Pore structure and column efficiency of silica monoliths in high performance liquid chromatography (HPLC)

Five different methods were critically examined to characterize the pore structure of the silica monoliths. The mesopore characterization was performed using: a) the classical BJH method of nitrogen sorption data, which showed overestimated values in the mesopore distribution and was improved by using the NLDFT method, b) the ISEC method implementing the PPM and PNM models, which were especially developed for monolithic silicas, that contrary to the particulate supports, demonstrate the two inflection points in the ISEC curve, enabling the calculation of pore connectivity, a measure for the mass transfer kinetics in the mesopore network, c) the mercury porosimetry using a new recommended mercury contact angle values. rnThe results of the characterization of mesopores of monolithic silica columns by the three methods indicated that all methods were useful with respect to the pore size distribution by volume, but only the ISEC method with implemented PPM and PNM models gave the average pore size and distribution based on the number average and the pore connectivity values.rnThe characterization of the flow-through pore was performed by two different methods: a) the mercury porosimetry, which was used not only for average flow-through pore value estimation, but also the assessment of entrapment. It was found that the mass transfer from the flow-through pores to mesopores was not hindered in case of small sized flow-through pores with a narrow distribution, b) the liquid penetration where the average flow-through pore values were obtained via existing equations and improved by the additional methods developed according to Hagen-Poiseuille rules. The result was that not the flow-through pore size influences the column bock pressure, but the surface area to volume ratio of silica skeleton is most decisive. Thus the monolith with lowest ratio values will be the most permeable. rnThe flow-through pore characterization results obtained by mercury porosimetry and liquid permeability were compared with the ones from imaging and image analysis. All named methods enable a reliable characterization of the flow-through pore diameters for the monolithic silica columns, but special care should be taken about the chosen theoretical model.rnThe measured pore characterization parameters were then linked with the mass transfer properties of monolithic silica columns. As indicated by the ISEC results, no restrictions in mass transfer resistance were noticed in mesopores due to their high connectivity. The mercury porosimetry results also gave evidence that no restrictions occur for mass transfer from flow-through pores to mesopores in the small scaled silica monoliths with narrow distribution. rnThe prediction of the optimum regimes of the pore structural parameters for the given target parameters in HPLC separations was performed. It was found that a low mass transfer resistance in the mesopore volume is achieved when the nominal diameter of the number average size distribution of the mesopores is appr. an order of magnitude larger that the molecular radius of the analyte. The effective diffusion coefficient of an analyte molecule in the mesopore volume is strongly dependent on the value of the nominal pore diameter of the number averaged pore size distribution. The mesopore size has to be adapted to the molecular size of the analyte, in particular for peptides and proteins. rnThe study on flow-through pores of silica monoliths demonstrated that the surface to volume of the skeletons ratio and external porosity are decisive for the column efficiency. The latter is independent from the flow-through pore diameter. The flow-through pore characteristics by direct and indirect approaches were assessed and theoretical column efficiency curves were derived. The study showed that next to the surface to volume ratio, the total porosity and its distribution of the flow-through pores and mesopores have a substantial effect on the column plate number, especially as the extent of adsorption increases. The column efficiency is increasing with decreasing flow through pore diameter, decreasing with external porosity, and increasing with total porosity. Though this tendency has a limit due to heterogeneity of the studied monolithic samples. We found that the maximum efficiency of the studied monolithic research columns could be reached at a skeleton diameter of ~ 0.5 µm. Furthermore when the intention is to maximize the column efficiency, more homogeneous monoliths should be prepared.rn

Surface-plasmon optical and electrochemical characterization of biofunctional surface architectures

