Synthesis and characterization of polymers containing oligothiophenes

In the present work a series of thiophene oligomers of three and six thiophene units were synthesized, starting from thiophene, and characterized. Polymers containing these electroative side groups were then prepared by two strategies. The oligomers were attached to existing polymer systems and were connected to a polymerizable unit leading to monomer containing the oligothiophenes as side groups. Subsequently the properties of the monomers and the polymers were investigated. A butylcellulose derivative carrying terthienyl side chains (BCTTE, 26) was synthesized starting from cellulose acetate and 5-(2-chloroethyl)-2,2':5',2'-terthiophene (4). The polymer had a degree of substitution (DS) of the butyl and terthienyl side chains of DSbutyl = 1.9 and DSterth = 0.35, respectively. It was successfully spread on a Langmuir-Blodgett (LB) trough and then transferred to several solid substrates. X-rays reflectometry showed an ordered architecture of the cellulose backbones. However, the terthiophene side groups were found as isotropically aligned by polarized UV-Vis spectroscopy. When used as anode material in the electropolymerization of 3-pentylthiophene (28), polythiophene was grafted onto the cellulose backbone through the terthienyl side groups. The polythiophene chains showed an average anisotropic alignment of 20 % along the LB dipping direction, calculated by means of polarized UV-Vis spectroscopy. A second butylcellulose derivative carrying sexithienyl side chains (BCST) was synthesized and investigated, starting from butylcellulose and 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl p-toluensulfonate (7). The polymer showed formation of stable LB monolayers at the air-water interface, but its transfer onto solid substrates was not successful. A poly(p-phenylene-ethynylene) bearing sexithienyl side chains (BzAcST, 31) was prepared by reaction of the two monomers 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl 2,5-diiodobenzoate (15) and 2-[b', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2':5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl 2,5-diethynylbenzoate (18). The polymer was obtained as insoluble product. Upon oxidation with FeCl3 (doping) of the polymer suspension, BzAcST showed an electrical conductivity of ó = 2.5 . 10 -6 S/cm, a typical value for semiconductors. The IR spectrum of the doped polymer presented the diagnostic bands of oxidized sexithiophene in good agreement with literature results. Along with the monomer and polymer synthesis, an a,a '-disubstituted sexithiophene, b ', b ''-dipentyl-5,5'''-bis-(2-hydroxyethyl)-2,2':5',2':5',2'':5'',2'':5'',2'''-sexithiophene (6a),was synthesized and characterized. The UV-Vis absorption of the chromophore wasinvestigated as a function of temperature and different solvents, showing a blue-shift of the absorption maximum with increasing temperature and a red-shift changing the solvent from hexane to ethanol to toluene. Monitoring the change of the UV-Vis spectrum upon electrochemical oxidation, the oxidized chromophore showed a new broad absorption band, red shifted with respect to the p -p* transition of the neutral state. Upon reduction, the new band disappeared and the UV-Vis spectrum of the chromophore was restored. Such oxidation-reduction cycles were totally reversible. This feature, together with the absorption maximum falling in the visible region, makes this chromophore a suitable compound for the development of an electrochemical sensor.Attempts to polymerize acrylic monomers carrying sexythienyl side chains both via radical polymerization, as in the case of 2-[b ', b ''-dipentyl-5'''-(2-hydroxyethyl)-2,2': 5',2':5',2'':5'',2'':5'',2'''-sexithiophen-5-yl]-ethyl acrylate (8), and anionic polymerization, as in the case of 2-{b ', b ''-dipentyl-5'''-[2-(tertbutyldimethylsiloxy)ethyl]-2,2':5',2':5',2'':5'',2'': 5'',2''' -sexithiophen-5-yl}-ethylacrylate (29), were not successful, probably due to the steric hindrance of the oligothiophene side group. However, due to the time consuming and therefore restricted availability of the monomers, a screening of the polymerization conditions towards the formation of polymeric material was not possible.

