26 resultados para bone plate
Resumo:
OBJECTIVES: To compare the histological features of bone filled with Bio-Oss, Ostim-Paste or PerioGlas placed in defects in the rabbit tibiae by evaluating bone tissue composition and the integration of titanium implants placed in the grafted bone. MATERIAL AND METHODS: Two cylindrical bone defects, about 4 mm in diameter and 6 mm in depth, were created in the tibiae of 10 rabbits. The defects were filled with either Bio-Oss, PerioGlas, Ostim-Paste or left untreated, and covered with a collagen membrane. Six weeks later, one titanium sandblasted and acid-etched (SLA) implant was inserted at the centre of each previously created defect. The animals were sacrificed after 6 weeks of healing. RESULTS: Implants placed in bone previously grafted with Bio-Oss, PerioGlas or Ostim-Paste obtained a larger extent of osseointegration, although not statistically significant, than implants placed in non-grafted bone. The three grafting materials seemed to perform in a similar way concerning their contribution towards implant osseointegration. All grafting materials appeared to be osteoconductive, thus leading to the formation of bridges of mineralized bone extending from the cortical plate towards the implants surface through the graft scaffold. CONCLUSIONS: Grafting with the above-mentioned biomaterials did not add any advantage to the osseointegration of titanium SLA implants in a self-contained defect.
Resumo:
This study reports on 15 mandibular reconstructions using the Dumbach Titan Mesh-System and particulate cancellous bone and marrow harvested from bilateral posterior ilia. All cases showed segmental defects. Eleven cases involved patients with malignant tumor. Six patients had received irradiation of 40-50 Gy. Reconstructions were performed immediately in 1 patient and secondarily in the remaining 14 patients. In 13 cases, mandibles were successfully reconstructed. Of these 13 patients, 9 reconstructions were completed without complications, whereas the other 4 cases showed complications. In 2 cases, reconstruction failed completely. Overall success rate was 87%. Statistical analysis revealed the extent of mandibular defect, but not malignancy of the original disease or radiotherapy of
Resumo:
BACKGROUND The treatment of proximal humerus fractures in patients with poor bone quality remains a challenge in trauma surgery. Augmentation with polymethylmethacrylate (PMMA) cement is a possible method to strengthen the implant anchorage in osteoporotic bone and to avoid loss of reduction and reduce the cut-out risk. The polymerisation of PMMA during cement setting leads, however, to an exothermic reaction and the development of supraphysiological temperatures may harm the bone and cartilage. This study addresses the issue of heat development during augmentation of subchondrally placed proximal humerus plate screws with PMMA and the possible risk of bone and cartilage necrosis and apoptosis. METHODS Seven fresh frozen humeri from geriatric female donors were instrumented with the proximal humerus interlocking system (PHILOS) plate and placed in a 37°C water bath. Thereafter, four proximal perforated screws were augmented with 0.5 ml PMMA each. During augmentation, the temperatures in the subchondral bone and on the articular surface were recorded with K-type thermocouples. The measured temperatures were compared to threshold values for necrosis and apoptosis of bone and cartilage reported in the literature. RESULTS The heat development was highest around the augmented tips of the perforated screws and diminished with growing distance from the cement cloud. The highest temperature recorded in the subchondral bone reached 43.5°C and the longest exposure time above 42°C was 86s. The highest temperature measured on the articular surface amounted to 38.6°C and the longest exposure time above 38°C was 5 min and 32s. CONCLUSION The study shows that augmentation of the proximal screws of the PHILOS plate with PMMA leads to a locally limited development of supraphysiological temperatures in the cement cloud and closely around it. The critical threshold values for necrosis and apoptosis of cartilage and subchondral bone reported in the literature, however, are not reached. In order to avoid cement extravasation, special care should be taken in detecting perforations or intra-articular cracks in the humeral head.
Resumo:
PURPOSE Fixation of periprosthetic hip fractures with intracortical anchorage might not be feasible in cases with bulky implants and/or poor bone stock. METHODS Rotational stability of new plate inserts with extracortical anchorage for cerclage fixation was measured and compared to the stability found using a standard technique in a biomechanical setup using a torsion testing machine. In a synthetic PUR bone model, transverse fractures were fixed distally using screws and proximally by wire cerclages attached to the plates using "new" (extracortical anchorage) or "standard" (intracortical anchorage) plate inserts. Time to fracture consolidation and complications were assessed in a consecutive series of 18 patients (18 female; mean age 81 years, range 55-92) with periprosthetic hip fractures (ten type B1, eight type C-Vancouver) treated with the new device between July 2003 and July 2010. RESULTS The "new" device showed a higher rotational stability than the "standard" technique (p < 0.001). Fractures showed radiographic consolidation after 14 ± 5 weeks (mean ± SD) postoperatively in patients. Revision surgery was necessary in four patients, unrelated to the new technique. CONCLUSION In periprosthetic hip fractures in which fixation with intracortical anchorage using conventional means might be difficult due to bulky revision stems and/or poor bone stock, the new device may be an addition to the range of existing implants.