The development and characterization of biomolecule sensor formats based on the optical technique Surface Plasmon Resonance (SPR) Spectroscopy and electrochemical methods were investigated. The study can be divided into two parts of different scope. In the first part new novel detection schemes for labeled targets were developed on the basis of the investigations in Surface-plamon Field Enhanced Spectroscopy (SPFS). The first one is SPR fluorescence imaging formats, Surface-plamon Field Enhanced Fluorescence Microscopy (SPFM). Patterned self assembled monolayers (SAMs) were prepared and used to direct the spatial distribution of biomolecules immobilized on surfaces. Here the patterned monolayers would serve as molecular templates to secure different biomolecules to known locations on a surface. The binding processed of labeled target biomolecules from solution to sensor surface were visually and kinetically recorded by the fluorescence microscope, in which fluorescence was excited by the evanescent field of propagating plasmon surface polaritons. The second format which also originates from SPFS technique, Surface-plamon Field Enhanced Fluorescence Spectrometry (SPFSm), concerns the coupling of a fluorometry to normal SPR setup. A spectrograph mounted in place of photomultiplier or microscope can provide the information of fluorescence spectrum as well as fluorescence intensity. This study also firstly demonstrated the analytical combination of surface plasmon enhanced fluorescence detection with analyte tagged by semiconducting nano- crystals (QDs). Electrochemically addressable fabrication of DNA biosensor arrays in aqueous environment was also developed. An electrochemical method was introduced for the directed in-situ assembly of various specific oligonucleotide catcher probes onto different sensing elements of a multi-electrode array in the aqueous environment of a flow cell. Surface plasmon microscopy (SPM) is utilized for the on-line recording of the various functionalization steps. Hybridization reactions between targets from solution to the different surface-bound complementary probes are monitored by surface-plasmon field-enhanced fluorescence microscopy (SPFM) using targets that are either labeled with organic dyes or with semiconducting quantum dots for color-multiplexing. This study provides a new approach for the fabrication of (small) DNA arrays and the recording and quantitative evaluation of parallel hybridization reactions. In the second part of this work, the ideas of combining the SP optical and electrochemical characterization were extended to tethered bilayer lipid membrane (tBLM) format. Tethered bilayer lipid membranes provide a versatile model platform for the study of many membrane related processes. The thiolipids were firstly self-assembled on ultraflat gold substrates. Fusion of the monolayers with small unilamellar vesicles (SUVs) formed the distal layer and the membranes thus obtained have the sealing properties comparable to those of natural membranes. The fusion could be monitored optically by SPR as an increase in reflectivity (thickness) upon formation of the outer leaflet of the bilayer. With EIS, a drop in capacitance and a steady increase in resistance could be observed leading to a tightly sealing membrane with low leakage currents. The assembly of tBLMs and the subsequent incorporation of membrane proteins were investigated with respect to their potential use as a biosensing system. In the case of valinomycin the potassium transport mediated by the ion carrier could be shown by a decrease in resistance upon increasing potassium concentration. Potential mediation of membrane pores could be shown for the ion channel forming peptide alamethicin (Alm). It was shown that at high positive dc bias (cis negative) Alm channels stay at relatively low conductance levels and show higher permeability to potassium than to tetramethylammonium. The addition of inhibitor amiloride can partially block the Alm channels and results in increase of membrane resistance. tBLMs are robust and versatile model membrane architectures that can mimic certain properties of biological membranes. tBLMs with incorporated lipopolysaccharide (LPS) and lipid A mimicking bacteria membranes were used to probe the interactions of antibodies against LPS and to investigate the binding and incorporation of the small antimicrobial peptide V4. The influence of membrane composition and charge on the behavior of V4 was also probed. This study displays the possibility of using tBLM platform to record and valuate the efficiency or potency of numerous synthesized antimicrobial peptides as potential drug candidates.

Mapping the elastic response of epithelial apical cell membranes suspended across porous array

As the elastic response of cell membranes to mechanical stimuli plays a key role in various cellular processes, novel biophysical strategies to quantify the elasticity of native membranes under physiological conditions at a nanometer scale are gaining interest. In order to investigate the elastic response of apical membranes, elasticity maps of native membrane sheets, isolated from MDCK II (Madine Darby Canine kidney strain II) epithelial cells, were recorded by local indentation with an Atomic Force Microscope (AFM). To exclude the underlying substrate effect on membrane indentation, a highly ordered gold coated porous array with a pore diameter of 1.2 μm was used to support apical membranes. Overlays of fluorescence and AFM images show that intact apical membrane sheets are attached to poly-D-lysine coated porous substrate. Force indentation measurements reveal an extremely soft elastic membrane response if it is indented at the center of the pore in comparison to a hard repulsion on the adjacent rim used to define the exact contact point. A linear dependency of force versus indentation (-dF/dh) up to 100 nm penetration depth enabled us to define an apparent membrane spring constant (kapp) as the slope of a linear fit with a stiffness value of for native apical membrane in PBS. A correlation between fluorescence intensity and kapp is also reported. Time dependent hysteresis observed with native membranes is explained by a viscoelastic solid model of a spring connected to a Kelvin-Voight solid with a time constant of 0.04 s. No hysteresis was reported with chemically fixated membranes. A combined linear and non linear elastic response is suggested to relate the experimental data of force indentation curves to the elastic modulus and the membrane thickness. Membrane bending is the dominant contributor to linear elastic indentation at low loads, whereas stretching is the dominant contributor for non linear elastic response at higher loads. The membrane elastic response was controlled either by stiffening with chemical fixatives or by softening with F-actin disrupters. Overall, the presented setup is ideally suitable to study the interactions of the apical membrane with the underlying cytoskeleton by means of force indentation elasticity maps combined with fluorescence imaging.

