had no influence on retention of pretreated posts luted with resin cement. Thus, retention of the posts was influenced by the type of luting cement, by the cement film thickness, and by the post pretreatment.

Push-out bond strength of CAD/CAM-ceramic luted to dentin with self-adhesive resin cements

OBJECTIVES: This study evaluated the initial and the artificially aged push-out bond strength between ceramic and dentin produced by one of five resin cements. METHODS: Two-hundred direct ceramic restorations (IPS Empress CAD) were luted to standardized Class I cavities in extracted human molars using one of four self-adhesive cements (SpeedCEM, RelyX Unicem Aplicap, SmartCem2 and iCEM) or a reference etch-and-rinse resin cement (Syntac/Variolink II) (n=40/cement). Push-out bond strength (PBS) was measured (1) after 24h water storage (non-aged group; n=20/cement) or (2) after artificial ageing with 5000 thermal cycles followed by 6 months humid storage (aged group; n=20/cement). Nonparametrical ANOVA and pairwise Wilcoxon rank-sum tests with Bonferroni-Holm adjustment were applied for statistical analysis. The significance level was set at alpha=0.05. In addition, failure mode and fracture pattern were analyzed by stereomicroscope and scanning electron microscopy. RESULTS: Whereas no statistically significant effect of storage condition was found (p=0.441), there was a significant effect of resin cement (p<0.0001): RelyX Unicem showed significantly higher PBS than the other cements. Syntac/Variolink II showed significantly higher PBS than SmartCEM2 (p<0.001). No significant differences were found between SpeedCEM, SmartCem2, and iCEM. The predominant failure mode was adhesive failure of cements at the dentin interface except for RelyX Unicem which in most cases showed cohesive failure in ceramic. SIGNIFICANCE: The resin cements showed marked differences in push-out bond strength when used for luting ceramic restorations to dentin. Variolink II with the etch-and-rinse adhesive Syntac did not perform better than three of the four self-adhesive resin cements tested.

Bonding of restorative materials to dentin with various luting agents

The aim was to compare eight types of luting agents when used to bond six indirect, laboratory restorative materials to dentin. Cylinders of the six restorative materials (Esteticor Avenir [gold alloy], Tritan [titanium], NobelRondo [feldspathic porcelain], Finesse All-Ceramic [leucite-glass ceramic], Lava [zirconia], and Sinfony [resin composite]) were ground and air-abraded. Cylinders of feldspathic porcelain and glass ceramic were additionally etched with hydrofluoric acid and were silane-treated. The cylinders were luted to ground human dentin with eight luting agents (DeTrey Zinc [zinc phosphate cement], Fuji I [conventional glass ionomer cement], Fuji Plus [resin-modified glass ionomer cement], Variolink II [conventional etch-and-rinse resin cement], Panavia F2.0 and Multilink [self-etch resin cements], and RelyX Unicem Aplicap and Maxcem [self-adhesive resin cements]). After water storage at 37°C for one week, the shear bond strength of the specimens (n=8/group) was measured, and the fracture mode was stereomicroscopically examined. Bond strength data were analyzed with two-factorial analysis of variance (ANOVA) followed by Newman-Keuls' Multiple Range Test (?=0.05). Both the restorative material and the luting agent had a significant effect on bond strength, and significant interaction was noted between the two variables. Zinc phosphate cement and glass ionomer cements produced the lowest bond strengths, whereas the highest bond strengths were found with the two self-etch and one of the self-adhesive resin cements. Generally, the fracture mode varied markedly with the restorative material. The luting agents had a bigger influence on bond strength between restorative materials and dentin than was seen with the restorative material.

The effect of polymerization procedure on Vickers hardness of dual-curing resin cements

To investigate the surface hardness (Vickers hardness, HVN) of one light-curing flowable resin composite and five dual-curing resin cements after different polymerization procedures.