Functionalization of hyperbranched polycarbosilanes - block copolymers and electrochemistry

Polycarbosilanes are a class of polymers at the interface between organic and inorganic chemistry. They are characterized by a high thermal and chemical inertness and high flexibility, especially pronounced for branched structures. Linear polycarbosilanes are well known as precursors for the preparation of SiCx ceramics. Additionally, more sophisticated architectures like dendrimers, hyperbranched polymers or block copolymers have been the subject of research for more than a decade. The scope of this work was to expand the properties and fields of application for polycarbosilane-containing structures. Thus, the work is divided in two major parts. The first part covers the synthesis and characterization of hyperbranched polycarbosilanes containing organometallic moieties. Hyperbranched poly-carbosilanes were synthesized using hydrosilylation of diallylmethylsilane and methyldiundecenylsilane. The degree of branching for polydiallymethylsilane was determined using standard 1H-NMR spectroscopy. The functional building blocks ferrocenyldimethylsilane and diferrocenylmethylsilane were synthesized which contain an isolated ferrocene unit or two ferrocenes bridged by silicon, respectively. Hyperbranched polycarbosilanes functionalized with ferrocenyl moieties were synthesized by modification of preformed polymers or by copolymerization of AB2 carbosilane monomers with AX-type ferrocenylsilanes. Polymers with Mn = 2500-9000g/mol and ferrocene contents of up to 67wt% were obtained. Electrochemical characterization by cyclic voltammetry revealed that polymers functionalized with isolated ferrocene units showed a single reversible oxidation wave, while voltammograms for polymers functionalized with diferrocenyl silane exhibited two well-separated reversible oxidation-reduction waves. This shows that the polymer bound ferrocenes bridged by silicon are electronically communicating and thus oxidation of the first ferrocene shifts the oxidation potential for the adjacent one. The polymers were utilized successfully for the preparation of modified electrodes with persistent and reproducible electrochemical response in organic solvents as well as in aqueous solution. The presented work has proven that ferrocenyl-functionalized hyperbranched polymers exhibit similar electrochemical properties as the analogous dendrimers. In a further approach it was shown that hyperbranched polymers containing organometallic moieties can be synthesized by polymerization of a new ferrocene-containing AB2 monomer - diallylferrocenylsilane. The second part of this work is dedicated to the preparation of core-functional hyperbranched polycarbosilanes. Low molecular weight ambifunctional molecules were synthesized that contain double bonds for the attachment of a polycarbosilane polymer as well as a second functionality available for further reaction and modification. Reactive vinyl groups in the core molecule allow an efficient attachment of hyperbranched polycarbosilane which was proven by MALDI-ToF and GPC. In combination with slow monomer addition techniques molecular weight and polydispersity of the polymers were controlled successfully. Core-functional polymers were characterized by NMR-spectroscopy, MALDI-ToF and GPC. Polymers with polydispersities <2 and molecular weights up to 5300g/mol were obtained. Transformation of the double bonds of the carbosilane was demonstrated with various silanes using hydrosilylation reaction or hydrogenation. Additionally, the core-functionality was varied resulting in polymers with bromo-, phthalimide-, amine- or azide moieties. Thus, a versatile synthetic strategy was developed that allows the synthesis of tailor-made polymers.A promising approach is the application of the polymer building blocks in copolymer synthesis. Bisglycidolization of amine-functional polycarbosilanes produces macro-initiators that are suitable for the multibranching-ring opening polymerization of glycidol. This experiments lead to the first example of hyperbranched-hyperbranched amphiphilic block copolymers, hb-PG-b-hb-PCS. Furthermore, the implementation of copper-catalyzed cycloaddition between azide-functional polycarbosilane and alkyne-functional poly(ethoxyethyl glycidylether) resulted in linear-hyperbranched block copolymers. The facile removal of acetal protecting groups provided convenient access to lin-PG-b-hb-PCS.

The sensitivity of the photostationary state of NOx and its implication for the oxidation capacity in a semi-rural and boreal forest region