Kinetic and affinity analysis of hybridization reactions between PNA probes and DNA targets using surface plasmon field-enhanced fluorescence spectroscopy (SPFS)

Sequenz spezifische biomolekulare Analyseverfahren erweisen sich gerade im Hinblick auf das Humane Genom Projekt als äußerst nützlich in der Detektion von einzelnen Nukleotid Polymorphismen (SNPs) und zur Identifizierung von Genen. Auf Grund der hohen Anzahl von Basenpaaren, die zu analysieren sind, werden sensitive und effiziente Rastermethoden benötigt, welche dazu fähig sind, DNA-Proben in einer geeigneten Art und Weise zu bearbeiten. Die meisten Detektionsarten berücksichtigen die Interaktion einer verankerten Probe und des korrespondierenden Targets mit den Oberflächen. Die Analyse des kinetischen Verhaltens der Oligonukleotide auf der Sensoroberfläche ist infolgedessen von höchster Wichtigkeit für die Verbesserung bereits bekannter Detektions - Schemata. In letzter Zeit wurde die Oberflächen Plasmonen feld-verstärkte Fluoreszenz Spektroskopie (SPFS) entwickelt. Sie stellt eine kinetische Analyse - und Detektions - Methode dar, die mit doppelter Aufzeichnung, d.h. der Änderung der Reflektivität und des Fluoreszenzsignals, für das Interphasen Phänomen operiert. Durch die Verwendung von SPFS können Kinetikmessungen für die Hybridisierung zwischen Peptid Nukleinsäure (PNA), welche eine synthetisierte Nukleinsäure DNA imitiert und eine stabilere Doppelhelix formt, und DNA auf der Sensoroberfläche ausgeführt werden. Mittels einzel-, umfassend-, und titrations- Experimenten sowohl mit einer komplementär zusammenpassenden Sequenz als auch einer mismatch Sequenz können basierend auf dem Langmuir Modell die Geschwindigkeitskonstanten für die Bindungsreaktion des oligomer DNA Targets bzw. des PCR Targets zur PNA ermittelt werden. Darüber hinaus wurden die Einflüsse der Ionenstärke und der Temperatur für die PNA/DNA Hybridisierung in einer kinetischen Analyse aufgezeigt.