Shear bond strength of resin cements to human dentin

OBJECTIVES: The objectives of this in vitro study were (1) to assess the bond strength of the universal cement RelyX Unicem to dentin and to compare it with three conventional resin cements, (2) to test the influence of aging on their bonding capacity and (3) to test the influence of the operator on bonding quality by performing the same test in two different centers. METHODS: 160 third molars, divided into 80 for tests at the University of Zurich (Z) and 80 for tests at the University of Berne (B), were assigned to 2 x 8 subgroups of 10 teeth each. The specimens were prepared with the corresponding bonding agents and acrylic rods were luted either with RelyX Unicem (U), RelyX ARC (A), Multilink (M) or Panavia 21 (P). All specimens were stored in water for 24h (W) and half of the specimens were subjected to 1500 cycles of thermocycling (5 degrees C and 55 degrees C) (T). Bond strength was measured by means of a shear test. RESULTS: After water storage RelyX Unicem exhibited lowest bond strength (UWZ: 9.2+/-1.6 MPa, UWB: 9.9+/-1.2 MPa, AWZ: 15.3+/-6.0 MPa, AWB: 12.2+/-4.3 MPa, MWZ: 15.6+/-3.3 MPa, MWB: 12.4 MPa+/-2.4, PWZ: 13.4+/-2.9 MPa, PWB: 14.9+/-2.6 MPa). Thermocycling affected the bonding performance of all four cements. However, bond strength of RelyX Unicem was least influenced by thermocycling (UTZ: 9.4+/-2.9 MPa, UTB: 8.6+/-1.3 MPa, ATZ: 11.4+/-6.3 MPa, ATB: 13.3+/-3.7 MPa, MTZ: 15.4+/-3.1 MPa, MTB: 10.3+/-2.4 MPa, PTZ: 11.1+/-2.8 MPa, PTB: 11.3+/-2.8 MPa). SIGNIFICANCE: Although the bond strength of RelyX Unicem to dentin was lower in comparison to RelyX ARC, Multilink and Panavia 21, its bond strength was less sensitive to variations in handling and aging.

Mechanical characterization of brushite and hydroxyapatite cements

Compression, tension and torsion tests were designed and completed successfully on a brushite and a precipitated hydroxyapatite cement in moist condition. Elastic and strength properties were measured for these three loading cases. For each cement, the full set of strength data was fitted to an isotropic Tsai-Wu criterion and the associated coefficients identified. Since the compressive Young's moduli were about 10% larger than the tensile moduli, the full set of elastic data of each cement was fitted to a conewise linear elastic model. Hysteresis of the stress-strain curves was also observed, indicating dissipation mechanisms within these cement microstructures. A comparison of the measured mechanical properties with human cancellous bone confirmed the indication of brushite as a bone filling material and the potential of the hydroxyapatite cement as a structural biomaterial.

Augmentation of mechanical properties in osteoporotic vertebral bones--a biomechanical investigation of vertebroplasty efficacy with different bone cements

Recent clinical trials have reported favorable early results for transpedicular vertebral cement reinforcement of osteoporotic vertebral insufficiencies. There is, however, a lack of basic data on the application, safety and biomechanical efficacy of materials such as polymethyl-methacrylate (PMMA) and calciumphospate (CaP) cements. The present study analyzed 33 vertebral pairs from five human cadaver spines. Thirty-nine vertebrae were osteoporotic (bone mineral density < 0.75 g/cm2), 27 showed nearly normal values. The cranial vertebra of each pair was augmented with either PMMA (Palacos E-Flow) or experimental brushite cement (EBC), with the caudal vertebra as a control. PMMA and EBC were easy to inject, and vertebral fillings of 20-50% were achieved. The maximal possible filling was inversely correlated to the bone mineral density (BMD) values. Cement extrusion into the spinal canal was observed in 12% of cases. All specimens were subjected to axial compression tests in a displacement-controlled mode. From load-displacement curves, the stiffness, S, and the maximal force before failure, Fmax, were determined. Compared with the native control vertebrae, a statistically significant increase in vertebral stiffness and Fmax was observed by the augmentation. With PMMA the stiffness increased by 174% (P = 0.018) and Fmax by 195% (P = 0.001); the corresponding augmentation with EBC was 120% (P = 0.03) and 113% (P = 0.002). The lower the initial BMD, the more pronounced was the augmentation effect. Both PMMA and EBC augmentation reliably and significantly raised the stiffness and maximal tolerable force until failure in osteoporotic vertebral bodies. In non-porotic specimens, no significant increase was achieved.