Für das Vermögen der Atmosphäre sich selbst zu reinigen spielen Stickstoffmonoxid (NO) und Stickstoffdioxid (NO2) eine bedeutende Rolle. Diese Spurengase bestimmen die photochemische Produktion von Ozon (O3) und beeinflussen das Vorkommen von Hydroxyl- (OH) und Nitrat-Radikalen (NO3). Wenn tagsüber ausreichend Solarstrahlung und Ozon vorherrschen, stehen NO und NO2 in einem schnellen photochemischen Gleichgewicht, dem „Photostationären Gleichgewichtszustand“ (engl.: photostationary state). Die Summe von NO und NO2 wird deshalb als NOx zusammengefasst. Vorhergehende Studien zum photostationären Gleichgewichtszustand von NOx umfassen Messungen an unterschiedlichsten Orten, angefangen bei Städten (geprägt von starken Luftverschmutzungen), bis hin zu abgeschiedenen Regionen (geprägt von geringeren Luftverschmutzungen). Während der photochemische Kreislauf von NO und NO2 unter Bedingungen erhöhter NOx-Konzentrationen grundlegend verstanden ist, gibt es in ländlicheren und entlegenen Regionen, welche geprägt sind von niedrigeren NOx-Konzetrationen, signifikante Lücken im Verständnis der zugrundeliegenden Zyklierungsprozesse. Diese Lücken könnten durch messtechnische NO2-Interferenzen bedingt sein - insbesondere bei indirekten Nachweismethoden, welche von Artefakten beeinflusst sein können. Bei sehr niedrigen NOx-Konzentrationen und wenn messtechnische NO2-Interferenzen ausgeschlossen werden können, wird häufig geschlussfolgert, dass diese Verständnislücken mit der Existenz eines „unbekannten Oxidationsmittels“ (engl.: unknown oxidant) verknüpft ist. Im Rahmen dieser Arbeit wird der photostationäre Gleichgewichtszustand von NOx analysiert, mit dem Ziel die potenzielle Existenz bislang unbekannter Prozesse zu untersuchen. Ein Gasanalysator für die direkte Messung von atmosphärischem NO¬2 mittels laserinduzierter Fluoreszenzmesstechnik (engl. LIF – laser induced fluorescence), GANDALF, wurde neu entwickelt und während der Messkampagne PARADE 2011 erstmals für Feldmessungen eingesetzt. Die Messungen im Rahmen von PARADE wurden im Sommer 2011 in einem ländlich geprägten Gebiet in Deutschland durchgeführt. Umfangreiche NO2-Messungen unter Verwendung unterschiedlicher Messtechniken (DOAS, CLD und CRD) ermöglichten einen ausführlichen und erfolgreichen Vergleich von GANDALF mit den übrigen NO2-Messtechniken. Weitere relevante Spurengase und meteorologische Parameter wurden gemessen, um den photostationären Zustand von NOx, basierend auf den NO2-Messungen mit GANDALF in dieser Umgebung zu untersuchen. Während PARADE wurden moderate NOx Mischungsverhältnisse an der Messstelle beobachtet (10^2 - 10^4 pptv). Mischungsverhältnisse biogener flüchtige Kohlenwasserstoffverbindungen (BVOC, engl.: biogenic volatile organic compounds) aus dem umgebenden Wald (hauptsächlich Nadelwald) lagen in der Größenordnung 10^2 pptv vor. Die Charakteristiken des photostationären Gleichgewichtszustandes von NOx bei niedrigen NOx-Mischungsverhältnissen (10 - 10^3 pptv) wurde für eine weitere Messstelle in einem borealen Waldgebiet während der Messkampagne HUMPPA-COPEC 2010 untersucht. HUMPPA–COPEC–2010 wurde im Sommer 2010 in der SMEARII-Station in Hyytiälä, Süd-Finnland, durchgeführt. Die charakteristischen Eigenschaften des photostationären Gleichgewichtszustandes von NOx in den beiden Waldgebieten werden in dieser Arbeit verglichen. Des Weiteren ermöglicht der umfangreiche Datensatz - dieser beinhaltet Messungen von relevanten Spurengasen für die Radikalchemie (OH, HO2), sowie der totalen OH-Reaktivität – das aktuelle Verständnis bezüglich der NOx-Photochemie unter Verwendung von einem Boxmodell, in welches die gemessenen Daten als Randbedingungen eingehen, zu überprüfen und zu verbessern. Während NOx-Konzentrationen in HUMPPA-COPEC 2010 niedriger sind, im Vergleich zu PARADE 2011 und BVOC-Konzentrationen höher, sind die Zyklierungsprozesse von NO und NO2 in beiden Fällen grundlegend verstanden. Die Analyse des photostationären Gleichgewichtszustandes von NOx für die beiden stark unterschiedlichen Messstandorte zeigt auf, dass potenziell unbekannte Prozesse in keinem der beiden Fälle vorhanden sind. Die aktuelle Darstellung der NOx-Chemie wurde für HUMPPA-COPEC 2010 unter Verwendung des chemischen Mechanismus MIM3* simuliert. Die Ergebnisse der Simulation sind konsistent mit den Berechnungen basierend auf dem photostationären Gleichgewichtszustand von NOx.