Functional polymer coatings — My-Patterning and My-Analysis

In dieser Arbeit werden Strukturen beschrieben, die mit Polymeren auf Oberflächen erzeugt wurden. Die Anwendungen reichen von PMMA und PNIPAM Polymerbürsten, über die Restrukturierung von Polystyrol durch Lösemittel bis zu 3D-Strukturen, die aus PAH/ PSS Polyelektrolytmultischichten bestehen. Im ersten Teil werden Polymethylmethacrylat (PMMA) Bürsten in der ionischen Flüssigkeit 1-Butyl-3-Methylimidazolium Hexafluorophospat ([Bmim][PF6]) durch kontrollierte radikalische Polymerisation (ATRP) hergestellt. Kinetische Untersuchungen zeigten ein lineares und dichtes Bürstenwachstum mit einer Wachstumsrate von 4600 g/mol pro nm. Die durchschnittliche Pfropfdichte betrug 0.36 µmol/m2. Als Anwendung wurden Mikrotropfen bestehend aus der ionischen Flüssigkeit, Dimethylformamid und dem ATRP-Katalysator benutzt, um in einer definierten Geometrie Polymerbürsten auf Silizium aufzubringen. Auf diese Weise lässt sich eine bis zu 13 nm dicke Beschichtung erzeugen. Dieses Konzept ist durch die Verdampfung des Monomers Methylmethacrylat (MMA) limitiert. Aus einem 1 µl großen Tropfen aus ionischer Flüssigkeit und MMA (1:1) verdampft MMA innerhalb von 100 s. Daher wurde das Monomer sequentiell zugegeben. Der zweite Teil konzentriert sich auf die Strukturierung von Oberflächen mit Hilfe einer neuen Methode: Tintendruck. Ein piezoelektrisch betriebenes „Drop-on-Demand“ Drucksystem wurde verwendet, um Polystyrol mit 0,4 nl Tropfen aus Toluol zu strukturieren. Die auf diese Art und Weise gebildeten Mikrokrater können Anwendung als Mikrolinsen finden. Die Brennweite der Mikrolinsen kann über die Anzahl an Tropfen, die für die Strukturierung verwendet werden, eingestellt werden. Theoretisch und experimentell wurde die Brennweite im Bereich von 4,5 mm bis 0,21 mm ermittelt. Der zweite Strukturierungsprozess nutzt die Polyelektrolyte Polyvinylamin-Hydrochlorid (PAH) und Polystyrolsulfonat (PSS), um 3D-Strukturen wie z.B. Linien, Schachbretter, Ringe, Stapel mit einer Schicht für Schicht Methode herzustellen. Die Schichtdicke für eine Doppelschicht (DS) liegt im Bereich von 0.6 bis 1.1 nm, wenn NaCl als Elektrolyt mit einer Konzentration von 0,5 mol/l eingesetzt wird. Die Breite der Strukturen beträgt im Mittel 230 µm. Der Prozess wurde erweitert, um Nanomechanische Cantilever Sensoren (NCS) zu beschichten. Auf einem Array bestehend aus acht Cantilevern wurden je zwei Cantilever mit fünf Doppelschichten PAH/ PSS und je zwei Cantilever mit zehn Doppelschichten PAH/ PSS schnell und reproduzierbar beschichtet. Die Massenänderung für die individuellen Cantilever war 0,55 ng für fünf Doppelschichten und 1,08 ng für zehn Doppelschichten. Der daraus resultierende Sensor wurde einer Umgebung mit definierter Luftfeuchtigkeit ausgesetzt. Die Cantilever verbiegen sich durch die Ausdehnung der Beschichtung, da Wasser in das Polymer diffundiert. Eine maximale Verbiegung von 442 nm bei 80% Luftfeuchtigkeit wurde für die mit zehn Doppelschichten beschichteten Cantilever gefunden. Dies entspricht einer Wasseraufnahme von 35%. Zusätzlich konnte aus den Verbiegungsdaten geschlossen werden, dass die Elastizität der Polyelektrolytmultischichten zunimmt, wenn das Polymer gequollen ist. Das thermische Verhalten in Wasser wurde im nächsten Teil an nanomechanischen Cantilever Sensoren, die mit Poly(N-isopropylacrylamid)bürsten (PNIPAM) und plasmapolymerisiertem N,N-Diethylacrylamid beschichtet waren, untersucht. Die Verbiegung des Cantilevers zeigte zwei Bereiche: Bei Temperaturen kleiner der niedrigsten kritischen Temperatur (LCST) ist die Verbiegung durch die Dehydration der Polymerschicht dominiert und bei Temperaturen größer der niedrigsten kritischen Temperatur (LCST) reagiert der Cantilever Sensor überwiegend auf Relaxationsprozesse innerhalb der kollabierten Polymerschicht. Es wurde gefunden, dass das Minimum in der differentiellen Verbiegung mit der niedrigsten kritischen Temperatur von 32°C und 44°C der ausgewählten Polymeren übereinstimmt. Im letzten Teil der Arbeit wurden µ-Reflektivitäts- und µ-GISAXS Experimente eingeführt als neue Methoden, um mikrostrukturierte Proben wie NCS oder PEM Linien mit Röntgenstreuung zu untersuchen. Die Dicke von jedem individuell mit PMMA Bürsten beschichtetem NCS ist im Bereich von 32,9 bis 35,2 nm, was mit Hilfe von µ-Reflektivitätsmessungen bestimmt wurde. Dieses Ergebnis kann mit abbildender Ellipsometrie als komplementäre Methode mit einer maximalen Abweichung von 7% bestätigt werden. Als zweites Beispiel wurde eine gedruckte Polyelektrolytmultischicht aus PAH/PSS untersucht. Die Herstellungsprozedur wurde so modifiziert, dass Goldnanopartikel in die Schichtstruktur eingebracht wurden. Durch Auswertung eines µ-GISAXS Experiments konnte der Einbau der Partikel identifiziert werden. Durch eine Anpassung mit einem Unified Fit Modell wurde herausgefunden, dass die Partikel nicht agglomeriert sind und von einer Polymermatrix umgeben sind.