Light curing through glass ceramics: effect of curing mode on micromechanical properties of dual-curing resin cements

OBJECTIVES The aim of this study was to investigate micromechanical properties of five dual-curing resin cements after different curing modes including light curing through glass ceramic materials. MATERIALS AND METHODS Vickers hardness (VH) and indentation modulus (Y HU) of Panavia F2.0, RelyX Unicem 2 Automix, SpeedCEM, BisCem, and BeautiCem SA were measured after 1 week of storage (37 °C, 100 % humidity). The resin cements were tested following self-curing or light curing with the second-generation light-emitting diode (LED) curing unit Elipar FreeLight 2 in Standard Mode (1,545 mW/cm(2)) or with the third-generation LED curing unit VALO in High Power Mode (1,869 mW/cm(2)) or in XtraPower Mode (3,505 mW/cm(2)). Light curing was performed directly or through glass ceramic discs of 1.5 or 3 mm thickness of IPS Empress CAD or IPS e.max CAD. VH and Y HU were analysed with Kruskal-Wallis tests followed by pairwise Wilcoxon rank sum tests (α = 0.05). RESULTS RelyX Unicem 2 Automix resulted in the highest VH and Y HU followed by BeautiCem SA, BisCem, SpeedCEM, and finally Panavia F2.0. Self-curing of RelyX Unicem 2 Automix and SpeedCEM lowered VH and Y HU compared to light curing whereas self-curing of Panavia F2.0, BisCem, and BeautiCem SA led to similar or significantly higher VH and Y HU compared to light curing. Generally, direct light curing resulted in similar or lower VH and Y HU compared to light curing through 1.5-mm-thick ceramic discs. Light curing through 3-mm-thick discs of IPS e.max CAD generally reduced VH and Y HU for all resin cements except SpeedCEM, which was the least affected by light curing through ceramic discs. CONCLUSIONS The resin cements responded heterogeneously to changes in curing mode. The applied irradiances and light curing times adequately cured the resin cements even through 1.5-mm-thick ceramic discs. CLINICAL RELEVANCE When light curing resin cements through thick glass ceramic restorations, clinicians should consider to prolong the light curing times even with LED curing units providing high irradiances.

Light curing through glass ceramics with a second- and a third-generation LED curing unit: effect of curing mode on the degree of conversion of dual-curing resin cements

Objectives The aim of this study was to measure the degree of conversion (DC) of five dual-curing resin cements after different curing modes with a second- and a third-generation light-emitting diode (LED) curing unit. Additionally, irradiance of both light curing units was measured at increasing distances and through discs of two glass ceramics for computer-aided design/manufacturing (CAD/CAM). Materials and methods Irradiance and spectra of the Elipar FreeLight 2 (Standard Mode (SM)) and of the VALO light curing unit (High Power Mode (HPM) and Xtra Power Mode (XPM)) were measured with a MARC radiometer. Irradiance was measured at increasing distances (control) and through discs (1.5 to 6 mm thickness) of IPS Empress CAD and IPS e.max CAD. DC of Panavia F2.0, RelyX Unicem 2 Automix, SpeedCEM, BisCem, and BeautiCem SA was measured with an attenuated total reflectance–Fourier transform infrared spectrometer when self-cured (negative control) or light cured in SM for 40 s, HPM for 32 s, or XPM for 18 s. Light curing was performed directly (positive control) or through discs of either 1.5- or 3-mm thickness of IPS Empress CAD or IPS e.max CAD. DC was analysed with Kruskal–Wallis tests followed by pairwise Wilcoxon rank sum tests (α = 0.05). Results Maximum irradiances were 1,545 mW/cm2 (SM), 2,179 mW/cm2 (HPM), and 4,156 mW/cm2 (XPM), and all irradiances decreased by >80 % through discs of 1.5 mm, ≥95 % through 3 mm, and up to >99 % through 6 mm. Generally, self-curing resulted in the lowest DC. For some cements, direct light curing did not result in higher DC compared to when light cured through ceramic discs. For other cements, light curing through ceramic discs of 3 mm generally reduced DC. Conclusions Light curing was favourable for dual-curing cements. Some cements were more susceptible to variations in curing mode than others. Clinical relevance When light curing a given cement, the higher irradiances of the third-generation LED curing unit resulted in similar DC compared to the second-generation one, though at shorter light curing times.

