Inorganic-organic hybrid polymers: Solution-processible coating materials for defined surface functionalization

A new class of inorganic-organic hybrid polymers could successfully been prepared by the combination of different polymerization techniques. The access to a broad range of organic polymers incorporated into the hybrid polymer was realized using two independent approaches.rnIn the first approach a functional poly(silsesquioxane) (PSSQ) network was pre-formed, which was capable to initiate a controlled radical polymerization to graft organic vinyl-type monomers from the PSSQ precursor. As controlled radical polymerization techniques atom transfer radical polymerization (ATRP), as well as reversible addition fragmentation chain transfer (RAFT) polymerization could be used after defined tuning of the PSSQ precursor either toward a PSSQ macro-initiator or to a PSSQ macro-chain-transfer-agent. The polymerization pathway, consisting of polycondensation of trialkoxy-silanes followed by grafting-from polymerization of different monomers, allowed synthesis of various functional hybrid polymers. A controlled synthesis of the PSSQ precursors could successfully be performed using a microreactor setup; the molecular weight could be adjusted easily while the polydispersity index could be decreased well below 2.rnThe second approach aimed to incorporate differently derived organic polymers. As examples, polycarbonate and poly(ethylene glycol) were end-group-modified using trialkoxysilanes. After end-group-functionalization these organic polymers could be incorporated into a PSSQ network.rnThese different hybrid polymers showed extraordinary coating abilities. All polymers could be processed from solution by spin-coating or dip-coating. The high amount of reactive silanol moieties in the PSSQ part could be cross-linked after application by annealing at 130° for 1h. Not only cross-linking of the whole film was achieved, which resulted in mechanical interlocking with the substrate, also chemical bonds to metal or metal oxide surfaces were formed. All coating materials showed high stability and adhesion onto various underlying materials, reaching from metals (like steel or gold) and metal oxides (like glass) to plastics (like polycarbonate or polytetrafluoroethylene).rnAs the material and the synthetic pathway were very tolerant toward different functionalities, various functional monomers could be incorporated in the final coating material. The incorporation of N-isopropylacrylamide yielded in temperature-responsive surface coatings, whereas the incorporation of redox-active monomers allowed the preparation of semi-conductive coatings, capable to produce smooth hole-injection layers on transparent conductive electrodes used in optoelectronic devices.rnThe range of possible applications could be increased tremendously by incorporation of reactive monomers, capable to undergo fast and quantitative conversions by polymer-analogous reactions. For example, grafting active esters from a PSSQ precursor yielded a reactive surface coating after application onto numerous substrates. Just by dipping the coated substrate into a solution of a functionalized amine, the desired function could be immobilized at the interface as well as throughout the whole film. The obtained reactive surface coatings could be used as basis for different functional coatings for various applications. The conversion with specifically tuned amines yielded in surfaces with adjustable wetting behaviors, switchable wetting behaviors or as recognition element for surface-oriented bio-analytical devices. The combination of hybrid materials with orthogonal reactivities allowed for the first time the preparation of multi-reactive surfaces which could be functionalized sequentially with defined fractions of different groups at the interface. rnThe introduced concept to synthesis functional hybrid polymers unifies the main requirements on an ideal coating material. Strong adhesion on a wide range of underlying materials was achieved by secondary condensation of the PSSQ part, whereas the organic part allowed incorporation of various functionalities. Thus, a flexible platform to create functional and reactive surface coatings was achieved, which could be applied to different substrates. rn

Synthesis and investigation of functional polymer materials

Funktionelle Materialien sind in einer Vielzahl von Materialklassen wie Polymeren, Biomaterialien, Gläsern, Metallen, Keramiken und Verbundwerkstoffen anzutreffen. Sie besitzen eine spezifische, intrinsische Funktion, welche auf dem zu Grunde liegenden Design der Verbindung beruht. In dieser Dissertation wurden zwei funktionelle Materialien studiert: ein durch Phosphonatadditive mechanisch verstärktes Epoxidharz und protonenleitende Blockcopolymere, welche Potential für den Einsatz in Brennstoffzellen besitzen. Die Materialien wurden vorranging mittels Festkörper Kernspinresonanzspektroskopie (NMR) untersucht, welche sich besonders für die Untersuchung der lokalen Struktur und Dynamik amorpher Polymere eignet.rnrnPhosphonate sind eine neue Klasse sogenannter molekularer Verstärker, die die mechanischen und thermischen Kennzahlen geeigneter Epoxidharze erhöhen. Es wurde eine Reihe von Phosphonatderivaten synthetisiert um systematische den Effekt der chemischen Struktur und des Aushärteprozesses auf die Eigenschaften eines Modellepoxidharzes zu untersuchen. Die Aufklärung des Verstärkungsmechanismus ergab, dass die Phosphonate währen der thermischen Aushärtung des Epoxidharzes die Aminofunktionalitäten des Härters alkylieren. Dies führt zu der Bildung von homogen verteilten, positiven Ladungen auf der Polymerkette, während negative Phosphonatanionen als Gegenionen wirken. Es konnte gezeigt werden, dass die Struktur des Additivs einen entscheidenden Einfluss auf die Eigenschaften des ausgehärteten Epoxidharzes sowie seine Alterung, d.h. den allmählichen Verlust der Verstärkung, hat.rnrnDes Weiteren wurde eine Serie von sulfonierten Blockcopolymeren synthetisiert. Es handelte sich hierbei um Multiblockcopolyimide, wobei die Polymerketten aus einer alternierenden Sequenz von sulfonierten (hydrophilen) und unsulfonierten (hydrophoben) Blöcken bestanden. Diese Polymere bilden nach einem ‚solvent cast‘ Prozess feste, duktile und transparente Membrane. Sulfonierte Blockcopolymermembrane zeigten im Vergleich mit statistisch sulfonierten Vergleichssubstanzen eine erhöhte Leitfähigkeit, sowie eine erhöhte Wasseraufnahme. Dies wurde auf eine bessere Phasenseparation im Festkörper zurückgeführt. Die Morphologie der Filme war eindeutig anisotrop und stark abhängig von der Blocklänge der Polymere. Durch diverse Festkörper-NMR Methoden konnte gezeigt werden, dass die Protonenmobilität in den Membranen von der betrachteten Längenskala abhängig ist und nicht notwendigerweise mit der makroskopisch beobachteten Leitfähigkeit korreliert.

Graphene based electrode materials for solar cell and electrochemical oxygen reduction

Diese Arbeit hat viele beispiellose synthetische Ansätze für neuartige Verbundwerkstoffe Graphen-und stickstoffhaltigen graphitischen Materialien erforscht. Die erhaltenen Materialien wurden als den transparenten Elektroden der Solarzellen, die freistehenden Elektroden mit verbesserter mechanischer Festigkeit, und die Kathoden der Brennstoffzellen der Sauerstoffreduktion aufgebracht.rnAlle Ergebnisse haben eindeutig das große Potenzial von Graphen basierenden Materialien und stickstoffhaltigen graphitische Kohlenstoffe als neuartige Elektrodenmaterialien für neue Energie-Geräten demonstriert.