Resumo:
BACKGROUND Vigorous sporting activity during the growth years is associated with an increased risk of having a cam-type deformity develop. The underlying cause of this osseous deformity is unclear. One may speculate whether this is caused by reactive bone apposition in the region of the anterosuperior head-neck junction or whether sports activity alters the shape of and growth in the growth plate. If the latter is true, then one would expect athletes to show an abnormal shape of the capital growth plate (specifically, the epiphyseal extension) before and/or after physeal closure. QUESTIONS/PURPOSES We therefore raised three questions: (1) Do adolescent basketball players show abnormal epiphyseal extension? (2) Does the epiphyseal extension differ before and after physeal closure? (3) Is abnormal epiphyseal extension associated with high alpha angles? METHODS We performed a case-control comparative analysis of young (age range, 9-22 years) male elite basketball athletes with age-matched nonathletes, substratified by whether they had open or closed physes. We measured epiphyseal extension on radial-sequence MRI cuts throughout the cranial hemisphere from 9 o'clock (posterior) to 3 o'clock (anterior). Epiphyseal extension was correlated to alpha angle measurements at the same points. RESULTS Epiphyseal extension was increased in all positions in the athletes compared with the control group. On average, athletes showed epiphyseal extension of 0.67 to 0.83 versus 0.53 to 0.71 in control subjects. In the control group epiphyseal extension was increased at all measurement points in hips after physeal closure compared with before physeal closure. In contrast, the subgroup of athletes with a closed growth plate only had increased epiphyseal extension at the 3 o'clock position compared with the athletes with an open [corrected] growth plate (0.64-0.70). We observed a correlation between an alpha angle greater than 55° and greater epiphyseal extension in the anterosuperior femoral head quadrant: the corresponding Spearman r values were 0.387 (all hips) and 0.285 (alpha angle>55°) for the aggregate anterosuperior quadrant. CONCLUSIONS These findings suggest that a cam-type abnormality in athletes is a consequence of an alteration of the growth plate rather than reactive bone formation. High-level sports activity during growth may be a new and distinct risk factor for a cam-type deformity.
Resumo:
Brushite and octacalcium phosphate (OCP) crystals are well-known precursors of hydroxylapatite (HAp), the main mineral found in bone. In this report, we present a new method for biomimicking brushite and OCP using single and double diffusion techniques. Brushite and OCP crystals were grown in an iota-carrageenan gel. The aggregates were analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD), infrared spectroscopy (IR) and thermal gravimetric analysis (TGA). SEM revealed different morphologies of brushite crystals from highly porous aggregates to plate-shaped forms. OCP crystals grown in iota-carrageenan showed a porous spherical shape different from brushite growth forms. The XRD method demonstrated that the single-diffusion method favors the formation of monoclinic brushite. In contrast, the double diffusion method was found to promote the formation of the triclinic octacalcium phosphate OCP phase. By combining the different parameters for crystal growth in carrageenan, such as ion concentration, gel pH and gel density, it is possible to modify the morphology of composite crystals, change the phase of calcium phosphate and modulate the amount of carrageenan inclusion in crystals. This study suggests that iota-carrageenan is a high-molecular-weight polysaccharide that is potentially applicable for controlling calcium phosphate crystallization.
Resumo:
OBJECTIVE To evaluate the role of the periosteum in preserving the buccal bone after ridge splitting and expansion with simultaneous implant placement. MATERIAL AND METHODS In 12 miniature pigs, the mandibular premolars and first molars were removed together with the interdental bone septa and the buccal bone. Three months later, ridge splitting and expansion of the buccal plate was performed with simultaneous placement of two titanium implants per quadrant. Access by a mucosal flap (MF) was prepared on test sides, while a mucoperiosteal flap (MPF) with complete denudation of the buccal bone was increased on control sides. After healing periods of six and 12 weeks, the animals were sacrificed for histologic and histometric evaluation. RESULTS In the MF group, all 16 implants were osseointegrated, while in the MPF group, four of 16 implants were lost. Noticeable differences of bone levels on the implant surface and of the bone crest (BC) were found between the MF and the MPF group. Buccally after 6 weeks, the median distance between the implant shoulder (IS) and the coronal-most bone on the implant (cBIC) was for the MF group -1.42 ± 0.42 mm and for the MPF group -4.80 ± 2.72 mm (P = 0.15). The median distance between the IS and the buccal BC was -1.24 ± 0.51 mm and -2.78 ± 1.98 mm (P = 0.12) for the MF and MPF group, respectively. After 12 weeks, median IS-cBIC was -2.12 ± 0.84 mm for MF and -7.19 mm for MPF, while IS-BC was -2.08 ± 0.79 mm for MF and -5.96 mm for MPF. After 6 weeks, the median buccal bone thickness for MF and MPF was 0.01 and 0 mm (P < 0.001) at IS, 1.48 ± 0.97 mm and 0 ± 0.77 mm (P = 0.07) at 2 mm apical to IS, and 2.12 ± 1.19 mm and 1.72 ± 01.50 mm (P = 0.86) at 4 mm apical to IS, respectively. After 12 weeks, buccal bone thickness in the MF group was 0 mm at IS, 0.21 mm at 2 mm apical to IS, and 2.56 mm at 4 mm apical to IS, whereas complete loss of buccal bone was measured from IS to 4 mm apical to IS for the MPF group. CONCLUSIONS In this ridge expansion model in miniature pigs, buccal bone volume was significantly better preserved when the periosteum remained attached to the bone.