The bonding of glass ionomer cements to caries-affected primary tooth dentin

PURPOSE The purpose of this study was to evaluate the bonding of glass ionomer cements (GICs) to sound and caries-affected dentin by microtensile bond strength (μTBS) and nanoleakage (NL) tests. METHODS Occlusal cavity preparations were made in 36 sound primary molars. Half of the specimens were submitted to a pH-cycling model to create simulated caries-affected dentin. Teeth were randomly restored with one of the three materials: (1) resin-modified GIC with nanoparticles (Ketac N100; KN); (2) resin-modified GIC (Vitremer; VI); and (3) high-viscosity GIC (Ketac Molar Easy Mix; KM). Specimens were tested using a microtensile test (1 mm/minute). One specimen from each tooth was immersed in ammoniacal silver nitrate for 24 hours and revealed after eight hours to assess interfacial NL. The μTBS means were analyzed by 2-way analysis of variance and Tukey's post hoc test. For NL, Kruskal-Wallis and Mann-Whitney tests were used (P<.05). RESULTS No difference was found between sound and caries-affected dentin (P>.05). KM showed the lowest GIC-dentin μTBS values, while VI and KN showed higher values. Infiltration of ammoniacal silver nitrate into the adhesive interface was not affected by sound or caries-affected dentin. CONCLUSION Caries-affected dentin does not jeopardize the bonding of glass ionomer cements to primary tooth dentin.

Dentinhaftung von Zementen. Der Haftverbund von Zementen mit Dentin in Kombination mit verschiedenen indirekten Restaurationsmaterialien

Einleitung: Die Anzahl zahnärztlicher Zemente sowie Restaurationsmaterialien steigt stetig. Die richtige Zementwahl für einen zuverlässigen Haftverbund zwischen Restaurationsmaterial und Zahnsubstanz ist von Interesse für den Kliniker. Ziel der vorliegenden in vitro-Studie war es daher, den Dentinhaftverbund von verschiedenen Zementen in Kombination mit verschiedenen indirekten Restaurationsmaterialien zu untersuchen. Material und Methoden: Zylindrische Probekörper aus sechs Restaurationsmaterialien (Goldlegierung, Titan, Feldspat-Keramik, Leuzit-Glaskeramik, Zirkon sowie Komposit) wurden an einem Ende plangeschliffen und sandgestrahlt. Die Zylinder aus Feldspat-Keramik und Leuzit-Glaskeramik wurden zusätzlich mit Flusssäure geätzt und silanisiert. Die Zylinder wurden anschliessend mit acht Zementen auf plangeschliffenes Dentin extrahierter menschlicher Zähne zementiert (ein Zink-Phosphatzement (DeTrey Zinc), ein konventioneller Glasionomerzement (Fuji I), ein kunststoffmodifizierter Glasionomerzement (Fuji Plus), ein "etch-&-rinse" Kompositzement (Variolink II), zwei "self-etch" Kompositzemente (Panavia F2.0 und Multilink) und zwei "self-adhesive" Kompositzemente (RelyX Unicem Aplicap und Maxcem)). Nach einwöchiger Wasserlagerung bei 37°C wurden die Dentinhaftwerte der Zylinder (n=8 pro Gruppe) mittels Scherkraft-Test gemessen. Zusätzlich wurde das Frakturmuster unter dem Lichtmikroskop bestimmt. Die Haftwerte wurden mittels zweifaktorieller ANOVA und einem post hoc-Test analysiert (Signifikanzniveau α = 0.05). Resultate: Sowohl das Restaurationsmaterial wie auch der Zement hatten einen statistisch signifikanten Effekt auf den Haftverbund. Der Zink-Phosphatzement sowie beide Glasionomerzemente zeigten die niedrigsten Haftwerte. Die höchsten Haftwerte wurden mit beiden "self-etch" und einem der zwei "self-adhesive" Kompositzementen erzielt. Im Allgemeinen variierte das Frakturmuster deutlich je nach Zement und Restaurationsmaterial. Schlussfolgerungen: Der Dentinhaftverbund wurde stärker vom Zement beeinflusst als vom Restaurationsmaterial. Die Kompositzemente erzielten im Grossen und Ganzen die höchsten Haftwerte.

Long-term storage affects adhesion between titanium and zirconia using resin cements.

PURPOSE To determine the impact of long-term storage on adhesion between titanium and zirconia using resin cements. MATERIALS AND METHODS Titanium grade 4 blocks were adhesively fixed onto zirconia disks with four resin cements: Panavia F 2.0 (Kuraray Europe), GC G-Cem (GC Europe), RelyX Unicem (3M ESPE), and SmartCem 2 (Dentsply DeguDent). Shear bond strength was determined after storage in a water bath for 24 h, 16, 90, and 150 days at 37°C, and after 6000 cycles between 5°C and 55°C. Fracture behavior was evaluated using scanning electron microscopy. RESULTS After storage for at least 90 days and after thermocycling, GC G-Cem (16.9 MPa and 15.1 MPa, respectively) and RelyX Unicem (10.8 MPa and 15.7 MPa, respectively) achieved higher shear bond strength compared to SmartCem 2 (7.1 MPa and 4.0 MPa, respectively) and Panavia F2 (4.1 MPa and 7.4 MPa, respectively). At day 150, GC G-Cem and RelyX Unicem caused exclusively mixed fractures. SmartCem 2 and Panavia F2 showed adhesive fractures in one-third of the cases; all other fractures were of mixed type. After 24 h (GC G-Cem: 26.0, RelyX Unicem: 20.5 MPa, SmartCem 2: 16.1 MPa, Panavia F2: 23.6 MPa) and 16 days (GC G-Cem: 12.8, RelyX Unicem: 14.2 MPa, SmartCem 2: 9.8 MPa, Panavia F2: 14.7 MPa) of storage, shear bond strength was similar among the four cements. CONCLUSION Long-term storage and thermocycling differentially affects the bonding of resin cement between titanium and zirconia.

Retrievability of implant-supported crowns when using three different cements: a controlled clinical trial

PURPOSE The purpose of this study was to analyze the removal of implant-supported crowns retained by three different cements using an air-accelerated crown remover and to evaluate the patients' response to the procedure. MATERIALS AND METHODS This controlled clinical trial was conducted with 21 patients (10 women, 11 men; mean age: 51 ± 10.2 years) who had received a total of 74 implants (all placed in the posterior zone of the mandible). Four months after implant surgery, the crowns were cemented on standard titanium abutments of different heights. Three different cements (two temporary: Harvard TEMP and Improv; and one definitive: Durelon) were used and randomly assigned to the patients. Eight months later, one blinded investigator removed all crowns. The number of activations of the instrument (CORONAflex, KaVo) required for crown removal was recorded. The patients completed a questionnaire retrospectively to determine the impact of the procedure and to gauge their subjective perception. A linear regression model and descriptive statistics were used for data analysis. RESULTS All crowns could be retrieved without any technical complications or damage. Both abutment height (P = .019) and cement type (P = .004) had a significant effect on the number of activations, but the type of cement was more important. An increased total number of activations had no or only a weak correlation to the patients' perception of concussion, noise, pain, and unwillingness to use the device. CONCLUSIONS Cemented implant crowns can be removed, and the application of an air-accelerated device is a practicable method. A type of cement with appropriate retention force has to be selected. The impact on the patients' subjective perception should be taken into account.

Shear bond strengths of three glass ionomer cements to enamel and dentine

OBJECTIVES The shear bond strength of three glass ionomer cements (GIC) to enamel and dentine was evaluated. STUDY DESIGN Sound permanent human molars (n=12) were grinded perpendicular to their axial axes, exposing smooth, flat enamel and dentine surfaces. The teeth were embedded in resin and conditioned with polyacrylic acid (25%; 10s). Twenty four specimens of each GIC: Fuji IX (FJ-GC), Ketac Molar Easymix (KM-3M ESPE) and Maxxion (MX-FGM) were prepared according to the Atraumatic Restorative Treatment (ART) (12 enamel and 12 dentine), in a bonding area of 4.91 mm² and immersed in water (37°C, 24h). The shear bond strength was tested in a universal testing machine. Non-parametric statistical tests (Friedman and post-hoc Wilcoxon Signed Ranks) were carried out (p=0.05). RESULTS The mean (±sd) of shear bond strength (MPa), on enamel and dentine, were: KM (6.4±1.4 and 7.6±1.5), FJ (5.9±1.5 and 6.0±1.9) and MX (4.2±1.5 and 4.9±1.5), respectively. There was a statistically significant difference between the GICs in both groups: enamel (p=0.004) and dentine (p=0.002). The lowest shear bond value for enamel was with MX and the highest for dentine was KM (p<0.05). CONCLUSION It is concluded that KM has the best adhesion to both enamel and dentine, followed by FJ and MX.