Resumo:
OBJECTIVE Proximal femoral osteotomy with stable fixation and sufficient correction. Low complication rates due to exact preoperative planning. INDICATIONS Congenital or traumatic femoral neck pseudarthrosis. Coxa vara. CONTRAINDICATIONS None. In severe deformities, a single femoral osteotomy may not solve the problem; thus, additional correction, e.g., a pelvic osteotomy, is required. SURGICAL TECHNIQUE Correct planning of the correction angle. Lateral approach. Subperiosteal detachment of vastus lateralis muscle. Place guide wire on the femoral neck to judge anteversion. Insert positioning wire 5 mm distal to trochanteric physis. Insert 2.8 mm Kirschner wire in the femoral neck. Osteotomy of the femur after marking the rotation by Kirschner wires or oscillating saw. Slide LC plate over Kirschner wires. Replace Kirschner wires with screws. Reduction of the femoral shaft to the plate with bone forceps. Definitive fixation of the plate to the femoral shaft by cortex or locking screws. Readaptation of vastus lateralis muscle over the plate. POSTOPERATIVE MANAGEMENT Partial weightbearing for 4-6 weeks depending on the age of the patient without any external fixation (e. g. cast) is possible. RESULTS Recent studies support the authors' findings of sufficient correction and stable fixation after proximal femoral osteotomy with the LCP pediatric hip plate. Low complication rates and stable fixation.
Resumo:
PURPOSE To compare the initial stability and stability after fatigue of three different locking systems (Synthes(®), Stryker(®) and Medartis(®)) for mandibular fixation and reconstruction. METHOD Standard mandible locking plates with identical profile height (1,5 mm), comparable length and screws with identical diameter (2,0 mm) were used. Plates were fixed with six screws according a preparation protocol. Four point bending tests were then performed using artificial bone material to compare their initial stability and failure limit under realistic loading conditions. Loading of the plates was performed using of a servo hydraulic driven testing machine. The stiffness of the implant/bone construct was calculated using a linear regression on the experimental data included in a range of applied moment between 2 Nm and 6 Nm. RESULTS No statistical difference in the elastic stiffness was visible between the three types of plate. However, differences were observed between the systems concerning the maximal load supported. The Stryker and Synthes systems were able to support a significantly higher moment. CONCLUSION For clinical application all systems show good and reliable results. Practical aspects such as handling, possible angulation of screw fixation, possibility of screw/plate removal, etc. may favour one or the other plating system.
Resumo:
Biodegradable magnesium plate/screw osteosynthesis systems were implanted on the frontal bone of adult miniature pigs. The chosen implant geometries were based on existing titanium systems used for the treatment of facial fractures. The aim of this study was to evaluate the in vivo degradation and tissue response of the magnesium alloy WE43 with and without a plasma electrolytic surface coating. Of 14 animals, 6 received magnesium implants with surface modification (coated), 6 without surface modification (uncoated), and 2 titanium implants. Radiological examination of the skull was performed at 1, 4, and 8 weeks post-implantation. After euthanasia at 12 and 24 weeks, X-ray, computed tomography, and microfocus computed tomography analyses and histological and histomorphological examinations of the bone/implant blocks were performed. The results showed a good tolerance of the plate/screw system without wound healing disturbance. In the radiological examination, gas pocket formation was found mainly around the uncoated plates 4 weeks after surgery. The micro-CT and histological analyses showed significantly lower corrosion rates and increased bone density and bone implant contact area around the coated screws compared to the uncoated screws at both endpoints. This study shows promising results for the further development of coated magnesium implants for the osteosynthesis of the facial skeleton.
Resumo:
GOAL We present the development of a boneanchored port for the painless long-term hemodialytic treatment of patients with renal failure. This port is implanted behind the ear. METHODS The port was developed based on knowledge obtained from long-term experience with implantable hearing devices, which are firmly anchored to the bone behind the ear. This concept of bone anchoring was adapted to the requirements for a vascular access during hemodialysis. The investigational device is comprised of a base plate that is firmly fixed with bone screws to the bone behind the ear (temporal bone). A catheter leads from the base plate valve block through the internal jugular vein and into the right atrium. The valves are opened using a special disposable adapter, without any need to puncture the blood vessels. Between hemodialysis sessions the port is protected with a disposable cover. RESULTS Flow rate, leak tightness and purification were tested on mockups. Preoperative planning and the surgical procedure were verified in 15 anatomical human whole head specimens. CONCLUSION Preclinical evaluations demonstrated the technical feasibility and safety of the investigational device. SIGNIFICANCE Approximately 1.5 million people are treated with hemodialysis worldwide, and 25% of the overall cost of dialysis therapy results from vascular access problems. New approaches towards enhancing vascular access could potentially reduce the costs and complications of hemodialytic therapy.